Intergranular Corrosion Detection Using Electromagnetic Transducers for Ultrasonic Testing
PublikacjaThe aim of this paper is to create a research methodology that allows a quick analysis of the structural state of high alloy austenitic steels using non-destructive ultrasonic tests, in contrast to destructive standard methods. Electromagnetic acoustic transducers (EMAT) are used to generate and receive the ultrasonic wave and detect the microstructural changes caused by sample sensitization in elevated temperature, even after...
-
Deis assessment of intergranular corrosion process proceeding on AISI 304 stainless steel
PublikacjaW pracy przedstawiono nowe podejście do badania mechanizmu i intensywności korozji międzykrystalicznej. Badania przeprowadzono przy wykorzystaniu techniki dynamicznej elektrochemicznej spektroskopii impedancyjnej (DEIS), która pozwala na jednoczesne rejestrowanie chwilowych zmian impedancji oraz prądu stałego badanego układu. Tym samym możliwe jest otrzymanie z jednego pomiaru informacji dotyczących zarówno mechanizmu korozji międzykrystalicznej,...
-
Aspects of intergranular corrosion of AISI 321 stainless steel in high-carbon-containing environments
PublikacjaPurpose – The purpose of this paper is to present a case study of unexpected sensitization to intergranular corrosion of highly resistant AISI 321 steel in petrochemical conditions, where it was subjected to the simultaneous influence of elevated temperature of 250°C and vapors from the asphalt production process. Design/methodology/approach – Corrosion coupons were exposed in an installation carrying asphalt vapors. To identify...
-
DEIS assessment of AISI 304 stainless steel dissolution process in conditions of intergranular corrosion
Publikacja -
Instantaneous impedance evaluation of dissolution of aisi 304 stainless steel during intergranular corrosion
PublikacjaCelem pracy było uzyskanie informacji dotyczących zróżnicowania parametrów elektrycznych uzyskanych na podstawie zarejestrowanych chwilowych widm impedancyjnych w zakresie aktywacji i reaktywacji roztwarzania wysokostopowej stali austenitycznej AISI podczas postępującego procesu korozji międzykrystalicznej. Badania prowadzono z wykorzystaniem dynamicznej elektrochemicznej spektroskopii impedancyjnej (DEIS). Pomiary wykonywano ''on-line''...
-
Electrical mapping of AISI 304 stainless steel subjected to intergranular corrosion performed by means of AFM-LIS in the contact mode
PublikacjaThe paper presents results of the AFM-based approach to local impedance spectroscopy (LIS) measurements performed in a 20 20 lm grid within an austenite grain–grain boundary region for sensitized AISI 304 stainless steel (SS). Maps of electrical parameters obtained on the basis of localized impedance spectra were demonstrated, presenting their changes and correlation with the sample topography. Performed research revealed significant...
-
DEIS evaluation of the relative effective surface area of AISI 304 stainless steel dissolution process in conditions of intergranular corrosion
Publikacja -
Impact of sensitization on dissolution process of AISI 304 stainless steel during intergranular corrosion evaluated using DEIS technique
Publikacja -
Impact of sensitization on dissolution process of AISI 304 stainless steel during intergranular corrosion evaluated using DES technique
Publikacja -
The AFM micrographs of austenitic stainless steel subjected to sensitization for intergranular corrosion
Dane BadawczeThe dataset contains atomic force microscopy (AFM) maps of topographic images of austenitic steel samples subjected to sensitization to the process of intergranular corrosion. Precipitations of carbides as well as other intermetallic phases can be observed and detected before the fragments of structures sensitized by improper thermal treatment are exposed...
-
Kazimierz Darowicki prof. dr hab. inż.
OsobyStudia wyższe ukończyłem w czerwcu 1981 roku po zdaniu egzaminu dyplomowego i obronie pracy magisterskiej. Opiekunem pracy magisterskiej był dr hab. inż. Tadeusz Szauer. W roku 1991, 27 listopada uzyskałem stopień naukowy broniąc pracę doktorską zatytułowaną „Symulacyjna i korelacyjna analiza widm immitancyjnych inhibitowanej reakcji elektrodowej”. Promotorem pracy był prof. dr hab. inż. Józef Kubicki (Wydział Chemiczny...
-
The SEM micrographs of the cavitation erosion-corrosion process of selected copper alloys degradation
Dane BadawczeThe dataset contains Scanning Electron Micrographs of CuZn40Mn3Fe brass compared with Superston and Novoston bronze after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The micrographs compare the topography of samples subjected cavitation erosion in 3% NaCl at room temperature, leading to the surface...
-
Scanning electron microscopy studies of the weld decay on SS 304 of water supply pipeline
Dane BadawczeThis dataset contains micrographs made with scanning electron microscope (SEM) Hitachi S-3400N, of the weld decay for water supply system pipelines made of AISI 304 stainless steel. Within the dataset one can see the different corrosion mechanisms. The micrographs were made after the Strauss test (excluding pictures labeled as pits_in_HAZ, done without...
-
Failure of austenitic stainless steel tubes during steam generator operation
PublikacjaThe article presents the failure process of austenitic stainless steels used in power devices, such as heat exchangers, steam generators, in terms of local corrosion: pitting, stress and intergranular corrosion, paying particular attention to welded joints area. The effect of steel chemical composition, microstructure, welding process and work environment was analyzed. The second part of the article presents the results of the...
-
The exemplary Kelvin probe microscopy studies of sensitized austenitic stainless steels
Dane BadawczeThe dataset summarizes the results of imaging the surface potential distribution using the Kelvin probe scanning technique. Due to the fact that the potential measured in this way is proportional to the electrochemical potential of metals or intermetallic phases, it is possible to assess the nobility differences of various alloy components. In the case...
-
Localized impedance measurements of AA2024 and AA2024-T3 performed by means of AFM in contact mode
PublikacjaPurpose: The purpose of this paper is to present the results of an atomic force microscopy (AFM) based approach to local impedance spectroscopy (LIS) measurement performed on AA2024 and AA2024-T3 aluminium alloys. Design/methodology/approach: AFM-LIS measurements were performed ex-situ without the electrolyte environment, so in fact the electrical not electrochemical impedance was obtained. Findings: Relative local impedance values...
-
Austenitic stainless steel sensitization
Dane BadawczeHigh-alloy steels, thanks to their composition and content of appropriate alloying additives, are characterized by increased resistance to many corrosive environments. However, this is due to the increased sensitivity of the described construction materials to specific environmental conditions during their use. An example may be the increased susceptibility...
-
Imaging of morphological and physicochemical changes occuring in the structure of austenitic steel due to the thermal sensitization
Dane BadawczeIn polycrystalline materials, grain boundaries are always where phenomena such as surface diffusion, sedimentation and corrosion occur. They have a significant impact on the macroscopic properties of the construction material [1]. In addition to inhomogeneities such as manganese sulphide inclusions formed during the metallurgical process, interfacial...
-
Effects of preheating on laser beam–welded NSSC 2120 lean duplex steel
PublikacjaDuplex stainless steels show sustainable alternative for the conventional austenitic grades, with higher strength, higher resistance against stress corrosion cracking, and lower purchase cost. Thus, duplex stainless steel gains more attention in construction, oil and gas, and chemical industries. Among duplex stainless steels, low nickel and low molybdenum alloyed lean duplex stainless steel are a cost-efective substitution of...
-
Mechanical and Microstructural Characterization of TIG Welded Dissimilar Joints between 304L Austenitic Stainless Steel and Incoloy 800HT Nickel Alloy
PublikacjaIn this article, the mechanical properties and microstructure of 304L austenitic stainless steel/Incoloy 800HT nickel alloy dissimilar welded joints are investigated. The joints were made of 21.3 mm × 7.47 mm tubes using the TIG process with the use of S Ni 6082 nickel filler metal. No welding imperfections were found and high strength properties of joints were obtained, meeting the assumed acceptance criteria of the product’s...
-
SEM micrographs of the austenitic stainless steel corrosion in asphalt fumes
Dane BadawczeThe dataset contains the scanning electron microscopy (SEM) studies of the austenitic stainless steels: AISI 304, AISI 316, AISI 321 and duplex stainless steel AISI 2205. The samples were polished and exposed to the installation carrying asphalt fumes at elevated temperatures (approx. ~210-240 Celsius). The exposition duration was three months. Some...