Filtry
wszystkich: 3379
wybranych: 528
-
Katalog
- Publikacje 1283 wyników po odfiltrowaniu
- Czasopisma 7 wyników po odfiltrowaniu
- Osoby 9 wyników po odfiltrowaniu
- Wynalazki 2 wyników po odfiltrowaniu
- Projekty 1 wyników po odfiltrowaniu
- Laboratoria 3 wyników po odfiltrowaniu
- Aparatura Badawcza 4 wyników po odfiltrowaniu
- Kursy Online 40 wyników po odfiltrowaniu
- Wydarzenia 2 wyników po odfiltrowaniu
- Dane Badawcze 2028 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: MMG
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 100 mm stroke subjected only to a mass load of 640 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 300 mm stroke subjected only to a mass load of 1530 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 150 mm stroke subjected only to a mass load of 1040 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 150 mm stroke subjected only to a mass load of 640 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 900 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 300 mm stroke subjected only to a mass load of 2570 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 150 mm stroke subjected only to a mass load of 2570 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 100 mm stroke subjected only to a mass load of 750 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 300 mm stroke subjected only to a mass load of 1040 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 100 mm stroke subjected only to a mass load of 1530 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 150 mm stroke subjected only to a mass load of 1640 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 1100 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 2570 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Ellipsometric monitoring during the polarization studies of Mg corrosion in alkaline environment
Dane BadawczeThe dataset contains the ellipsometric results from the Mg polarization studies aiming at understanding the Mg(OH)2 passive layer formation mechanism and conditions. The single-wavelength ellipsometer ELX-02C from Dr Riss GmbH was utilized, operating He-Ne laser at 632.8 nm. The polarization conditions for the experiment are depicted in the related...
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - 3D fracture scan
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
Frequency Response Functions for Sandvik CoroBore 825 XL boring tool, 733 mm
Dane BadawczeFrequency Response Functions (FRF) obtained for Sandvik CoroBore® 825 XL mounted at WHN 13-15 TOS VARNSDORF CNC machine at the minimum extension of the spindle adaptor. Tool set to bore a hole with a diameter 733mm
-
EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.5
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.6
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - CMOD - force record, a0/W = 0.6
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 60 mm) - CMOD - force record, a0/W = 0.6
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 50 mm) - CMOD - force record, a0/W = 0.5
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
Raw data for the paper "Mutually polarizable QM/MM model with in situ optimized localized basis functions"
Dane BadawczeThis dataset contains raw data used to generate plots in the paper Mutually polarizable QM/MM model with in situ optimized localized basis functions. The paper is devoted to a second generation of the TINKTEP model -- an QM/MM approach combining linear-scaling DFT (ONETEP) and a polarizable force field (AMOEBA).
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - CMOD - force record, a0/W = 0.5
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
The microstructure of AA5754 alloy under corrosion in alkaline media (pH=11) with 20 mM of various carboxylic acids
Dane BadawczeThis dataset contains scanning electron microscopy (SEM) micrographs taken for polished aluminum AA5754 alloy samples, exposed for 100 min in bicarbonate buffer (pH=11) with the addition of 20 mM of carboxylic acids, namely: citric acid, malic acid, maleic acid, succinic acid, tartaric acid, tricarballylic acid and serine. The goal of this study was...
-
The microstructure of AA5754 alloy under corrosion in alkaline media (pH=11) with 4.5 mM of various carboxylic acids
Dane BadawczeThis dataset contains scanning electron microscopy (SEM) micrographs taken for polished aluminum AA5754 alloy samples, exposed for 100 min in bicarbonate buffer (pH=11) with the addition of 4.5 mM of carboxylic acids, namely: citric acid, malic acid, maleic acid, succinic acid, tartaric acid, tricarballylic acid and serine. The goal of this study was...
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 10 mm
Dane BadawczeOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 14 mm
Dane BadawczeOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 20 mm
Dane BadawczeOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.88 mm measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Measurement file of PEEK 70 mm bushing measurements in original condition perforemed on custom-built 3d measuring stand
Dane BadawczeAfter manufacturing process (lathe turning) bearing was measured on custom bulit measurement stan developed during research project financed by National Centre of Science. Measurements consist of 110 000 points in 3D space taken on bushing inner surface. Bearing was measured taking vertical steps of 0,2 mm.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Substrate characterization in a electrochemically derived Manganium-Cobaltium thin films
Dane BadawczeManganium-Cobaltium thin films were electrochemically deposited on a Ni foams subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
IKE1-IKE3 (C-1305 derivatives) inhibitory effect of the Yeast Topoisomerase II relaxation activity
Dane BadawczeInhibition of Yeast Topoisomerase II were analyzed according to relaxation assay kit from Inspiralis. Briefly, 250 ng of supercoiled pBR322 DNA, 1 mM ATP, 1-200 μM of analyzed compound were mixed with reaction buffer (1 mM Tris-HCl (pH 7.9), 10 mM KCl, 0.5 mM MgCl 2, 0.2 % (v/v) glycerol). The reaction was initiated by the addition of an enzyme, allowed...
-
Mn-Co nanofilms on nickel foam measured by XPS mehod
Dane BadawczeManganium-Cobaltium based thin films were electrochemically deposited on a Ni based subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
The complete lists of 1D reversible number-conserving cellular automata with radius one of up to 7 states
Dane BadawczeThis dataset contains complete lists of all one-dimensional reversible number-conserving k-ary cellular automata with radius one of up to 7 states, i.e. with state sets {0,1}, {0,1,2}, {0,1,2,3}, {0,1,2,3,4}, {0,1,2,3,4,5} and {0,1,2,3,4,5,6}.
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Involvement of human glutathione S-transferase M1-1 in the glutathione conjugation of the antitumor unsymmetrical bisacridine derivative C-2028.
Dane BadawczeUnsymmetrical bisacridines (UAs) are a novel potent class of antitumor-active therapeutics. The aim of this study was to investigate the possible role of human glutathione S-transferase M1-1 (hGSTM1-1) in the glutathione (GSH) conjugation of a representative UA, C‑2028.
-
Non-enzymatic glutathione-mediated conjugation of unsymmetrical bisacridine C-2028 with anticancer activity
Dane BadawczeThe presented data complement the studies on the interplay between C-2028 (anticancer-active unsymmetrical bisacridine) and the glutathione S-transferase/glutathione (GST/GSH) system.
-
Glutathione conjugation of the antitumor-active 1-nitroacridine derivatives compounds C-857 and C-1748 – the major role of glutathione S-transferase M1-1
Dane BadawczeObjectives: C-857 and C-1748 are antitumor-active agents, monomers of unsymmetrical bisacridine derivatives. The aim of this study was to analyze their glutathione (GSH) conjugation in vitro in the presence of glutathione S-transferase (GST) M1-1.
-
X-ray Photoelectron Spectroscopy studies of ammonium vanadate
Dane BadawczeThe DataSet contains the high-resolution XPS studies of the ammonium vanadate nanostructures obtained by the hydrothermal method. XPS analyses were carried out with an X-ray photoelectron spectrometer (Omicron NanoTechnology) with a 128-channel collector. The measurements were performed at room temperature in an ultra-high vacuum condition (below 1.1x10-8...
-
Chemical composition of La-Sr-Ce-Ni-Ti ceramics material measured by XPS method
Dane BadawczeLa-Sr-Ce-Ni-Ti (LSCNT) based ceramics sample was manufactured by standard solid state reaction.Prepared powder was pressed into pilled and sintered in a furnace in air atmosphere for 10h. Annealing temperature was 1200 Celsius degree. To calculate chemical composition and determine valence states of the elements, X-Ray photoemission spectroscopy (XPS)...
-
Study of the chemical state of Gd in a Ba-La-Gd-Co based ceramic
Dane BadawczeBarium, Lanthanum, Gadolinium and Cobaltium precursors were used for production of ceramic materials. Samples were produced by standard solid state reaction. Samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing on a Gadolinum were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology....
-
The effect of chitosan concentration and molecular weight on endotoxin content
Dane BadawczeThe dataset includes results to determine the effect of chitosan concentration and molecular weight on endotoxin content as well as the effect of purification methods. The endotoxin concentration was determined using the PyroGene Recombinant Factor C Endpoint Fluorescent Assay. Chitosan 0.6% in 0.1M glycolic acid from Chemat LMW, MMW, and HMW were used...