Hydrogenation process ofTiO2/BiVO4/PEDOT:PSS observed by XPS method
Dane BadawczeTitania nanotubes synthesis was based on a two-stage anodization process at water/ethylene glycol (5%/95%) electrolyte containing 0.27 M NH4F and 1 M H3PO4 described previously. Anodization process was performed in two-electrode cell compartment using platinum mesh as a cathode. The distance between electrodes was about 2 cm. The anodization voltage...
-
Influence of reactive oxygen species during deposition of iron oxide films by high power impulse magnetron sputtering.
PublikacjaIron oxide films were deposited using high power impulse magnetron sputtering (HiPIMS) of an iron cathode in an argon/oxygen gas mixture at different gas pressures (0.5~Pa, 1.5~Pa, and 5.0~Pa). The HiPIMS system was operated at a repetition frequency $f = 100$~Hz with a duty cycle of 1~\%. A main goal is a comparison of film growth during conventional and electron cyclotron wave resonance-assisted HiPIMS. The deposition plasma...
-
Structure and electrical properties of Y, Fe-based perovskite mixed conducting composites fabricated by a modified polymer precursor method
PublikacjaIn this work, samples of Y0.07Sr0.93Ti1-xFexO3-d with 20, 40, 60 and 80 mol% of iron amount were prepared by a low-temperature polymer precursor method. The SEM-EDS analysis proved that analyzed Y0.07Sr0.93Ti1-xFexO3-d samples were composites of two Ti- and Fe-rich perovskite samples. This kind of composite consists of two phases in which one has a good ionic and the other electronic conductivity, which makes such a composite a...
-
Advanced Lithium-Ion Battery Model for Power System Performance Analysis
PublikacjaThe paper describes a novel approach in battery storage system modelling. Different types of lithium-ion batteries exhibit differences in performance due to the battery anode and cathode materials being the determining factors in the storage system performance. Because of this, the influence of model parameters on the model accuracy can be different for different battery types. These models are used in battery management system...
-
Properties of LiMnBO3 glasses and nanostructured glass-ceramics
PublikacjaPolycrystalline LiMnBO3 is a promising cathode material for Li-ion batteries. In this work, we investigated the thermal, structural and electrical properties of glassy and nanocrystallized materials having the same chemical composition. The original glass was obtained via a standard melt-quenching method. SEM and 7Li solid-state NMR indicate that it contains a mixture of two distinct glassy phases. The results suggest that the...
-
Influence of pore formers on electrical properties of CaTi0.9Fe0.1O3-δ perovskite-type ceramics
PublikacjaPorous CaTi0.9Fe0.1O3-δ (CTF) perovskites were synthesized by the standard solid state method at different sintering temperatures with carbon black (CB), corn starch (CS) and potato starch (PS) as pore-forming agents. The ceramic samples of porosity between 9% and 42% with 5 - 40 μm pore sizes, were obtained by a 6 h sintering at either 1130º C or 1200º C of precursor powder prepared at 1470º C. X-ray diffraction analysis proved...
-
Degradation of xylose using a microbial fuel cell
PublikacjaIt is generally known, that many kind of microorganisms are capable of using carbohydrates as a source of carbon and energy in an environment. The biodegradation process of monosaccharides from pentoses (in this case- racemic mixture of D - and L – xylose) is an immense opportunity for an entire reduction of biological contamination to neutral compounds through MFC. The process is occurred in a single-chamber MFC, which is contained...
-
High-performance anode-supported solid oxide fuel cells with co-fired Sm0.2Ce0.8O2-δ/La0.8Sr0.2Ga0.8Mg0.2O3−δ/Sm0.2Ce0.8O2-δ sandwiched electrolyte
PublikacjaIn this study, intermediate-temperature solid oxide fuel cells (IT-SOFCs) with a nine-layer structure are constructed via a simple method based on the cost-effective tape casting-screen printing-co-firing process with the structure composed of a NiO-based four-layer anode, a Sm0.2Ce0·8O2-δ(SDC)/La0·8Sr0.2Ga0.8Mg0·2O3−δ (LSGM)/SDC tri-layer electrolyte, and an La0·6Sr0·4Co0·2Fe0·8O3-δ (LSCF)-based bi-layer cathode. The resultant...
-
Noise and Electro-Ultrasonic Spectroscopy of Conducting PolymerThick Films
PublikacjaThick conducting films based on conducting polymer are characterized by DC conductivity and noise in temperature range 10 to 300 K. Conducting polymers could be used e.g. for the top electrode (cathode) in the solid tantalum or niobium capacitors. On the conducting polymer layer the top layer of carbon/graphite and/or silver polymer based pastes is applied in the capacitor technology. Our samples structure consists of conducting...
-
Stable Field Electron Emission and Plasma Illumination from Boron and Nitrogen Co‐Doped Edge‐Rich Diamond‐Enhanced Carbon Nanowalls
PublikacjaSuperior field electron emission (FEE) characteristics are achieved in edge-rich diamond-enhanced carbon nanowalls (D-ECNWs) grown in a single-step chemical vapor deposition process co-doped with boron and nitrogen. The structure consists of sharp, highly conductive graphene edges supplied by a solid, diamond-rich bottom. The Raman and transmission electron microscopy studies reveal a hybrid nature of sp3-diamond and sp2-graphene...
-
Effects of thermal history on the performance of low-temperature solid oxide fuel cells with Sm0.2Ce0.8O2-δ electrolyte and LiNi0.81Co0.15Al0.04O2 electrodes
PublikacjaIn this study, low-temperature solid oxide fuel cells with an ∼560 μm thick Sm0.2Ce0.8O2−δ (SDC) electrolyte and ∼890 μm thick LiNi0.81Co0.15Al0.04O2−δ (NCAL) electrodes are constructed and characterized under three experimental conditions. The cell with an NCAL cathode pre-reduced under an H2 atmosphere at 550 °C presents the best electrochemical performance. This is ascribed to facts that the reduction reaction generating Ni–Co...
-
Fluoroaromatic substituents attached to carbon nanotubes help to increase oxygen concentration on biocathode in biosensors and biofuel cells
PublikacjaBased on the known ability of perfluorodecalin/perfluorohydrocarbons to enhance oxygen solubility we modified oxygen sensitive biocathode by adding perfluorinated components to the catholite. This procedure improved the efficiency of the oxygen sensitive cathodes. Glassy carbon electrodes covered with single-wall carbon nanotubes (SWCNTs) with covalently bonded perfluoroaromatic groups were shown to be more sensitive to oxygen,...
-
Boron doped Nanocrystalline Diamond-Carbon Nanospike Hybrid Electron Emission Source
PublikacjaElectron emission signifies an important mechanism facilitating the enlargement of devices that have modernized large parts of science and technology. Today, the search for innovative electron emission devices for imaging, sensing, electronics, and high-energy physics continues. Integrating two materials with dissimilar electronic properties into a hybrid material is an extremely sought-after synergistic approach envisioning a...
-
An investigation of microstructural basis for corrosion behavior of Al-CNT composites fabricated by SPS
PublikacjaIn this research effect of the addition of multi-wall carbon nanotubes (MWCNTs) as additive powder on microstructure and corrosion behavior of fabricated Al-CNT composites was studied. The aluminum powder and CNTs were mixed with high energy planetary ball-mill. It is observed that by increasing milling time, the uniformity of CNTs on aluminum matrix and consequently corrosion resistance of Al-CNT composite is increased. On the...
-
MINERAL CONTENT OF TREE SAP FROM THE SUBCARPATHIAN REGION
Publikacjabut also as medicinal substance in folk medicine. Traditionally, it was used to treat various conditions, mostly anaemia and chronic fatigue. This study has been designed to establish the content of metallic elements (sodium, potassium, calcium, magnesium, zinc and copper) in sap collected from eight different species (silver birch, downy birch, hornbeam, Norway maple, boxelder maple, black walnut, black alder and white willow)...
-
Tuning Electrochemical Performance by Microstructural Optimization of the Nanocrystalline Functional Oxygen Electrode Layer for Solid Oxide Cells
PublikacjaFurther development of solid oxide fuel cell (SOFC) oxygen electrodes can be achieved through improvements in oxygen electrode design by microstructure miniaturisation alongside nanomaterials implementation. In this work, improved electrochemical performance of an La0.6Sr0.4Co0.2Fe0.8O3-d (LSCF) cathode was achieved by the controlled modification of the La0.6Sr0.4CoO3-d (LSC) nanocrystalline interlayer introduced between a porous...
-
Design and characterization of apatite La9.8Si5.7Mg0.3O26±δ-based micro-tubular solid oxide fuel cells
PublikacjaIn this study, electrolyte-supported (Cell A) and anode-supported (Cell B) micro-tubular solid oxide fuel cells (SOFCs) based on the La9.8Si5.7Mg0.3O26±δ (LSMO) electrolyte is built through an extrusion and dip-coating processes. The formulations and process conditions for these cells are established and optimized. Both cell configurations show no visible delamination or cracking, and reaction zones and inter-diffusion of any species...
-
A Multi Rig Screening Test for Thin Ceramic Coatings in Bio - Tribological Applications
PublikacjaA method is presented for the comparative testing of wear resistance of ceramic coatings made from materials potentially feasible in tribo - medical applications, mainly orthopaedic implants made from ceramics coated metals for low cost, long life and low wear particle emission into the body. The method was devised as the main tool for use in research and is comprised of flat on flat and ball on flat surface (sliding) tests. Seven...
-
Characteristics of La0.8Sr0.2Ga0.8Mg0.2O3-delta -supported micro-tubular solid oxide fuel cells with bi-layer and tri-layer electrolytes
PublikacjaIn this study, La0.8Sr0.2Ga0.8Mg0.2O3−δ (LSGM)-supported micro tubular solid oxide fuel cells (T-SOFCs) with two different configurations, one containing an LSGM–Ce0.6La0.4O2−δ (LDC) bi-layer electrolyte (Cell A) and one containing an LDC–LSGM–LDC tri-layer electrolyte (Cell B), were fabricated using extrusion and dip-coating. After optimizing the paste formulation for extrusion, the flexural strength of the dense and uniform LSGM...
-
Effects of La0.8Sr0.2MnO3 and Ag electrodes on bismuth-oxide-based low-temperature solid electrolyte oxygen generators
PublikacjaIn this study, La0.8Sr0.2MnO3 (LSM) was used as the ceramic electrode in a (Bi1.50Y0.50)0.98Zr0.04O3+δ (BYO)-based solid electrolyte oxygen generator (SEOG) and its performance was compared with that of a previously studied high-fire Ag electrode. Among La0.6Sr0.4Co0.2Fe0.8O3, LaNi0.6Fe0.4O3, Cu1.4Mn1.6O4, and LSM materials, only LSM materials did not trigger any chemical reaction or interdiffusion with BYO at temperatures up to...
-
Cyclic voltammetry curves of the V2O5 nanorods (Na-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanorods obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Cyclic voltammetry curves of the V2O5 nanorods (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Na-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Electrochemical impedance spectra and CV curves of V2O5 nanocrystals
Dane BadawczeThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanocrystals obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz...
-
Electrochemical impedance spectra and CV curves of V2O5 nanorods
Dane BadawczeThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanorods obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz for...
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...