Assessment of hydrogenation of deposited metal of P 62 MR covered electrodes
PublikacjaThe determination of diffusible hydrogen content in deposited metal of P 62 MR covered electrodes for manual metal arc welding by mercury method was carried out. The test results indicate that covered electrodes 62 P MR grade generate a mean of 4.02 ml/100g of diffusible hydrogen in deposited metal, which is consistent with H5 class.
-
Determination of moisture resistance of covered electrodes according to PN-EN ISO 14372
PublikacjaMoisture present in the electrode covering is one of the sources of diffusible hydrogen in welded joints. In order to study the diffusible hydrogen content in deposited metal, a stand for moisturizing covered electrodes, in accordance with the PN-EN ISO 14372 standard, was built. After the stand was completed, a test of moisturizing the electrodes was carried out and measurements of the diffusible hydrogen content in deposited...
-
Insightful Analysis of Phenomena Arising at the Metal|Polymer Interphase of Au-Ti Based Non-Enzymatic Glucose Sensitive Electrodes Covered by Nafion
PublikacjaThis paper focuses on the examination of glucose oxidation processes at an electrode material composed of gold nanoparticles embedded in a titanium template. Three dierent conditions were investigated: the chloride content in the electrolyte, its ionic conductivity and the presence of a Nafion coating. The impact of the provided environment on the oxidation reaction was evaluated by cyclic voltammetry (CV) and electrochemical impedance...
-
Effect of the welding environment and storage time of electrodes on the diffusible hydrogen content in deposited metal
PublikacjaIn the study the glycerin displacement method was used for determination of diffusible hydrogen content in deposited metal. Specimens were welded in the air and in the water with covered rutile electrodes. The first part of the specimens was made immediately after opening the package of the electrodes. The electrodes were then stored in opened packages in laboratory conditions that allowed for contact with the air for three years....
-
Effect of electrode waterproof coating on quality of underwater wet welded joints
PublikacjaIn this paper, the effects of different hydrophobic coatings on the surface of covered electrodes on the quality of wet welded carbon steel joints were discussed. Commonly available hydrophobic substances used in industrial applications were selected for the research. The aim of using waterproof coatings was to check the possibility to decreasing the susceptibility of highstrength low-alloy S460N steel to cold cracking. During...
-
Diffusible hydrogen content in deposited metal of multilayer welded joints
PublikacjaThe article describes manufacturing technology of multilayer joints in terms of control the diffusible hydrogen content. Diffusible hydrogen content in deposited metal for multilayer welded joints made of covered rutile electrodes or covered cellulosic and basic electrodes was determined. It was found that after four beads, the diffusible hydrogen content decreases in the case of the first technology from 36 ml/100 g to 18 ml/100...
-
Induced-fit binding of laccase to gold and carbon electrodes for the biological fuel cell applications
PublikacjaAnalogues of laccase natural substrates (syringic, veratric, ferulic, vanillic, isovanillic, 3,5-dimethoxybenzoic aldehydes) were employed to bind and orient laccase molecules in a way which facilitates adsorption of the catalyst molecules and their electrical connection with the conductive support. Laccase was bound efficiently to these substrates both on gold and carbon electrodes forming, respectively, 2D and 3D films sensitive...
-
Biobatteries and biofuel cells with biphenylated carbon nanotubes
PublikacjaSingle-walled carbon nanotubes covalently biphenylated are used for the construction of cathodes in a flow biobattery and in flow biofuel cell. Zinc covered with a hopeite layer is the anode in the biobattery and glassy carbon electrode covered with bioconjugates of single-walled carbon nanotubes with glucose oxidase and catalase is anode of the biofuel cell. The potentials of the electrodes are measured vs. the Ag/AgCl reference...
-
Anna Danuta Dettlaff dr inż.
OsobyTytuł magistra inżyniera uzyskała z wyróżnieniem w 2013 roku w Wydziale Chemii Analitycznej. W latach 2013-2017 była doktorantką na kierunku Technologia Chemiczna, podczas których zajmowała się pracą pt. "Badania nad nanokompozytami bazującymi na polimerach przewodzących oraz materiałach węglowych w celu zastosowania ich w superkondensatorach". W 2015 roku odbyła trzymiesięczny staż naukowy w Oldenburgu w Niemczech. Stopień doktora...
-
Weldability of S460ML High Strength Low Alloy Steel in Underwater Conditions
PublikacjaThe paper presents experimental evaluation of susceptibility of the high strength S460ML steel to cold cracking in the conditions of wet welding with the use of covered electrodes. From the results of Tekken tests it was found out that the investigated steel was characterised, in the conditions of the carried out experiments (underwater wet welding and air welding with rutile electrodes), of high susceptibility to cold cracking....
-
Effect of underwater wet welding conditions on the diffusible hydrogen content in deposited metal
PublikacjaIn the study mercury displacement method was used for determination of diffusible hydrogen amount in deposited metal obtained during underwater wet welding with covered electrodes in laboratory conditions according to a two-level full factorial design for three factors. The factors and their levels were chosen among conditions and parameters of welding in accordance with the results of own preliminary studies. A statistical analysis...
-
Aquatic biomass containing porous silica as an anode for lithium ion batteries
PublikacjaA composite electrode was manufactured by pyrolysis of Red Algae (Polysiphonia fucoides) covered by diatoms (Diatomophyceae). Electrodes were tested as a half cell with capacity of 500 mA h g−1 after 80 cycles. XPS analysis shows formation of lithium silicate under reduction of silica in an aprotic electrolyte containing LiPF6 salt.
-
Effect of Arc Strikes on High Strength Low Alloy Steels Welded by SMAW
PublikacjaWet welding with covered electrodes (Shielded Metal Arc Welding – SMAW) is the most commonly used method of carrying out welding repair works in a water environment. Limited visibility and the inability to move freely under water result in an increased risk of formation of welding imperfections such as lack of fusion, lack of penetration and arc strikes. The work focused on changes in the properties and structure of steel subjected...
-
Weldability of Underwater Wet-Welded HSLA Steel: Effects of Electrode Hydrophobic Coatings
PublikacjaThe paper presents the effects of waterproof coatings use to cover electrodes on the weldability of high-strength, low-alloy (HSLA) steel in water. With the aim of improving the weldability of S460N HSLA steel in water, modifications of welding filler material were chosen. The surfaces of electrodes were covered by different hydrophobic substances. The aim of the controlled thermal severity (CTS) test was to check the influence...
-
Weldability of S500MC Steel in Underwater Conditions
PublikacjaWet welding with the use of covered electrodes is one of the methods of underwater welding. This method is the oldest, the most economic and the most versatile. The main difficulties during underwater wet welding are: high cooling rates of the joint, the presence of hydrogen in the arc area and formation of hard martensitic structure in the weld. These phenomena are often accompanied by porosity of welds and large number of spatters,...
-
COLD CRACKING OF S460N STEEL WELDED IN WATER ENVIRONMENT
PublikacjaThis paper shows results of weldability testing of fine-grained high -strength low- alloy S460N steel welded in water environment by covered electrodes. The tests were carried out by using the CTS test specimens with fillet welds. Four specimens were welded under water and one specimen in air. Welded joints were subjected to non-destructive visual and penetration tests. The accepted joints were then subjected to macroscopic and...
-
Underwater Wet Repair Welding of API 5L X65M Pipeline Steel
PublikacjaThis paper presents results of the research of effect of polymer insulation of pipeline made of API 5L X65M steel as well as underwater wet welding parameters on properties of joints made by covered electrodes. Effect of heat input on structure and hardness of joints during repair of underwater pipeline was analyzed. Welding defects like microcracks, micro-lacks of fusion, slag inclusions, as well as HAZ hardness increase over...
-
The influence of the welding environment on the properties of Tekken joints made from S355J2C+N steel
PublikacjaThere are three main methods of underwater welding: dry, wet and intermediate between them, by using the local dry chamber. Due to low costs, the most common method is the wet welding with the use of covered electrodes. Water as a welding environment carries out a lot of problems. The first is limited visibility and instability of the welding arc. The biggest problem during underwater welding is high susceptibility to cold cracking,...
-
Temper bead welding of S420G2+M steel in water environment
PublikacjaThe article presents the idea of the use of Temper Bead Welding (TBW) technique to improve the weldability of high strength steel at underwater wet welding conditions. Wet welding method with the use of covered electrodes is described. This work shows results of metallographic examinations and hardness measurements of samples of S420G2+M steel with weld beads performed under water. It has been shown that Temper Bead Welding technique...
-
Role of bead sequence in underwater welding
PublikacjaThis paper presents examinations of the role of the bead sequence in underwater welding. Two specimens of wet welded layers made by covered electrodes with the use of normalized S355G10+N steel were welded by a reasonable bead sequence. For each specimen, metallographic macro- and micro-scopic tests were done. Then, Vickers HV10 hardness measurements were conducted for each pad weld in the welded layer. The results show that welding...
-
The abrasive wear resistance of coatings manufactured on high-strength low-alloy (HSLA) offshore steel in wet welding conditions
PublikacjaSome marine and offshore structure elements exploited in the water cannot be brought to the surface of the water as this will generate high costs, and for this reason, they require in-situ repairs. One of the repair techniques used in underwater pad welding conditions is a wet welding method. This paper presents an investigation of the abrasive wear resistance of coatings made in wet welding conditions with the use of two grades...
-
Oxygen biosensor based on carbon nanotubes directly grown on graphitic substrate
PublikacjaFilms of carbon nanotubes were synthesized on the graphitic substrates by CVD method in the presence of catalyst. Two different catalysts were used, that is nickel and iron, supported on graphitic substrates. The as-obtained nanotubes were analyzed by SEM imaging with EDX and Raman spectroscopy. The results revealed their multi-walled morphology. Free radical reaction was carried out in order to chemically functionalize synthesized...
-
Spawalność ferrytyczno-austenitycznej stali odpornej na korozję typu dupleks 2205 w warunkach podwodnych
PublikacjaPraca dotyczy problemów spawalności stali odpornej na korozję typu dupleks w warunkach spawania mokrego elektrodami otulonymi i lokalną komorą suchą. Całość rozprawy składa się z dwóch części. Część pierwsza to przegląd literatury, w którym omówiono główne problemy wynikające z przeniesienia procesu spawania pod wodę oraz sposoby minimalizowania negatywnego wpływu środowiska. Część druga jest częścią doświadczalną, zawiera tezę...
-
Fluoroaromatic substituents attached to carbon nanotubes help to increase oxygen concentration on biocathode in biosensors and biofuel cells
PublikacjaBased on the known ability of perfluorodecalin/perfluorohydrocarbons to enhance oxygen solubility we modified oxygen sensitive biocathode by adding perfluorinated components to the catholite. This procedure improved the efficiency of the oxygen sensitive cathodes. Glassy carbon electrodes covered with single-wall carbon nanotubes (SWCNTs) with covalently bonded perfluoroaromatic groups were shown to be more sensitive to oxygen,...
-
Improvement of S355G10+N steel weldability in water environment by Temper Bead Welding
PublikacjaThe normalized S355G10 + N steel was chosen for testing, it is used in a variety of applications including the building of offshore structures, which may require repairs in water environment. The main aim of the work was to check susceptibility to cold cracking for fillet welds – Controlled Thermal Severity (CTS) tests and butt welds – Tekken tests and in the next step evaluation of effectiveness of Temper Bead Welding (TBW) application...
-
Hydrogenation process ofTiO2/BiVO4/PEDOT:PSS observed by XPS method
Dane BadawczeTitania nanotubes synthesis was based on a two-stage anodization process at water/ethylene glycol (5%/95%) electrolyte containing 0.27 M NH4F and 1 M H3PO4 described previously. Anodization process was performed in two-electrode cell compartment using platinum mesh as a cathode. The distance between electrodes was about 2 cm. The anodization voltage...
-
Imaging and chemical investigation of silver coating
Dane BadawczeThe recovery of silver from materials such as plates, still used in clinical radiography [1], or scrap jewelery is still very popular. The subject of the research, part of which was microscopic imaging, was to recreate the behavior of an electrochemically deposited silver coating. The copper electrodes were covered with a layer of silver obtained from...
-
Dissimilar underwater wet welding of HSLA steels
PublikacjaThe high-strength low-alloy S460ML and S460N steels were chosen for underwater wet welding of dissimilar T-joints using covered electrodes. For improving the quality of joints, the temper bead welding (TBW) method was used. The application of TBW in pad welding conditions has been investigated earlier but the possibility of usage of this technique in welded joints was not analyzed. The main aim of the study was to check the influence...
-
APPLICATION POSSIBILITIES OF THE S960 STEEL IN UNDERWATER WELDED STRUCTURES
PublikacjaIn this paper, the application possibilities of the ultra-high strength (UHSS). Domex 960 steel in the underwater welded structures are analyzed. In the research, the investigated material has been tested in bead-on-plate wet welding conditions with the usage of different heat input values, namely 0.63 kJ/mm, 0.72 kJ/mm and 0.93 kJ/mm. Specimens were performed by the manual metal arc (MMA) welding method with the usage of rutile...
-
Scanning electrochemical micrographs of poly(lactic acid) 3D printed electrodes ablated by femtosecond laser
Dane BadawczeThe dataset contains the scanning electrochemical micrographs of the femtosecond laser (FSL) ablation at the surface of commercially available carbon black-filled poly(lactic acid) 3D printed electrode. The process is used for the increase of the charge transfer of this electrode in electrochemical studies.
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 33 mA. Sample 51.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 33 mA.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface emission....
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 204 mA. Sample 51, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 204 mA. Experiment run #1.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 561 mA. Sample 71, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 561 mA. Sample 71, experiment run #1.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 560 mA. Sample 42, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 560 mA. Sample 42. Experiment run #1.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 336 mA. Sample 71.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 336 mA. Sample 71.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 54 mA. Sample 61.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 54 mA. Sample 61.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 306 mA. Sample 51, run #3.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 306 mA. Experiment run #3. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 306 mA. Sample 51, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 306 mA. Experiment run #1. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 204 mA. Sample 51, run #8.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 204 mA. Experiment run #8. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 560 mA. Sample 42, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 560 mA. Sample 42. Experiment run #2.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 400 mA. Sample 42.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 400 mA. Sample 42.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 162 mA. Sample 61.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 162 mA. Sample 61.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 51 mA. Sample 51.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 51 mA.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface emission....
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,1 V at 561 mA. Sample 71, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,1 V and discharged to 10 mV by constant current 561 mA. Sample 71, experiment run #2The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 480 mA. Sample 42.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 480 mA. Sample 42.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,0 V at 561 mA. Sample 71.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,0 V and discharged to 10 mV by constant current 561 mA. Sample 71. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 102 mA. Sample 51, run #1.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 102 mA. Experiment run #1.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 27 mA. Sample 61.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 27 mA. Sample 61.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform surface...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 306 mA. Sample 51, run #2.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 306 mA. Experiment run #2. The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to ensure uniform...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,1 V at 561 mA. Sample 71, run #3.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,1 V and discharged to 10 mV by constant current 561 mA. Sample 71, experiment run #3.The images were taken with thermographic camera VigoCAM V50. The sample was covered by black graphite paint to...