Novel Polyurethanes as Antifouling Paint Matrices

Abstract

The new poly(ester-ether urethane)s (PEEUR) were prepared in two stage synthesis from formerly obtained oligo(alkylene ester-ether)diols (OAEE) and 4,4‘-diphenylmethane diisocyanate (MDI). PEEUR samples were subjected to crosslinking with styrene in the presence of radical polymerization initiators: methyl ethyl ketone peroxide (MEKPO) or cobalt 2-ethyl cyclohexanoate (EtHCo). Crosslinked PEEUR were characterized by their physicochemical and mechanical properties. Tensile strength of crosslinked PEEURs was in the range 63-29 MPa, hardness values were from 92 to 97°ShA, and glass transition temperature was in the range 59-74°C. For PEEURs filled with biocides tensile strength was in the range 6,8-8,5MPa, hardness values were from 82 to 92°ShA, and glass transition temperature was in the range 57-72°C. Optical microscopic observations showed that the materials obtained were homogeneous in micrometric scale.

Citations

  • 0

    CrossRef

  • 0

    Web of Science

  • 0

    Scopus

Cite as

Full text

download paper
downloaded 2 times
Publication version
Accepted or Published Version
DOI:
Digital Object Identifier (open in new tab) 10.2478/adms-2013-0001
License
Creative Commons: CC-BY-NC-ND open in new tab

Keywords

Details

Category:
Articles
Type:
artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
Published in:
Advances in Materials Science no. 13, pages 5 - 10,
ISSN: 1730-2439
Language:
English
Publication year:
2013
Bibliographic description:
Kucińska-Lipka J., Janik H., Gubańska I.: Novel Polyurethanes as Antifouling Paint Matrices// Advances in Materials Science. -Vol. 13., nr. 1 (2013), s.5-10
DOI:
Digital Object Identifier (open in new tab) 10.2478/adms-2013-0001
Verified by:
Gdańsk University of Technology

seen 65 times

Recommended for you

Meta Tags