Filtry
wszystkich: 1869
wybranych: 50
-
Katalog
- Publikacje 1681 wyników po odfiltrowaniu
- Czasopisma 5 wyników po odfiltrowaniu
- Osoby 37 wyników po odfiltrowaniu
- Wynalazki 6 wyników po odfiltrowaniu
- Projekty 10 wyników po odfiltrowaniu
- Laboratoria 1 wyników po odfiltrowaniu
- Zespoły Badawcze 4 wyników po odfiltrowaniu
- Aparatura Badawcza 4 wyników po odfiltrowaniu
- Kursy Online 29 wyników po odfiltrowaniu
- Wydarzenia 2 wyników po odfiltrowaniu
- Dane Badawcze 90 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: anionic surfactants
-
Autocorrelation function for the chosen effective potential of the diatomic silver anion
Dane BadawczeThe process of a two-channel decay of the diatomic silver anion (Ag2-), namely the spontaneous electron ejection giving Ag2 + e- and the dissociation leading to Ag- + Ag is theoretically studied. The ground state potential energy curves (PECs) of the neutral silver dimer and anionic silver diatomic molecule are calculated using the single reference...
-
Non-adiabatic coupling elements between the diatomic silver anion and neutral silver dimer plus continuum electron
Dane BadawczeThe process of a two-channel decay of the diatomic silver anion (Ag2-), namely the spontaneous electron ejection giving Ag2 + e- and the dissociation leading to Ag- + Ag is theoretically studied. The ground state potential energy curves (PECs) of the neutral silver dimer and anionic silver diatomic molecule are calculated using the single reference...
-
The biotic and abiotic mercury at the coastal zone of Gulf of Gdańsk
Dane BadawczeConcentration of neurotoxin Hg (mercury) was determined monthly form 01.2012 to 05.2013 (total and suspended) in the surface microlayer and the surface water as well as in: phytoplankton, zooplankton, epilithon, epifithon, phytobenthos (macroalgae and angiosperms), zoobenthos, and in the sediment. The study was conducted in the coastal zone of the Puck...
-
The BDD electrodes wettability modification by anodic polarization treatment
Dane BadawczeThe dataset contains the raw images, photographs obtained for the contact angle measurement at the surface of the boron-doped diamond (BDD) electrode. The measurements were carried out on after potentiodynamic polarization procedure, at various anodic polarization scan range (no polarization - HTBDD; 1.0 V; 1.4 V; 1.9 V; 2.5 V vs Ag|AgCl, scan rate...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Potential energy curves and spectroscopic parameters of the diatomic silver anion and neutral silver dimer
Dane BadawczeThe process of a two-channel decay of the diatomic silver anion (Ag2-), namely the spontaneous electron ejection giving Ag2 + e- and the dissociation leading to Ag- + Ag is theoretically studied. The ground state potential energy curves (PECs) of the neutral silver dimer and anionic silver diatomic molecule are calculated using the single reference...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Selection of material for infiltration of non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ
Dane BadawczeThe porous electrodes used for the infiltration were prepared from A-site non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ synthesized by the conventional solid state reaction method. Screen printed electrodes (0.5 cm2) on CGO-20 substrate, were fired at 800 °C for 2 hours in an air atmosphere. Infiltration of the scaffolds was performed by a water-based precursor...
-
The rovibrational energy levels of the diatomic silver anion and neutral silver dimer
Dane BadawczeThe process of a two-channel decay of the diatomic silver anion (Ag2-), namely the spontaneous electron ejection giving Ag2 + e- and the dissociation leading to Ag- + Ag is theoretically studied. The ground state potential energy curves (PECs) of the neutral silver dimer and anionic silver diatomic molecule are calculated using the single reference...
-
SEM micrographs of cavitation erosion-corrosion of aluminium alloy 2024 with anodic polarization
Dane BadawczeThe dataset contains Scanning Electron Micrographs of aluminium alloy 2024 samples made after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The experiment duration was 240 min, with cyclic cavitation exposure in on/off cycles 30s:30s. The electrolyte was 0.1 M KNO3 solution. Some samples were anodically...
-
THERMION-C2S_10 Ionic thermoelectri effect in the phase transition in Cu2Se
Dane BadawczeThe dataset contains results of measurements of the ionic thermoelectric effect in copper selenide with Cu1.99Se and Cu1.8Se compositions. X-Ray diffraction data, SEM images and EDX spectra of the samples are also in the dataset.
-
The spontaneous electron emission and rotational predissociation lifetimes of the diatomic silver anion
Dane BadawczeThe process of a two-channel decay of the diatomic silver anion (Ag2-), namely the spontaneous electron ejection giving Ag2 + e- and the dissociation leading to Ag- + Ag is theoretically studied. The ground state potential energy curves (PECs) of the neutral silver dimer and anionic silver diatomic molecule are calculated using the single reference...
-
Results of the effect of mixtures of ketoprofen with three anions on the germination of Sorghum bicolor (sorghum) seeds
Dane BadawczeThe research data includes an attempt to verify whether the addition of anions (bromide, chloride and fluoride) at levels found in the environment would affect the toxicity of pharmaceuticals to Sorghum Bicolor grain. Ion concentrations were selected based on studies of water samples collected in water bodies receiving wastewater from wastewater treatment...
-
The microstructure of aluminium alloys AA1050 and AA7075 subjected to anodic polarization at 8V in KOH electrolyte
Dane BadawczeThe dataset contains SEM pictures of the microstructure of aluminum alloy AA1050 and AA7075 exposed in aqueous KOH in the pH range between 14–11. Two sets of samples are presented, revealing the topography of the alloys when exposed to aggressive media under open circuit potential conditions as well as when subjected potentiodynamic polarization ranging...
-
Influence of the presence of rhamnolipids and ionic cross-linking conditions on the mechanical properties of alginate hydrogels.
Dane BadawczeThe dataset contains the results of determination the effect of rhamnolipids concentration, calcium chloride concentration and ionic cross-linking time on the mechanical properties of alginate hydrogels prepared by immersing the alginate mixture limited by the dialysis membrane in an appropriate cross-linking solution containing calcium ions. The mechanical...
-
Gold nanocubic structures functionalization with organic layers
Dane BadawczeThis dataset contains the XPS spectra obtained for gold nanocubes (AuNC), which were deposited at the gold electrode surface and dried. The AuNC's were first functionalized with either cysteamine in EtOH or mercaptopropionic acid in EtOH. The concentration of these compounds was 20 mM. The interaction of the functionalized with the AuNC surface was...
-
Alms-panel of Anton Moeller in St. Mary's Church in Gdańsk
Dane BadawczeThe data set concerns epigraphy. It refers to the Alms-panel placed in St. Mary’s Church in Gdańsk, that is the work of Gdańsk painter Antoni Moller, made in 1607, or rather – to be more specific – to lower part of this work, which are the verses from Holy Bible. Data set contains one general photo of the inscription, transcription of its text in Latin...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
The scanning spreading resistance microscopy (SSRM) of some CoCrMo alloys subjected to electrochemical litography
Dane BadawczeThe dataset contains the results of the experiment consisting of performing electrochemical lithography on the surface of the CoCrMo prosthetic alloy. First, by applying local anodic polarization, oxide structures were created on the surface of the material. Next, they were imaged in the SSRM (scanning spreading resistance microscopy) mode to visualize...
-
The electrochemical studies of CB-PLA surface activation by electrolysis in 1M NaOH
Dane BadawczeThe dataset contains the electrochemical studies performed under different conditions of surface activation of the CB-PLA 3D printed electrodes. The activation was performed by electrolysis in 1M NaOH solution under cycling polarization with different anodic or cathodic overpotentials (data in different subfolders). The file names contain the exact...
-
The cyclic voltammetry studies of CB-PLA electrode after surface activation by electrolysis in 1M NaOH
Dane BadawczeThe dataset contains the electrochemical studies performed for surface activation of the CB-PLA 3D printed electrodes by electrolysis in 1M NaOH solution. The studies were performed after treatment at an anodic overpotential of 1V, found to be optimal for surface activation. The measurements were carried out with cyclic voltammetry (CV) under different...
-
Electrochemical impedance spectroscopy measurements - conductivity vs. temperature and conductivity vs. oxygen partial pressure - BaCe0.6Zr0.2Y0.1Tb0.1O3-δ
Dane BadawczeThe dataset consists of two main catalogs consisting of measurement data: of the electrical conductivity of the BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) sample as a function of temperature and of the electrical conductivity as a function of oxygen partial pressure (pO2). Measurements as a function of temperature were carried out in dry and wet air (pH2O ~...
-
Imaging of the effects of pitting corrosion with the use of AFM
Dane BadawczePitting corrosion is a local attack on a metal surface, limited to a point or small area, which appears as a hole. Pitting corrosion is one of the most harmful forms of corrosion due to the fact that it is associated with small, difficult to detect damage, that can even lead to perforation of the structure. A single pit may range in size from micrometers...
-
Adiabatic calorimetry results for fresh concrete mixes M0 and M100
Dane BadawczeAdiabatic calorimetry results for fresh 3D printed concrete mixes (M0 and M100) determined using Controls S.p.A., Italy calorimeter
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B48/#A45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B37/#A35
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B21/#A21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 25 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B41/#A39
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A39/#B41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A23/#B22
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 12 min. The...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A35/#B37
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B39/#A41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#A47
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 20 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B34/#A33
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A45/#B48
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#B45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 90 min. The test...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A41/#B39
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The...
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A25/#B21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B22/#A23
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 6 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A33/#B34
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...