Morphology of the gold nanoislands
Dane BadawczeDewetting of the thin metallic films leads to formation of an isolated islands. morphology of nanostructures was measured by SEM microscope. Thin gold films with a thickness of 1.2 nm, 1.5 nm and 3.4 nm were anealed at 550, 600 and 650 Celcius degress.
-
SEM images of dewetted gold films
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. as a result of dewetting process. Thin golds films were deposited using a table-top dc magnetron sputtering coater under pure Ar plasma conditions . The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness...
-
Plasmon resonance in gold-silver nanoalloys
Dane BadawczeSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Formation of gold anostructures detected by SEM microscope
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air...
-
Formation of gold nanostructures detected by XPS method
Dane BadawczeGold nanostructers were manufactured by thermal dewetting of thin film. Film with thickness of 2.8 nm was deposited by magnetron sputtering method. As a result of annealing at 550 deg, nanostructures appear. Bulk gold, as-deposited gold film and metallic nanostructures were measured by XPS method.
-
Gold nanocubic structures functionalization with organic layers
Dane BadawczeThis dataset contains the XPS spectra obtained for gold nanocubes (AuNC), which were deposited at the gold electrode surface and dried. The AuNC's were first functionalized with either cysteamine in EtOH or mercaptopropionic acid in EtOH. The concentration of these compounds was 20 mM. The interaction of the functionalized with the AuNC surface was...
-
The AFM micrographs of gold nanoparticles on silicon substrate
Dane BadawczeThe dataset contains the first approach towards AFM topographic imaging of gold nanoparticles synthesized and immobilized on the silicon surface. Measurements were made in the semi-contact mode on the NTEGRA Prima device, manufactured by NT-MDT. Scans were performed with amplitude detection at an operating value of 60% of the free oscillation amplitude....
-
Depth profile of the gold-silver bimetallic structures
Dane BadawczeSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
SEM images of tge gold nanostructures on silicon
Dane BadawczeAu nanostructures were prepared on Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air Products 99.999%)....
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Ultra-thin film of aluminum oxide influence on the plasmon resonance in gold nanostructures
Dane BadawczeUltra-thin film of aluminum oxide influence on the plasmon resonance in gold nanostructures was measured by UV-VIS spectroscopy. Ultra thin film of Al2O3 was deposited on a gold nanostructures. Thickness of film was 2nm - 8nm. Shift of plasmon resonance was observed, as a result of various dielectric constant of layer.
-
Maximum temperature of 0.5-W infrared laser-Illuminated gold nanorod platforms
Dane BadawczeData concern a system consisted of two pieces of borosilicate glass surrounded by air and joined together by a transparent glue, which is to serve as a thermal transducer. On the top and bottom sides of the smaller piece, gold nanorods are dislocated. Glass is prepared here due to its high transparency, facilitating heat to be produced within the system....
-
Elgold: gold standard, multi-genre dataset for named entity recognition and linking
Dane BadawczeThe dataset contains 276 multi-genre texts with marked named entities, which are linked to corresponding Wikipedia articles if available. Each entity was manually verified by at least three people, which makes the dataset a high-quality gold standard for the evaluation of named entity recognition and linking algorithms.
-
X-Ray diffraction of the metallic nanostructures
Dane BadawczeMetallic nanostructures (gold and silver) were manufactured as a thermal annealing of gold or silver thin film. Gold films with thickness of 2.8 nm were deposited on a silicon substrates using a table-top dc magnetron sputtering coater (EM SCD 500, Leica), equipped with quartz microbalance for in-situ thickness measurements. Films were deposited from...
-
Electrical measurements of the dewetting of metal thin films
Dane BadawczeIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
TEM imaging of metal nanoparticle cross section
Dane BadawczeTEM microscope was used for a imaging of metallic nanostructures. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.