Wyniki wyszukiwania dla: DIFFERENTIAL IMPEDANCE ANALYSIS
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
XPS analysis of TBBO glass
Dane BadawczeGlasses and glass-ceramics with nominal composition 73 TeO2– 4BaO– 3Bi2O3–18SrF2-2RE2O3 (where RE = Eu, Dy) have been synthesized by conventional melt-quenching technique and subsequent heat treatment at 370 °C for 24 h in air atmosphere. Various Eu3+ to Dy3+ molar ratio have been applied to investigate luminescence properties in both glass and glass-ceramic...
-
Impedance spectra of ZnO varistor type 680 model O M ver. 65 13
Dane BadawczeThe impedance spectrum of high-voltage ZnO varistor obtained using FRA EIS impedance spectrosocpy measurement method. The 1V sinusoidal excitation was used. The frequency range was chosen from 10 kHz down to 100 uHz. The object under test and the measuring instrument were placed in a Faraday cage due to high impedance of the object. The data was acquired...
-
Impedance spectra of ZnO varistor type 680 model O M ver. 65 60
Dane BadawczeThe impedance spectrum of high-voltage ZnO varistor obtained using FRA EIS impedance spectrosocpy measurement method. The 1V sinusoidal excitation was used. The frequency range was chosen from 10 kHz down to 10 uHz. The object under test and the measuring instrument were placed in a Faraday cage due to high impedance of the object. The data was acquired...
-
Linear impedance of vanadate glass-ceramics containing BaTiO3
Dane BadawczeThe linear impedance of vanadate glass-ceramics containing BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
Electrochemical Impedance Spectroscopy data of PDA-modified TiO2 nanotubes
Dane BadawczeThis dataset contains Electrochemical Impedance Spectroscopy data of the samples from TiO2 nanotubes modified with polydopamine. The studies were presented as a part of the research on "Band Gap Engineering toward Semimetallic Character of Quinone-Rich Polydopamine" (DOI: 10.1021/acs.jpcc.2c08804).
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 annealed glass was measured by impedance spectroscopy method.
-
Impedance spectroscopy of the lithium titanate doped by copper thin films
Dane BadawczeLithium titanate doped by copper thin films were derived by sol-gel method. Prepared gel was deposited by spin-coating technique. Samples with various content of Cu were measured by impedance spectroscopy method in a wide range of temperature, from -120 up to 150 deg.
-
Testing high impedance analyzer in the field on high-voltage line pylon cell 1 exposition 2
Dane BadawczeThe dataset presents impedance spectrum of anticorrosion coating on high-voltage line pylon presented in the figure below. This object was used to test high-impedance analyzer for diagnostic of anticorossion coatings (HIADAC) realized in the frame of Eureka project E!3174. The dataset contains comparative measurements with Atlas-Sollich ATLAS98HI analyser....
-
Testing high impedance analyzer in the field on high-voltage line pylon cell 1 exposition 1
Dane BadawczeThe dataset presents impedance spectrum of anticorrosion coating on high-voltage line pylon presented in the figure below. This object was used to test high-impedance analyzer for diagnostic of anticorossion coatings (HIADAC) realized in the frame of Eureka project E!3174. The dataset contains comparative measurements with Atlas-Sollich ATLAS98HI analyser....
-
Testing high impedance analyzer in the field on high-voltage line pylon cell 2 exposition 1
Dane BadawczeThe dataset presents impedance spectrum of anticorrosion coating on high-voltage line pylon presented in the figure below. This object was used to test high-impedance analyzer for diagnostic of anticorossion coatings (HIADAC) realized in the frame of Eureka project E!3174. The dataset contains comparative measurements with Atlas-Sollich ATLAS98HI analyser....
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
The surface of the sensor used in the analysis of odorous substances
Dane BadawczeHuman industrial activity usually leads to smaller or larger interference with the ecosystem, contributing to changes affecting the quality of life. An example may be the emission of gaseous substances, not necessarily toxic, but due to their intense smell, they can cause discomfort to people exposed to their inhalation. The problem is so important...
-
Testing high impedance analyzer in the field on high-voltage line pylon cell 2 exposition 2
Dane BadawczeThe dataset presents impedance spectrum of anticorrosion coating on high-voltage line pylon presented in the figure below. This object was used to test high-impedance analyzer for diagnostic of anticorossion coatings (HIADAC) realized in the frame of Eureka project E!3174. The dataset contains comparative measurements with Atlas-Sollich ATLAS98HI analyser....
-
Phylogenetic trees of genus Oncidium Sw. based on analysis of DNA sequences
Dane BadawczeGenus Oncidium Sw. is widely regarded as a polyphiletic, and the taxonomic boundaries between him and such genera as Odontoglossum Kunth. or Miltonia Lindley remain blurred. The goal of the study was to determine the phylogenetic relationships within the genus Oncidium s.lato based on the DNA sequences analysis. The correlation between molecular data...
-
The AFM micrographs and impedance study of epoxy coatings after exposure in corrosive media
Dane BadawczeThe dataset contains Atomic Force Microscopy (AFM) images and local impedance measurements of epoxy organic coating used as anti-corrosion protection, before and after 2-month exposure to sodium chloride solution. Additionally, there two local impedance spectra recorded after the coating exposure. The first one was recorded on intact coating surface,...
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at low temperatures
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
ArchBGal32cB 441Glu mutein gene analysis dataset
Dane Badawcze -
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Testing HIADAC high impedance analyzer in Trento University laboratory on "unknown" object using 2-wire probe
Dane BadawczeThe dataset presents impedance spectrum of "black-box" object with interesting phase characteristics. This object was used to test high-impedance analyzer for diagnostic of anticorossion coatings (HIADAC) realized in the frame of Eureka project E!3174. The impedance spectrum frequency range (1 Hz – 100 kHz) was selected in order to test the whole measureement...
-
Impedance spectra of RC model as a result of testing pulse excitation measurement method
Dane BadawczeThe impedance spectrum of RC model object obtained using pulse excitation EIS impedance spectrosocpy measurement method. The 1V voltage pulse excitation duration was set to 0.1s and the total acqusition time was set to 1000s. The object under test was built using RC components connected as Baunier model of anticorrosion coating with the following components...
-
Linear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
CFD analysis of a flow in commutation window in PWK pump
Dane BadawczeThe included data is a result of CFD analysis of a flow in a commutation window in PWK pump. The results were obtained for different pressures, viscosities and geometrical parameters of the gap. All the rows and columns have descriptions similar as in PhD Thesis: "Kompensacja skoków ciśnienia w pompie tłoczkowej o zmiennej wydajności z rozrządem krzywkowym",...
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 fully crystallized glass at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 partially crystallized glass at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 partially crystallized glass was measured by impedance spectroscopy method.
-
Thermogravimetric analysis (TGA ) and derivative thermogravimetry (DTG) results for potassium citrate
Dane BadawczeThese data contains thermogravimetric analysis (TGA ) and derivative thermogravimetry (DTG) results for thermal decomposition of potassium citrate.
-
Phylogenetic analysis of Oncidieae subtribe - ITS1-5,8S-ITS2
Dane BadawczeThe dataset contains alignment and consensus matrix files, and results of phylogenetic analysis of ITS1- 5,8S-ITS2 region from 186 orchid species considered to belong Oncidieae subtribe. Sequences were assessed from NCBI GeneBank (list of all records with identifiers in the separate file)
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Testing HIADAC high impedance analyzer in Trento University laboratory on Baunier's RC model using 2 wire probe
Dane BadawczeThe dataset presents impedance spectrum of Baunier's RC model. This object was used to test high-impedance analyzer for diagnostic of anticorossion coatings (HIADAC) realized in the frame of Eureka project E!3174. The impedance spectrum frequency range (1 mHz – 100 kHz) was selected in order to test the whole measureement range of the analyzer. In...
-
Testing HIADAC high impedance analyzer in Trento University laboratory on Baunier's RC model using 3 wire probe
Dane BadawczeThe dataset presents impedance spectrum of Baunier's RC model. This object was used to test high-impedance analyzer for diagnostic of anticorossion coatings (HIADAC) realized in the frame of Eureka project E!3174. The impedance spectrum frequency range (1 mHz – 100 kHz) was selected in order to test the whole measureement range of the analyzer. In...
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-35Nb2O5 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH) and Nb2O5 (≥99.9%, PLUKA AG) were...
-
Chemical analysis of the Au-Ag nanoaloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
Data for meta-analysis on interversions reducing car use
Dane BadawczeThis dataset contains the results of a meta-analysis of reported interventions reducing car use. To standardise intervention effects reported in different scales, the Hedges’ g effect size measure was used (ratio of raw difference in samples’ means and pooled standard deviation). The standardised studies outcomes, along with overall outcome, were...
-
Analysis of induction of DNA DSBs on telomeres in A549 cells
Dane BadawczeData consist of an analysis of DNA DSBs on telomeres. A549 were treated with compounds (TXT4, MTX, DMSO) at IC90 concentration for the indicated time. Images were acquired with an LSM 800 inverted laser scanning confocal microscope (Carl Zeiss; Dresden, Germany) equipped with an Airyscan detector using a ×63 1.4 NA Plan Apochromat objective (Carl Zeiss)....
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.