Depth profile of the chemical composition of the Au-Ag multilayers
Dane BadawczeSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
Distance measurement by the low coherent interferometer
Dane BadawczeThe obtained data was acquired by the interferometric fiber-optic sensor of distance. The setup was constructed of a broadband light source working at the central wavelength of 1560 nm, an optical spectrum analyzer and a fiber-optic 2x1 coupler (with the power split 50:50). All elements were connected by standard single-mode optical fibers. The measurement...
-
Distance measurement by the low coherent interferometer with NND layer (the source wavelegth 1310 nm)
Dane BadawczeThe obtained data was acquired by the interferometric fiber-optic sensor of distance. The setup was constructed of a broadband light source working at the central wavelength of 1310 nm, an optical spectrum analyzer, and a fiber-optic 2x1 coupler (with the power split 50:50). All elements were connected by standard single-mode optical fibers. The measurement...
-
SEM images of dewetted gold films
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. as a result of dewetting process. Thin golds films were deposited using a table-top dc magnetron sputtering coater under pure Ar plasma conditions . The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness...
-
Oxidation of silver nanostructures
Dane BadawczeSilver nanostructures were prepared on Si substrate. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma. The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1 , and the incident power was in the range of 30–40 W. The layer thickness...
-
Comparison of XPS spectra of Ag3d for silver nanostructures and bulk material
Dane BadawczeAg nanostructures were prepared on borosilicate glass (Corning 1737F) and Si substrates. In both cases, the substrateswere cleaned with acetylacetone and then rinsed in ethanol. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The...
-
Investigation of plasmon resonance in a silver nanoparticles
Dane BadawczeSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
SEM images of tge gold nanostructures on silicon
Dane BadawczeAu nanostructures were prepared on Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air Products 99.999%)....
-
Simulation of perovskite-based CuI/CH3NH3PbI3/TiO2 solar cell performance
Dane BadawczeThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/TiO2 model structure (Model 1) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/SnO2 solar cell performance
Dane BadawczeThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/SnO2 model structure (Model 2) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/ZnO solar cell performance
Dane BadawczeThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/ZnO model structure (Model 3) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
TEM imaging of Ag-Au nanoalloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of metal thin layers (Au/Ag or Ag/Au) followed by annealing under 550 Celsius degree in an argon atmosphere. The basic single layer thickness was usually ca. 3 nm. For investigations two samples wih 50% Au and 50% Ag were selected and samples 1/3 Ag - 2/3 Au and 2/3 Ag - 1/3...
-
Formation of gold anostructures detected by SEM microscope
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air...
-
Hemocompatibility of nanocrystalline diamond layers
Dane BadawczeThe biocompatibility of the diamond films were investigated with whole human blood samples. Blood used in this study was drawn from 10 healthy human patients of different age, sex, and blood group. A 2 ml samples were collected into standard tubes with EDTA anticoagulation agent. Blood was used within 6 hours from the collection time. A reference blood...
-
Chemical analysis of the Au-Ag nanoaloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Data obtained by computation for X-ray imaging of grating with magnification factor equal 2 using oriented Gaussian beams
Dane BadawczeThe propagation of X-ray waves through an optical system consisting of grating and X-ray refractive lenses is considered. In this approach, the propagating wave is represented as a superposition of the oriented Gaussian beams. The direction of wave propagation in each Gaussian beam is consistent with the local propagation direction of the X-ray wavefront.
-
Data obtained by computation for X-ray imaging of grating with magnification factor equal 4 using oriented Gaussian beams
Dane BadawczeThe propagation of X-ray waves through an optical system consisting of grating and X-ray refractive lenses is considered. In this approach, the propagating wave is represented as a superposition of the oriented Gaussian beams. The direction of wave propagation in each Gaussian beam is consistent with the local propagation direction of the X-ray wavefront.
-
Data obtained by computation for X-ray imaging of grating with magnification factor equal 8 using oriented Gaussian beams
Dane BadawczeThe propagation of X-ray waves through an optical system consisting of grating and X-ray refractive lenses is considered. In this approach, the propagating wave is represented as a superposition of the oriented Gaussian beams. The direction of wave propagation in each Gaussian beam is consistent with the local propagation direction of the X-ray wavefront.
-
Data obtained by computation for X-ray imaging of grating without magnification using oriented Gaussian beams
Dane BadawczeThe propagation of X-ray waves through an optical system consisting of grating and X-ray refractive lenses is considered. In this approach, the propagating wave is represented as a superposition of the oriented Gaussian beams. The direction of wave propagation in each Gaussian beam is consistent with the local propagation direction of the X-ray wavefront.
-
Mn-Co nanofilms on nickel foam measured by XPS mehod
Dane BadawczeManganium-Cobaltium based thin films were electrochemically deposited on a Ni based subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
The influence of chitosan hydrogel coating on different redox probes kinetics
Dane BadawczeThis dataset contains cyclic voltammetry studies of three redox probes: 1 mM K3[Fe(CN)6], [K4Fe(CN)6], C12H14FeO2, and [Ru(NH3)6]Cl2 dissolved in 0.1 M KCl or PBS as the primary electrolyte. The studies are made for glassy carbon electrode (GC) and glassy carbon electrode covered with thin chitosan hydrogel membrane (C2A2). Cyclic voltammograms were...
-
Investigation of the C-1311 glucuronidation: an electrochemical approach
Dane BadawczeThis study was undertaken to investigate the glucuronidation of the compound C-1311 (5-diethylaminoethylamino-8-hydroxyimidazoacridinone – the model anticancer acridine derivative) using electrochemistry/mass spectrometry (EC/MS) as a complementary technique to in vitro (liver microsomes) and in silico approaches.
-
Sounding rocket temperature and heat transfer data
Dane BadawczeThis dataset contains temperature and heat transfer data measured during REXUS 25 sounding rocket HEDGEHOG Experiment launched from Esrange Space Centre, Kiruna, Sweden. For experiment details, please see: