Filtry
wszystkich: 1253
wybranych: 113
-
Katalog
- Publikacje 463 wyników po odfiltrowaniu
- Czasopisma 25 wyników po odfiltrowaniu
- Wydawnictwa 2 wyników po odfiltrowaniu
- Osoby 14 wyników po odfiltrowaniu
- Wynalazki 1 wyników po odfiltrowaniu
- Projekty 32 wyników po odfiltrowaniu
- Laboratoria 1 wyników po odfiltrowaniu
- Aparatura Badawcza 1 wyników po odfiltrowaniu
- Kursy Online 404 wyników po odfiltrowaniu
- Wydarzenia 7 wyników po odfiltrowaniu
- Dane Badawcze 303 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: JEZYK SQL
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 700°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon...
-
Luminescence properties of TeOx-Tb gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Tb gel. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The sol was...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C dependent on film thickness
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (2-3 AsP layers) were deposited on a silicon substrate and were annealing at 1000°C under an argon...
-
Luminescence properties of TeOx-Eu gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Eu gels. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The sol...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 500°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon...
-
Optical properties of TeOx gels doped with a mix of rare-earth ions
Dane BadawczeThe DataSet contains the UV-Vis spectra of the TeOx gels doped with a mix of rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the different molar concentration of rare-earth ions was added, nitrates were used...
-
Optical properties TeOx gels doped with the rare-earth ions
Dane BadawczeThe DataSet contains the UV-Vis spectra of TeOx gels doped with the rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of the rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
XRD patterns of TeOx powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised to 75°C for the...
-
Thermal behavior of TeOx xerogel powder under different atmospheres
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx xerogel powder measured under different atmospheres. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution...
-
Analysis of the electrical parameters of the LTO thin films
Dane BadawczeLithium titanate thin films were derived by sol-gel technique. Films with thickness ca. 800 nm were annealed for various time, in a range of 10h-80h at 550 deg. Electrical conductivity in a wide range of temperature was measured.
-
Thermal behavior of TeOx powder
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
Depth XPS profile of vanadium pentoxide
Dane BadawczeVanadium pentoxide sample was manufactured by sol-gel method and deposited on a substrate by spin coating technique. To determine depth profile of chemical composition of thin film, etching by Argon ion gun was used. Thin film was etched three times. Chemical composition was measured by XPS method.
-
Impedance spectroscopy of the lithium titanate doped by copper thin films
Dane BadawczeLithium titanate doped by copper thin films were derived by sol-gel method. Prepared gel was deposited by spin-coating technique. Samples with various content of Cu were measured by impedance spectroscopy method in a wide range of temperature, from -120 up to 150 deg.
-
TEM micrographs of V2O5 nanostructures
Dane BadawczeThe DataSet contains the TEM images of V2O5 nanostructures obtained by the sol-gel method.
-
Decomposition kinetics of vanadium xerogel powder
Dane BadawczeThe DataSet contains the TGA curves of vanadium As-prepared xerogel powder with different heating rates. The information about sol synthesis is described in the Journal of Nanomaterials.
-
XRD patterns of TeOx-BaO-BiO powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx-BaO-BiO powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor), barium carbonate, and bismuth carbonate with thetraetylene glycol, water, ethanol, and acetic acid. (Samples molar concentration: 73TeO2-4BaO-3Bi2O3 and 73TeO2-3BaO-4Bi2O3)....
-
Measurements of the chemical composition of LTO:Cu powders
Dane BadawczeLithium titanate doped by copper was measured by X-ray photoemission spectroscopy (XPS). For sol-gel synthesis lithium acetate dehydrate and titanium (IV) butoxide 97% and copper (II) nitrate from Alfa Aesar were used as a reagents. Cu precursor was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate...
-
Crystallization kinetics of V2O5 nanorods
Dane BadawczeThe DataSet contains the DSC curves of As-prepared xerogel powder with different heating rates. The information about sol synthesis is described in the Journal of Nanomaterials.
-
XRD investigations of the lithium titanate thin films
Dane BadawczeNanocrystalline thin films with 800 nm thickness were prepared by sol–gel method. To examine the influence of the annealing temperature on as-prepared films crystallization, the coatings were heated at temperature from 500 °C up to 600 °C for 20h. Structure of manufactured thin films was investigated using X-ray diffraction (XRD). The most visible...
-
XPS study of the lithium titanate doped by copper
Dane BadawczeLithium titanate doped by copper was measured by X-ray photoemission spectroscopy. For sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal...
-
SEM micrographs of morphology evolution of V2O5 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of morphology evolution of vanadium pentaoxide nanostructures obtained by the sol-gel, depending on annealing temperature under synthetic air. The results show that the morphology dependent on the annealing temperature.
-
Cyclic voltammetry curves of the V2O5 nanorods (Na-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanorods obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
XRD patterns of V2O5 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of vanadium pentaoxide nanostructures obtained by the sol-gel with different annealing temperatures under synthetic air. The results show that crystallinity dependent on the annealing temperature.
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Na-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
XRD patterns of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
Rate performance of the V2O5 nanocrystals as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
XRD patterns of V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that crystallinity dependent on the annealing temperature.
-
Cyclic voltammetry curves of the V2O5 nanorods (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Rate performance of the V2O5 nanorods as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
Thermal properties of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the DSC and TG curves of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere at the selected temperature: 500C, 600C, and 1000C.
-
SEM micrographs of morphology evolution of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-800C. The...
-
Attitudes to tree removal on private property in rural and urban Polish municipalities.
Dane BadawczeThe urban-rural divide is an important factor known to affect public opinion on issues related to environmental protection and management. The present data set allows for a deeper understanding of this issue with respect to policies dealing with tree removal on private property in two municipalities located in southern Poland: Racibórz (an urban municipality)...
-
Morphological and electrochemical characterization of ceramic carbon foam electrodes water treatment applications
Dane BadawczeThis dataset contains morphological and electrochemical characterization of ceramic carbon foam employed as an electrode (CFFE) for the oxidation of a target pollutant. The dataset includes:
-
SEM micrographs of morphology evolution of V2O3 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that the morphology dependent on the annealing temperature.
-
Cycling performances of the V2O5 nanorods as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 and 2C current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1. The...
-
Cycling performances of the V2O5 nanocrystals as cathode material in Li-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 and 2C current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1. ...
-
Cycling performances of the V2O5 nanostructures as cathode material in Na-ion batteries
Dane BadawczeThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanostructures with different morphology obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here...
-
FTIR spectra of V2O5 nanostructures
Dane BadawczeThe DataSet contains FTIR spectra of vanadium pentaoxide nanostructures obtained by the sol-gel with different annealing temperatures under synthetic air.
-
Electrochemical impedance spectra and CV curves of V2O5 nanocrystals
Dane BadawczeThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanocrystals obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz...
-
Electrochemical impedance spectra and CV curves of V2O5 nanorods
Dane BadawczeThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanorods obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz for...
-
FTIR spectra of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the FTIR spectra of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
Structural investigations of the LTO:Cu thin films
Dane BadawczeLithium titanate (Li1+xTi2-xO4) doped with Cu2+ ions was synthesized by sol-gel processing method. The structure was characterized by X-ray Diffraction (XRD). All samples revealed presence of LTO spinel phase. X-ray pattern of undoped LTO was free of any impurities and other crystal phases. Similarly, samples with low amount of copper dopant (x = 0.05...
-
Linear impedance of V2O5 nanorods obtained at 903K
Dane BadawczeThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 500°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 500°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 1000°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 1000°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 650°C under reducing atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 650°C under a reducing atmosphere (95% Ar 5% H2). The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 400°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 400°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 700°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 700°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Linear impedance of V2O5 nanorods obtained at 913K
Dane BadawczeThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...