Chemical composition of La-Sr-Ce-Ni-Ti ceramics material measured by XPS method
Dane BadawczeLa-Sr-Ce-Ni-Ti (LSCNT) based ceramics sample was manufactured by standard solid state reaction.Prepared powder was pressed into pilled and sintered in a furnace in air atmosphere for 10h. Annealing temperature was 1200 Celsius degree. To calculate chemical composition and determine valence states of the elements, X-Ray photoemission spectroscopy (XPS)...
-
Results of SEM examination of chitosan/Eudragit E 100 coatings electrophoretically deposited on the Ti grade 2 substrate
Dane BadawczeThe database contains the images of the microstructure of the coatings observed with the SEM scanning electron microscope. The chitosan/Eudragit E 100 coatings deposited on the Ti grade 2 substrate by an electrophoresis process were tested. Different process parameters like Eudragit E 100 concentration (0.25 g and 0.5 g in 100 mL of 1% (v/v) acetic...
-
XPS measurement of the Fe-Ti based materials
Dane BadawczeThe mono‐ and bimetal‐modified (Pd, Cu) titanium(IV) oxide and iron oxide (III) photocatalysts were prepared by chemical reduction method and characterized using XPS method. The composition of elements incorporated in the surface layer of mono- and bimetallic photocatalysts was determined by XPS analysis, as well as the valence state of elements. Measurements...
-
SEM micrographs of Ti tooth implant corrosion
Dane BadawczeThe dataset contains micrographs made with a scanning electron microscope (SEM) Hitachi S-3400N of the tooth implant removed after inflammation. The inflammation was induced by the increased corrosion rate of the titanium screw. The reason for the corrosion to occur was the appearance of the concentration cell of different aeration for various areas...
-
Simulation of signal acquisition from a rotary flowmeter
Dane BadawczeThe dataset contains results of simulation measuring the flow of homogeneous substances by rotational flow meter: a moment of impulse at the output of flow meter, time between successive pulses, number of pulses counted from standard generator and relative error of measurement.
-
The influence of microstructure on the corrosion resistance for some titanium-based alloys
Dane BadawczeThis dataset contains scanning electron microscopy (SEM) micrographs revealing the microstructure of some Ti-based alloys, namely: Ti-6Al-4V (file name: TiV), Ti-6Al-7Nb (file name: TiNb) and TC21 (file name: TiAlSnZrMoCrNbSi) alloys and their localized corrosion as a result of passive layer breakdown in a corrosive environment, ie. 0.9% NaCl solution...
-
XPS-TiO2 heated in H2
Dane BadawczeThese XPS spectra were recorded for TiO2 heat-treated at 450-600oC in H2. Surface oxygen groups were determined. Deconvolution of Ti 2p peak allowed to determine Ti3+ on the titania surface.
-
The EDS elemental maps of reduced LSCNT (SEM)
Dane BadawczeThe dataset includes elemental maps of La, Ce, Ti, O, Sr, Ni in La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s produced using Pechini method sintered at 1200oC under air atmosphere and reduced at 900 for 12 h in wet H2.
-
The reductivity of the transition metals - calculations
Dane BadawczeThe dataset includes the reduction enthalpy and Gibbs energy simulated for Co, Cu, Fe, La, Mo, Ni, Sr, Ti, and W from oxide form into metallic form in hydrogen. Simulations were performed using HSC Chemistry software.
-
Nanoindentation tests of the hydroxyapatite composite coatings applicated on titanium alloys by the electrophoretic method
Dane BadawczeCurrently, there are no metal materials that meet all biomechanical and biochemical requirements needed for long life implantable biomaterials. The main purpose of the study was to functionalize the surface of the titanium alloys used in biomaterial implants.
-
SPTNO ceramics measured by XPS method
Dane BadawczeSPTNO (Sr-Pr-Ti-Ni-O) ceramic were manufactured by solid state reaction, from oxides compounds. Synthesis conducted in air atmosphere at temperature in a range of 800-900 deg. Chemical composition of prepared materials were measured by XPS (X-Ray photoemision spectroscopy) method. UHV OmicronNanotechnology system with 128 channel Argus hemispherical...
-
Physicochemical and photocatalytic data of Nb-doped faceted TiO2
Dane BadawczeRaw numerical data, obtained from the physicochemical measurements (XRD, DR-UV/Vis, EPR) and numerical data on photocatalytic activity (phenol degradation and 4-nitrophenol reduction) extracted from the HPLC-DAD results, obtained for the TiO2 nanoparticles that expose majority of the {0 0 1}, {1 0 0} or {1 0 1} facets and were doped with the nominal...
-
XPS study of the TiO2-WO2 composites
Dane BadawczeValence state of W and Ti was measured in a TiO2-WO3 composites with a various composition.Powder samples of pure titanium dioxide, tungsten oxide and mix of 50% titanium oxide and 50% od tungsten oxide were measured. Oxides were annealed at the temperature in the range of 300 Celsius degree up to 900 deg. Measurements were performed by XPS UHV Omicron...
-
The luminescence study of Sr2TiO4:Sm3+ coumpounds.
Dane BadawczeA luminescent material based on the strontium orthotitanate (Sr2TiO4) matrix doped with 1% of a mole of samarium was obtained using the typical solid-state synthesis method under a neutral atmosphere of nitrogen. The sample was investigated using powder X-ray diffraction (XRD) and several luminescence techniques to study the phase composition, luminescence...
-
Nonlinear impedance of as-quenched Bi2VO5.5 glass-ceramic was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched Bi2VO5.5 glass-ceramic was measured by impedance spectroscopy method.
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K was measured by impedance spectroscopy method.
-
Non-linear impedance of V2O5 nanorods obtained at 923K
Dane BadawczeThe DataSet contains the non-linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-35Nb2O5 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH) and Nb2O5 (≥99.9%, PLUKA AG) were...
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 3 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 10 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
The XRD diffraction patterns of as-preapred (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials
Dane BadawczeThe ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co)
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co) were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated at 693 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass heat treated two times was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 613 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 annealed glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 50(Bi2VO5.5)-50SrB4O7 glass was measured by impedance spectroscopy method.