Jumping wave photographs
Open Research DataThe photographs of the outer surface obtained in the burnishing process showing the shape of the jumping wave and the displacement of the material in the surface layer.
-
Jumping Wave 2D Profiles
Open Research DataThe file contains 2D profiles obtained from a jumping wave study in front of the tool during burnishing of 1.0562 steel by the toroidal-cone tool. Burnishing speed 30.5 m/min, feed of burnishing 0.2mm/rev Force 550 and 800 N.
-
Simulations of wave propagation and attenuation in fields of colliding ice floes
Open Research DataThis dataset contains results of numerical smulations of sea ice-wave interactions, corresponding to laboratory experiments conducted at the Large Ice Model Basin (LIMB) at the Hamburg Ship Model Basin (HSVA) as part of the LS-WICE ("Loads on Structure and Waves in Ice"; https://zenodo.org/record/1067170#.XrLt_dhpxhE) project. THe simulations were conducted...
-
Wave propagation signals for ultrasonic tomography of concrete during splitting
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube with dimensions 70 x 70 x 70 cm3under the splitting test. Three cubes were tested: cube 1 (concrete with polymer fibres), cube 2 (concrete with steel fibres) and cube 3 (plain concrete).
-
Wave propagation signals in concrete beams under 3-point bending
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beams with dimensions 40 x 40 x 160 cm3under the 3-point bending. The beams were made of concrete with the following ingredients: CEM I 42.5R (450 kg/m3), water (177 kg/m3), sand 0-2 (675 kg/m3) and gravel 2-8 (675 kg/m3). The bending test was performed using a Zwick/Roell Z10...
-
Measurements of guided wave propagation in CFRP/steel adhesive joints obtained by scanning laser vibrometry
Open Research DataThe DataSet contains guided wave signals measured in adhesive joints of steel plates (steel of type S355 with a thickness of 11.9 mm ) and carbon fibre reinforced polymer (CarboDur S1012 with a thickness of 1.24 mm). The samples were as follows: #0 – intact; #1 – 10% disbond; #2 – 20% disbond; #3 – 50% disbond; #4 – 80% disbond; #5 – 100% disbond.
-
High-resolution wind wave parameters in the area of the Gulf of Gdańsk during 21 extreme storms
Open Research DataThis dataset contains the results of wind-wave parameter modelling in the area of the Gulf of Gdańsk (Southern Baltic). For the simulations, a high resolution SWAN model was used. The dataset consists of the significant wave height, the direction of the wave approaching the shore and the wave period during 21 historical, extreme storms. The storms were...
-
High-resolution wind wave parameters in the area of the Gulf of Gdańsk during 21 extreme storms (GIS dataset)
Open Research DataThis GIS dataset contains the results of wind-wave parameter modelling in the area of the Gulf of Gdańsk (Southern Baltic). For the simulations, a high resolution SWAN model was used. The dataset consists of the significant wave height, the direction of the wave approaching the shore and the wave period during 21 historical, extreme storms (rasters)....
-
Guided wave propagation signals measured on corroded stiffened panels
Open Research DataThe fundamental antisymmetric Lamb mode was excited by piezoelectric transducers attached at the pre-selected points on stiffened panels, representing typical structural ship components. The specimens were exposed to accelerated marine corrosion degradation, so the signals were collected to analyze the influence of the degree of degradation on the wave...
-
Measurements of ultrasonic bulk and guided wave propagation in additively manufactured cubes and plates obtained by ultrasonic pulse velocity analyzer and scanning laser vibrometry
Open Research DataThe DataSet contains the results of measurements of ultrasonic wave propagation in additively manufactured samples made of polylactic acid (PLA). Three types of raster angles in two consecutive layers were assumed: 0°/90° (#1), 45°/-45° (#2) and 90°/90° (#3) with respect to the x-axis. For each printing variants a cubic sample (#C1-3) with dimensions...
-
Ultrasonic wave propagation and digital image correlation measurements of steel bars under 3-point bending
Open Research DataThe DataSet contains the results of the mechanical behaviour of a bar under a 3-point bending test. The bar was made of steel and had a cross-section of 5.96 × 5.96 mm2 and a length of 200 mm. The three-point bending test was performed using a Zwick/Roell Z10 universal testing machine (UTM), with a distance between supports of 12 cm. The parameters...
-
Potential energy curve, rovibrational energies and nuclear wave functions of 2 singlet Pi state in KLi dimer
Open Research DataThis data sets contains potential energy curve, energy levels and nuclear wave functions of rovibrational states of KLi dimer in 2 singlet Pi electronic state. Potential energy curve (PEC) for the electronic state was calculated in the Born-Oppenheimer approximation by the means of effective core potentials and MRCI method. Nuclear wave functions and...
-
Elastic wave propagation signals in concrete cube (experimental and calculated using discrete element method)
Open Research DataThe DataSet contains the results of the elastic wave propagation. Both experimental and numerical signals were obtained for the concrete cube with dimensions of 50 × 50 × 50 mm3. The specimen was made of concrete with called mortar concrete. The ingredients of the concrete mix were as follows: CEM I 42.5R (500 kg/m3), sand 0 – 2 (1500 kg/m3) and water...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #3)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #1)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #4)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation, digital image correlation and X-ray micro-computed tomography measurements of concrete during splitting (cube #2)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete cube under the splitting test. The cube had dimensions 70 x 70 x 70 cm3 and was made of concrete with the following ingredients: cement type CEM I 42.5R (330 kg/m3), water (165 kg/m3), aggregate 0/2 mm (710 kg/m3), aggregate 2/8 mm (664 kg/m3), aggregate 8/16 mm (500 kg/m3),...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-002)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-Con)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-004)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ultrasonic wave propagation and digital image correlation measurements of polyolefin fibre-reinforced concrete beams under 3-point bending (beam B-006)
Open Research DataThe DataSet contains the results of the mechanical behaviour of a concrete beam under a 3-point bending test. The beams had dimensions 15 x 15 x 70 cm3. The beam B-Con was made of concrete without fibres (as the reference beam), while beams B-002, B-004, and B-006 were manufactured from the concrete mix containing 2 kg/m3, 4 kg/m3 and 6 kg/m3 of fibres,...
-
Ocean mixed layer dynamics: high-resolution simulations of wind, wave and convective effects
Open Research DataThis dataset contains results of high-resolution numerical simulations of the ocean mixed layer (OML) forced by wind, waves and cooling from the atmosphere, i.e., under strongly turbulent, convective conditions. The goal is to provide detailed, three-dimensional information about OML circulation, turbulent kinetic energy, and temperature and salinity...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Simulations of flows in the coastal zone of the Baltic Sea
Open Research DataThe study area is located in the Southern Baltic, within Polish Marine Areas, adjacent to the coastline in the vicinity of Lubiatowo village, where The Coastal Research Station (CRS) – a field laboratory of the Institute of Hydro-Engineering of the Polish Academy of Sciences (IBW PAN) –is situated. The numerical reconstruction of the coastal flow was...
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.88 mm measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Open Research DataThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Open Research DataThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-35Nb2O5 glass
Open Research DataThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH) and Nb2O5 (≥99.9%, PLUKA AG) were...
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 glass
Open Research DataThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Open Research DataNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 3 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 10 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Data obtained by computation for X-ray focusing using oriented Gaussian beams
Open Research DataThe propagation of X-ray waves through an optical system consisting of several X-ray refractive lenses is considered. Gaussian beams are exact solutions of the paraxial equation. The Helmholtz equation describes the propagation of a monochromatic electromagnetic wave. Since the widths of the beams are much larger than the wavelength of X-rays, Gaussian...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Open Research DataNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 613 K was measured by impedance spectroscopy method.
-
Continuum orbitals in low energy scattering of electrons from Ar, Kr, Xe, Rn and Og atoms
Open Research DataThe dataset includes relativistic continuum electron wave functions (continuum orbitals, continuum spinors) for elastic scattering of electrons from Argon (Ar), Krypton (Kr), Xenon (Xe), Radon (Rn) and Oganesson (Og) atoms, calculated using the Multiconfiguration Dirac-Hartree-Fock method (MCDHF), at very low electron energies (0.0001 - 0.001 eV). Only...
-
Nonlinear impedance of as-quenched Bi2VO5.5 glass-ceramic was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of as-quenched Bi2VO5.5 glass-ceramic was measured by impedance spectroscopy method.
-
Sea ice floe size and shape data from a very high resolution satellite image (Knox Coast, East Antarctica)
Open Research DataThis dataset contains floe size distribution data from a very high resolution (pixel size: 0.3 m) optical satellite image of sea ice, acquired on 16. Feb. 2019 off the Knox Coast (East Antarctica). The image shows relatively small ice floes produced by wave-induced breakup of landfast ice between the Mill Island and Bowman Island. The ice floes are...
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K was measured by impedance spectroscopy method.