Plasmon resonance in gold-silver nanoalloys
Dane BadawczeSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Depth profile of the gold-silver bimetallic structures
Dane BadawczeSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
Dewetting of silver films detected by XPS method
Dane BadawczeDewetting of silver thin films was detected by XPS method. Thin metallic films were deposited by magnetron sputtering method. Formation of nanostructures , as a result of thermal annealing, was confirmed by SEM microscope. For comparision three samples were measured. Bulg gold, as-deposited silver film with thickness of 3 nm and nanostructures.
-
X-Ray diffraction of the metallic nanostructures
Dane BadawczeMetallic nanostructures (gold and silver) were manufactured as a thermal annealing of gold or silver thin film. Gold films with thickness of 2.8 nm were deposited on a silicon substrates using a table-top dc magnetron sputtering coater (EM SCD 500, Leica), equipped with quartz microbalance for in-situ thickness measurements. Films were deposited from...
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
Electrical measurements of the dewetting of metal thin films
Dane BadawczeIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
TEM imaging of metal nanoparticle cross section
Dane BadawczeTEM microscope was used for a imaging of metallic nanostructures. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.
-
Interface diffusion between metallic nanoparticles and silicon substrate
Dane BadawczeInterface diffusion between metallic nanoparticles and silicon substrate was detected by EDX method. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.
-
Chemical analysis of the Au-Ag nanoaloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Depth profile of the chemical composition of the Au-Ag multilayers
Dane BadawczeSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
Linear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe linear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Linear impedance of vanadate glass-ceramics containing BaTiO3
Dane BadawczeThe linear impedance of vanadate glass-ceramics containing BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
Linear impedance of 35P2O5-30Fe2O3-20Nb2O5-15TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and...
-
Linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2 (≥99.9%, anatase...
-
High temperature linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
High temperature linear impedance of 35P2O5-30Fe2O3-25Nb2O5-15TiO2
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%,...
-
High temperature linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...