Open Research Data
Filters
total: 878
Open Research Data
-
Structural investigations of the Al2O3 ultra thin films
Open Research DataUltra-thin layers of Al2O3 were deposited by atomic layer deposition (ALD) (Beneq TFS 200 ALD system). This method provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. Samples with a thickness of 2...
-
Depth profile of the gold-silver bimetallic structures
Open Research DataSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
Depth profile of the chemical composition of the Au-Ag multilayers
Open Research DataSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched Bi2VO5.5 glass-ceramic was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of as-quenched Bi2VO5.5 glass-ceramic was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 glass-ceramic measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 glass-ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Thermal behavior of (NH4)V4O10xH2O
Open Research DataThe DataSet contains the results of the thermal behavior of the (NH4)V4O10xH2O obtained by the hydrothermal method using different precursors: microstructured (commercially available) or nanostructured. The information about samples synthesis is described in the Materials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 1000°C under argon atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 1000°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal properties of VO2 and V2O3 nanostructures
Open Research DataThe DataSet contains the DSC and TG curves of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere at the selected temperature: 500C, 600C, and 1000C.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 473 K for 3h and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 650°C under reducing atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 650°C under a reducing atmosphere (95% Ar 5% H2). The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 800°C under argon atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 800°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 700°C under argon atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 700°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 600°C under argon atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 600°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 500°C under argon atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 500°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
TEM imaging of Ag-Au nanoalloys
Open Research DataThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of metal thin layers (Au/Ag or Ag/Au) followed by annealing under 550 Celsius degree in an argon atmosphere. The basic single layer thickness was usually ca. 3 nm. For investigations two samples wih 50% Au and 50% Ag were selected and samples 1/3 Ag - 2/3 Au and 2/3 Ag - 1/3...
-
TEM and EDX study of the Al2O3 ultra thin films
Open Research DataThe ultra-thin layers of Al2O3 were deposited on a silicon substrates. The method of atomic layer deposition (Beneq TFS 200 ALD system) was chosen as the proper method of dielectric layer deposition. This method provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water....
-
XPS measurements of the iron elements covered by chromium
Open Research DataAnticorrosive coatings are an important issue in modern materials engineering. One of the most commonly used, for that coating materials, is chrome. Three metal elements were measured, named as Turcja, WB Tech and Nomet. Names were given according to producer of elements. XPS measurements of the Cr 2p region give an ansver concering on surface chemical...
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Linear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of as-quenched 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 400°C under argon atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 400°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Linear impedance of V2O5 nanorods obtained at 893K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 903K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 913K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 923K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Non-linear impedance of V2O5 nanorods obtained at 923K
Open Research DataThe DataSet contains the non-linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
XRD patterns of VO2 and V2O3 thin films obtained at 500°C
Open Research DataThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon atmosphere.
-
XRD patterns of VO2 and V2O3 thin films obtained at 700°C
Open Research DataThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (5-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon atmosphere.
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C dependent on film thickness
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (2-3 AsP layers) were deposited on a silicon substrate and were annealing at 1000°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films were deposited on a silicon and quartz glass substrate and were annealing at 1000°C under an argon atmosphere.
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 500°C
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 700°C
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon...
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Open Research DataThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
Powder x-ray diffraction pattern of polycrystalline synthetic leningradite, PbCu3V2O8Cl2
Open Research DataPolycrystalline sample of Cu2+ (S=1/2) antiferromagnetic PbCu3V2O8Cl2 (synthetic analogue of the mineral leningradite) was prepared by solid state reaction of PbCl2, CuO, and V2O5.
-
Powder x-ray diffraction pattern of polycrystalline Cu(IO3)2*xH2O
Open Research DataHydrated copper(II) iodate sample was prepared in water solution by reacting copper(II) sulfate and potassium iodate, following the method described by Peterson (J. Chem. Educ. 1957, 34, 12, 612). The sample was subsequently dried at various temperatures in order to produce an anhydrous Cu(IO3)2:
-
Electrical measurements of the dewetting of metal thin films
Open Research DataIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...