Filters
total: 3245
filtered: 477
-
Catalog
- Publications 939 available results
- Journals 14 available results
- Conferences 1 available results
- Publishing Houses 7 available results
- People 47 available results
- Inventions 8 available results
- Projects 7 available results
- Laboratories 3 available results
- Research Equipment 5 available results
- e-Learning Courses 48 available results
- Events 20 available results
- Open Research Data 2146 available results
Chosen catalog filters
Search results for: MOM
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 150 mm stroke subjected only to a mass load of 640 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 900 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 300 mm stroke subjected only to a mass load of 2570 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 150 mm stroke subjected only to a mass load of 2570 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 100 mm stroke subjected only to a mass load of 750 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 300 mm stroke subjected only to a mass load of 1040 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 100 mm stroke subjected only to a mass load of 1530 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 150 mm stroke subjected only to a mass load of 1640 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 1100 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 2570 g
Open Research DataThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Results of OM examination of acrylic bone cements incorporating various components
Open Research DataThe database contains the images of the microstructure of modified bone cements observed on the cross-section with the optical microscope (OM). The following modifications were evaluated: the addition of biodegradable components (including chitosan, cellulose, tricalcium phosphate, polydioxanone or magnesium), the addition of bioactive components (bioglasses)...
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - 3D fracture scan
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
Frequency Response Functions for Sandvik CoroBore 825 XL boring tool, 733 mm
Open Research DataFrequency Response Functions (FRF) obtained for Sandvik CoroBore® 825 XL mounted at WHN 13-15 TOS VARNSDORF CNC machine at the minimum extension of the spindle adaptor. Tool set to bore a hole with a diameter 733mm
-
EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
UV-VIS spectra of adsorption of methyl orange (MO) and methylene blue (MB) by porous carbon material
Open Research DataThis dataset contains UV-VIS spectra of adsorption of dyes: methyl orange (MO) and methylene blue (MB) by porous carbon material.
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - CMOD - force record, a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 60 mm) - CMOD - force record, a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 50 mm) - CMOD - force record, a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
Raw data for the paper "Mutually polarizable QM/MM model with in situ optimized localized basis functions"
Open Research DataThis dataset contains raw data used to generate plots in the paper Mutually polarizable QM/MM model with in situ optimized localized basis functions. The paper is devoted to a second generation of the TINKTEP model -- an QM/MM approach combining linear-scaling DFT (ONETEP) and a polarizable force field (AMOEBA).
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - CMOD - force record, a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
The microstructure of AA5754 alloy under corrosion in alkaline media (pH=11) with 20 mM of various carboxylic acids
Open Research DataThis dataset contains scanning electron microscopy (SEM) micrographs taken for polished aluminum AA5754 alloy samples, exposed for 100 min in bicarbonate buffer (pH=11) with the addition of 20 mM of carboxylic acids, namely: citric acid, malic acid, maleic acid, succinic acid, tartaric acid, tricarballylic acid and serine. The goal of this study was...
-
The microstructure of AA5754 alloy under corrosion in alkaline media (pH=11) with 4.5 mM of various carboxylic acids
Open Research DataThis dataset contains scanning electron microscopy (SEM) micrographs taken for polished aluminum AA5754 alloy samples, exposed for 100 min in bicarbonate buffer (pH=11) with the addition of 4.5 mM of carboxylic acids, namely: citric acid, malic acid, maleic acid, succinic acid, tartaric acid, tricarballylic acid and serine. The goal of this study was...
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 10 mm
Open Research DataOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 14 mm
Open Research DataOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 20 mm
Open Research DataOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.88 mm measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Measurement file of PEEK 70 mm bushing measurements in original condition perforemed on custom-built 3d measuring stand
Open Research DataAfter manufacturing process (lathe turning) bearing was measured on custom bulit measurement stan developed during research project financed by National Centre of Science. Measurements consist of 110 000 points in 3D space taken on bushing inner surface. Bearing was measured taking vertical steps of 0,2 mm.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Magnetic properties of of lead-silicate glasses and nanocomposites doped with iron oxide
Open Research DataMagnetic properties of iron-doped glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15 and 20 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere...
-
Linear impedance of 10Na2O–60P2O5–30CaO glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of 10Na2O–60P2O5–30CaO glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Measurement data of cyclic voltammetry and electrochemical impedance measurements of carbon samples synthesized on axes and off axes
Open Research DataThe electrochemical performance of the multielectrode samples were investigated by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) using a VMP-300 BioLogic galvanostat potentiostat (France) under the EC-lab software. All electrochemical investigations were carried out in a three-electrode cell system. The carbon multi-electrode,...
-
The morphology of lead-borate glasses and nanocomposites doped with iron oxide
Open Research DataThe topography of iron-doped borate glasses and glass-ceramics were studied. Samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 < x < 37 in mol%) were prepared by the conventional meltquenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate...
-
The structure of lead-borate glasses containing nanocrystallites of iron oxides
Open Research DataThe structure of iron-doped glasses and glass-ceramics were studied. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and...
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Linear and nonlinear impedance of iron containing silicate glasses
Open Research DataThe linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to...
-
Linear impedance of vanadate glasses containing BaTiO3
Open Research DataThe linear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Topography of barium-vanadate glasses
Open Research DataThe topography of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was performed...
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Open Research DataElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
Dielectric properties of barium-vanadate glasses
Open Research DataThe linear impedance of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was...
-
Linear impedance of vanadate glass-ceramics containing BaTiO3
Open Research DataThe linear impedance of vanadate glass-ceramics containing BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
Linear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.