Wyniki wyszukiwania dla: ATMOSPHERIC OPACITY
-
Thermal stability of V2O5 nanorods under inert atmosphere
Dane BadawczeThe DataSet contains the TGA curves of V2O5 nanorods obtained at 650°C. The information about nanorods synthesis is described in the Journal of Nanomaterials.
-
Lanthanum investigations in ceramics annealed in a dry and wet atmosphere
Dane BadawczeCeramics based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by standard solid state reaction from oxides and carbonate powders. After sintring, samples were annealed for 2 hours or 72 hours at 300 Celsius degree in a both: wet and dry atmosphere. Results of annealing on a chemical composition and valence state of lanthanum were observed...
-
Thermal stability of V2O5 nanorods under oxidizing atmosphere
Dane BadawczeThe DataSet contains the TGA curves of V2O5 nanorods obtained at 650°C. The information about nanorods synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of TeOx xerogel powder under different atmospheres
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx xerogel powder measured under different atmospheres. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution...
-
Measurements of radiation emission of a portable power bank with a capacity of 10400 mAh
Dane BadawczeThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell (Fig. 1). The test setup was configured to measure a portable power...
-
Measurements of radiation emission of a portable power bank with a capacity of 5200 mAh
Dane BadawczeThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell. The test setup was configured to measure a portable power bank...
-
Measurements of radiation emission of a portable power bank with a capacity of 2600 mAh
Dane BadawczeThe dataset contains the emission measurement results that are part of comprehensive tests carried out for portable power banks with different capacities. The measurements were performed in the frequency range from 30 MHz to 3 GHz using a Gigahertz Transverse Electromagnetic (GTEM) cell. The test setup was configured to measure a portable power bank...
-
Changes in heat flow of V2O5 nanorods under inert atmosphere
Dane BadawczeThe DataSet contains the DSC curves of V2O5 nanorods obtained at 650°C. The information about nanorods synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of vanadium xerogel powder under oxidizing atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Changes in heat flow of V2O5 nanorods under oxidizing atmosphere
Dane BadawczeThe DataSet contains the DSC curves of V2O5 nanorods obtained at 650°C. The information about nanorods synthesis is described in the Journal of Nanomaterials.
-
Changes in heat of vanadium xerogel powder under different atmosphere
Dane BadawczeThe DataSet contains the DSC curves of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of vanadium xerogel powder under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of vanadium xerogel powder under different inert atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Luminescence properties of TeOx thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
XRD patterns of the V2O5 nanorods after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 nanorods after thermal treatment under a reducing atmosphere. Samples were annealed at 450C for 2, 20, and 40h under a reducing atmosphere (94% Ar, 6% H2).
-
SEM micrographs of the V2O5 nanorods after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the SEM micrographs of V2O5 nanorods after thermal treatment under a reducing atmosphere. Samples were annealed at 450C for 2, 20, and 40h under a reducing atmosphere (94% Ar, 6% H2).
-
XRD patterns of the V2O5 coatings after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 coatings on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 500C, 600C, and 700C for 10 under a reducing atmosphere (94% Ar, 6% H2).
-
SEM micrographs of the V2O5 coatings after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 coatings on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 600C and 700C for 10 under a reducing atmosphere (94% Ar, 6% H2).
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1W0.9O3-s precursor calcined under air atmosphere
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1W0.9O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
Luminescence properties of TeOx-Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s precursor calcined under air atmosphere
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1W0.45Mo0.45O3-s precursor calcined under air atmosphere
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1W0.45Mo0.45O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
Luminescence properties of TeOx-Tb thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Thermal behaviour of vanadium xerogel powder and V2O5 nanorods under helium atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder and V2O5 nanorods obtained at 650C. The information about xerogel powder and V2O5 nanorods synthesis is described in the Journal of Nanomaterials.
-
Luminescence properties of TeOx-Eu thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
The electrical conductivity of pristine, La-, and Nb-doped SFM measured in air and hydrogen atmospheres
Dane BadawczeThis dataset consists of an Excel sheet with the result of DC4W method of electrical measurements. The measurements were conducted on pristine strontium ferrite molubdate as well as ones doped with La and Nb. Additionally two samples co-doped with La and Ni/Co were analyzed. Pellets were prepared by high temperature sintering at 1400 deg. C, then cut...
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 500°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 500°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 1000°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 1000°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 650°C under reducing atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 650°C under a reducing atmosphere (95% Ar 5% H2). The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 400°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 400°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 700°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 700°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 800°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 800°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 600°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 600°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Caffeine detection using CB-PLA electrode after Nd:YAG laser ablation in He atmosphere
Dane BadawczeThe dataset contains electrochemical studies in form of cyclic voltammetry (CV) and differential pulse voltammetry (DPV) of laser-activated 3D printed CB-PLA electrodes. The ablation of the 3D-printed CB-PLA electrodes was carried out using a pulsed LaserBlast 500 Nd:YAG laser (Quantel, France) operating at 1064 nm and a 6 ns pulse duration.
-
Oxygen partial pressure and temperature dependence of R-CPE1 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Luminescence properties of TeOx-2%Eu1.5%Tb1.5%Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-2%Eu1.5%Tb1.5%Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Luminescence properties of TeOx-2%Eu1.5%Tb1.5%Tm thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-2%Eu1.5%Tb1.5%Tm thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Luminescence properties of TeOx-1%Eu1.5%Tb2.5%Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-1%Eu1.5%Tb2.5%Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Bio based PUR-PIR foams thermal degradation (TG) and isoconversional kinetics
Dane BadawczeIn the present work, we perform a thorough thermogravimetric (TG) analysis of the bio-based polyurethane – polyisocyanurate (PUR-PIR) foams in both nitrogen and oxygen atmosphere. A sustainable element of the foam was a biopolyol obtained via acid-catalyzed liquefaction of Zostera Marina and Enteromorpha Algae biomass. Based on isoconversional analysis...
-
Thermogravimetric analysis data of hydration in air and nitrogen for BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Dane BadawczeThe dataset consists of 6 files of thermogravimetric analysis (TGA) data. The TGA experiments of hydration for BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were conducted on Netzsch STA 449.
-
Maximum forces in tendon connections for an anchor with a pin in the full sample experiment
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the load capacity of the anchoring element with a pin (see figure 1) was examined. Tendons from fresh swine legs (commercially available) served as the biological material. All samples were subjected...
-
Maximum forces in tendon connections for an anchor without pin in the single-side sample experiment
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the load capacity of the anchoring element without a pin (see figure 1) was examined. Tendons from fresh swine legs (commercially available) served as the biological material. All samples were...
-
Maximum forces in tendon connections for an anchor with pin in the single-side sample experiment
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the load capacity of the anchoring element with a pin (see figure 1) was examined. Tendons from fresh swine legs (commercially available) served as the biological material. All samples were subjected...
-
Maximum forces in tendon connections for the Kessler suture in the single-side sample experiment
Dane BadawczeThe main objective of the all study was to assess the load capacity of a new implant device for knotless tendon anastomosis. During this series of experiments the load capacity of the traditional two-strand Kessler sutures (3-0 sutures) was examined. Tendons from fresh swine legs (commercially available) served as the biological material. All samples...
-
Thermal behavior of TeOx powder
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...