Filtry
wszystkich: 5465
wybranych: 693
-
Katalog
- Publikacje 618 wyników po odfiltrowaniu
- Czasopisma 12 wyników po odfiltrowaniu
- Konferencje 1 wyników po odfiltrowaniu
- Wydawnictwa 1 wyników po odfiltrowaniu
- Osoby 30 wyników po odfiltrowaniu
- Wynalazki 1 wyników po odfiltrowaniu
- Projekty 5 wyników po odfiltrowaniu
- Laboratoria 3 wyników po odfiltrowaniu
- Aparatura Badawcza 3 wyników po odfiltrowaniu
- Kursy Online 251 wyników po odfiltrowaniu
- Wydarzenia 6 wyników po odfiltrowaniu
- Dane Badawcze 4534 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: CMM/CMMI
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 150 mm stroke subjected only to a mass load of 640 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 900 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 300 mm stroke subjected only to a mass load of 2570 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 150 mm stroke subjected only to a mass load of 2570 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 100 mm stroke subjected only to a mass load of 750 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 300 mm stroke subjected only to a mass load of 1040 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 50 mm piston diameter and 100 mm stroke subjected only to a mass load of 1530 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 63 mm piston diameter and 150 mm stroke subjected only to a mass load of 1640 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 1100 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
Dynamics of a linear pneumatic actuator with 80 mm piston diameter and 100 mm stroke subjected only to a mass load of 2570 g
Dane BadawczeThe aim of the study was to determine the dynamics of a linear pneumatic cylinder subjected only to mass load. An actuator of one of the well known European manufacturers was tested.The experiment were to measure pressure changes in both chambers of the actuator and the position of the piston during stroke and retracting. The test was repeated 11 times....
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - 3D fracture scan
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
Frequency Response Functions for Sandvik CoroBore 825 XL boring tool, 733 mm
Dane BadawczeFrequency Response Functions (FRF) obtained for Sandvik CoroBore® 825 XL mounted at WHN 13-15 TOS VARNSDORF CNC machine at the minimum extension of the spindle adaptor. Tool set to bore a hole with a diameter 733mm
-
EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.5
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.6
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - CMOD - force record, a0/W = 0.6
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 60 mm) - CMOD - force record, a0/W = 0.6
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 50 mm) - CMOD - force record, a0/W = 0.5
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
Raw data for the paper "Mutually polarizable QM/MM model with in situ optimized localized basis functions"
Dane BadawczeThis dataset contains raw data used to generate plots in the paper Mutually polarizable QM/MM model with in situ optimized localized basis functions. The paper is devoted to a second generation of the TINKTEP model -- an QM/MM approach combining linear-scaling DFT (ONETEP) and a polarizable force field (AMOEBA).
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - CMOD - force record, a0/W = 0.5
Dane BadawczeThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
The microstructure of AA5754 alloy under corrosion in alkaline media (pH=11) with 20 mM of various carboxylic acids
Dane BadawczeThis dataset contains scanning electron microscopy (SEM) micrographs taken for polished aluminum AA5754 alloy samples, exposed for 100 min in bicarbonate buffer (pH=11) with the addition of 20 mM of carboxylic acids, namely: citric acid, malic acid, maleic acid, succinic acid, tartaric acid, tricarballylic acid and serine. The goal of this study was...
-
The microstructure of AA5754 alloy under corrosion in alkaline media (pH=11) with 4.5 mM of various carboxylic acids
Dane BadawczeThis dataset contains scanning electron microscopy (SEM) micrographs taken for polished aluminum AA5754 alloy samples, exposed for 100 min in bicarbonate buffer (pH=11) with the addition of 4.5 mM of carboxylic acids, namely: citric acid, malic acid, maleic acid, succinic acid, tartaric acid, tricarballylic acid and serine. The goal of this study was...
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 10 mm
Dane BadawczeOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 14 mm
Dane BadawczeOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Mechanical properties of VL E27 steel for shipbuilding – tensile test in +20°C, specimens diameter 20 mm
Dane BadawczeOne of the basic divisions of steels used for ship hulls and ocean engineering structures is the division into: normal strength steels, high strength steels and extra high strength steels. The belonging to the group is determined by the mechanical properties of the steel, such as: yield point, ultimate strength and plastic elongation after fracture....
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.88 mm measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Measurement file of PEEK 70 mm bushing measurements in original condition perforemed on custom-built 3d measuring stand
Dane BadawczeAfter manufacturing process (lathe turning) bearing was measured on custom bulit measurement stan developed during research project financed by National Centre of Science. Measurements consist of 110 000 points in 3D space taken on bushing inner surface. Bearing was measured taking vertical steps of 0,2 mm.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Concrete temperature measurements of cubic specimens cured under isothermal and semi-adiabatic conditions
Dane BadawczeThe DataSet contains temperature measurements of concrete cubes (150 x 150 x 150 mm) cured under isothermal and semi-adiabatic conditions. The specimens were moulded from six types of concrete mixtures produced in the laboratory conditions. Mix #1: Portland cement CEM I 42.5R and gravel aggregate, mix #2: CEM I 42.5R and basalt aggregate, mix#3: Portland-composite...
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Acoustic emission signals in concrete beams under 3-point bending (plain concrete, steel fibre reinforced concrete, steel bar reinforced concrete)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of concrete beams with dimensions 40 x 40 x 160 cm3under the 3-point bending. Two concrete mixes, both based on the same design, were produced in the test programme. Mixture #1 was the plain concrete (PC), consisting of cement CEM I 42.5R (380 kg/m3), water (165 kg/m3), aggregate 0/2 mm (648...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #3)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #1)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #4)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #2)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Acoustic emission signals in concrete beams under 3-point bending (polyolefin and steel fibre concrete)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of concrete beams with dimensions 40 x 40 x 160 cm3 under the 3-point bending. All specimens were manufactured based on the same concrete mixture composed of cement CEM I 42.5R (380 kg/m3), water (165 kg/m3), aggregate 0/2 mm (648 kg/m3), aggregate 2/8 mm (426 kg/m3), aggregate 8/16 mm (754...
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Compression test results of fused filamend fabricated polylactyde and polylactyde with carbon fiber filler
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of cube specimens with dimensions 30 x 30 x 30 cm3. The specimens were additively manufactured with the fused filament fabrication (FFF) method. They used two different materials polylactide (PURE PLA) and polylactide with carbon fibre filler (PLA+CF). The specimens were segregated into three...
-
IKE1-IKE3 (C-1305 derivatives) inhibitory effect of the Yeast Topoisomerase II relaxation activity
Dane BadawczeInhibition of Yeast Topoisomerase II were analyzed according to relaxation assay kit from Inspiralis. Briefly, 250 ng of supercoiled pBR322 DNA, 1 mM ATP, 1-200 μM of analyzed compound were mixed with reaction buffer (1 mM Tris-HCl (pH 7.9), 10 mM KCl, 0.5 mM MgCl 2, 0.2 % (v/v) glycerol). The reaction was initiated by the addition of an enzyme, allowed...
-
Linear impedance of V2O5 nanorods obtained at 903K
Dane BadawczeThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 913K
Dane BadawczeThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 893K
Dane BadawczeThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Measurements of the heat of hydration released by concrete specimens cured under adiabatic conditions
Dane BadawczeThe DataSet contains measurements of heat of hydartion of concrete cubes (150 x 150 x 150 mm) cured under adiabatic conditions. The specimens were moulded from six types of concrete mixtures produced in the laboratory conditions. Mix #1: Portland cement CEM I 42.5R and gravel aggregate, mix #2: CEM I 42.5R and basalt aggregate, mix#3: Portland-composite...