Thermogravimetric analysis (TGA ) and derivative thermogravimetry (DTG) results for potassium citrate
Dane BadawczeThese data contains thermogravimetric analysis (TGA ) and derivative thermogravimetry (DTG) results for thermal decomposition of potassium citrate.
-
Raman spectra of PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures of carbonization)
Dane BadawczeThese data contain Raman spectra of PCMCA-700 (potassium citrate derived porous carbon materials obtained at 700°C ), PCMCA-800 (potassium citrate derived porous carbon materials obtained at 800°C ), PCMCA-900 (potassium citrate derived porous carbon materials obtained at 900°C ). The D peak at 1340 cm−1 and the G peak at 1592 cm−1 can be seen in all...
-
The morphology of lead-borate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe topography of iron-doped borate glasses and glass-ceramics were studied. Samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 < x < 37 in mol%) were prepared by the conventional meltquenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate...
-
The structure of lead-borate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and...
-
CO2 adsorption isotherms on PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures of carbonization)
Dane BadawczeThis dataset contains static CO2 adsorption isotherms on PCMCA-700 (potassium citrate derived porous carbon material obtained at 700 °C), PCMCA-800 (potassium citrate derived porous carbon material obtained at 800 °C), PCMCA -900 (potassium citrate derived porous carbon material obtained at 900 °C) adsorbents.
-
Vident-synth: a synthetic intra-oral video dataset for optical flow estimation
Dane BadawczeWe introduce Vident-synth, a large dataset of synthetic dental videos with corresponding ground truth forward and backward optical flows and occlusion masks. It can be used for:
-
CO2 uptake capacities of PCMCA-900 (potassium citrate-derived porous carbon prepared at 900 °C) adsorbent at various temperatures
Dane BadawczeThese data contain CO2 uptake capacities of PCMCA-900 (potassium citrate-derived porous carbon prepared at 900 °C) adsorbent at various temperatures. Adsorption experiments were carried out at temperatures 0 °C, 25 °C, and 50 °C at 1 bar.
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Dane BadawczeElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
XPS (X-ray photoelectron spectroscopy) spectra and high-resolution spectra of C 1 s and O 1 s of the PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures)
Dane BadawczeThese data include XPS full spectra and high-resolution spectra of C 1 s and O 1 s of the (potassium citrate derivedporous carbon material obtained at 700 °C), PCMCA-800 (potassium citrate derived porous carbon material obtained at 800 °C), PCMCA (potassium citrate derived porous carbon material obtained at 900 °C). The elemental composition on the...
-
The topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with SEM method
Dane BadawczeThe topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by SEM.
-
Linear impedance of strontium–borate glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
-
Linear impedance of strontium–borate glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
-
The topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with SEM method
Dane BadawczeThe topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by SEM.
-
Thermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by DSC.
-
Thermal properties of ceramic Bi2VO5.5 and strontium–borate glass-ceramics containing crystalites of Bi2VO5.5. measured with DSC
Dane BadawczeThermal properties of ceramic Bi2VO5.5 and strontium–borate glass-ceramics containing Bi2VO5.5 crystallites was measured by DSC.
-
The SEM images of Ce0.8La0.2O2 nanocatalyst infiltrated with 10wt.% Ni prepared using soft template method
Dane BadawczeThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method and infiltrated to 10wt.% Ni in the catalyst. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate...
-
The structure of strontium–borate glass-ceramics containing crystalites of Bi2VO5.5. measured with X-ray diffraction and SEM methods
Dane BadawczeThe structure of strontium–borate glass-ceramics containing Bi2VO5.5 crystallites was measured by XRD and SEM.
-
The structure of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing Bi2VO5.5 nanocrystallites was measured by XRD.
-
Thermal properties of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by DSC.
-
The XRD diffraction patterns of Ce0.8La0.2O2/Ni prepared using soft template method and impregnation
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s nanopowders (nanoparticles,nanocatalyst) prepared using soft template method and further impregnated with 10wt.%Ni using aqueous nitrate solution.
-
The structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by XRD.
-
The XRD diffraction patterns of reduced LSCNT prepared using two methods and two sintering temperatures
Dane BadawczeThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s produced using two methods, namely organic (citrate assisted) and Pechini sintered at 1000 or 1200oC under air atmosphere and reduced at 900 for 12 h in wet H2.
-
Imaging of biological samples: crassula arborescens
Dane BadawczeOne of the tasks of modern botany is to describe the relationship between climatic conditions and other environmental factors and the anatomical structure and adaptation of species present in given geographic areas. The work [1] focuses on anatomical and morphological studies of leaves of plants from the coarse family. Species tested belong to leaf...
-
The XRD pattern of CeO2/10wt.%Ni with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor nitrate solution (betacyclodextrin). The dataset includes 5-90 2 theta degree measurement. Nonreduced. Sintered at 400oC for 4h.
-
Measurements of the chemical composition of LTO:Cu powders
Dane BadawczeLithium titanate doped by copper was measured by X-ray photoemission spectroscopy (XPS). For sol-gel synthesis lithium acetate dehydrate and titanium (IV) butoxide 97% and copper (II) nitrate from Alfa Aesar were used as a reagents. Cu precursor was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate...
-
Sol-gel derived lithium titanate powders measured by XPS method
Dane BadawczeFor sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate and copper nitrate were dissolved...
-
The SEM images of Ce0.8La0.2O2 nanopowder prepared using soft template method
Dane BadawczeThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed...
-
The SEM images of CeO2 nanopowder prepared using soft template method
Dane BadawczeThe dataset includes SEM images of CeO2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed several...
-
XPS study of the lithium titanate doped by copper
Dane BadawczeLithium titanate doped by copper was measured by X-ray photoemission spectroscopy. For sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal...
-
The XRD diffraction patterns of Ce0.8La0.2O2 and CeO2 prepared using soft template method
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s and CeO2-s nanopowders (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC, centrifuged...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 25xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method - 50xCMC
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 50xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
Temperture-programmed reduction (H2-TPR) of Ni-Mo2CTx_Mo2Ga2C and Ni-Mo2CTx_Mo3AlC2 catalysts
Dane BadawczeThe dataset includes the data for the preparation of plots illustrating the reduction peaks versus the temperature of the catalyst sample.
-
Scanning Electron Microscopy images of nanocubes suspension 1 month after synthesis
Dane BadawczeThis dataset contains the SEM images of the gold nanocubes suspension in citrate buffer. The goal of the study was to evaluate the size of the synthesized nanocubes, their stability one month after the synthesis process, and to verify the optimal conditions regarding nanocubes concentration for the SEM analysis. Solutions with two different AuNC concentrations...
-
The XRD pattern of CeO2/10wt.%Cu prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Fe prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Fe. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Mn prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Mn. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Co prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Co. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Ni prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XPS spectra of Al2O3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of Al2O3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/1%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/1%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of ZrO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of ZrO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of CeO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of CeO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of SrTiO3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of SrTiO3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
SEM images of Ni-Mo2CTx/Mo2Ga2C before and after catalytic dry reforming of methane
Dane BadawczeThe dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using modified Pechini/EDTA method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using modified Pechini method consisting of CA (citric acid), PEG (propylene glycol) and EDTA. Exact amount of metal nitrates were dissolved in water followed by addition of gelling agents and heated to 100C. Obtained gel was calcined at 600C for 4h. The powder...
-
SEM images of Ni-Mo2CTx/Mo3AlC2 before and after catalytic dry reforming of methane
Dane BadawczeThe dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
-
The XRD diffraction patterns of annealed Ce0.9M0.1O2 powders prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution of nitrates using TMAOH. The sediment was cetrifuged and rinsed with alcohol several times. Powders were dried and calcinated at 500 degrees for 2 h, followed...
-
Luminescence properties of TeOx-Dy gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Dy gel. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions. The sol...