SPTNO ceramics measured by XPS method
Open Research DataSPTNO (Sr-Pr-Ti-Ni-O) ceramic were manufactured by solid state reaction, from oxides compounds. Synthesis conducted in air atmosphere at temperature in a range of 800-900 deg. Chemical composition of prepared materials were measured by XPS (X-Ray photoemision spectroscopy) method. UHV OmicronNanotechnology system with 128 channel Argus hemispherical...
-
Ograniczenie trwałości skojarzeń ceramicznych w wyniku propagacji pęknięć powierzchniowych = Fatigue life limitation of ceramic materials due to surface crack propagation
PublicationPrzedstawiono krótką analizę literaturową dotyczącą mechanizmów propagacji pęknięć w materiałach ceramicznych oraz wyniki dotychczasowych badań doświadczalnych wybranych materiałów ceramicznych z uwzględnieniem wpływu pęknięć powierzchniowych na trwałość ceramicznych skojarzeń tocznych.
-
Materiały ceramiczne w łożyskach ślizgowych
PublicationOpisano obszary zastosowań ceramiki maszynowej w węzłach ślizgowych maszyn. Przedstawiono rodzaje ceramiki stosowane w łożyskowaniu ślizgowym. Przedstawiono produkowane fabrycznie ceramiczne łożyska ślizgowe.
-
Characteristics of LaCo 0.4 Ni 0.6-x Cu x O 3-δ ceramics as a cathode material for intermediate-temperature solid oxide fuel cells
PublicationIn this study, the effects of Cu-ion substitution on the densification, microstructure, and physical properties of LaCo0.4Ni0.6-xCuxO3-δ ceramics were investigated. The results indicate that doping with Cu ions not only enhances the densification but also promotes the grain growth of LaCo0.4Ni0.6-xCuxO3-δ ceramics. The Cu substitution at x ≤ 0.2 can suppress the formation of La4Ni3O10, while the excess Cu triggers the formation...
-
Effect of chemical composition on corrosion and wear behaviour of the composite Ni-Fe-Al2O3 coatings.
PublicationPrzedstawiono wyniki badań powłoki kompozytowej otrzymanej przez osadzanie katodowe galwaniczne w roztworze zawierającym sole niklu, żelaza oraz cząstki ceramiki Al2O3 o różnej wielkości i stężeniu. Wykazano, że charakterystyka ceramiki posiada wpływ na szybkość korozji i zużycia ściernego. W szczególności, zawartość ceramiki wpływa dodatnio na odporność na zużycie ścierne, ale nieco obniża odporność na zużycie korozyjne.
-
Kuei Suan Jen Hsueh Pao/ Journal of the Chinese Ceramic Society
Journals -
MAX phase ternary carbide derived 2-D ceramic nanostructures [CDCN] as chemically interactive functional fillers for damage tolerant epoxy polymer nanocomposites
Publication -
Badania uszkodzeń powłok ceramicznych wskutek tarcia ślizgowego w ruchu postępowo-zwrotnym = Wear pattern testing of ceramic coatings under reciprocating sliding
PublicationBadano (wykorzystując mikroskop optyczny oraz skaningowy) morfologię uszkodzeń wybranych powłok ceramicznych ( m.in. DLC z dodatkiem wolframu) nakładanych na podłoże stalowe, będących skutkiem tarcia slizgowego w ruchu postępowo-zwrotnym skojarzenia kula-powierzchnia płaska. Ślady zużycia na kulach, czyli obszary wygładzonych plateau, mają kształt zbliżony do elipsy. Praca, przy zmiennym zwrocie sił stycznych działających na powierzchnię...
-
The structure of vanadate glass-ceramics containing BaTiO3.
Open Research DataThe structure of vanadate glass-ceramics doped with BaTiO3 was measured by SEM technique. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on...
-
The morphology of vanadate glass-ceramics containing BaTiO3
Open Research DataThe morphology of vanadate glass-ceramic doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Investigations of the valence state of Co in a MnCoO ceramics
Open Research DataMcCoO ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. Chemical behaviour of the Cobaltium was measured by XPS method. The analyses were...
-
A Novel Microstructural Evolution Model for Growth of Ultra-Fine Al2O3 Oxides from SiO2 Silica Ceramic Decomposition during Self-Propagated High-Temperature Synthesis
Publication -
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Open Research DataThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Linear impedance of vanadate glass-ceramics containing BaTiO3
Open Research DataThe linear impedance of vanadate glass-ceramics containing BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
Sb measurements in a Bi-Sb-Te ceramics materials
Open Research DataThe influence of the temperature of the annealing of ceramic materials with the composition Bi0.5Sb1.5Te3O9 was investigated. The materials were annealed at the temperature of 440 degrees Celsius and 450 degrees Celsius. There were no significant differences in the valence of antimony and other elements.
-
Influence of the annealing condictions on the chemical structure of LaBaGdCo ceramics
Open Research DataCeramic samples based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by solid state reaction. After sintring in a furnance, samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology. XPS analysis...
-
Lanthanum investigations in ceramics annealed in a dry and wet atmosphere
Open Research DataCeramics based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by standard solid state reaction from oxides and carbonate powders. After sintring, samples were annealed for 2 hours or 72 hours at 300 Celsius degree in a both: wet and dry atmosphere. Results of annealing on a chemical composition and valence state of lanthanum were observed...
-
Autonomic hybrid photovoltaic installations supported by thermoelectric generators
PublicationGeneratory termoelektryczne są urządzeniami dokonującymi bezpośredniej konwersji energii cieplnej na elektryczną.W ostatnich latach obserwuje się dynamiczny rozwój ich technologii, konstrukcji oraz obszarów zastosowań. Ponieważ ich sprawności systematycznie rosną, zatem w niektórych realizacjach celowe staje się ich zastosowanie do wspomagania autonomicznych hybrydowych instalacji fotowoltaicznych.W artykule dokonano przeglądu...
-
Numerical analysis of crack propagation in silicone nitride
PublicationThe properties of ceramics, specifically low density, high hardness, high temperature capability and low coefficient of thermal expansion are of most interest to rolling element manufacturers. The influence of ring crack size on rolling contact fatigue failure has been studied using numerical fracture analysis. Such cracks are very often found on ceramic bearing balls and decrease fatigue life rapidly. The numerical calculation...
-
Chłodzenie materii poprzez fluorescencję antystokesowską
Publicationnane są różne metody chłodzenia wykorzystujące procesy termodynamiczne, zjawiska termoelektryczne i magnetoelektryczne. W artykule przedstawiono możliwości chłodzenia materii poprzez fluorescencję antystokesowską materiału luminezującego oświetlanego światłem laserowym o określonej długości fali. Materiałami szczególnie korzystnymi są szkła domieszkowane metalami ziem rzadkich n.p. szkło typu ZBLAN, zawierające iterb. Układy takie...
-
A Pilot Study on Machining Difficult-to-Cut Materials with the Use of Tools Fabricated by SLS Technology
PublicationThe growing use of contemporary materials in various industrial sectors, such as aerospace, automotive, as well as the oil and gas industry, requires appropriate machining methods and tools. Currently, apart from the necessity to obtain high-dimensional and shape accuracy, the efficiency and economic aspects of the selected manufacturing process are equally important, especially when difficult-to-cut materials, such as hard and...
-
Badania porównawcze docierania powierzchni płaskich elementów miedzianych, ceramicznych i z węglików spiekanych = Comparative research of lapping of flat surfaces of parts made from copper, ceramics and sintered carbides
PublicationPrzedstawiono badania porównawcze jakości i intensywności docierania elementów miedzianych, ceramicznych i z węglików spiekanych. Analizowano skażenie powierzchni miedzi ścierniwem oraz porównano mechanizmy usuwania materiału w przypadku obróbki metali i ceramiki.
-
Analysis of the properties of the YSTF ceramics materials before and after reduction
Open Research DataThe valence of titanium in reduced YSTF ceramics materials was investigated. Ceramics were reduced by annealing in a hydrogen atmosphere. For comparison unreduced sample was also measured. Valance state was measured by XPS method.
-
The topography of Bi2VO5.5 ceramic measured with SEM and confocal microscope
Open Research DataThe topography of Bi2VO5.5 ceramics was measured by SEM and confocal microscope.
-
Tool wear, surface roughness, cutting temperature and chips morphology evaluation of Al/TiN coated carbide cutting tools in milling of Cu–B–CrC based ceramic matrix composites
Publication -
The structure of Bi2VO5.5 ceramic prepared by 3 different ways measured with X-ray diffraction
Open Research DataThe structure of Bi2VO5.5 ceramics was measured by XRD.
-
Laser stimulated third harmonic generation studies in ZnO–Ta 2 O 5 –B 2 O 3 glass ceramics entrenched with Zn 3 Ta 2 O 8 crystal phases
Publication -
Sebastian Lech Wachowski dr inż.
PeopleBorn in 1987 in Bydgoszcz, Poland. In 2012 graduated MSc in Applied Physics: Nanotechnology and in 2017 finished, with honours, PhD in physics at Gdańsk University of Technology. Since the beginning of his academic journey interested in functional materials, especially in high-tech ceramics. Devoted to the development of high temperature protonic conductors for water vapour electrolyzers and fuel cells. During his career has several...
-
Synteza i badanie właściwości materiałów termoelektrycznych typu AgSbTe2-xSex
PublicationMateriały termoelektryczne, takie jak domieszkowane chalkogenki AgSbTe2, są przedmiotem dużego zainteresowania w poszukiwaniach nowych rozwiązań energetycznych. Celem badań była synteza materiałów termoelektrycznych o stechiometrii AgSbTe2-xSex metodą redukcji tlenków i określenie ich morfologii oraz niektórych parametrów termoelektrycznych. Otrzymane próbki cechowały niejednorodność i wielofazowość. Materiały wykazywały przewodność...
-
The morphology of vanadate glass-ceramics containing BaTiO3 measured with the use of AFM
Open Research DataThe structure of vanadate glass-ceramics doped with BaTiO3 was measured by AFM technique. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on...
-
Ocena stanu powierzchni kulek ceramicznych po nagniataniu tocznym stali hartowanej Cf53
PublicationW artykule przedstawiono wyniki z badań eksperymentalnych dotyczących przydatności kulek wykonanych z ceramiki technicznej, do nagniatania tocznego, narzędziami z dociskiem hydrostatycznym. W badaniach wykorzystano narzędzie umożliwiające wymianę kulek nagniatających. Badania wykonano poprzez nagniatanie wałków wykonanych ze stali Cf53 w stanie utwardzonym (zahartowanym). Wyniki badań obejmują charakterystyki stanu powierzchni...
-
Results of abrasive slurry dosage in lapping process
PublicationPrzedstawiono wyniki badań dawkowania zawiesiny ściernej w docieraniu powierzchni płaskich elementów ceramicznych. Analizowano wpływ dawkowania na podstawowe parametry chropowatości powierzchni ceramiki Al2O3 i Al2O3-ZrO2.
-
Dissolution of Nb-doped hydroxyapatite prepared via low-temperature mechanochemical method: Spectroscopy studies
PublicationCalcium phosphate glass ceramics with nominal hydroxyapatite stoichiometry doped with niobium were synthesized using simple as well as low-temperature mechanochemical method and then in the form of compressed pellet were submitted to the static dissolution process in distilled water for one month. The results of structural analysis, performed mainly on the base of spectroscopic methods such as: infrared absorption spectroscopy,...
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Open Research DataElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
X-Ray photoemission spectroscopy measurements of the Nb-V-Sr-O ceramics
Open Research DataNiobium doped strontium vanadate based perovskite SrV1-xNbxO3-δ materials were prepared via conventional solid state reaction (SSR) method. For comparison, different samples with a various amount of niobium dopant in the structure were synthesized; x = 0; 0,2; 0,5; 0,8 and 1. Samples were sintered by two-steps: first under a pure hydrogen (purity >99.999%)...
-
ZUŻYCIE POWIERZCHNI KULEK CERAMICZNYCH W PROCESIE NAGNIATANIA TOCZNEGO STALI HARTOWANEJ
PublicationPrzedstawiono wyniki z badań eksperymentalnych dotyczących przydatności kulek wykonanych z ceramiki technicznej, do nagniatania tocznego, narzędziami z dociskiem hydrostatycznym. W przeprowadzonych badaniach zastosowano narzędzie umożliwiające wymianę kulek ceramicznych zastosowanych jako elementów nagniatające. Badania wykonano poprzez nagniatanie próbek - wałków wykonanych ze stali Cf53 w stanie utwardzonym (zahartowanym). Wyniki...
-
D.C. electrical measurements of Bi2VO5.5 ceramic measured at high temperature region
Open Research DataD.C. electrical properties of Bi2VO5.5 ceramic was measured.
-
Wpływ dawkowania zawiesiny ściernej na efekty docierania powierzchni płaskich
PublicationPrzedstawiono wyniki badań dawkowania zawiesiny ściernej podczas docierania powierzchni płaskich. Określono wpływ wielkości dawki ścierniwa na wydajność obróbki i podstawowe parametry chropowatości powierzchni. Obrabiano elementy z ceramiki tlenkowej oraz miedziane.
-
Analiza czasochłonności docierania technologicznego powierzchni płaskich w operacjach montażowych.
PublicationPrzedstawiono wyniki analiz docierania i mikroszlifowania elementów płaskich na docierarce jednotarczowej mikroziarnami węglika krzemu. Obrabiano elementy ze stali 100Cr oraz z tlenkowej ceramiki technicznej Al2O3. Analizowano czas obróbki i koszty operacji.
-
Udział nośny powierzchni elementów ceramicznych i węglików spiekanych po docieraniu.
PublicationPrzedstawiono wyniki badań docierania jednotarczowego powierzchni elementów z ceramiki technicznej i węglików spiekanych. Analizowano jakość obróbki i udział nośny powierzchni po docieraniu. Docieranie powierzchni płaskich jest technologią pozwalającą uzyskać duży udział nośny.