Filtry
wszystkich: 2838
wybranych: 125
-
Katalog
- Publikacje 1460 wyników po odfiltrowaniu
- Czasopisma 51 wyników po odfiltrowaniu
- Konferencje 919 wyników po odfiltrowaniu
- Osoby 117 wyników po odfiltrowaniu
- Projekty 2 wyników po odfiltrowaniu
- Kursy Online 15 wyników po odfiltrowaniu
- Wydarzenia 9 wyników po odfiltrowaniu
- Dane Badawcze 265 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: CONVERGENCE PATTERNS
-
XRD patterns of MXenes catalysts
Dane BadawczeData contain results from XRD measurements of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios....
-
XRD patterns of V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that crystallinity dependent on the annealing temperature.
-
XRD patterns of V2O5 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of vanadium pentaoxide nanostructures obtained by the sol-gel with different annealing temperatures under synthetic air. The results show that crystallinity dependent on the annealing temperature.
-
XRD patterns of TeOx powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised to 75°C for the...
-
Database of the convergence analysis results of the nonstandard approximation of the generalized Burgers–Huxley equation for the solution bounded within [0,1].
Dane BadawczeThe presented dataset is a result of the convergence analysis of the Mickens-type, nonlinear, finite-difference discretization of a generalized Burgers–Huxley partial differential equation.
-
XRD patterns of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the XRD patterns of ammonium vanadate nanobelts obtained by the hydrothermal method with different conditions. The results show that the structure and phase compositions of samples dependent on reaction conditions.
-
XRD patterns of VO2 and V6O13 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V6O13 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under a reducing atmosphere (94% Ar, 6% H2) at 500, 600 and 700C for 10h.
-
XRD patterns of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
XRD patterns of nickel-modified V2CTx
Dane BadawczeThe set includes data for XRD pattern preparation of nickel-modified V2CTx samples.
-
XRD patterns of TeOx-BaO-BiO powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx-BaO-BiO powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor), barium carbonate, and bismuth carbonate with thetraetylene glycol, water, ethanol, and acetic acid. (Samples molar concentration: 73TeO2-4BaO-3Bi2O3 and 73TeO2-3BaO-4Bi2O3)....
-
Database of the convergence analysis results of the nonstandard approximation of the generalized Burgers–Huxley equation for the solution bounded within [0, γ^(1/p)].
Dane BadawczePresented dataset is a result of the convergence analysis of the Mickens-type, nonlinear, finite-difference discretization of a generalized Burgers–Huxley partial differential equation. The generalized Burgers–Huxley equation is a diffusive partial differential equation with nonlinear advection and diffusion. The boundary problem for this equation possesses...
-
The XRD diffraction patterns of LSCNT sintered at various temperatures
Dane BadawczeThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
The XRD diffraction patterns of LSCNT of different A site nonstoichiometry
Dane BadawczeThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s and La0.3Sr0.6Ce0.1Ni0.1Ti0.9O3-s sintered at 1200oC under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
XRD patterns of MXenes ashes obtained after TGA measurement
Dane BadawczeData contain results from XRD measurements of the product (ashes) produced after TGA of MAX Phase, MXene HF, MXene HF/HCl 1:3 and MXene HF/H2SO4 1:3 . The measurements were performed in AERIS PANalytical X-ray diffractometer with Cu-Ka radiation.
-
XRD patterns of V2O5 thin films deposited on silicon substrate
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range of 300-600C. The results show that the structure of the films dependent on the annealing temperature.
-
XRD patterns of V2O5 thin films deposited on quartz glass
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 thin films deposited on a quartz glass substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range 200-600C. The results show that the structure of the films dependent on the annealing temperature.
-
The XRD diffraction patterns of La0.3Sr1.7Fe1.5Mo0.5O6 powder calcined at 1200oC in air
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr1.7Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The XRD diffraction patterns of Sr1.9Fe1.4Ni0.1Mo0.5O6 powder calcined at 1100oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr1.9Fe1.4Ni0.1Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1100oC for 12 h in air.
-
The XRD diffraction patterns of Sr1.9Fe1.5Mo0.5O6 powder calcined at 1100oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr1.9Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1100oC for 12 h in air.
-
The XRD diffraction patterns of Sr1.9Fe1.4Ni0.1Mo0.5O6 powder calcined at 1200oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr1.9Fe1.4Ni0.1Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The XRD diffraction patterns of Sr1.9Fe1.5Mo0.5O6 powder calcined at 1200oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr1.9Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr2Al0.1FeMoO6 powder calcined at 1200oC in air
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr2Al0.1FeMoO6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1200oC for 12 h in air.
-
The XRD diffraction patterns of Sr2Al0.1Fe1.4Mo0.5O6 powder calcined at 1100oC in air
Dane BadawczeThe dataset includes XRD patterns of Sr2Al0.1Fe1.4Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1100oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr1.7Al0.1Fe1.5Mo0.5O6 powder calcined at 1100oC in air
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr1.7Al0.1Fe1.5Mo0.5O6 powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 1100oC for 12 h in air.
-
The XRD diffraction patterns of annealed Ce0.9M0.1O2 powders prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution of nitrates using TMAOH. The sediment was cetrifuged and rinsed with alcohol several times. Powders were dried and calcinated at 500 degrees for 2 h, followed...
-
The XRD diffraction patterns of Ce(Pr,Sm)O2-s samples
Dane BadawczeThe dataset includes XRD diffraction patterns of Ce(Pr,Sm)O2-s samples of various stoichiometries of Pr and Sm dopants. Samples were produced using aqueous soft chemistry methods (microemulsion method).
-
The XRD diffraction patterns of Ce0.9M0.1O2 prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution using tetramethylammonium hydroxide (TMAOH). After the precipitation, the sediment was centrifuged and rinsed with alcohol several times. Precursors powder...
-
XRD patterns of V2O5 thin film morphology dependent on substrate types
Dane BadawczeThe DataSet contains the XRD patterns of the V2O5 thin film structure dependent on substrate types. The as-prepared thin films were deposited on alumina, zirconium, zirconium oxide and metallic vanadium substrate, then was annealing under an oxidizing atmosphere at 600C for 10h.
-
The XRD diffraction patterns of Ce(Gd,Pr)O2-s samples
Dane BadawczeThe dataset includes XRD diffraction patterns of Ce0.8Gd0.2O2-s and Ce0.8Pr0.2O2-s sintered at 600oC under air atmosphere for 4 h. Samples were produced using aqueous soft chemistry methods (Pechini).
-
XRD patterns of VO2 and V2O3 thin films obtained at 500°C
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon atmosphere.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s powder calcined at 800oC in air
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 800oC for 12 h in air.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s powder calcined at 800oC in H2
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s powder prepared using wet chemistry methods, namely modified Pechini route. The powders were sintered at 800oC for 12 h in H2. Pure perovskite phase was formed
-
XRD patterns of VO2 and V2O3 thin films obtained at 700°C
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (5-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon atmosphere.
-
The XRD pattern of CeO2/10wt.%Ni with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor nitrate solution (betacyclodextrin). The dataset includes 5-90 2 theta degree measurement. Nonreduced. Sintered at 400oC for 4h.
-
X-ray diffraction patterns of BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Dane BadawczeThe dataset consists of three raw X-ray diffraction (XRD) files collected using a Phillips X’Pert Pro diffractometer (CuKα radiation (𝜆 = 1.541 Å), under 40 kV and 30 mA). The diffraction patterns of BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were collected at room temperature. Collected...
-
XRD patterns of the V2O5 nanorods after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 nanorods after thermal treatment under a reducing atmosphere. Samples were annealed at 450C for 2, 20, and 40h under a reducing atmosphere (94% Ar, 6% H2).
-
The XRD diffraction patterns of Ce0.8La0.2O2 and CeO2 prepared using soft template method
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s and CeO2-s nanopowders (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC, centrifuged...
-
XRD patterns of the V2O5 coatings after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 coatings on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 500C, 600C, and 700C for 10 under a reducing atmosphere (94% Ar, 6% H2).
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1W0.9O3-s precursor calcined under air atmosphere
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1W0.9O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s precursor calcined under air atmosphere
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1Mo0.9O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
XRD patterns of vanadium oxide nanostructures on silicon substrate obtained by V2O5 recrystallization
Dane BadawczeThe DataSet contains the XRD patterns of vanadium oxide nanostructures on silicon substrates obtained by recrystallization of V2O5 thin films between 800-1200°C under synthetic air. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials.
-
The XRD diffraction patterns of La0.3Sr0.6Ce0.1Ni0.1W0.45Mo0.45O3-s precursor calcined under air atmosphere
Dane BadawczeThe dataset includes XRD patterns of La0.3Sr0.6Ce0.1Ni0.1W0.45Mo0.45O3-s precursor gel prepared using wet chemistry methods, namely modified Pechini route. The powders were calcined at 550oC for 5 h in air.
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 25xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using modified Pechini/EDTA method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using modified Pechini method consisting of CA (citric acid), PEG (propylene glycol) and EDTA. Exact amount of metal nitrates were dissolved in water followed by addition of gelling agents and heated to 100C. Obtained gel was calcined at 600C for 4h. The powder...
-
The XRD pattern of CeO2/10wt.%Mn prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Mn. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Fe prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Fe. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Cu prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Ni prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4h in air.
-
The XRD pattern of CeO2/10wt.%Co prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Co. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement.
-
XRD (X-ray Diffraction) patterns of PMH, PMD and simulated MIL-53(Al)
Dane BadawczeThese data contain XRD (X-ray Diffraction) patterns of PMH, PMD and simulated MIL-53(Al). The results were recorded by a Philipsdiffractometer using Cu Ka radiation. Sample abbreviations (PMH, PMD, MIL-53(Al)) are in agreement with the markings used in the linked publication.