Filtry
wszystkich: 1044
-
Katalog
- Publikacje 803 wyników po odfiltrowaniu
- Osoby 16 wyników po odfiltrowaniu
- Wynalazki 7 wyników po odfiltrowaniu
- Projekty 1 wyników po odfiltrowaniu
- Zespoły Badawcze 2 wyników po odfiltrowaniu
- Kursy Online 5 wyników po odfiltrowaniu
- Wydarzenia 1 wyników po odfiltrowaniu
- Dane Badawcze 209 wyników po odfiltrowaniu
wyświetlamy 1000 najlepszych wyników Pomoc
Wyniki wyszukiwania dla: IMPEDANCJA UZIEMIEŃ
-
Simultaneous measurements of ECG, body Impedance and temperature
Dane BadawczeThe data are complementary part of the experiment designed to demonstrate how to use the network protocols to transmit medical data. The dataset contains biomedical signals of ECG, Impedanc and temperature acquired simultaneously. The data allow students to become familiar with data acquisition methods (simulate data transmission by medical device over...
-
Grzegorz Lentka dr hab. inż.
OsobyGrzegorz Lentka uzyskał tytuł magistra inżyniera w roku 1996 na Wydziale Elektroniki, Telekomunikacji i Informatyki Politechniki Gdańskiej w zakresie systemów pomiarowych. Stopień doktora nauk technicznych uzyskał w roku 2003, a doktora habilitowanego w 2014. Obecnie zatrudniony jest w Katedrze Metrologii i Optoelektroniki na stanowisku profesora PG. W ramach prowadzonej dydaktyki zajmuje się zagadnieniami związanymi z interfejsami...
-
Poszukiwanie wygodnego analitycznie opisu funkcyjnego dla praktycznych kształtów udaru prądowego
PublikacjaZaproponowano kilka opisów funkcyjnych dla prądowego pobudzania uziemień. Wyznaczono pełną reakcję uziemienia na prądowy udar opisany badanymi rodzinami funkcji. Naszkicowano ogólny schemat analizy, wspólny dla wiekszości badanych opisów.
-
Michał Ziółko dr inż.
Osoby -
Protection against electric shock in electrical installations with low voltage generating sets
PublikacjaW referacie przedstawiono zasady ochrony przeciwporażeniowej, zgodne z wymaganiami międzynarodowymi, w sytuacji kiedy instalacja elektryczna jest zasilana z niskonapięciowych zespołów prądotwórczych. Zwrócono uwagę na dobór zabezpieczeń przeciwporażeniowych oraz na wymiarowanie uziemień.
-
Nonlinear impedance of as-quenched Bi2VO5.5 glass-ceramic was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched Bi2VO5.5 glass-ceramic was measured by impedance spectroscopy method.
-
Linear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance of 10Na2O–60P2O5–30CaO glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of 10Na2O–60P2O5–30CaO glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance of 40Na2O-20CaO-40P2O5 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of 40Na2O-20CaO-40P2O5 glass was measured by impedance spectroscopy method.
-
Electrochemical cell impedance spectra at Eoc
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2 (≥99.9%, anatase...
-
High gain/bandwidth off‑chip antenna loaded with metamaterial unit‑cell impedance matching circuit for sub‑terahertz near‑field electronic systems
PublikacjaAn innovative off-chip antenna (OCA) is presented that exhibits high gain and efficiency performance at the terahertz (THz) band and has a wide operational bandwidth. The proposed OCA is implemented on stacked silicon layers and consists of an open circuit meandering line. It is shown that by loading the antenna with an array of subwavelength circular dielectric slots and terminating it with a metamaterial unit cell, its impedance...
-
Multifrequency Nanoscale Impedance Microscopy (m-NIM): A novel approach towards detection of selective and subtle modifications on the surface of polycrystalline boron-doped diamond electrodes
PublikacjaIn this paper, we describe the modification of Nanoscale Impedance Microscopy (NIM), namely, a combination of contact-mode atomic force microscopy with local impedance measurements. The postulated approach is based on the application of multifrequency voltage perturbation instead of standard frequency-by-frequency analysis, which among others offers more time-efficient and accurate determination of the resultant impedance spectra...
-
Lightning impulse efficiency of horizontal earthings
PublikacjaSystem uziemień współczesnych obiektów jest zwykle bardzo rozległy, a na łączenie poszczególnych elementów uziemiających za pomocą głównej szyny wyrównania potencjałów uwzględnia także uziemienia stacji transformatorowej. Ocena przydatności takiego systemu uziemień do celów ochrony odgromowej nie jest prosta, bo tylko jego część określana, jako długość efektywna bierze udział w odprowadzaniu do gruntu prądu piorunowego. Praca zawiera...
-
Effective length of lightning protection earthings
PublikacjaSystem uziemień współczesnych obiektów jest zwykle bardzo rozległy, a na łączenie poszczególnych elementów uziemiających za pomocą głównej szyny wyrównania potencjałów uwzględnia także uziemienia stacji transformatorowej. Ocena przydatności takiego systemu uziemień do celów ochrony odgromowej nie jest prosta, bo tylko jego część określana, jako długość efektywna bierze udział w odprowadzaniu do gruntu prądu piorunowego. Praca zawiera...
-
Jacek Ryl dr hab. inż.
OsobyStopień doktora nauk technicznych uzyskał w roku 2010. W tym samym roku podjął pracę w Katedrze Elektrochemii, Korozji i Inżynierii Materiałowej na Wydziale Chemicznym. W 2018 roku uzyskał stopień doktora habilitowanego nauk technicznych w dyscyplinie technologia chemiczna. Od 2021 roku zatrudniony w Instytucie Nanotechnologii i Inżynierii Materiałowej Wydziału Fizyki Technicznej i Matematyki Stosowanej PG. W pracy naukowej skupia...
-
Jerzy Wtorek prof. dr hab. inż.
OsobyJerzy Wtorek uzyskał tytuł magistra inżyniera w 1976 roku na Wydziale Elektroniki Politechniki Gdańskiej, a stopień doktora nauk technicznych i doktora habilitowanego na Wydziale Elektroniki, Telekomunikacji i Informatyki Politechniki Gdańskiej, odpowiednio w 1986 i 2004 roku. Tytuł profesora uzyskał w 2016 r. Jego zainteresowania dotyczą nieinwazyjnych metod oceny układu krążenia, elektrycznych (aktywnych i pasywnych) właściwości...
-
Nonlinear impedance of 45Bi2VO5.5-55SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 45Bi2VO5.5-55SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.88 mm measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Linear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Linear impedance of 25Na2O–20CaO–5P2O5–50SiO2 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of 25Na2O–20CaO–5P2O5–50SiO2 glass was measured by impedance spectroscopy method.
-
Linear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Linear impedance as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass measured with impedance spectroscopy method
Dane BadawczeThe linear electrcial properties as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Potential and strain rate impact on the electrochemical properties of 304L stainless steel under tensile stresses.
PublikacjaPraca skupia się na badaniach aspektu elektrochemicznego i mechanicznego pękania warstwy pasywnej obecnej na stali 304L. Przedstawione zostały wyniki chwilowych zmian impedancji oraz zmiany parametrów elektrochemicznych warstwy pasywnej podczas testów rozciągania przy różnych poziomach polaryzacji anodowej oraz szybkości rozciągania. Na ich podstawie można stwierdzić, że zarówno czynnik elektrochemiczny, jak i mechaniczny wpływają...
-
Impedance Evaluation of the Effect of Ru[sub 0.3]Ti[sub 0.7]O[sub 2] on Electrochemical Properties of Polymeric Conducting Electrodes Used in Cathodic Protection
Publikacja -
Nonlinear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K was measured by impedance spectroscopy method.
-
Linear impedance of 2Si3N4–98(40Na2O-20CaO-40P2O5) glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of 2Si3N4–98(40Na2O-20CaO-40P2O5) glass was measured by impedance spectroscopy method.
-
Linear impedance of 0.5Si3N4–99.5(40Na2O-20CaO-40P2O5) glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of 0.5Si3N4–99.5(40Na2O-20CaO-40P2O5) glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 annealed glass was measured by impedance spectroscopy method.
-
Linear impedance of 1Si3N4–99(40Na2O-20CaO-40P2O5) glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of 1Si3N4–99(40Na2O-20CaO-40P2O5) glass was measured by impedance spectroscopy method.
-
Linear impedance of 1SiO2–99(40Na2O-20CaO-40P2O5) glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of 1SiO2–99(40Na2O-20CaO-40P2O5) glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Electrochemical cell impedance spectra at Eoc+100mV
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Electrochemical cell impedance spectra at Eoc+200mV
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Electrochemical cell impedance spectra at Eoc-100mV
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Electrochemical cell impedance spectra at Eoc-200mV
Dane BadawczeThe dataset presents impedance spectrum of electrochemical cell filled with 3% NaCl solution presented in the figure below. This cell was used measured using Atlas-Sollich 0531 impedance analyser with built-in potentiostat. When changing the DC polarisation of the cell the non-linear phenomena could be observed. The impedance spectrum frequency range...
-
Linear impedance of 35P2O5-30Fe2O3-20Nb2O5-15TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and...
-
Linear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe linear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...