Wyniki wyszukiwania dla: BIMETALLIC PHOTOCATALYST
-
Depth profile of the gold-silver bimetallic structures
Dane BadawczeSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
XPS measurement of the Fe-Ti based materials
Dane BadawczeThe mono‐ and bimetal‐modified (Pd, Cu) titanium(IV) oxide and iron oxide (III) photocatalysts were prepared by chemical reduction method and characterized using XPS method. The composition of elements incorporated in the surface layer of mono- and bimetallic photocatalysts was determined by XPS analysis, as well as the valence state of elements. Measurements...
-
Physicochemical and photocatalytic data of TiO2/MXene/MnFe2O4 photocatalysts
Dane BadawczeThis dataset includes data regarding the physicochemical properties (i.e. XRD, DR/UV-vis, TEM images, photoluminescence) and photocatalytic activity of TiO2/MXene/MnFe2O4 photocatalysts. The data comprise the results of the photocatalytic reaction of carbamazepine and ibuprofen degradation.
-
X-Ray diffraction of the metallic nanostructures
Dane BadawczeMetallic nanostructures (gold and silver) were manufactured as a thermal annealing of gold or silver thin film. Gold films with thickness of 2.8 nm were deposited on a silicon substrates using a table-top dc magnetron sputtering coater (EM SCD 500, Leica), equipped with quartz microbalance for in-situ thickness measurements. Films were deposited from...
-
XPS-Ni foam as received, after photocatalysis and after oxidation at 500_C.
Dane BadawczeThis dataset contains XPS spectra recorded for nickel foam as received from supplier, after photocatalytic process and after oxidation at 500C. Each set contains: survery spectrum, O1, C1s, Ni2p. The detailed equipment and measurement data was described in "readme XPS.txt" file
-
Interface diffusion between metallic nanoparticles and silicon substrate
Dane BadawczeInterface diffusion between metallic nanoparticles and silicon substrate was detected by EDX method. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.
-
Research 1: Heterojunction of (P, S) co-doped g-C3N4 and 2D TiO2 for improved carbamazepine and acetaminophen photocatalytic degradation
Dane BadawczeThe first research article consisted on the synthesis of phosphorus and sulfur co-doped graphitic carbon nitride incorporated in 2D TiO2 structure for solar-driven degradation of emerging pollutants from the group of pharmaceuticals not susceptible to biodegradation. The hybrid photocatalysts with different loadings of (P, S)-doped g-C3N4 were characterized...
-
Photocatalytic degradation of acetaldehyde in high temperature reaction chamber
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using TiO2 (titanium dioxide) as photocatalysts. It includes data on the influence of flow rate, TiO2 (titanium dioxide) filling the entire reactor, a thin layer of TiO2 (titanium dioxide) supported on KBr...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Dane BadawczeThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed to force the exsolution process of bimetallic nanoparticles.
-
SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of nickel (Ni) foam as received, after photocatalysis and after oxidation at 500_C.
Dane BadawczeThis dataset contains SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of Ni (nickel) foam as received from the supplier, after photocatalytic treatment and after oxidation at 500C. The detailed equipment and measurement data was described in "readme SEM.txt" file
-
TEM imaging of metal nanoparticle cross section
Dane BadawczeTEM microscope was used for a imaging of metallic nanostructures. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.
-
The reductivity of the transition metals - calculations
Dane BadawczeThe dataset includes the reduction enthalpy and Gibbs energy simulated for Co, Cu, Fe, La, Mo, Ni, Sr, Ti, and W from oxide form into metallic form in hydrogen. Simulations were performed using HSC Chemistry software.
-
Morphology of the gold nanoislands
Dane BadawczeDewetting of the thin metallic films leads to formation of an isolated islands. morphology of nanostructures was measured by SEM microscope. Thin gold films with a thickness of 1.2 nm, 1.5 nm and 3.4 nm were anealed at 550, 600 and 650 Celcius degress.
-
SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Dane BadawczeThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed in order to force the exsolution process of metallic nanoparticles.
-
Formation of gold nanostructures detected by XPS method
Dane BadawczeGold nanostructers were manufactured by thermal dewetting of thin film. Film with thickness of 2.8 nm was deposited by magnetron sputtering method. As a result of annealing at 550 deg, nanostructures appear. Bulk gold, as-deposited gold film and metallic nanostructures were measured by XPS method.
-
Dewetting of silver films detected by XPS method
Dane BadawczeDewetting of silver thin films was detected by XPS method. Thin metallic films were deposited by magnetron sputtering method. Formation of nanostructures , as a result of thermal annealing, was confirmed by SEM microscope. For comparision three samples were measured. Bulg gold, as-deposited silver film with thickness of 3 nm and nanostructures.
-
XPS measurements of the Fe-Bi based glass
Dane BadawczeFe-Si-O and Fe-Si-Pb-O glass was measured by XPS method. The influence of Pb dopand on the glass structure, including the valence of iron, was investigated. The influence of the annealing temperature on the behavior of iron in glass was also investigated. Studies have confirmed the mixed valence of iron in glasses and a high proportion of metallic Fe.
-
Photocatalytic decomposition of acetaldehyde over TiO2 (titanium dioxide) supported on nickel foam and Ni-doped (nickel-doped) TiO2
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using as photocatalytic systems TiO2 (titanium dioxide) supported on nickel foam, TiO2 supported on oxidized nickel foam and TiO2 doped by metallic nickel (Ni) powder. The detailed equipment and measurement...
-
Chemical investigations of the MoO3 doped by K films deposited FTO
Dane BadawczeMoO3 thin films were synthesized via thermal annealing of thin, metallic Mo films deposited onto the FTO substrate using a magnetron sputtering system. The influence of photointercalation of alkali metal cation (K+) into the MoO3 structure on the photoelectrochemical properties of the molybdenum trioxide films was investigated. The chemical characterisation...
-
XRD patterns of V2O5 thin film morphology dependent on substrate types
Dane BadawczeThe DataSet contains the XRD patterns of the V2O5 thin film structure dependent on substrate types. The as-prepared thin films were deposited on alumina, zirconium, zirconium oxide and metallic vanadium substrate, then was annealing under an oxidizing atmosphere at 600C for 10h.
-
XPS investigations of tge tin/tin oxides - CNT composites
Dane BadawczeThe composite of tin/tin oxide nanoparticles with graphene oxide and CMC based on laser ablation technique as an electrode material for energy storage devices were manufactured. The material exhibited a three-dimensional conducting graphene oxide network decorated with tin or tin oxide nanoparticles. The presence of tin/tin oxide in composites was...
-
XPS measurements of the iron elements covered by chromium
Dane BadawczeAnticorrosive coatings are an important issue in modern materials engineering. One of the most commonly used, for that coating materials, is chrome. Three metal elements were measured, named as Turcja, WB Tech and Nomet. Names were given according to producer of elements. XPS measurements of the Cr 2p region give an ansver concering on surface chemical...
-
SEM micrographs of V2O5 thin film morphology dependent on substrate types
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 thin film morphology dependent on substrate types. The as-prepared thin films were deposited on alumina, zirconium, zirconium oxide and metallic vanadium substrate, then was annealing under an oxidizing atmosphere at 600C for 10h. The results show that the morphology of...
-
The AFM topographic measurements of the surface heterogeneity of iron hexacyanoferrate on a steel surface
Dane BadawczeMeasurements in semi-contact mode. NTEGRA Prima (NT-MDT) device. NSG 01 probe.
-
Optical properties of tellurium dioxide thin films
Dane BadawczeTeO2 and TeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by optical spectroscopy. Metallic Te target and Te-Eu mosaic target with diameter of 50.8 mm were sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate...
-
Anomalous anisotropy of deuterium-grown boron-doped diamond and the role of boron-tetramers in the Mott-Insulator transition
Dane BadawczeWe show anisotropy in the superconductivity for boron-doped diamond thin films prepared with Microwave Plasma Assisted Chemical Vapor Deposition using deuterium-rich plasma. This anomalous phase transition is linked with the emergence of boson quantum entanglement states behaving as a bosonic insulating state. Here, we show that the superconducting...
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Dane BadawczeThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...