Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
The XPS studies of the CB-PLA electrodes after different surface treatments (chemical, electrochemical, enzymatic)
Dane BadawczeThe dataset contains the Xray Photoelectron Spectroscopy results of the studies performed under different conditions of surface activation of the CB-PLA 3D printed electrodes. The activation was performed by hydrolysis in different solvents (DMF, 1M HCl, 1M NaOH), electrolysis in 1M NaOH, enzymatic treatment in polymerase or simultaneous electrolysis...
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 473 K for 3h and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 fully crystallized glass at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 partially crystallized glass at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 partially crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Elemental composition of deposited sediments at the tram-route junction
Dane BadawczeThis data set contains the elemental composition results of deposited sediments collected at the tram-route junction in Gdańsk. Sample collection began in July 2022, when the tram lines were completed and before the rails were scrubbed (27/07/2022). The second sample round was carried out following rail scrubbing in October 2022 (7/10/2022). Since February...
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Dane BadawczeThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials
Dane BadawczeIn the dataset are included raw data for the preparation of XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials.
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Dane BadawczeData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.
-
The luminescence study ofNaK2Li[Li3SiO4]4:Ce coumpounds.
Dane BadawczePhosphors with a rigid and symmetrical structure are urgently needed. The alkali lithosilicate family (A[Li3SiO4]) has been extensively studied with a narrow emission band due to its unique cuboid-coordinated environment and rigid structure. However, here we demonstrate for the first time Ce-doped NaK2Li[Li3SiO4]4 phosphors with a broad emission band,...
-
Imaging and chemical investigation of silver coating
Dane BadawczeThe recovery of silver from materials such as plates, still used in clinical radiography [1], or scrap jewelery is still very popular. The subject of the research, part of which was microscopic imaging, was to recreate the behavior of an electrochemically deposited silver coating. The copper electrodes were covered with a layer of silver obtained from...
-
The topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with SEM method
Dane BadawczeThe topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by SEM.
-
Transmission electron microscope (TEM) and optical microscope images of pristine and silica-coated bismuth oxide and gadolinium oxide particles
Dane BadawczeCollection of raw transmission electron microscope (TEM) micrographs and optical microscope images used in the associated manuscript. All data in accessible *.tif format. Zip package contains:
-
Temperture-programmed reduction (H2-TPR) of Ni-Mo2CTx_Mo2Ga2C and Ni-Mo2CTx_Mo3AlC2 catalysts
Dane BadawczeThe dataset includes the data for the preparation of plots illustrating the reduction peaks versus the temperature of the catalyst sample.
-
Selection of material for infiltration of non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ
Dane BadawczeThe porous electrodes used for the infiltration were prepared from A-site non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ synthesized by the conventional solid state reaction method. Screen printed electrodes (0.5 cm2) on CGO-20 substrate, were fired at 800 °C for 2 hours in an air atmosphere. Infiltration of the scaffolds was performed by a water-based precursor...
-
Sea surface temperature in the Baltic Sea derived from Landsat 8 satellite data - path 194
Dane BadawczeThe data set contains high resolution sea surface temperature (SST) maps estimated from Landsat 8 Level 1 Thermal Infrared Sensor (TIRS) data using NLSST algorithm. SST was calculated only for granules (185 x 180 km) from satellite path number 194, that covered at least 2000 km2 of the cloud-free area of the Baltic Sea.
-
Sea surface temperature in the Baltic Sea derived from Landsat 8 satellite data - path 192
Dane BadawczeThe data set contains high resolution sea surface temperature (SST) maps estimated from Landsat 8 Level 1 Thermal Infrared Sensor (TIRS) data using NLSST algorithm. SST was calculated only for granules (185 x 180 km) from satellite path number 192, that covered at least 2000 km2 of the cloud-free area of the Baltic Sea.
-
Sea surface temperature in the Baltic Sea derived from Landsat 8 satellite data - path 191
Dane BadawczeThe data set contains high resolution sea surface temperature (SST) maps estimated from Landsat 8 Level 1 Thermal Infrared Sensor (TIRS) data using NLSST algorithm. SST was calculated only for granules (185 x 180 km) from satellite path number 191, that covered at least 2000 km2 of the cloud-free area of the Baltic Sea.
-
Sea surface temperature in the Baltic Sea derived from Landsat 8 satellite data - path 193
Dane BadawczeThe data set contains high resolution sea surface temperature (SST) maps estimated from Landsat 8 Level 1 Thermal Infrared Sensor (TIRS) data using NLSST algorithm. SST was calculated only for granules (185 x 180 km) from satellite path number 193, that covered at least 2000 km2 of the cloud-free area of the Baltic Sea.
-
Sea surface temperature in the Baltic Sea derived from Landsat 8 satellite data - path 190
Dane BadawczeThe data set contains high resolution sea surface temperature (SST) maps estimated from Landsat 8 Level 1 Thermal Infrared Sensor (TIRS) data using NLSST algorithm. SST was calculated only for granules (185 x 180 km) from satellite path number 190, that covered at least 2000 km2 of the cloud-free area of the Baltic Sea.