Filters
total: 2567
filtered: 552
-
Catalog
Chosen catalog filters
Search results for: pulse counting
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Man 29 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Woman 27 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Woman 28 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Man 53 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Man 30 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Woman 24 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Woman 30 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
Caffeine detection using CB-PLA electrode after Nd:YAG laser ablation in He atmosphere
Open Research DataThe dataset contains electrochemical studies in form of cyclic voltammetry (CV) and differential pulse voltammetry (DPV) of laser-activated 3D printed CB-PLA electrodes. The ablation of the 3D-printed CB-PLA electrodes was carried out using a pulsed LaserBlast 500 Nd:YAG laser (Quantel, France) operating at 1064 nm and a 6 ns pulse duration.
-
Opposite pressure impact on electron-phonon coupling in Eu2+ and Ce3+ doped AlN
Open Research DataThis data analyzes the influence of pressure on electron–lattice interactions in the 5d excited states of Ce3+ and Eu2+ in the AlN host based on pressure-dependent photoluminescence and photoluminescence excitation spectra. High-pressure measurements on AlN samples doped with Eu2+ and Ce3+ ions reveal that the Stokes shift increases with pressure for...
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Second Man 29 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Man 29 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Woman 27 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Woman 28 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Man 30 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Woman 24 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Man 53 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Woman 30 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
The Mott-Schottky characteristics of microwave pulsed-plasma polymerized allylamine by DEIS analysis
Open Research DataThe dataset contains the results obtained for the Mott-Schottky analysis of the microwave pulsed-plasma polymerized allylamine using the multifrequency perturbation signal with Dynamic Electrochemical Impedance Spectroscopy (DEIS) technique. The results were obtained using the perturbation composed of the elementary signals with a frequency range between...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Second Man 29 age
Open Research DataThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
The dataset of coupling coefficients for rotating receiver of multicoil dynamic wireless power transfer system
Open Research DataThe provided dataset is part of the simulation results shown in related journal paper "Optimal Rotating Receiver Angles Estimation for Multicoil Dynamic Wireless Power Transfer".
-
DLC coating in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
XRD and electrochemical results for MoO3 films deposited using pulsed laser deposition system
Open Research DataThe attached data contains XRD and electrochemical results for MoO3 films deposited on fluorine-doped tin oxide glasses. Films were deposited using a pulsed laser deposition system at different conditions. Part of the samples was deposited at room temperature and then annealed at 575°C for given times (samples labeled PLD_RT_575C_xmin, where x stands...
-
Measurements of ultrasonic bulk and guided wave propagation in additively manufactured cubes and plates obtained by ultrasonic pulse velocity analyzer and scanning laser vibrometry
Open Research DataThe DataSet contains the results of measurements of ultrasonic wave propagation in additively manufactured samples made of polylactic acid (PLA). Three types of raster angles in two consecutive layers were assumed: 0°/90° (#1), 45°/-45° (#2) and 90°/90° (#3) with respect to the x-axis. For each printing variants a cubic sample (#C1-3) with dimensions...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
Output voltage, current and DC-link voltages under SVPWM, experimental results
Open Research DataThe dataset contains the experimental results of the project: A universal algorithm of space vector pulse width modulation for three-level three and multi-phase NPC inverters with DC-link voltage balancing. The output line-to-line voltage, output current and DC-link voltages were included. The comparison studies between proposed Space Vector Pulse-Width...
-
Luminescence properties of TeOx thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
Non-adiabatic coupling elements between the diatomic silver anion and neutral silver dimer plus continuum electron
Open Research DataThe process of a two-channel decay of the diatomic silver anion (Ag2-), namely the spontaneous electron ejection giving Ag2 + e- and the dissociation leading to Ag- + Ag is theoretically studied. The ground state potential energy curves (PECs) of the neutral silver dimer and anionic silver diatomic molecule are calculated using the single reference...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
Luminescence properties of TeOx-Eu thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Tb thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Dy thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
Images revealing the effect of local femtosecond laser ablation of conductive poly(lactic acid) 3D printed electrodes
Open Research DataThe dataset reveals the images of the femtosecond laser (FSL) ablation at the surface of commercially available carbon black-filled poly(lactic acid) 3D printed electrode. The process is used for the increase of the charge transfer of this electrode in electrochemical studies.
-
Luminescence properties of TeOx-Dy thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
Luminescence properties of TeOx-Tb thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Eu thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A23/#B22
Open Research DataWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 12 min. The...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B39/#A41
Open Research DataWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#A47
Open Research DataWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 20 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B34/#A33
Open Research DataWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#B45
Open Research DataWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 90 min. The test...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A41/#B39
Open Research DataWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The...
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B22/#A23
Open Research DataWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 6 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A33/#B34
Open Research DataWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
Data on bicycle traffic in Lodz (Poland) paired with weather and air quality data
Open Research DataThe file contains data on bicycle traffic registered by counting stations loacted in Lodz in the years 2016-2019. The data are paired with weather and air quality data from Lodz collected for the same period. The data is described below:
-
Data on bicycle traffic in Gdansk paired with weather and air quality data
Open Research DataThe file contains data on bicycle traffic registered by counting stations loacted in Gdańsk in the years 2013-2020. The data are paired with weather and air quality data from Gdansk collected for the same period. The data is described below:
-
Optical Parameters Stability Over Time of Porous Phantoms Mimicking Tissues
Open Research DataOptical phantoms are used to validate optical measurement methods. The stability of their optical parameters over time allows them to be used and stored over long-term periods while maintaining their optical parameters. The aim of the presented research was to investigate the stability of fabricated porous phantoms, which can be used as a lung phantom...
-
Tagged images with LEGO bricks
Open Research DataThe data set conatins tagged images conatining LEGO bricks used for traning LEGO bricks detecting network. The dataset contains two types of images: