TG-hydroxyl groups in TiO2-P25
Dane BadawczeTG analyses were performed for powdered TiO2 - commercial P25 sample, which was heat-treated from room temperature to 500 C in the nitrogen atmosphere. Mass loss at lower temperature such as 120 C was related to the physisorbed water, and that one occurring at 500 C to the chemisorbed hydroxyl groups.
-
TiO2-TG analyses -OH groups
Dane BadawczeTG analyses of TiO2 were performed under nitrogen flow to monitor desorption of hydroxyl groups. Physisorbed weak-bonded hydroxyl groups were desorbed totally at around 120oC, whereas chemisorbed ones at around 500oC. The mass loss at these temperatures was used as concentration of hydroxyl groups on TiO2 surface. The amount of analysed TiO2 was 10...
-
TG analyses - content of SiO2 and TiO2 in polystyrene
Dane BadawczeTG analyses were performed for polystyrene spheres coating by SiO2 and then coating by SiO2-TiO2. Thermal analyses of polystyrene spheres only were also performed. The content of inorganic remaining was used for calculation the quantity of coating SiO2 and TiO2 in the polystyrene spheres.
-
TG and DTG profiles for plastics: LDPE, HDPE, PP, PD and PET
Dane BadawczeThe dataset includes:
-
DSC and TG results for strontium ferrite molybdate: pristine La, or Nb-doped
Dane BadawczeThis dataset consists of DSC and TG data collected for SFM, LSFM (La-doped) and SFMNb (Nb-doped) compounds, which were undertaken to analyze the reoxidation process of reduced compounds and its transition to double-perovskite structure .The appropriate amount of the powder (~10 mg with 10% tolerance factor) were placed into the alumina crucible and...
-
Thermogravimetric measurement (TG) of 20wt.% Ce0.8La0.2O2-NiO-YSZ anode for DIR-SOFC
Dane BadawczeThe daataset includes the thermogravimetric measurement (TG) of Ce0.8La0.2O2-NiO-YSZ anode for DIR-SOFC. The mesurement was performed under synthestic air atmosphere. The anode was composed of NiO-YSZ cermet composite (80 wt%) and Ce0.8La0.2O2-s additive (20wt%) with the addition of poroformer - PMMA granules 8um diameter (40 vol.% of whole powder volume)....
-
Bio based PUR-PIR foams thermal degradation (TG) and isoconversional kinetics
Dane BadawczeIn the present work, we perform a thorough thermogravimetric (TG) analysis of the bio-based polyurethane – polyisocyanurate (PUR-PIR) foams in both nitrogen and oxygen atmosphere. A sustainable element of the foam was a biopolyol obtained via acid-catalyzed liquefaction of Zostera Marina and Enteromorpha Algae biomass. Based on isoconversional analysis...
-
Thermogravimetric measurement (TG) of 10 wt.% Ce0.8La0.2O2-NiO-YSZ anode for DIR-SOFC
Dane BadawczeThe daataset includes the thermogravimetric measurement (TG) of Ce0.8La0.2O2-NiO-YSZ anode for DIR-SOFC. The mesurement was performed under synthestic air atmosphere. The anode was composed of NiO-YSZ cermet composite (90 wt%) and Ce0.8La0.2O2-s additive (10wt%) with the addition of poroformer - PMMA granules 8um diameter (40 vol.% of whole powder volume)....
-
TGA data of MXenes catalysts
Dane BadawczeData contain results from TGA measurement of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios. ...
-
Results of calibration of the piezoelectric scanner using the probe TGQ1
Dane BadawczeTeaching file. Results of calibration of the piezoelectric scanner using the probe TGQ1. Scanning in contact mode. NTEGRA Prima (NT-MDT) device. CSG probe 10.
-
SEM images of tge gold nanostructures on silicon
Dane BadawczeAu nanostructures were prepared on Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air Products 99.999%)....
-
XPS investigations of tge tin/tin oxides - CNT composites
Dane BadawczeThe composite of tin/tin oxide nanoparticles with graphene oxide and CMC based on laser ablation technique as an electrode material for energy storage devices were manufactured. The material exhibited a three-dimensional conducting graphene oxide network decorated with tin or tin oxide nanoparticles. The presence of tin/tin oxide in composites was...
-
Measurements of electrically small antenna radiation patterns in non-anechoic environments using TGM
Dane BadawczeThe dataset contains raw and processed measurements of radiation pattern characteristics performed in non-anechoic regime for four antenna structures: a spline-parameterized Vivaldi structure, a compact spline-based monopole, super-ultrawideband antenna, and a quasi-Yagi component. The responses have been obtained at the selected frequencies of interest...
-
XRD patterns of MXenes ashes obtained after TGA measurement
Dane BadawczeData contain results from XRD measurements of the product (ashes) produced after TGA of MAX Phase, MXene HF, MXene HF/HCl 1:3 and MXene HF/H2SO4 1:3 . The measurements were performed in AERIS PANalytical X-ray diffractometer with Cu-Ka radiation.
-
Thermogravimetric analysis (TGA ) and derivative thermogravimetry (DTG) results for potassium citrate
Dane BadawczeThese data contains thermogravimetric analysis (TGA ) and derivative thermogravimetry (DTG) results for thermal decomposition of potassium citrate.
-
Thermgravimetric analysis (TGA) data of cement pastes containing pristine and silica-coated bismuth oxide and gadolinium oxide particles
Dane BadawczeThermogravimetric (TGA) data of cement pastes after 2, 7 and 28 days. Samples designations: Control, BG, BG-A and BG-B are associated with the specimen names in the associated publication.
-
Thermal properties of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the DSC and TG curves of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere at the selected temperature: 500C, 600C, and 1000C.
-
Thermal behaviour of vanadium xerogel powder under different inert atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal stability of vanadium xerogel powder under different atmpshere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of vanadium xerogel powder and V2O5 nanorods under helium atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder and V2O5 nanorods obtained at 650C. The information about xerogel powder and V2O5 nanorods synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of vanadium xerogel powder under oxidizing atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of vanadium xerogel powder under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of (NH4)V4O10xH2O
Dane BadawczeThe DataSet contains the results of the thermal behavior of the (NH4)V4O10xH2O obtained by the hydrothermal method using different precursors: microstructured (commercially available) or nanostructured. The information about samples synthesis is described in the Materials.
-
Thermal behavior of TeOx xerogel powder under different atmospheres
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx xerogel powder measured under different atmospheres. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution...
-
Thermal behaviour of NH4VO3 microcasketoids
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microcasketoids under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 nanoflowers
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate nanoflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 elongated microcrystals
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate elongated microcrystals under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass...
-
Thermal behaviour of commercial avaible NH4VO3
Dane BadawczeThe DataSet contains the results of the thermal behavior of the commercially available ammonium metavanadate (CAS 7803-55-6) under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also...
-
Thermal behaviour of NH4VO3 microflowers
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the thermal behavior of the ammonium vanadate nanostructures obtained by the hydrothermal method with different conditions. Thermogravimetric analysis (TG) was carried out under an argon atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 500°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 500°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 1000°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 1000°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 650°C under reducing atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 650°C under a reducing atmosphere (95% Ar 5% H2). The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 400°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 400°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 700°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 700°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of TeOx powder
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 800°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 800°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 600°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 600°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Analysis of the chemical composition of MnO-B2O3 glass
Dane BadawczeStructural and thermal properties of xMnO−(100−x)B2O3 (where x = 40, 50 and 60 mol%) glass samples have been investigated with the employment of various techniques. Fourier transform infrared spectroscopy results revealed the influence of MnO on glass matrix. Decrease of B–O bond-related band intensities has been observed. MnO addition was found to...