Determination of t8/5 cooling times for underwater local dry welding of steel
PublicationKnowledge of thermal history is the basic condition for studying the structure - properties of welded joints. The determinant of thermal history is the thermal cycle, whose in-situ measurements are still a big challenge. Water as the welding environment complicates this issue even more. The article presents a method to determine an equation for calculating t8/5 cooling times for underwater gas metal arc welding of unalloyed steels...
-
Storage of High-Strength Steel Flux-Cored Welding Wires in Urbanized Areas
PublicationThe condition of the consumables is a key factor determining the waste reduction in the welding processes and the quality of the welded joint. The paper presents the results of tests of four types of fux-cored wires dedicated for welding high-strength steels, stored for 1 month and 6 months in Poland in two urbanized areas: in a large seaside city (Gdańsk) and in Warsaw, located in the center of the country. The wires were subjected...
-
Effect of Arc Strikes on High Strength Low Alloy Steels Welded by SMAW
PublicationWet welding with covered electrodes (Shielded Metal Arc Welding – SMAW) is the most commonly used method of carrying out welding repair works in a water environment. Limited visibility and the inability to move freely under water result in an increased risk of formation of welding imperfections such as lack of fusion, lack of penetration and arc strikes. The work focused on changes in the properties and structure of steel subjected...
-
Thermo-Mechanical Simulation of Underwater Friction Stir Welding of Low Carbon Steel
PublicationThis article investigates the flow of materials and weld formation during underwater friction stir welding (UFSW) of low carbon steel. A thermo-mechanical model is used to understand the relation between frictional heat phenomena during the welding and weld properties. To better understand the effects of the water environment, the simulation and experimental results were compared with the sample prepared by the traditional friction...
-
Possibilities of using interlayers during diffusion welding of Ti Gr2 and AISI 316L
Publication -
Evaluation of the Mechanical Parameters of Ultrasonically Welded Textile Composite Structures for Protective Footwear
Publication -
Application of Barkhausen effect in the impact assessment of welding to internal stress distribution in steel
PublicationThe paper presents identification method of internal stresses in plane steel elements in the chase of deliverance and welding assembly. The assessment was made by means of a non-destructive experimental method based on measurements incorporating local external magnetic field and the measurement of induced voltage, including Barkhausen noise. This method allows a degradation assessment due to internal and external actions, causing...
-
Application of Barkhausen effect in the impact assessment of welding to internal stress distribution in steel
PublicationThe paper presents identification method of internal stresses in plane steel elements in the chase of deliverance and welding assembly. The assessment was made by means of a non-destructive experimental method based on measurements incorporating local external magnetic field and the measurement of induced voltage, including Barkhausen noise. This method allows a degradation assessment due to internal and external actions, causing...
-
THE EFFECT OF WET UNDERWATER WELDING ON COLD CRACKING SUSCEPTIBILITY OF DUPLEX STAINLESS STEEL
PublicationABSTRACT The present work was conducted to assess the weldability of duplex stainless steel in underwater conditions. Metal manual arc welding (MMA) with the use of coated electrodes was used in the investigations. Tekken weldability tests were performed underwater at 0.5 m depth and in the air. Nondestructive tests, metallographic examinations of welds, ferrite content assessment in microstructure and hardness test were performed....
-
Effect of underwater wet welding conditions on the diffusible hydrogen content in deposited metal
PublicationIn the study mercury displacement method was used for determination of diffusible hydrogen amount in deposited metal obtained during underwater wet welding with covered electrodes in laboratory conditions according to a two-level full factorial design for three factors. The factors and their levels were chosen among conditions and parameters of welding in accordance with the results of own preliminary studies. A statistical analysis...
-
Bead-on-plate welding on S235JR steel by underwater local dry chamber process
PublicationThe article presents the results of the effect of parameters of underwater local dry chamber welding on the properties of padding welds. The effect of heat input and the type of shielding gas on the structure and hardness of welds was established. the functions for estimating the maximum hardness of the heat affected zone have been also elaborated.
-
Analysis of features of stainless steels in dissimilar welded joints in chloride inducted corrosion
PublicationStainless steels of femtic-austenitic microstructure that means the duplex Cr-Ni-Mo steels, in comparison with austenitic steel includes less expensive nickel and has much better mechanical properties with good formability and corrosion resistance, even in environments containing chloride ions. Similar share of high chromium ferrite and austenite, which is characterized by high ductility, determines that the duplex steels have...
-
Problems of analysis of axially loaded steel behavior under laser welded panel
PublicationWprowadzanie do praktyki nowych rozwiązań konstrukcyjnych wymaga posiadania danych wejściowych do procesu modelowania ich zachowania. Takim nowym elementem jest stalowy, spawany laserowo panel typu sandwich. W pracy pokazano wy-brane problemy towarzyszące modelowaniu zachowań takiej struktury. Pokazano podstawy teoretyczne wyznaczania sztyw-ności panelu a następnie omówiono wyniki badań wyboczenio-wych serii modeli o zmiennej geometrii.
-
Cold Cracking Of Underwater Wet Welded S355G10+N High Strength Steel
PublicationWater as the welding environment determines some essential problems influencing steel weldability. Underwater welding of high strength steel joints causes increase susceptibility to cold cracking, which is an effect of much faster heat transfer from the weld area and presence of diffusible hydrogen causing increased metal fragility. The paper evaluates the susceptibility to cold cracking of the high strength S355G10+N steel used,...
-
Hydrogen embrittlement of X2CrNiMoCuN25-6-3 super duplex stainless steel welded joints under cathodic protection
PublicationThe effect of cathodic polarization conditions on hydrogen degradation of X2CrNiMoCuN25-6-3 super duplex stainless steel welded joints, obtained using flux cored arc and submerged arc welding methods, was evaluated. Slow strain rate tensile tests of base material and welded specimens, ferrite content measurements, scanning electron microscopy observations, and statistical analysis were performed. It was found that hydrogenation...
-
The effect of pre-hydrogen charging on corrosion behaviour of superduplex stainless steel welded joints
PublicationThe paper presents results of research undertaken to determine the influence of hydrogen on passivity and corrosion resistance of 2507 super duplex stainless steel welded joints. Butt welded joints were made with low heat input using flux corded arc welding (FCAW) method. Coupons of 5.0 x 5.0 mm were cut from the welded joints containing weld metal (WM), heat affected zone (HAZ) and parent metal (PM). Hydrogen was introduced...
-
Autogenous Fiber Laser Welding of 316L Austenitic and 2304 Lean Duplex Stainless Steels
PublicationThis study presents results of experimental tests on quality of dissimilar welded joints between 316L austenitic and 2304 lean duplex stainless steels, welded without ceramic backing. Fiber laser welded butt joints at a thickness of 8 mm were subjected to non‐destructive testing (visual and penetrant), destructive testing (static tensile test, bending test, and microhardness measurements) and structure observations (macro‐ and...
-
Friction stir welds (FSW) of aluminium alloy AW6082-T6
PublicationW pracy przedstawiono badania właściwości mechanicznych złącz stopu aluminium AW6082-T6 wykonanych metodą tarciowego zgrzewania z wymieszaniem zgrzeiny. Złącza wykonano z różnymi parametrami procesu technologicznego. Wykazano, że wytrzymałość złącz jest proporcjonalna do prędkości zgrzewania oraz, że spadek twardości SWC jest większy po stronie ''advancing'' złącz.
-
Mechanical properties and corrosion resistance of dissimilar stainless steel welds
PublicationW artykule przedstawiono właściwości mechaniczne oraz odporność korozyjną doczołowych złączy różnoimiennych stali odpornych na korozję, austenitycznej 316L oraz duplex 2205. Blachy o grubości 15 mm spawano automatycznie łukiem krytyn z różnymi energiami liniowymi. Wykazano, że właściwości mechaniczne złączy spełniają wymagania okrętowych towarzystw klasyfikacyjnych, natomiast najbardziej narażoną strefą złącza na działanie korozji...
-
Zastosowanie techniki ściegu odpuszczającego do spawania mokrego
PublicationW artykule przedstawiono zastosowanie techniki ściegu odpuszczającego do poprawy właściwości złączy ze stali konstrukcyjnych wykonywanych w warunkach mokrego spawania pod wodą. Scharakteryzowano spawanie mokre elektrodami otulonymi zmiany struktury i właściwości złączy spawanych przez nakładanie ściegów odpuszczających. Przedstawiono metodykę oraz wyniki badań metalograficznych i twardości próbek ze stali konstrukcyjnej o podwyższonej...
-
Simulation of Structure Formation Processes of Dissimilar Steels Welded Joints Using an Intermediate Layer
Publication -
Friction Stir Welding of Aluminum in the Aerospace Industry: The Current Progress and State-of-the-Art Review
PublicationThe use of the friction stir welding (FSW) process as a relatively new solid-state welding technology in the aerospace industry has pushed forward several developments in different related aspects of this strategic industry. In terms of the FSW process itself, due to the geometric limitations involved in the conventional FSW process, many variants have been required over time to suit the different types of geometries and structures,...
-
Influence of friction stir welding technological parameters on the properties of the joints of selected aluminum alloys
PublicationThe purpose of this dissertation was to determine the effect of friction stir welding technological parameters on the properties of selected aluminum alloy joints, with consideration of the residual stresses and dislocation density in the joints. The goal of the present work was also to produce defect-free joints with high mechanical and electrochemical properties. In the dissertation, similar welds of AA6082 alloy and dissimilar...
-
The energy approach to fatigue crack growth of S355 steel welded specimens subjected to bending
PublicationThe study presents the results of the research on the rate of fatigue crack growth subjected to bending in the ferritic-pearlitic structure. The studies were carried out at a constant amplitude of the moment and at various values of the load ratios R and at the operating frequency of the machine of 28.4 Hz. Flat specimens made of S355 steel and with fillet welds and with double-sided blunt external notches as well as concave...
-
Effect of the welding environment and storage time of electrodes on the diffusible hydrogen content in deposited metal
PublicationIn the study the glycerin displacement method was used for determination of diffusible hydrogen content in deposited metal. Specimens were welded in the air and in the water with covered rutile electrodes. The first part of the specimens was made immediately after opening the package of the electrodes. The electrodes were then stored in opened packages in laboratory conditions that allowed for contact with the air for three years....
-
The influence of the welding environment on the properties of Tekken joints made from S355J2C+N steel
PublicationThere are three main methods of underwater welding: dry, wet and intermediate between them, by using the local dry chamber. Due to low costs, the most common method is the wet welding with the use of covered electrodes. Water as a welding environment carries out a lot of problems. The first is limited visibility and instability of the welding arc. The biggest problem during underwater welding is high susceptibility to cold cracking,...
-
The influence of solution annealing temperature on the properties of Lean Duplex 2101 welded joints in tubes
PublicationThe article presents a technology of TIG longitudinal welding without filler material (142) of heat exchanger tubes made of Lean Duplex 2101. The results of studies on the effect of heat treatment (solution annealing) on tensile strength, plasticity, delta ferrite and the structure of smooth tubes are shown. It was found, that the change in solution annealing temperature across the tested range has an impact on mechanical properties...
-
Effect of shielded electrode wet welding conditions on diffusible hydrogen content in deposited metal
PublicationWet welding is the most popular method of joining in water enviroment. During underwater welding, the weldability of steel is limited by the higher cooling rates and hydrogen content in weld metal. Article presents results of preliminary tests on the effects of wet welding conditions on diffusible hydrogen amount. Seven parameters were optimized using a Plackett-Burman plan to get the most relevant variables. These parameters were:...
-
Influence of Filler Metal on Electrochemical Characteristics of a Laser-Welded CoCrMoW Alloy Used in Prosthodontics
Publication -
Testing of PTA automatic braze-welding technology for producing absorber joints of solar collectors
Publication -
Technology of braze welding absorber tubes to copper foil in solar collectors by the GTA method
Publication -
Modifications of the heat source model in numerical analyses of the metal-cored arc welding process
Publication -
Bearing Capacity of aluminum bars with built-up cross section and glued or welded connections
PublicationThe paper is focused on numerical analysis and experimental test of aluminum bars with glued and welded connections between separate members. The connection properties were tested experimentally. The numerical analysis were conducted for the beam and shell model of the structure. The shape and magnitude of initial geometric imperfection was taken into account
-
Application of the Mathar method to identify internal stress variation in steel as a welding process result
PublicationThe paper deals with the method to identify internal stresses in two-dimensional steel members. Steel members were investigated in the delivery stage and after assembly, by means of electric-arc welding. In order to perform the member assessment two methods to identify the stress variation were applied. The first is a non-destructive measurement method employing local external magnetic field and to detecting the induced voltage,...
-
Diffusible hydrogen management in underwater wet self-shielded flux cored arc welding
PublicationThis article reports the effect of underwater wet welding parameters and conditions on the diffusible hydrogen content in deposited metal for welding with a self-shielded flux cored wire. The diffusible hydrogen content in deposited metal was determined using the glycerin method according to the Plackett-Burman design determining the significance of the effect of the stick out length, welding current, arc voltage, travel speed...
-
The analysis of the mechanical properties of welding joints of high-strength steels for offshore and ships structures
PublicationW artykule przedstawiono równania korelacyjne właściwości mechanicznych złaczy spawanych stali wysokiej wytrzymałości, które umożliwiają ocenę wpływu technologii spawania tych stali. W pracy zaproponowana dwa równania. Pierwsze umożliwa wstępną ocenę spawalności obecnie produkowanych stali wysokiej wytrzymałości, natomiast równania korelacyjne pozwalają obliczyć maksymalną twardość strefy wpływu ciepła materiału.
-
ENVIRONMENTAL DEGRADATION OF DISSIMILAR AUSTENITIC 316L AND DUPLEX 2205 STAINLESS STEELS WELDED JOINTS
PublicationThe paper describes structure and properties of dissimilar stainless steels welded joints between duplex 2205 and austenitic 316L steels. Investigations were focused on environmentally assisted cracking of welded joints. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement was determined in slow strain rate tests (SSRT) with the strain rate of 2.2 × 10–6 s–1. Chloride-inducted SCC was determined in the...
-
Problems of Determination of Welding Angular Distortions of T-fillet Joints in Ship Hull Structures
PublicationShip hull structure elements are in majority joined by welding. Welding distortions can cause a lot of problems during the manufacturing process. In the literature it is proposed wide spectrum of suggestions for a correct estimation of welding deformation in particular angular deformation in the fillet welded T joint. In the work verification of selected methods is proposed basing upon of the results of the laboratory measurements....
-
The analysis of the mechanical properties of welding joints of high-strength steels for offshore and ships structures
PublicationW artykule przedstawiono równania korelacyjne właściwości mechanicznych złaczy spawanych stali wysokiej wytrzymałości, które umożliwiają ocenę wpływu technologii spawania tych stali.W pracy zaproponowana dwa równania. Pierwsze umożliwa wstępną ocenę spawalności obecnie produkowanych stali wysokiej wytrzymałości, natomiast równania korelacyjne pozwalają obliczyć maksymalną twardość strefy wpływu ciepła materiału.
-
Prediction of corrosion fatigue crack propagation life for welded joints under cathodic potentials
PublicationPrzy ochronie katodowej poniżej potencjału optymalnego obserwuje się przyspieszenie propagacji pęknięcia korozyjno-zmęczeniowego w porównaniu do konstrukcji nie chronionej. Zaproponowano własną formułę empiryczną na wpływ potencjału ochronnego na prędkość propagacji pęknięcia oraz własny wzór na [delta]K w złączu pachwinowym. Wyprowadzono wzór na krzywą ''S-Np'' (naprężenie - długość okresu propagacji pęknięcia). Zaprezentowana...
-
The Influence of Modelling Material Zones on Strains and Stresses at Weld Toe Notch
PublicationThe latest development in the field of welding technology enabled prefabrication of thin-walled sandwich structures in an industrial scale. Sandwich structures fabricated of steel, or aluminium alloy plates and stiffeners are welded with the use of hi-power CO2 lasers. Strength analysis of such structures with the use of finite element method needs proper material modelling.In this paper the material model of steel sandwich panel...
-
Activated Tungsten Inert Gas Weld Characteristics of P91 Joint for Advanced Ultra Supercritical Power Plant Applications
PublicationActivated Tungsten Inert Gas (A-TIG) welding, a variant of tungsten inert gas (TIG) welding, was used for welding P91. In Generation IV power plants, P91 welds are prone to premature failure due to the presence and formation of brittle phases and creep at high temperatures. When performing A-TIG welding, the flux composition plays a role in the reversal of the Marangoni flow in the weld pool, which ultimately determines the level...
-
Mechanical and Microstructural Characterization of TIG Welded Dissimilar Joints between 304L Austenitic Stainless Steel and Incoloy 800HT Nickel Alloy
PublicationIn this article, the mechanical properties and microstructure of 304L austenitic stainless steel/Incoloy 800HT nickel alloy dissimilar welded joints are investigated. The joints were made of 21.3 mm × 7.47 mm tubes using the TIG process with the use of S Ni 6082 nickel filler metal. No welding imperfections were found and high strength properties of joints were obtained, meeting the assumed acceptance criteria of the product’s...
-
Badania wytrzymałościowe zgrzein łączących pręty zbrojeniowe o średnicy Ø30mm
PublicationZakres badań dotyczy oceny wytrzymałościowej zgrzein doczołowych, wykonanych metodą zwarciową. Elementami zgrzewanymi były pręty zbrojeniowe o średnicy Ø30mm. Badania związane są z okresową kontrolą stabilności parametrów zgrzewarki, szczególnie w odniesieniu do górnych, dopuszczalnych przez producenta zakresów parametrów zgrzewania oraz analizą wyników i porównaniu rezultatów prób wytrzymałościowych uzyskanych w 2019 i 2020 w...
-
Assessment of Corrosive Behaviour and Microstructure Characterization of Hybrid Friction Stir Welded Martensitic Stainless Steel
PublicationThis study examined the effect of induction heating on the microstructure and corrosion characteristics of hybrid friction stir welded AISI 410 stainless steel. Five joints have been produced with different friction stir welding parameters like welding speed, spindle speed, plunge depth, and induction power. Their microstructures were evaluated using a scanning electron microscope, and chemical composition was examined using...
-
Effect of water salinity on properties of multipass underwater wet manual metal arc welded joints
PublicationThe weldability of steel under the water is limited due to the influence of the environment. Water causes limited visibility, presence of the residual stresses, increasing the cooling rate, and increasing the diffusible hydrogen content in deposited metal, leading to the formation of brittle microstructures in heat-affected zone (HAZ). The paper presents the results of mechanical properties testing of S420G2+M steel welded joints...
-
Evaluation of drawability of tailor-welded blanks made of titanium alloys Grade 2 || Grade 5
Publication -
Investigations of methods to measure longitudinal forces in continuous welded rail tracks using the tamping machine.
PublicationPraca przedstawia w sposób poglądowy próby znalezienia efektywnej metody określania sił podłużnych w szynach toru bezstykowego. Szczególną uwagę poświęcono metodzie wymuszonych przemieszczeń poprzecznych. Podstawowym stwierdzeniem z przeprowadzonych własnych badań była konieczność odejścia od podnoszenia odłączonego od podkładów odcinka szyny i skoncentrowanie się na przemieszczeniach poprzecznych; doprowadziło to koncepcji zastosowania...
-
Effect of underwater local cavity welding method conditions on diffusible hydrogen content in deposited metal
PublicationOne of the methods with great potential for applications in underwater repairs is local cavity welding. In local cavity method, cooling conditions and diffusible hydrogen amount in weld metal are nearly the same as those existed during welding in the air. This paper presents the results of literature survey and preliminary tests of the effect of local cavity welding conditions on diffusible hydrogen amount in a deposited metal....
-
Opinion about causes of framing of Kingston chest (box cooler) damage, on PSV vessel VS4411 DF-PSV (B-855)
PublicationThe subject of analysis is a damage of welded connection of box cooler framing segments, made as separate bars 50mm thickness, connected by the welds in corners. Studies of documents delivered by Customer shows cracks on the fusion of filet welds and twisting of box cooler frame. The subject of analysis is a damage of welded connection of box cooler framing segments, made as separate bars 50mm thickness, connected by the welds...