SEM images of dewetted gold films
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. as a result of dewetting process. Thin golds films were deposited using a table-top dc magnetron sputtering coater under pure Ar plasma conditions . The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness...
-
Oxidation of silver nanostructures
Dane BadawczeSilver nanostructures were prepared on Si substrate. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma. The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1 , and the incident power was in the range of 30–40 W. The layer thickness...
-
Comparison of XPS spectra of Ag3d for silver nanostructures and bulk material
Dane BadawczeAg nanostructures were prepared on borosilicate glass (Corning 1737F) and Si substrates. In both cases, the substrateswere cleaned with acetylacetone and then rinsed in ethanol. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The...
-
Investigation of plasmon resonance in a silver nanoparticles
Dane BadawczeSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
SEM images of tge gold nanostructures on silicon
Dane BadawczeAu nanostructures were prepared on Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air Products 99.999%)....
-
Formation of gold anostructures detected by SEM microscope
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air...
-
X-Ray diffraction of the metallic nanostructures
Dane BadawczeMetallic nanostructures (gold and silver) were manufactured as a thermal annealing of gold or silver thin film. Gold films with thickness of 2.8 nm were deposited on a silicon substrates using a table-top dc magnetron sputtering coater (EM SCD 500, Leica), equipped with quartz microbalance for in-situ thickness measurements. Films were deposited from...
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
AFM images of the platinum (111) single crystal surface as delivered, without the polishing treatment
Dane BadawczePlatinum (111) single crystal surface images as delivered, without polishing treatment. Topographic measurements in contact mode. NTEGRA Prima (NT-MDT) device. CSG probe 10.