Hydrothermal modification of TiO2 nanotubes in water and alkali metal electrolytes (LiNO3, NaNO3, KNO3) – Direct evidence for photocatalytic activity enhancement
PublikacjaThe influence of hydrothermal annealing (HA) of TiO2 nanotubes (TiO2-NTs) in various baths (H2O, LiNO3, NaNO3, KNO3 performed for 4 h, 24 h, 64 h), on their photocatalytic and photoelectrocatalytic properties, was studied. The use of electrolytes was to enable the monitoring of photoactivity changes as a result of the expected impact on the population of hydroxyl groups on the surface. The assumption turned out to be correct and...
Rok 2021
-
Hydrothermal Cobalt Doping of Titanium Dioxide Nanotubes towards Photoanode Activity Enhancement
PublikacjaDoping and modification of TiO2 nanotubes were carried out using the hydrothermal method. The introduction of small amounts of cobalt (0.1 at %) into the structure of anatase caused an increase in the absorption of light in the visible spectrum, changes in the position of the flat band potential, a decrease in the threshold potential of water oxidation in the dark, and a significant increase in the anode photocurrent. The material...
-
Influence of alkali metal cations on the photoactivity of crystalline and exfoliated amorphous WO3 – photointercalation phenomenon
PublikacjaIn order to investigate the effect of photointercalation on photoelectrochemical properties, two types of WO3-based photoanodes, bulk and exfoliated have been prepared and investigated. An aqueous exfoliation method is introduced for the simple fabrication of amorphous and hydrated WO3 nanomaterial using commercial bulk WO3 precursor. The comparison of obtained material with bulk WO3 was performed using Raman, UV–vis, and XPS as...
Rok 2020
-
Diatoms Biomass as a Joint Source of Biosilica and Carbon for Lithium-Ion Battery Anodes
PublikacjaThe biomass of one type cultivated diatoms (Pseudostaurosira trainorii), being a source of 3D-stuctured biosilica and organic matter—the source of carbon, was thermally processed to become an electroactive material in a potential range adequate to become an anode in lithium ion batteries. Carbonized material was characterized by means of selected solid-state physics techniques (XRD, Raman, TGA). It was shown that the pyrolysis...
-
Enhanced Photoelectrocatalytical Performance of Inorganic-Inorganic Hybrid Consisting BiVO4, V2O5, and Cobalt Hexacyanocobaltate as a Perspective Photoanode for Water Splitting
PublikacjaThin layers of BiVO4/V2O5 were prepared on FTO substrates using pulsed laser deposition technique. The method of cobalt hexacyanocobaltate (Cohcc) synthesis on the BiVO4/V2O5 photoanodes consists of cobalt deposition followed by electrochemical oxidation of metallic Co in K3[Co(CN)6] aqueous electrolyte. The modified electrodes were tested as photoanodes for water oxidation under simulated sunlight irradiation. Deposited films...
-
Improving the Performance of a Graphite Foil/Polyaniline Electrode Material by a Thin PEDOT:PSS Layer for Application in Flexible, High Power Supercapacitors
PublikacjaIn this study, we present a novel strategy for enhancing polyaniline stability and thus obtaining an electrode material with practical application in supercapacitors. A promising (graphite foil/polyaniline/poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) GF/PANI/PEDOT:PSS) electrode material was characterized and used in the construction of a symmetric supercapacitor that provides an outstanding high power density. For this...
-
Nano Tin/Tin Oxide Attached onto Graphene Oxide Skeleton as a Fluorine Free Anode Material for Lithium-Ion Batteries
PublikacjaHerein, we show a composite formation method of tin/tin oxide nanoparticles with graphene oxide and CMC based on laser ablation technique as an electrode material for energy storage devices. The material exhibited a three-dimensional conducting graphene oxide network decorated with tin or tin oxide nanoparticles. The structure, homogeneous distribution of nanoparticles, and direct contact between inorganic and organic parts were...
-
Photoinduced K+ Intercalation into MoO3/FTO Photoanode—the Impact on the Photoelectrochemical Performance
PublikacjaIn this work, thin layers of MoO3 were tested as potential photoanodes for water splitting. The influence of photointercalation of alkali metal cation (K+) into the MoO3 structure on the photoelectrochemical properties of the molybdenum trioxide films was investigated for the first time. MoO3 thin films were synthesized via thermal annealing of thin, metallic Mo films deposited onto the FTO substrate using a magnetron sputtering...
-
The effect of morphology and crystalline structure of Mo/MoO3 layers on photocatalytic degradation of water organic pollutants
PublikacjaMolybdenum oxide layers were formed by anodization of the Mo metallic foil in a water/ethylene glycol-based electrolyte containing fluoride ions. The as-prepared, amorphous samples were annealed in air at different temperatures in a range from 100 �C to 700 �C. The crystal phase and morphology of anodized and annealed MoO3 layers were investigated using X-ray diffraction, Raman spectroscopy, and scanning electron microscopy. The...
Rok 2019
-
A negative effect of carbon phase on specific capacity of electrode material consisted of nanosized bismuth vanadate embedded in carbonaceous matrix
PublikacjaLithium-ion batteries (LIBs) are widely used all over the world. The LIBs belong to a renewable energy source and energy storage devices. The increase in energy demand causes that new materials of higher energy and higher power densities are still under investigation. Herein, we compare electrochemical properties of bismuth vanadate (BiVO4) embedded and not embedded into carbonaceous matrix as an anode material along with structural...
-
Electrochemical behavior of a composite material containing 3D-structured diatom biosilica
Publikacja3D-structured diatom biosilica mixed with conducting carbon black was investigated as an active electrode material for lithium-ion batteries. Diatom biosilica was obtained by cultivation of the selected diatom species under laboratory conditions. Several instrumental techniques (XRD, FTIR, Raman, SEM-EDX, TGA) were used to characterize the physicochemical properties of applied biosilica. It was evidenced that the prepared new composite...
-
The bismuth vanadate thin layers modified by cobalt hexacyanocobaltate as visible-light active photoanodes for photoelectrochemical water oxidation
PublikacjaBismuth vanadate thin films deposited using the pulsed laser deposition technique were modified using cobalt hexacyanocobaltate (Cohcc). The 2-step method of Cohcc nanocubes preparation was applied: i) metallic cobalt deposition and ii) cobalt electrooxidation in Co(CN)63− containing electrolyte. The presence of CN stretching vibrations was confirmed by Raman spectroscopy. The energy band gap was equal to 2.5 eV and was estimated...
-
Widening of the electroactivity potential range by composite formation – capacitive properties of TiO2/BiVO4/PEDOT:PSS electrodes in contact with an aqueous electrolyte
PublikacjaComposites based on the titania nanotubes were tested in aqueous electrolyte as a potential electrode material for energy storage devices. The nanotubular morphology of TiO2 was obtained by Ti anodization. TiO2 nanotubes were covered by a thin layer of bismuth vanadate using pulsed laser deposition. The formation of the TiO2/BiVO4 junction leads to enhancement of pseudocapacitance in the cathodic potential range. The third component,...
Rok 2018
-
Does the low optical band gap of yellow Bi3YO6 guarantee the photocatalytical activity under visible light illumination?
PublikacjaBi3YO6, which is known as an ionic conductor, was tested here as an electrode and photoanode in contact with aqueous electrolytes. Bi3YO6 was deposited onto the Pt substrate and the such prepared electrode was polarized in various aqueous electrolytes. The optical energy band gap of the material equal to 1.89 eV was determined using the Kubelka-Munk function resulting from the UV-Vis spectrum (allowed indirect transition) and also...
-
Electrochemical and photoelectrochemical properties of the interface between titania nanotubes covered by conducting polymer in aqueous by conducting polymer in aqueous electrolytes – The effect of various geometry and electrolytes concentration
PublikacjaIn the present work we show the impact of nanotubes (NTs) geometry of titania utilized as a substrate in organic-inorganic systems acting as a p-n junction on efficient conversion of radiation energy into electrochemical energy. The electrolytic bath composition and electrolysis conditions were controlled in order to obtain TiO2NTs of various geometry as a result of electrochemical oxidation of titanium foil. The electrode material...
-
The influence of photointercalaction and photochromism effects on the photocatalytic properties of electrochemically obtained maze-like MoO3 microstructures
PublikacjaMolybdenum oxide (α-MoO3) thin films with oriented crystalline facets were synthesised by anodization of Mo foils. The obtained samples were exposed to UV–Vis illumination in aqueous electrolytes providing different cations. The morphology and structure of modified samples were investigated. The effect of photointercalated alkali metal cations (Li+, Na+, K+) on optical and structural properties was studied using UV–vis and Raman...
-
The influence of polarization of titania nanotubes modified by a hybrid system made of a conducting polymer PEDOT and Prussian Blue redox network on the Raman spectroscopy response and photoelectrochemical properties
PublikacjaIn this work we show the impact of applied potential on network vibrations and photoelectrochemical properties of a composite material containing hydrogenated titania nanotubes and poly (3,4-ethylenedioxythiophene) with iron hexacyanoferrate (H-TiO2/pEDOT:Fehcf) acting as a redox centre. For this purpose, Raman spectroscopy measurements under the working electrode (WE) polarization were carried out, allowing investigation of changes...
-
Titania nanotubes modified by a pyrolyzed metal-organic framework with zero valent iron centers as a photoanode with enhanced photoelectrochemical, photocatalytical activity and high capacitance
PublikacjaThe paper discusses the synthesis, photoelectrochemical and electrochemical behaviour of titania nanotube arrays modified by a pyrolyzed metal-organic framework (MOF). A poly(3,4–ethylenedioxyphene) (PEDOT) matrix with an embedded inorganic network of iron hexacyanoferrate (BP) covering TiO2 nanotubes (TNT) is used as a MOF for the further sintering procedure, resulting in a novel, thin film of carbonaceous wrap supported Fe catalytic...
Rok 2017
-
Biosilica from sea water diatoms algae—electrochemical impedance spectroscopy study
PublikacjaHere, we report on an electrochemical impedance study of silica of organic origin as an active electrode material. The electrode material obtained from carbonized marine biomass containing nanoporous diatoms has been characterised by means of XRD, IR, SEM and EIS. Dif- ferent kinds of crystallographic phases of silica as a result of thermal treatment have been found. The electrode is electrochemically stable during subsequent cyclic...
-
Electrodes consisting of PEDOT modified by Prussian Blue analogues deposited onto titania nanotubes – Their highly improved capacitance
PublikacjaIn this work we present the outstanding energy storage of prepared inorganic-organic heterojunction where hydrogenated ordered titania nanotubes (H-TiO2NT) were modified by the hybrid made of poly(3,4-ethylenedioxythiophene) (pEDOT) and iron hexacyanoferrate centres (Fehcf, Prussian Blue). The material TiO2NT/pEDOT:Fechf was obtained electrochemically by means of: anodization, hydrogenation and finally, electropolymerization of...
-
Fabrication and photoactivity of organic-inorganic systems based on titania nanotubes and PEDOT containing redox centres formed by different Prussian Blue analogues
PublikacjaHerein, the heterojunction composed of an inorganic substrate: ordered hydrogenated titania nanotubes (H-TiO2NTs) and a deposited organic film: poly(3,4-ethylenedioxythiophene) (PEDOT) is reported. The conducting polymer is modified with different transition metal haxacyanoferrates (Mehcf), wherein as metal: copper, iron, cobalt and nickel are introduced. The presence of various metal centres provides characteristic redox activity...
-
Flexible dye-sensitized solar cells based on Ti/TiO2 nanotubes photoanode and Pt-free and TCO-free counter electrode system
PublikacjaFlexible dye-sensitized solar cells (DSSCs) are getting more attention compared to standard glass covered DSSCs due to their unique commercial applications (e.g. tents or sail surfaces) and the possibility of rolling up into a small, portable device. In this work, titania nanotubes (TiO2 NT) modified with titania nanoparticles (TiO2 NP) were photoelectrochemically characterized as an anode for flexible dye-sensitized solar cells....
-
Optical and photoelectrochemical characterization of pulsed laser deposited Bi4V2O11, BICUVOX, and BIZNVOX
PublikacjaThin layers of three compounds from the BIMEVOX family (Bi4V2O11, Bi2V0.9Cu0.1O5.35, and Bi2V0.9Zn0.1O5.35) were prepared via pulsed laser deposition technique on quartz, silicon, and platinum foil and tested as photoanodes for water photooxidation. The film formation, as well as the crystallization upon heating, was characterized using X-ray diffraction and Raman spectroscopy. The optical properties were investigated using spectroscopic...
-
Photocatalytical properties of maze-like MoO3 microstructures prepared by anodization of Mo plate
PublikacjaIn this work, we present a simple method of the formation of MoO3 microstructures via an electrochemical anodization of Mo plate carried out under varied conditions. The morphology, composition and structure of samples were investigated by SEM, EDX, XRD and Raman spectroscopy. The band gap energy was estimated using the Kubelka–Munk function and was found to be 2.87 eV. Finally, the photocatalytic activities of MoO3 samples were...
Rok 2016
-
Electroactive polymer/graphene oxide nanostructured composites; evidence for direct chemical interactions between PEDOT and GOx
PublikacjaThis work concerns electrochemical synthesis of nanocomposites consisting of conducting polymer and reduced graphene oxide (rGOx) as electrode materials for supercapacitors. The electrosynthesis was performed in an aqueous solution of the 3,4-ethylenedioxytiophene (EDOT) monomer and graphene oxide (GOx) without supporting electrolyte. The amount of GOx was optimized to obtain the best electrochemical performance of the nanocomposite...
-
Electrochemical and photoelectrochemical characterization of photoanodes based on titania nanotubes modified by a BiVO4 thin film and gold nanoparticles
PublikacjaTitania nanotubes (TNT) modified with thin films of bismuth vanadate (BiVO4) and gold nanoparticles (GNP) were photoelectrochemically characterized as photoanodes for water photooxidation. Presence of bismuth vanadate enhanced efficiency of photocurrent generation in comparison with pristine TNTs under visible light illumination. Besides an extended range of absorbed light, the presence of both BiVO4 and GNP reduced the charge...
-
Enhanced photoelectrochemical performance of inorganic-organic hybrid consisting of BiVO4 and PEDOT:PSS
PublikacjaThe PEDOT:PSS (poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate)) was electrodeposited on a thin layer of bismuth vanadate (BiVO 4 ) prepared using the pulsed laser deposition technique onto FTO. The inorganic-organic junction was characterized by Raman spectroscopy, UV-Vis spectroscopy and sc anning electron microscopy. Chronoamperometry curves, recorded under simulated solar light illumination,...
-
Highly stable organic–inorganic junction composed of hydrogenated titania nanotubes infiltrated by a conducting polymer
PublikacjaA poly(3,4-ethylenedioxythiophene) conducting polymer doped with poly(2-styrene sulfonate) (pEDOT:PSS) was efficiently electrodeposited on a layer composed of ordered titania nanotubes. TiO2 nanotubes were formed during an anodization process and, after calcinations, a layer was subjected to hydrogen plasma. Hydrogenation leads to Ti(III) formation, a decrease in resistance, and a huge increase of donor density when compared with...
-
Micropatterning of BiVO 4 Thin Films Using Laser-Induced Crystallization
PublikacjaRelatively high temperatures even up to 500 °C are required to obtain bismuth vanadate (BiVO4) films with the scheelite monoclinic (s-m) structure that shows the highest photocatalytic activity. This requirement limits the possible choice of substrates. Moreover, high quality thin layers of crystalline BiVO4 cannot be prepared with current methods. In this study a light-induced crystallization approach is presented, which is a...
-
Non-metaldoped TiO2 nanotube arrays for high efficiency photocatalytic decomposition of organic species in water
PublikacjaTitanium dioxide is a well-known photoactive semiconductor with a variety of possible applications. The procedure of pollutant degradation is mainly performed using TiO2 powder suspension. It can also be exploited an immobilized catalyst on a solid support. Morphology and chemical doping have a great influence on TiO2 activity under illumination. Here we compare photoactivity of titania nanotube arrays doped with non-metal atoms:...
-
Optimization of boron-doping process of titania nanotubes via electrochemical method toward enhanced photoactivity
PublikacjaIn this work, we were focused on the development of the electrochemical approach resulting in a stable boron doping of titania nanotubes. The doping procedure concerns anodic polarization of as-anodized titania in a H3BO3 solution acting as n boron precursor. The series of attempts were taken in order to elaborate the most beneficial doping conditions. The parameters of electrochemical doping allowing to obtain boron-doped titania...
-
Optimization of electrochemical doping approach resulting in highly photoactive iodine-doped titania nanotubes
PublikacjaThe paper focuses on the optimization procedure concerning the synthesis method resulting in highly ordered titania nanotubes doped with iodine atoms. The doping process was based on the electrochemical treatment of a titania nanotube layer immersed in a potassium iodide (KI) solution acting as an iodine precursor. A number of endeavors were undertaken in order to optimize the doping conditions. Electrolyte concentration, reaction...
-
Preparation and Characterization of Nanomaterial Consisting of Silica Aerogel & Carbon Tested as an Electrode in Non-Aqueous Media Containing Lithium Salt.
PublikacjaSilica aerogel (SiO2ag) was combined with carbonaceous material in the pyrolysis process of hydrocarbons. The obtained nanocomposite SiO2ag/C was amorphous, partially preserving the porous structure of SiO2ag. The specific surface area changes from 445.6 m2/g for pure SiO2ag to 205.52 m2/g SiO2ag/C. The 29Si MAS-NMR shows a three-dimensional matrix with silicon atoms connected to other silicon atoms by four...
-
Semi-transparent ordered TiO2 nanostructures prepared by anodization of titanium thin films deposited onto the FTO substrate
PublikacjaIn a significant amount of cases, the highly ordered TiO2nanotube arrays grow through anodic oxidationof a titanium metal plate immersed in electrolyte containing fluoride ions. However, for some practicalapplications, e.g. solar cells or electrochromic windows, the semi-transparent TiO2formed directly onthe transparent, conductive substrate is very much desired. This work shows that high-quality Ti coatingcould be formed at room...
-
Synthesis and photoelectrochemical behaviour of hydrogenated titania nanotubes modified with conducting polymer infiltrated by redox active network
PublikacjaIn this work, we show preparation of ordered inorganic-organic composite electrode material where hydrogenated titania nanotubes H-TiO2 with tubularly developed surface modified with poly(3,4-ethylenedioxythiophene) matrix permeated by Prussian Blue (PB) inorganic redox network in order to reach highly photoactive heterojunction. The polymer deposition was realized via two subsequent processes covering: i) potentiostatic polymerization...
-
Titania nanotubes infiltrated with conducting polymer PEDOT modified by Prussian Blue – a novel type of organic-inorganic heterojunction characterised with enhanced photoactivity.
PublikacjaA highly ordered p–n heterojunction was formed based on titania nanotubes containing a conducting polymer with Prussian blue matrix. The study demonstrates, for the first time, cases when a composite based on titania array scaffolding and Prussian blue embedded in PEDOT exhibits reversible FeII/FeIII redox activity. Highly enhanced photoactivity and capacitance of the obtained material are depicted in comparison to pristine titania....
-
Visible light activity of pulsed layer deposited BiVO4/MnO2 films decorated with gold nanoparticles: The evidence for hydroxyl radicals formation
PublikacjaThin films containing BiVO4 and MnO2 deposited on FTO and modified by Au nanoparticles were studied towards their photoelectrochemical and photocatalytical activities in an aqueous electrolyte. Electrodes were prepared by the pulsed laser deposition (PLD) method. The surfactant-free ablation process was used for preparation of the gold nanoparticles (GNP) water suspension. Obtained layers of varied thicknesses (27–115 nm) were...
Rok 2015
-
Electrochemical characterization of a composite comprising PEDOT/PSS and N doped TiO2 performed in aqueous and non-aqueous electrolytes
PublikacjaNitrogen doped titania (N-TiO2) was used as an inorganic component of composite electrodes containing poly(3,4-ethylenedioxythiophene) with poly(4-styrenesulphonate) PEDOT/PSS/N-TiO2. The composite materials were obtained by direct electrodeposition from an N-TiO2 suspension containing polyelectrolyte (NaPSS) and monomer EDOT. The electrodes were electrochemically tested in aqueous and non-aqueous electrolytes using cyclic voltammetry...
-
Enhanced photoelectrochemical and photocatalytic performance of iodine-doped titania nanotube arrays
PublikacjaThe paper discusses the synthesis and performance of iodine doped titania nanotube arrays exhibited under irradiation. The doping procedure was performed as an additional, electrochemical process carried out after formation of nanotube arrays via anodization of Ti substrate. The optical and structural properties were characterized using Raman, UV-vis, photoluminescence and X-ray photoelectron spectroscopy. The surface morphology...
-
Fabrication and properties of electrode material composed of ordered titania nanotubes and pEDOT:PSS
PublikacjaWe report on the two-stage preparation method of electrode material composed of titania nanotubes and poly(3,4-ethylenedioxythiopene):poly(2-styrenesulphonate) conductive polymer (pEDOT:PSS). Initially, titania nanotube arrays were produced by the anodization process of Ti substrate. Next, the polymer was potentiostatically deposited onto the thermally annealed nanotube arrays from the electrolyte containing monomer and counter...
-
Facile preparation of extremely photoactive boron-doped TiO2 nanotubes arrays
PublikacjaDoping of TiO2 nanotube arrays with boron was realized via electrochemical treatment of as-anodized titania immersed in electrolyte containing boric acid. The photoactivity of doped and pure titania was examined by means of photoelectrochemical and photocatalytic response under UV-vis irradiation. The results showed that photocurrent density of B-TNTs is remarkably higher (7.5 times) than density of pure TiO2 nanotube arrays. Furthermore,...
-
Novel nitrogen precursors for electrochemically driven doping of titania nanotubes exhibiting enhanced photoactivity
PublikacjaNitrogen doped titania nanotubes were successfully sensitized by electrochemical method, i.e. as-anodized titania was immersed in different amine (diethyleneamine-DETA, triethyleneamine-TEA, ethylenediamine-EDA) and urea (U) solution and a constant potential was applied. The highly ordered morphology of fabricated N-TiO2 was investigated by using scanning electron microscopy. Spectroscopic techniques, i.e. UV-Vis spectroscopy,...
-
Photoelectrochemical properties of BIMEVOX (ME=Cu, Zn, Mn) electrodes in contact with aqueous electrolyte
PublikacjaLayered oxide Bi4O2O11 and mixed oxides of bismuth, vanadium and a third metal (ME = Cu, Zn, Mn) were synthesized and characterized using XRD, Raman and SEM. The energy band gap (Eg) of samples determined using UV–VIS reflectance spectra equals to 2.46, 2.34, 2.27 and 2.18 eV for Bi4V2O11, BICUVOX (Bi2V1 − xCuxO5.5 − 3x/2), BIZNVOX (Bi2V1 − xZnxO5.5 − 3x/2) and BIMNVOX (Bi2V1 − xMnxO5.5 − x/2) (x = 0.1), respectively. Open circuit...
-
Thin layer of ordered boron-doped TiO2 nanotubes fabricated in a novel type of electrolyte and characterized by remarkably improved photoactivity
PublikacjaThis paper reports a novel method of boron doped titania nanotube arrays preparation by electrochemical anodization in electrolyte containing boron precursor – boron trifluoride diethyl etherate (BF3 C4H10O), simultaneously acting as an anodizing agent. A pure, ordered TiO2 nanotubes array, as a reference sample, was also prepared in solution containing a standard etching compound: ammonium fluoride. The doped and pure titania...
-
Tin oxide nanoparticles from laser ablation encapsulated in a carbonaceous matrix – a negative electrode in lithium-ion battery applications
PublikacjaThis report concerns carbonaceous electrodes doped with tin(II) oxide nanoparticles. Tin nanoparticles are obtained by pulsed laser ablation in water. Crystalline nanoparticles have been encapsulated in a carbonaceous matrix formed after pyrolysis of a mixture consisting of tin/tin(IV) oxide nanoparticles and gelatine. The obtained material is characterized by means of X-ray diffraction, selected area diffraction, scanning electron...
Rok 2014
-
Aquatic biomass containing porous silica as an anode for lithium ion batteries
PublikacjaA composite electrode was manufactured by pyrolysis of Red Algae (Polysiphonia fucoides) covered by diatoms (Diatomophyceae). Electrodes were tested as a half cell with capacity of 500 mA h g−1 after 80 cycles. XPS analysis shows formation of lithium silicate under reduction of silica in an aprotic electrolyte containing LiPF6 salt.
-
Determination of Chemical Diffusion Coefficient of Lithium Ions in Ceramics Derived from Pyrolysed Poly(1,2-dimethylsilazane) and Starch
PublikacjaThe apparent chemical diffusion coefficient Li+ (DappLI+) in pyrolysed poly(1,2-dimethylsilazane)/starch (PSN/S) (weight ratio: 30/70) ceramic anode composite is determined by galvanostatic intermittent titration technique (GITT). The electrode material composition is C6.00N0.14H0.47O0.12Si0.13. The calculated values of DappLI+, depend on the applied potential, vary from 10-14 to 10-9 [cm2/s]. The diffusion coefficient of lithium...
-
Electrochemical Activity of Electrode Material Consisting of Porous Copper and Silica Aerogel
PublikacjaElectrochemically obtained copper was combined with silica aerogel (SiO2ag). Obtained composite (SiO2@Cu/CuxOy) was tested as an electrode in contact with LiPF6 in EC/DMC electrolyte. The electrochemical measurements showed the presence of complex redox couple activities of SiO2@Cu/CuxOy. This experiment was employed to help in understanding the carbon role used as an electric contact for silica in Li-Ion batteries and clarify...
-
Electrochemical Characterization of Gelatine Derived Ceramics
PublikacjaNew materials obtained by pyrolysis of gelatine (G) and poly(1,2-dimethylsilazane) (PSN) (weight ratio: G/PSN 70/30) at temperatures 700 and 900 °C were characterized by SEM and Raman spectroscopy. The presence of ceramics influences on the cluster size of the materials. Electrochemical tests were performed by cyclic voltammetry and galvanostatic cyclic polarization. The capacity of G/PSN was 464 and 527 mAh/g for materials pyrolysed...
-
New ceramic materials derived from pyrolyzed poly(1,2-dimethylsilazane) and starch as a potential anode for Li-ion batteries
PublikacjaNewmaterialswere obtained by pyrolysis of starch (S) and poly(1,2-dimethylsilazane) (PSN) (weight ratio: PSN/S 30/70) at temperature a) 500 °C, b) 700 °C and c) 900 °C. Ceramic materials were characterized by infrared spectroscopy, TGA, Raman spectroscopy and SEM. New Si\O and shifted Si\C stretching vibration modes emerged confirming direct interaction between silicon originating fromsilazane and oxygen coming fromstarch. The...