The electrical properties mesurements of DIR-SOFC with Ce0.8Co0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Co0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Mn0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Mn0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Ni0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Ni0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with CeO2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with CeO2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
The electrical properties mesurements of DIR-SOFC with Ce0.8Cu0.2O2-s functional layer
Dane BadawczeThe dataset includes the electrical properties mesurements of SOFC with Ce0.8Cu0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
-
Instantaneous power signal measurements for bearing diagnostics
Dane BadawczeBearing diagnostics can be carried out based on the method, which relies on the measurement and analysis of the variability of the signal instantaneous power, defined as the product of instantaneous current and voltage power supplied to the engines. Bearing damage causes the appearance of deformations, which are in the form of additional harmonic components...
-
Analysis of the instantaneous power signal for bearing diagnostics -bearing damaged
Dane BadawczeThe attached dataset contains the measurement results of the instantaneous values of current and voltage, recorded during the diagnostics of a damaged bearing. Bearing diagnostics can be carried out based on the method, which relies on the measurement and analysis of the variability of the signal instantaneous power, defined as the product of instantaneous...
-
Analysis of the instantaneous power signal for bearing diagnostics - bearing undamaged
Dane BadawczeThe attached dataset contains the measurement results of the instantaneous values of current and voltage, recorded during the diagnostics of an undamaged bearing. Bearing diagnostics can be carried out based on the method, which relies on the measurement and analysis of the variability of the signal instantaneous power, defined as the product of instantaneous...
-
The luminescence study of CsPbI3 nanoparticles embedded in Cs4PbI6 crystals.
Dane BadawczeCs4PbI6, as a rarely investigated member of the Cs4PbX6 (X is a halogen element) family, has been successfully synthesized atlow temperatures by collaborators from National Taiwan University. Strong red to near-infrared (NIR) emission properties have been detected, and its optical emission centers have been identified to be numerous embedded perovskite-type...
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 500°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 500°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 1000°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 1000°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Graphene oxide thin films deposited on a PCB board - chemical analysis
Dane BadawczeGraphene oxides based films were measured by X-ray photoemission spectroscopy (XPS) method. TheXPS measurements were carried out with the Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The...
-
Investigation of plasmon resonance in a silver nanoparticles
Dane BadawczeSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 650°C under reducing atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 650°C under a reducing atmosphere (95% Ar 5% H2). The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Study of the chemical state of Gd in a Ba-La-Gd-Co based ceramic
Dane BadawczeBarium, Lanthanum, Gadolinium and Cobaltium precursors were used for production of ceramic materials. Samples were produced by standard solid state reaction. Samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing on a Gadolinum were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology....
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 400°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 400°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 700°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 700°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Chemical investigation of the Al2O3 ultra-thin films
Dane BadawczeUltra-thin layers of oluminum oxide (Al2O3) were deposited by ALD method. Atomic layer deposition provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. Samples with a thickness of 2 and 8 nm of alumina...
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 800°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 800°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of VO2/V2O3 nanostructures obtained at 600°C under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the VO2/V2O3 nanostructures. The vanadium oxides nanostructures were synthesized by the sol-gel method, where obtained xerogel powder was annealing at 600°C under an argon atmosphere. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
The luminescence study of Sr0.98Li2.5 + zAl1.5 – zO3 + 2zN1 – 2z:0.02Eu coumpounds.
Dane BadawczeEu2+-doped UCr4C4-type oxynitride phosphors are emerging innovative materials to replace oxide and nitride phosphors for high-end light-emitting devices. A series of Sr0.98Li2.5 + zAl1.5 – zO3 + 2zN1 – 2z:0.02Eu phosphors were synthesized by collaborators from the National Taiwan University by precursor engineering, and these products showed an unexpected...
-
The luminescence study of Sr2−xSrxPN3:Eu2+ nitridophosphate.
Dane BadawczeIn this work, a series of Ca2−xSrxPN3:Eu2+ nitridophosphate phosphors through a solid-solution strategy involving a hot isostatic press was developed by collaborators from National Taiwan University. Unexpected dual emissions in the red and infrared regions are observed, different from previous research results. The unique change in red and near-infrared...
-
Chromium Cluster Luminescence: Advancing Near‐Infrared Light‐Emitting Diode Design for Next‐Generation Broadband Compact Light Sources
Dane BadawczeIn modern technology devices, an energy-saving miniature near-infrared (NIR) light source plays a critical role in non-destructive, non-invasive sensing applications and further advancement of technology. This dataset reports the broadband NIR luminescence of Cr3+ clusters for designing phosphor-converted NIR light-emitting diodes as an alternative...
-
The Mott-Schottky characteristics of microwave pulsed-plasma polymerized allylamine by DEIS analysis
Dane BadawczeThe dataset contains the results obtained for the Mott-Schottky analysis of the microwave pulsed-plasma polymerized allylamine using the multifrequency perturbation signal with Dynamic Electrochemical Impedance Spectroscopy (DEIS) technique. The results were obtained using the perturbation composed of the elementary signals with a frequency range between...
-
Linear and nonlinear impedance of iron containing silicate glasses
Dane BadawczeThe linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to...
-
Depth profile of the composition of 8 nm Al2O3 thin film
Dane Badawcze8 nm layer of aluminum oxide (Al2O3) was deposited by ALD method on a s. Atomic layer deposition provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. To investigate the profile of concenration of...
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Dane BadawczeElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Influence of the annealing condictions on the chemical structure of LaBaGdCo ceramics
Dane BadawczeCeramic samples based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by solid state reaction. After sintring in a furnance, samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology. XPS analysis...
-
Selected results of measurements carried out in a ship power station with two generators working in parallel with the use of the NI PXIe-1062Q based measurement system
Dane BadawczeThe presented dataset is part of research focusing on the assessment of metrological properties of the instrument, Estimator/Analyzer (A/E v.2), developed and made at the Faculty of Electrical Engineering, Department of Marine Electrical Power Engineering, of Gdynia Maritime University. The attached data set contains the results of measurements made...
-
The luminescence study of LiGa5(1−x)O8:5xCr3+ coumpounds
Dane BadawczeInfrared luminescent materials have evoked much attention from chemists and material scientists. Although substantial progress is made in materials design, the luminescent mechanism remains ambiguous in the complex structures, presenting major barriers to developing novel infrared luminescent materials. Herein, this study aims to deliberate a complete...
-
Raman data of deuterium and hydrogen grown boron-doped diamond
Dane BadawczeRaman spectra were recorded at room temperature using a micro-Raman spectrometer (Invia, Renishaw) equipped with an edge filter with different excitation wavelengths and lasers: UV λ = 325 nm (HeCd), blue λ = 488 nm (Ar+), green λ = 514 nm (Ar+), and IR λ = 785 nm (IR diode) and 50× microscope objective. To avoid sample heating, the radiation power...
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Dane BadawczeThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
Lanthanum investigations in ceramics annealed in a dry and wet atmosphere
Dane BadawczeCeramics based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by standard solid state reaction from oxides and carbonate powders. After sintring, samples were annealed for 2 hours or 72 hours at 300 Celsius degree in a both: wet and dry atmosphere. Results of annealing on a chemical composition and valence state of lanthanum were observed...
-
Investigations of the valence state of Co in a MnCoO ceramics
Dane BadawczeMcCoO ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. Chemical behaviour of the Cobaltium was measured by XPS method. The analyses were...
-
The luminescence study of Ga1.98–xAlxO3:0.02Cr3+ coumpounds.
Dane BadawczeA chemical and mechanical pressure-induced photoluminescence tuning method was developed through structural evolution and hydrostatic pressure involving phase transition. A series of Ga1.98−xAlxO3:0.02Cr3+ phosphors were synthesized by collaborators from National Taiwan University. Structural evolution reveals a crystal phase change with the incorporation...
-
The luminescence study ofNaK2Li[Li3SiO4]4:Eu coumpounds.
Dane BadawczeNarrowband green phosphors with high quantum efficiency are required for backlighting white light-emitting diode (WLED) devices. Materials from the A[Li3SiO4]4:Eu2+ family have recently been proposed as having superior properties to industry-standard β-SiAlON green phosphors. Here, we show that a cheap, easily synthesized host NaK2Li[Li3SiO4]4 (NKLLSO)...
-
The luminescence study ofNaK2Li[Li3SiO4]4:Ce coumpounds.
Dane BadawczePhosphors with a rigid and symmetrical structure are urgently needed. The alkali lithosilicate family (A[Li3SiO4]) has been extensively studied with a narrow emission band due to its unique cuboid-coordinated environment and rigid structure. However, here we demonstrate for the first time Ce-doped NaK2Li[Li3SiO4]4 phosphors with a broad emission band,...
-
Substrate characterization in a electrochemically derived Manganium-Cobaltium thin films
Dane BadawczeManganium-Cobaltium thin films were electrochemically deposited on a Ni foams subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
XPS study of the YST ceramics
Dane BadawczeYttrium-doped strontium titanate was prepared via conventional solid-state reaction method from Y2O3 (Sigma Aldrich, 99,9%), TiO2 (Sigma Aldrich, 99%) and SrCO3 (Sigma Aldrich,98%). For comparision, two other techniques were used for synthesis: Pechini and wet methods. Both kind of samples were measured, after and before reduction process (in a hydrogen)....
-
Chemical analysis of the Au-Ag nanoaloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - full run
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - pre-run (10s)
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...