Wyniki wyszukiwania dla: TEMPERATURE
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_v_3
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_h_3
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 019_v_5
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_h_5
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_h_4
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 039_h_4
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 019_v_4
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 019_h_5
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 039_v_4
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_v_4
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 039_v_3
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 019_v_3
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 019_h_3
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 039_h_5
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
Phytoplankton in the Gulf of Gdańsk– microscope photos archive
Dane BadawczeHarmful blooms of cyanobacteria an dinoflagellates are recorded every year in various areas of the Baltic Sea. The data set contains photos of potentially toxic phytoplankton species found in the Gulf of Gdańsk and Puck Bay. These photos show potentialy toxic cyanobacteria and dinoflagellates observed in the surface water samples collected between 2010-2020....
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 019_h_4
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 039_v_2
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 039_h_3
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
The influence of microstructure on the corrosion resistance for some titanium-based alloys
Dane BadawczeThis dataset contains scanning electron microscopy (SEM) micrographs revealing the microstructure of some Ti-based alloys, namely: Ti-6Al-4V (file name: TiV), Ti-6Al-7Nb (file name: TiNb) and TC21 (file name: TiAlSnZrMoCrNbSi) alloys and their localized corrosion as a result of passive layer breakdown in a corrosive environment, ie. 0.9% NaCl solution...
-
Deformation Sweep Test of Cement Bitumen Treated Material Mixture C3E5.5 (field cores; field curing)
Dane BadawczeDataset presents data of results of deformation sweep test determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Specimen size: f=100...
-
The morphology of vanadate glasses containing BaTiO3
Dane BadawczeThe morphology of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573 K) brass...
-
Luminescence properties of TeOx-Eu thin films
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Tb thin films
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Dy thin films
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
The luminescence study of Sc2(1–x)Ga2xO3:Cr3+/4+ coumpounds
Dane BadawczeThe growing interest in the use of near-infrared (NIR) radiation for spectroscopy, optical communication, and medical applications spanning both NIR-I (700–900 nm) and NIR-II (900–1700 nm) has driven the need for new NIR light sources. NIR phosphor-converted light-emitting diodes (pc-LEDs) are expected to replace traditional lamps mainly due to their...
-
Hydrodynamic reanalysis of sea level in the Baltic Sea using the PM3D model
Dane BadawczeThe data set contains the results of numerical modelling of sea level fluctuations in the Baltic Sea in the Baltic Sea since 1998. A long-term reanalysis was performed using a three-dimensional hydrodynamic model PM3D (Kowalewski and Kowalewska-Kalkowska, 2017), a new version of the M3D model (Kowalewski, 1997).
-
Fatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)
Dane BadawczeFatigue data of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)
-
Complex modulus of Cement Bitumen Treated Material Mixture C3E5.5 (over 28 days of curing at 20C)
Dane BadawczeDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement and 5.5% emulsion (C3E5.5). Mixture was designed according to Polish requirements for the base course of pavement. Mixture contains 60% of RAP material. Specimen size: f=100 mm, h=130 mm. Specimen...
-
Structure of ammonium vanadate synthesis by LPE-IonEx method
Dane BadawczeThe DataSet contains the XRD patterns, FTIR spectra of NH4VO3 crystals with different morphology obtained by the LPE-IonEx method.
-
Linear impedance of V2O5 nanorods obtained at 903K
Dane BadawczeThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Luminescence properties of TeOx-Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
Graphene oxide thin films deposited on a PCB board - chemical analysis
Dane BadawczeGraphene oxides based films were measured by X-ray photoemission spectroscopy (XPS) method. TheXPS measurements were carried out with the Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The...
-
Study of the chemical state of Gd in a Ba-La-Gd-Co based ceramic
Dane BadawczeBarium, Lanthanum, Gadolinium and Cobaltium precursors were used for production of ceramic materials. Samples were produced by standard solid state reaction. Samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing on a Gadolinum were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology....
-
Luminescence properties of TeOx-Tb thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Eu thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Chemical investigation of the Al2O3 ultra-thin films
Dane BadawczeUltra-thin layers of oluminum oxide (Al2O3) were deposited by ALD method. Atomic layer deposition provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. Samples with a thickness of 2 and 8 nm of alumina...
-
Linear impedance of V2O5 nanorods obtained at 913K
Dane BadawczeThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 893K
Dane BadawczeThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Hydrometeorological and hydrochemical conditions in the Gulf of Gdańsk in the vicinity of Vistula river mouth in July of 1977
Dane BadawczeSome results of the complex measurements in the coastal zone of the Gulf of Gdańsk in the vicinity of the Vistula river mouth are included in this archival data set. The measurements were carried out by Institute of the Oceanography of the University of Gdańsk (IO UG) in July of 1977. The list of parameters includes wind direction and speed, Secchi...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,5 V at 241 mA. Sample 24
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,5 V and discharged to 10 mV by constant current 241 mA. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface emission....
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,0 V at 250 mA. Sample 23, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,0 V and discharged to 10 mV by constant current 250 mA. Sample 23, experiment run #2.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to...
-
The Mott-Schottky characteristics of microwave pulsed-plasma polymerized allylamine by DEIS analysis
Dane BadawczeThe dataset contains the results obtained for the Mott-Schottky analysis of the microwave pulsed-plasma polymerized allylamine using the multifrequency perturbation signal with Dynamic Electrochemical Impedance Spectroscopy (DEIS) technique. The results were obtained using the perturbation composed of the elementary signals with a frequency range between...
-
Linear and nonlinear impedance of iron containing silicate glasses
Dane BadawczeThe linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,5 V at 80 mA. Sample 24
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,5 V and discharged to 10 mV by constant current 80 mA. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface emission....
-
FTIR spectra and IGC chromatograms for chemically reduced graphene oxide aerogels (rGOA)
Dane BadawczeThe effect of selected synthesis parameters on reduced graphene oxide aerogels properties was investigated using Fourier-transform infrared spectroscopy and dynamic adsorption method (Inverse Gas Chromatography, IGC). Samples were synthesized by sol-gel method by reduction induced self-assembly of graphene oxide. As a reductant l-ascorbic acid was used....
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,75 V at 241 mA. Sample 24, run #4.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,75 V and discharged to 10 mV by constant current 241 mA, experiment run #4.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Simulation of perovskite-based CuI/CH3NH3PbI3/SnO2 solar cell performance
Dane BadawczeThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/SnO2 model structure (Model 2) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/ZnO solar cell performance
Dane BadawczeThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/ZnO model structure (Model 3) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,75 V at 241 mA. Sample 24, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,75 V and discharged to 10 mV by constant current 241 mA. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface emission....