Filters
total: 670
filtered: 139
-
Catalog
Chosen catalog filters
Search results for: LOW TEMPERATURES
-
API 5L X65 steel - tensile properties in room temperature +20°C, along rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - fracture documentation of CMOD-force test in -10°C, along rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - fracture documentation of CMOD-force test in -10°C, across rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
Dual role of oxygen-related defects in the luminescence kinetics of AlNMn2+
Open Research DataThis dataset presents the impact of temperature and pressure on AlN:Mn2+ luminescence kinetics. Unusual behavior of Mn2+ optical properties during UV excitation is observed, where a strong afterglow luminescence of Mn2+ occurs even at low temperatures. When the temperature increases, the contribution of the afterglow luminescence is further enhanced,...
-
CO2 uptake capacities of PCMCA-900 (potassium citrate-derived porous carbon prepared at 900 °C) adsorbent at various temperatures
Open Research DataThese data contain CO2 uptake capacities of PCMCA-900 (potassium citrate-derived porous carbon prepared at 900 °C) adsorbent at various temperatures. Adsorption experiments were carried out at temperatures 0 °C, 25 °C, and 50 °C at 1 bar.
-
SEM images of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.05Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr1.00Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
Structural analysis of the tellurium dioxide thin films
Open Research DataTeO2 thin films were deposited by magnetron sputtering method. After deposition, amorphous samples were annealed at various temperatures. Influence of annealing temperature on a presence of crystalline phase was investigated.
-
The XRD diffraction patterns of LSCNT sintered at various temperatures
Open Research DataThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
CTD Gdańsk Deep_2001_2005
Open Research DataDataset includes measurements of conductivity (mS cm-1), temperature (°C), sound speed (m s-1) and salinity (PSU) made with the probe Falmouth Scientific Inc. The research was carried out in 2001 (at the turn of May and June), 2003 (beginning of May), 2005 (end of April) and in 2002 and 2004 (at the turn of September and October). In 2002, only temperature...
-
Distribution of Relaxation Times analysis results of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode (sintered at 1000 °C) as a function of measuring temperature at 0.1% pO2
Open Research DataThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of porous Sr0.86Ti0.65Fe0.35O3 oxygen electrode as a function of measuring temperature at 0.1% pO2. Electrode was sintered at 1000 °C and measured at different temperatures (800 °C, 750 °C, 700 °C).
-
Optical properties of MnO-B2O3 based glass
Open Research DataMnO-B2O3 based glass with Au nanoparticles samples were annealing for a various time (in a range of 24-96 hours) at various temperatures (from 340 up to 350 deg.). Presence of silver nanoparticles was detected by UV-VIS measurements. On the basis of change optical bandgap, Ag NPs was detected.
-
Vibration signals collected for concrete beams with GFRP reinforcement subjected to elevated temperatures (120C-240C)
Open Research DataThe dataset contains the time domain signals obtained during dynamic tests of concrete beams reinforced with GFRP bars. The vibration were induced with the use of modal hammer, while the signals were collected by the accelerometers attached at the beam surface. The signals were captured before and after subjecting the concrete beams to elevated temperatures.
-
Testing an evaporator operation with a concave manifold, condenser temperature 30, evaporator temperature 70 and preheater temperature 60
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a bifurcation manifold, condenser temperature 20 and evaporator temperature 85
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a concave manifold, condenser temperature 30, evaporator temperature 70 and preheater temperature 40
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a trapezoidal manifold, condenser temperature 90 and evaporator temperature 90
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a bifurcation manifold, condenser temperature 20 and evaporator temperature 70
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a rectangular manifold, condenser temperature 30 and evaporator temperature 90
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a trapezoidal manifold, condenser temperature 70 and evaporator temperature 60
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a bifurcation manifold, condenser temperature 20 and evaporator temperature 95
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Testing an evaporator operation with a bifurcation manifold, condenser temperature 20 and evaporator temperature 90
Open Research DataThe experiment was conducted to test the evaporator operation. The heat exchanger was equipped with minigeometry (set of 50 parallel minichannels or single minigap). The studies were conducted for various mass flow rate of the working fluid and for various temperatures at the inlet of the evaporator. Accurate information about the test rig, the parameters...
-
Series resistance (at 800 °C - 500 °C) of the Sr0.86Ti0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Open Research DataIn this dataset are presented results of the ohmic contribution of differently sintered Sr0.86Ti0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C, 1000 °C and 1050 °C. The measurement temperature range was between 800 °C and 500 °C in stationary air. Results converted to electrode surfaces area.
-
Influence of sintering temperature of porous SrTi0.30Fe0.70O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Influence of sintering temperature of porous SrTi0.50Fe0.50O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
Influence of sintering temperature of porous SrTi0.65Fe0.35O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
TiO2-TG analyses -OH groups
Open Research DataTG analyses of TiO2 were performed under nitrogen flow to monitor desorption of hydroxyl groups. Physisorbed weak-bonded hydroxyl groups were desorbed totally at around 120oC, whereas chemisorbed ones at around 500oC. The mass loss at these temperatures was used as concentration of hydroxyl groups on TiO2 surface. The amount of analysed TiO2 was 10...
-
Area specific resistance (at 800 °C - 500 °C) of the Sr0.86Ti0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Open Research DataIn this dataset are presented results of the polarization resistance of differently sintered Sr0.86Ti0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C, 1000 °C and 1050 °C. The measurement temperature range was between 800 °C and 500 °C in stationary air. Results converted to electrode surfaces...
-
Optical transmission of the Niobium thin films
Open Research DataNiobium thin films with a thickness of 200nm were deposited n a Corning glass substrate by magnetron sputtering method. The optical transmission spectra in a visible light range were.recorded. Investigations showed a good optical transmission thru the layers for each samples, annealed at various temperatures. For measurements samples annealed at 500,...
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.50Fe0.50O3 porous oxygen electrodes sintered at different temperatures
Open Research DataIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.50Fe0.50O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at different temperatures
Open Research DataIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.30Fe0.70O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Series resistance (at 800 °C - 500 °C) of the SrTi0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Open Research DataIn this dataset are presented results of the ohmic contribution of differently sintered Sr0Ti0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic ari flow (21% O2, 40 ml min-1). Results converted to electrode...
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Open Research DataThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Open Research DataThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Open Research DataThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Oxygen partial pressure and temperature dependence of Gerischer element of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of Gericher element at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C)and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent circuit...
-
Oxygen partial pressure and temperature dependence of middle frequency capacitance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of middle frequency capacitance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of series resistance (R) at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of middle frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of middle frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.50Fe0.50O3 porous oxygen electrodes sintered at different temperatures
Open Research DataIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.50Fe0.50O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at different temperatures
Open Research DataIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.30Fe0.70O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.65Fe0.35O3 porous oxygen electrodes sintered at different temperatures
Open Research DataIn this dataset are presented results of the polarization resistance of differently sintered SrTi0.65Fe0.35O3 porous oxygen electrodes in symetrical cell. Applied sintering temperatures were 900 °C, 950 °C and 1000 °C. The measurement temperature range was between 800 °C and 500 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to...
-
SEM images of symmetrical cell interface with Sr0.90Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr0.90Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
SEM images of symmetrical cell interface with Sr0.95Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at 800 °C, 900 °C and 1000 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell interface with Sr0.95Ti0.30Fe0.70O3-d electrodes and CGO-20 substrate sintered at three different temperatures 800 °C, 900 °C and 1000 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating...
-
XRD patterns of V2O5 nanostructures
Open Research DataThe DataSet contains the XRD patterns of vanadium pentaoxide nanostructures obtained by the sol-gel with different annealing temperatures under synthetic air. The results show that crystallinity dependent on the annealing temperature.
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Open Research DataThis dataset contains values of equivalent circuit element series resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Physicochemical studies (Raman) of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains Raman spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Oxygen partial pressure and temperature dependence of R-CPE1 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Open Research DataThis dataset contains values of equivalent circuit element R-CPE1 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Open Research DataThis dataset contains values of equivalent circuit element R-CPE2 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Open Research DataThis dataset contains values of equivalent circuit element R-CPE1 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...