Filtry
wszystkich: 38206
wybranych: 1939
-
Katalog
- Publikacje 14189 wyników po odfiltrowaniu
- Czasopisma 778 wyników po odfiltrowaniu
- Konferencje 288 wyników po odfiltrowaniu
- Osoby 438 wyników po odfiltrowaniu
- Wynalazki 1 wyników po odfiltrowaniu
- Projekty 37 wyników po odfiltrowaniu
- Zespoły Badawcze 3 wyników po odfiltrowaniu
- Aparatura Badawcza 3 wyników po odfiltrowaniu
- Kursy Online 378 wyników po odfiltrowaniu
- Wydarzenia 19 wyników po odfiltrowaniu
- Dane Badawcze 22072 wyników po odfiltrowaniu
Filtry wybranego katalogu
wyświetlamy 1000 najlepszych wyników Pomoc
Wyniki wyszukiwania dla: heating systems , wind , temperature dependence , image analysis , smart cities , detectors , cameras
-
Oxygen partial pressure and temperature dependence of low frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of low frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of middle frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of middle frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of R-CPE1 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Nonlinear impedance of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
D.C. electrical measurements of Bi2VO5.5 ceramic measured at high temperature region
Dane BadawczeD.C. electrical properties of Bi2VO5.5 ceramic was measured.
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 fully crystallized glass at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 partially crystallized glass at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 partially crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Analysis of cell cycle distribution
Dane BadawczeThe dataset comprehensively details the distribution of A549, H226, and H460 cell lines in various cell cycle phases following treatment with the IC90 concentration of selected anthraquinones. The analysis was performed using the Flowing Software 2.
-
Chemical analysis of the Au-Ag nanoaloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Sensory analysis of bread samples with the addition of beetroot
Dane BadawczeThe data set presents the results of the sensory analysis of bread samples with the addition of beetroot, which was carried out by the sensory profiling analysis method based on the PN-ISO 11035: 1999 standard – “Sensory analysis - Identification and selection of descriptors for determining the sensory profile using multivariate methods”. The method...
-
Nonlinear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Sieve analysis of natural and magnetite aggregate
Dane BadawczeSieve analysis of natural river sand and magnetite aggregate used for concrete production
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Rain Gardens GC_MS analysis dataset
Dane BadawczeThis dataset contains the results of samples analysis (no-target analysis: scan mode) using gas chromatography coupled with mass spectrometry GC–MS (GC-2030 NEXIS MS, Shimadzu, Japan or Thermo Scientific, Waltham, USA).
-
The power spectral density of audible noise and electric disturbances in ship’s electrical drive systems with frequency converters
Dane BadawczeThe presented dataset is part of research focusing on the impact of the ship's electrical drive systems with frequency converters on vibrations and the level of audible noise on ships.
-
The profiles and spectrum of aqua solution of tannic acid by HPLC-DAD-MS analysis.
Dane BadawczeThe profiling of tannic acid is determined by examining the content and proportion / ratio of gallotannins [Aras et al. 2016, Clifford et al. 2007, Gauri et al. 2012, Nishizawa et al. 1982]. In order to check the ion mass distribution (TIC) in an aqueous solution of commercial tannic acid, a direct sample injection (TA) was performed into the mass spectrometer....
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
The Mott-Schottky characteristics of microwave pulsed-plasma polymerized allylamine by DEIS analysis
Dane BadawczeThe dataset contains the results obtained for the Mott-Schottky analysis of the microwave pulsed-plasma polymerized allylamine using the multifrequency perturbation signal with Dynamic Electrochemical Impedance Spectroscopy (DEIS) technique. The results were obtained using the perturbation composed of the elementary signals with a frequency range between...
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-35Nb2O5 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH) and Nb2O5 (≥99.9%, PLUKA AG) were...
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 473 K for 3h and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Chemical composition analysis of the LSNO ceramics
Dane BadawczeThe chemical composition of a series of La-Sb-Nb-O ceramics manufactured by the solid-phase reaction method was analyzed. The samples with a various antimony content were measured by XPS method (OmicronNanotechnology UHV system). Analysis confirmed presence of elements: La, Sb, Nb.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Rain Gardens LC_MS/MS analysis dataset
Dane BadawczeThis dataset contains the results of samples analysis (target analysis with certified reference materials) using ultra-high performance liquid chromatography tandem mass spectrometry (UHPLC-MS/MS, Shimadzu, Japan).
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
XPS analysis of strontium titanate ceramics
Dane BadawczeThe chemical composition of the strontium titanite doped with yttrium and iron ceramic samples was investigated. Samples of Y0.07Sr0.93Ti0.8Fe0.2 were prepared by solid phase reaction and sintered for 24 and 48 hours. Chemical composition was measured by UHV OmicronNanotechnology XPS system. The analysis confirmed the chemical composition of the ceramics...
-
XRD analysis of the tellurium dioxide thin films
Dane BadawczeTellurium dioxide thin films were deposited by magnetron sputtering method. The XRD analysis of the films annealed at 200, 500, 650 and 700 celsius degree showed appearing of crystalline phase in a higher temeratures.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Thermogravimetric analysis data of hydration in air and nitrogen for BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Dane BadawczeThe dataset consists of 6 files of thermogravimetric analysis (TGA) data. The TGA experiments of hydration for BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were conducted on Netzsch STA 449.
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.