Wyniki wyszukiwania dla: cosy
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 3 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 10 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Techno-economic analysis of a hybrid energy system for electrification using an off-grid solar/biogas/battery system employing HOMER: A case study in Vietnam
PublikacjaThe electrification of off-grid /island villages is a critical step towards improving the techno-economic circumstances of rural regions and the overall general growth of the country. However, consistent supply from a single source is not possible in these areas. Thus, a hybrid renewable energy system performs better in these conditions. The research challenge now is to identify the optimal combinations of HRES from the available...
-
Strategies for achieving energy neutrality in biological nutrient removal systems - a case study of the Slupsk WWTP (northern Poland)
PublikacjaThe paper presents a model-based evaluation of technological upgrades on the energy and cost balance in a large biological nutrient removal wastewater treatment plant (WWTP) in the city of Slupsk (northern Poland). The proposed upgrades include chemically enhanced primary sludge removal and reduction of the nitrogen load in the deammonification process employed for reject water treatment. Simulations enabled to estimate the increased...
-
Strategies for Achieving Energy Neutrality in Biological Nutrient Removal Systems – a Case Study of the Slupsk WWTP (northern Poland)
PublikacjaThe paper presents a model-based evaluation of technological upgrades on the energy and cost balance in a large biological nutrient removal wastewater treatment plant (WWTP) in the city of Slupsk (northern Poland). The proposed upgrades include chemically enhanced primary sludge removal and reduction of the nitrogen load in the deammonification process employed for reject water treatment. Simulations enabled to estimate the increased...
-
Piotr Figura dr inż.
OsobyPiotr Figura jest pracownikiem Katedry Finansów na Wydziale Zarządzania i Ekonomii Politechniki Gdańskiej, a także członkiem Komisji Wydziałowej ds. Weryfikacji Efektów Uczenia się oraz recenzentem akademickim zadań z zakresu rachunkowości Centralnej Komisji Edukacyjnej. Jest autorem lub współautorem kilku monografii naukowych w tym: Wartości wzorcowe wskaźników finansowych przedsiębiorstw giełdowych; Classical and modern concepts...
-
Elementy farmakologii - wykład, Biotechnologia sem. VII, 2022/2023
Kursy OnlineCelem przedmiotu jest pogłębienie wiedzy o substancjach leczniczych w zakresie farmakologii ogólnej ze szczególnym uwzględnieniem farmakokinetyki i farmakodynamiki. Studenci poznają losy leku w organizmie oraz zależności między dawką a efektem działania farmakologicznego leku. Ponadto, omówione zostają różne postaci leku i sposoby tworzenia formy leku.
-
Elementy farmakologii - wykład, Inżynieria biomedyczna sem. I, 2021/2022
Kursy OnlineCelem przedmiotu jest pogłębienie wiedzy o substancjach leczniczych w zakresie farmakologii ogólnej ze szczególnym uwzględnieniem farmakokinetyki i farmakodynamiki. Studenci poznają losy leku w organizmie oraz zależności między dawką a efektem działania farmakologicznego leku. Ponadto, omówione zostają różne postaci leku i sposoby tworzenia formy leku.
-
Podstawy farmakologii - Chemia biologiczna i medyczna, sem. 2, 2024/2025
Kursy OnlineCelem przedmiotu jest pogłębienie wiedzy o substancjach leczniczych w zakresie farmakologii ogólnej ze szczególnym uwzględnieniem farmakokinetyki i farmakodynamiki. Studenci poznają losy leku w organizmie oraz zależności między dawką a efektem działania farmakologicznego leku. Ponadto, omówione zostają różne postaci leku i sposoby tworzenia formy leku.
-
Approaching Secure Industrial Control Systems
PublikacjaThis study presents a systematic approach to secure industrial control systems based on establishing a business case followed by the development of a security programme. To support these two fundamental activities the authors propose a new method for security cost estimation and a security assessment scheme. In this study they explain the cost evaluation technique and illustrate with a case study concerning the assessment of the...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 613 K was measured by impedance spectroscopy method.
-
The stereostructure of candicidin D.
PublikacjaThe candicidin D stereostructure was established based on NMR studies including DQF-COSY, ROESY, HSQC and HMBC experiments. The relative configurations of the candicidin D stereogenic centers were assigned as the following: 9R*, 11S*, 13S*, 15R*, 17S*, 18R*, 19S*, 21R*, 36S*, 37R*, 38S*, 40S* and 41S*. The geometry of the heptaene chromophore was defined as 22E, 24E, 26Z, 28Z, 30E, 32E and 34E.
-
Healthcare Supply Chain Reliability: The Case of Medical Air Transport
Publikacja -
Magdalena Gajewska prof. dr hab. inż.
OsobyMagdalena Gajewska (ur. 1.06.1968 r. w Gdańsku) ukończyła studia w 1993 roku na Wydziale Hydrotechniki Politechniki Gdańskiej. Jest adiunktem w Katedrze Technologii Wody i Ścieków na Wydziale Inżynierii Lądowej i Środowiska Politechniki Gdańskiej. Doktorat (2001) i habilitacja (2013) w dyscyplinie inżynierii środowiska. W kadencji 2016–2020 pełni funkcję prodziekana ds. nauki. Specjalizuję się w technologiach związanych z ekoinżynierią:...
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 annealed glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
Model obliczania kosztu cyklu życia obiektu na przykładzie budynku mieszkalnego jednorodzinnego
PublikacjaW artykule przedstawiono model obliczania kosztu cyklu życia budynku mieszkalnego jednorodzinnego oraz wskazano możliwości ograniczenia wydatków związanych z jego użytkowaniem w okresie trzydziestu lat. Celem prezentowanej analizy rachunku kosztu cyklu życia jest porównanie i ocena kosztów nabycia i użytkowania domu realizowanego według alternatywnych technologii z uwzględnieniem przyjętych rozwiązań w zakresie pozyskania energii,...
-
Absolute configurations of C34 and C35 of antibiotic niphimycin A
PublikacjaThe relative configurations of four stereogenic centers of the C33-C42 fragment of niphimycin A were assigned as 2S*, 3R*, 4S* and 6S*, based upon (1)H NMR analysis with double-quantum filtered COSY and nuclear Overhauser spectroscopy experiments. These data were then correlated with absolute configurations at C36 and C38 of niphimycin A, which were declared previously as 36S and 38S [3]. This allowed for the assignment of the...
-
Absolute configurations of C34 and C35 of antibiotic niphimycin A
PublikacjaThe relative configurations of four stereogenic centers of the C33-C42 fragment of niphimycin A were assigned as 2S*, 3R*, 4S* and 6S*, based upon 1H NMR analysis with double-quantum filtered COSY and nuclear Overhauser spectroscopy experiments. These data were then correlated with absolute configurations at C36 and C38 of niphimycin A, which were declared previously as 36S and 38S [3]. This allowed for the assignment of the absolute...
-
Marcin Sikorski prof. dr hab. inż.
OsobyMarcin Sikorski jest profesorem w Katedrze Informatyki w Zarządzaniu na Wydziale Zarządzania i Ekonomii Politechniki Gdańskiej. Wcześniej odbył liczne pobyty w instytucjach naukowych, m.in. w Niemczech (Uniwersytety w Bonn i w Heidelbergu), Szwajcarii (ETH Zurich), Holandii (TU Eindhoven) i USA (Harvard University). Prof. Sikorski jest przedstawicielem Polski w komitecie TC13 Human-Computer-Interaction w międzynarodowej organizacji...
-
Tomasz Edward Berezowski dr inż.
OsobyUrodził się w 1986 r. w Warszawie. Ukończył w 2009r. z wyróżnieniem Międzywydziałowe Studium Ochrony Środowiska SGGW w Warszawie, specjalność Restoration and Management of Environment. Doktorat obronił z wyróżnieniem na Vrije UIniversiteit Brussels w 2015 roku. W latach 2015-2017 pracował jako asystent, a następnie adiunkt na Wydziale Budownictwa i Inżynierii Środowiska SGGW. W roku 2017 został zatrudniony jako adiunkt na Wydziale...
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 473 K for 3h and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 fully crystallized glass at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 partially crystallized glass at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 partially crystallized glass was measured by impedance spectroscopy method.