Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Oxygen partial pressure and temperature dependence of R-CPE1 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Distribution of Relaxation Times analysis results of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C) as a function of measuring temperature at 0.1% pO2
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode as a function of measuring temperature at 0.1% pO2. Electrode was sintered at 1000 °C and measured at different temperatures (800 °C, 750 °C, 700 °C).
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.50Fe0.50O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.65Fe0.35O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Comparisson of area specific resistance of the SrTi1-xFexO3-d porous oxygen electrodes and state-of-the-art LSCF sintered at optimal conditions
Dane BadawczeIn this dataset are presented results of the polarization resistance of optimaly sintered SrTi1-xFexO3-d porous oxygen electrodes in symetrical cell (1000 °C; 800 °C and 800°C respectively x = 0.35; 0.50 and 0.70). For commparison were selected commercially avilable state-of-the-art LSCF (Europa) sintered at 1050 °C. The measurement temperature range...
-
WIG rate of return histogram and normal distribution curve
Dane BadawczeThe conducted market analysis covered the period of stock exchange quotations from the beginning of 2010 to the end of 2019 (04/01/2010 - 30/12/2019). Daily data was used, in the form of closing prices of indices operating on the Warsaw Stock Exchange. In order to obtain a complete and generalized picture of the market, the quotations of 4 indices were...
-
The fertility rate (TFR) in selected EU countries in 2015
Dane BadawczeThe main reasons for the negative consequences of demographic changes are: natural increase in the life span of the population, decline in fertility and emigration of unusual dimensions.
-
SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrodes sintered at 1050 °C before and after test
Dane BadawczeThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrode sintered at 1050 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using...
-
SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C before and after test
Dane BadawczeThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrode sintered at 800 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using a FEI...
-
Determination of changes in viscosity of chitosan solutions depending on shear rate.
Dane BadawczeThe rheological characteristics of chitosan solutions were based on viscosity measurements using a Brookfield viscometer, using LV SC4 - 25 spindles and shear rates from 4 to 53 s-1 (Fig. 1). Chitosan solutions with different molecular weights (low, medium and high) were prepared in concentrations from 1.5 to 3.0% in 0.5M acetic acid. The data allowed...
-
Fitted impedance spectra of a symmetrical porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C, measured at 700 °C and 0.1% pO2) with an individual contributions of the respective fitting elements
Dane BadawczeThis dataset contains exemplary impedance spectra (measured at 700 °C and 0.1% pO2) for porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode sintered at 1000 °C. Results of symmetric cell impedance measurement were converted to electrode surfaces area and dived by two electrodes. Dataset conatins also fitting results and individual contributions of the respective...
-
Fitted impedance spectra of a symmetrical porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C, measured at 800 °C and 0.1% pO2) with an individual contributions of the respective fitting elements
Dane BadawczeThis dataset contains exemplary impedance spectra (measured at 800 °C and 0.1% pO2) for porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode sintered at 1000 °C. Results of symmetric cell impedance measurement were converted to electrode surfaces area and dived by two electrodes. Dataset conatins also fitting results and individual contributions of the respective...
-
Rate performance of the V2O5 nanocrystals as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
Determination of changes in viscosity of chitosan cosmetic preparations depending on shear rate.
Dane BadawczeThe rheological characteristics of chitosan were made on the basis of a viscosity measurement using a Brookfield viscometer, using LV SC4 - 25 spindles and shear rates from 0.3 to 32 s-1 (Fig. 1). Chitosan solutions at 1% concentrations in acetic acid were prepared. The samples were subjected to storage tests.
-
Rate performance of the V2O5 nanorods as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
Rate performance of (NH4)2V10O25·8H2O as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the ammonium vanadate nanostructures obtained by the hydrothermal method under an initial pressure of 50 bar ((NH4)2V10O25·8H2O). The battery tests of the samples were performed using the ATLAS 0961 MBI multichannel battery testing system with different current densities in the voltage...
-
Determination of changes in viscosity of hydrogel depending on shear rate (1.1 to 55 s-1).
Dane BadawczeThe rheological characteristics of hydrogel were made on the basis of a viscosity measurement using a Brookfield viscometer, using LV SC4 - 25 spindle and shear rates from 1.1 to 55 s-1.
-
Determination of changes in viscosity of hydrogel depending on shear rate (1.7 to 34 s-1).
Dane BadawczeThe rheological characteristics of hydrogel were made on the basis of a viscosity measurement using a Brookfield viscometer, using LV SC4 - 27 spindle and shear rates from 1.7 to 34 s-1.
-
Determination of changes in viscosity of poly(acrylic acid) PAA solutions depending on shear rate.
Dane BadawczeThe rheological characteristics of poly(acrylic acid) PAA solutions were based on viscosity measurements using a Brookfield viscometer, using LV SC4 - 27 spindles and shear rates from 1,7 to 39 s-1 (Fig. 1). PAA solutions with were prepared in water. The data allowed to characterize the used PAA and assess their functional parameters as rheology modifying...
-
Determination of changes in viscosity of pectin gel depending on shear rate (1.1 to 55 s-1).
Dane BadawczeThe rheological characteristic of pectin gel (with concetration 0,45% m/m, in three independent repetition of sample) was made on the basis of a viscosity measurement using a Brookfield viscometer, using LV SC4 - 25 spindle and shear rates from 1.1 to 55 s-1.The data allowed to characterize the used hydrogel preparations and assess their functional...
-
Determination of changes in viscosity of pectin gel depending on shear rate (1.7 to 85 s-1).
Dane BadawczeThe rheological characteristic of pectin gel (with concetration 0,25% m/m, in two independent repetitions) wasmade on the basis of a viscosity measurement using a Brookfield viscometer, using LV SC4 - 27 spindle and shear rates from 1.7 to 85 s-1, in temperature of 25 C degee .The data allowed to characterize the used hydrogel preparations and assess...
-
Dual role of oxygen-related defects in the luminescence kinetics of AlNMn2+
Dane BadawczeThis dataset presents the impact of temperature and pressure on AlN:Mn2+ luminescence kinetics. Unusual behavior of Mn2+ optical properties during UV excitation is observed, where a strong afterglow luminescence of Mn2+ occurs even at low temperatures. When the temperature increases, the contribution of the afterglow luminescence is further enhanced,...
-
Photocatalytic degradation of acetaldehyde in high temperature reaction chamber
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using TiO2 (titanium dioxide) as photocatalysts. It includes data on the influence of flow rate, TiO2 (titanium dioxide) filling the entire reactor, a thin layer of TiO2 (titanium dioxide) supported on KBr...
-
Rate performance of mixture (NH4)2V6O16 and (NH4)2V10O25·8H2O as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the ammonium vanadate nanostructures obtained by the hydrothermal method without initial pressure (mixture (NH4)2V6O16 and (NH4)2V10O25·8H2O). The battery tests of the samples were performed using the ATLAS 0961 MBI multichannel battery testing system with different current densities...
-
The hydrogen evolution reaction (HER) performance of some FTO/MoS2/SnO2 electrodes
Dane BadawczeTo demonstrate the electrochemical performance of the FTO/MoS2/SnO2 for HER (hydrogen evolution reaction), the LSV (linear sweep voltammetry) was performed. The polarization curves of the obtained composite were measured in 1 M H2SO4 at room temperature with a scan rate 10 mV/s. For comparison, the LSV for the FTO, pure MoS2 and Pt plate electrode were...
-
SEM images of Mo2Ga2C MAX material
Dane BadawczeIn the dataset, are included SEM images of molybdenum gallium carbide MAX materials.
-
XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials
Dane BadawczeIn the dataset are included raw data for the preparation of XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials.
-
X-ray photoelectron spectroscopy (XPS) results for nickel(II) oxide (NiO) functionalized borophene and boron
Dane BadawczeThis dataset contain X-ray photoelectron spectroscopy (XPS) results for nickel(II) oxide (NiO) functionalized borophene before and after oxygen evolution reacion (OER) nad bulk boron.
-
XPS-TiO2 heated in H2
Dane BadawczeThese XPS spectra were recorded for TiO2 heat-treated at 450-600oC in H2. Surface oxygen groups were determined. Deconvolution of Ti 2p peak allowed to determine Ti3+ on the titania surface.
-
Results of experimental research of hydraulic satellite motor
Dane BadawczeThe study of the flow rate in the motor and the torque on the motor shaft at low constant speed were carried out.The file contains measurement data of the torque on the motor shaft and the flow rate in the motor as a function of the angle of shaft rotation at various constant pressure drops in the motor.
-
FTIR-TiO2 heated at 400-600oC in Ar or H2
Dane BadawczeData contain FTIR diffuse eflectance spectra of TiO2, which was heat-treated at 400-600oC in Ar or H2. Hydrogen reduced TiO2 revealed new bands due to the adsorption of some species on the titania oxygen vacancy sites.
-
Income tax rates for special activities in Czech Republic
Dane BadawczeThe standard corporate income tax rate is 19%. Since 2015, the tax rates for special activities have changed as follows: the tax rate for pension funds is 0% (with some exemption); The tax regulations define a new so-called "Basic investment fund" and only that particular fund can benefit from the lower tax rate of 5%. Other mutual funds that do not...
-
X-ray diffraction (XRD) patterns of nickel(II) oxide (NiO) functionalized borophene and bulk boron
Dane BadawczeThese data include X-ray diffration (XRD) patterns of nickel(II) oxide (NiO) functionalized borophene before and after oxygen evolution reaction (OER), bulk boron (B), graphiic foil (GF) and nickel(II) oxide nanoparticles (NiO).
-
Electrical conductivity relaxation measurements - oxidation and reduction of BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Dane BadawczeThe dataset consists of 2 main catalogs: measurements performed for oxidation/reduction in dry conditions and in humid conditions. For Electrical Conductivity Relaxation (ECR) measurements, platinum reversible electrodes were applied in a four-probe arrangement and the sample was measured in the ProboStat™ measurement system. The ECR measurements were...
-
Molecular differences in mitochondrial DNA (mtDNA) genomes of dogs with malignant mammary tumours
Dane BadawczeThe aim of this study was to determine molecular defects in mitochondrial DNA with the use of large-scale genome analysis in malignant canine mammary gland tumours and indicate whether these changes were linked with the carcinogenesis process. With the use of the NGS technology, we sequenced 27 samples of mtDNA isolated from blood and tumours obtained...
-
Thermogravimetric analysis data of hydration in air and nitrogen for BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Dane BadawczeThe dataset consists of 6 files of thermogravimetric analysis (TGA) data. The TGA experiments of hydration for BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were conducted on Netzsch STA 449.