Filtry
wszystkich: 6227
wybranych: 232
-
Katalog
- Publikacje 4794 wyników po odfiltrowaniu
- Czasopisma 441 wyników po odfiltrowaniu
- Konferencje 6 wyników po odfiltrowaniu
- Osoby 233 wyników po odfiltrowaniu
- Wynalazki 3 wyników po odfiltrowaniu
- Projekty 11 wyników po odfiltrowaniu
- Aparatura Badawcza 8 wyników po odfiltrowaniu
- Kursy Online 182 wyników po odfiltrowaniu
- Wydarzenia 5 wyników po odfiltrowaniu
- Dane Badawcze 544 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: KEROGEN, TRANSFORMATION, MACERALS, MINERALS
-
Tagged images with LEGO bricks - Transportation - Land
Dane BadawczeThe set contains images of LEGO bricks (from Transportation - Land category). The images were prepared for training neural network for recognition and labeling of LEGO bricks. The images contain one brick each. The images were taken from different sides by handheld camera hovering over the bricks lying on a white, non reflective surface.
-
Tagged images with LEGO bricks - Transportation - Sea and Air
Dane BadawczeThe set contains images of LEGO bricks (from Transportation - Sea and Air category). The images were prepared for training neural network for recognition and labeling of LEGO bricks. The images contain one brick each. The images were taken from different sides by handheld camera hovering over the bricks lying on a white, non reflective surface.
-
Effect of C-1748 derivatives on the morphological transformation of C. albicans ATCC 10231 cells
Dane BadawczeThe datasets contain the results of the impact of five C-1748 derivatives (IKE28 - IKE32) on morphological transformation of Candida albicans strain ATCC 10231 cells. Photographic documentation prepared with the TECAN Spark 10M titration plate reader.
-
Kinetics of hexane and cyclohexane biodegradation using Candida subhashii in mineral salt medium in the presence of DES solution
Dane BadawczeDataset presents results of investigations on kinetics of biodegradation of hexane and cyclohexane in Candida subhashii.
-
Decomposition kinetics of vanadium xerogel powder
Dane BadawczeThe DataSet contains the TGA curves of vanadium As-prepared xerogel powder with different heating rates. The information about sol synthesis is described in the Journal of Nanomaterials.
-
Thermal behavior of TeOx xerogel powder under different atmospheres
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx xerogel powder measured under different atmospheres. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution...
-
Thermal stability of vanadium xerogel powder under different atmpshere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of vanadium xerogel powder under oxidizing atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Changes in heat of vanadium xerogel powder under different atmosphere
Dane BadawczeThe DataSet contains the DSC curves of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Thermal behaviour of vanadium xerogel powder under argon atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
XPS analysis of the GO based materials
Dane BadawczeGraphene oxides samples were measured by XPS method. The X-ray photoemission spectroscopy measurements were carried out with Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The photoelectrons...
-
Thermal behaviour of vanadium xerogel powder under different inert atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
XPS measurement of the Fe-Ti based materials
Dane BadawczeThe mono‐ and bimetal‐modified (Pd, Cu) titanium(IV) oxide and iron oxide (III) photocatalysts were prepared by chemical reduction method and characterized using XPS method. The composition of elements incorporated in the surface layer of mono- and bimetallic photocatalysts was determined by XPS analysis, as well as the valence state of elements. Measurements...
-
Vision of the development of transformations in the district – Lower Sopot (Dolny Sopot) district case study, study proposal no 1, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Lower Sopot (Dolny Sopot) district, study proposal no 1, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located in Lower...
-
Vision of the development of transformations in the district – Lower Sopot (Dolny Sopot) district case study, study proposal no 3, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Lower Sopot (Dolny Sopot) district, study proposal no 3, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located in Lower...
-
Vision of the development of transformations in the district – Lower Sopot (Dolny Sopot) district case study, study proposal no 4, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Lower Sopot (Dolny Sopot) district, study proposal no 4, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located in Lower...
-
Vision of the development of transformations in the district – Lower Sopot (Dolny Sopot) district case study, study proposal no 2, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Lower Sopot (Dolny Sopot) district, study proposal no 2, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located in Lower...
-
Vision of the development of transformations in the district – Lower Sopot (Dolny Sopot) district case study, study proposal no 5, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Lower Sopot (Dolny Sopot) district, study proposal no 5, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located in Lower...
-
Vision of the development of transformations in the district – Lower Sopot (Dolny Sopot) district case study, study proposal no 6, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Lower Sopot (Dolny Sopot) district, study proposal no 6, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located in Lower...
-
Thermal behaviour of vanadium xerogel powder and V2O5 nanorods under helium atmosphere
Dane BadawczeThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder and V2O5 nanorods obtained at 650C. The information about xerogel powder and V2O5 nanorods synthesis is described in the Journal of Nanomaterials.
-
Powder x-ray diffraction pattern of polycrystalline synthetic leningradite, PbCu3V2O8Cl2
Dane BadawczePolycrystalline sample of Cu2+ (S=1/2) antiferromagnetic PbCu3V2O8Cl2 (synthetic analogue of the mineral leningradite) was prepared by solid state reaction of PbCl2, CuO, and V2O5.
-
Sb measurements in a Bi-Sb-Te ceramics materials
Dane BadawczeThe influence of the temperature of the annealing of ceramic materials with the composition Bi0.5Sb1.5Te3O9 was investigated. The materials were annealed at the temperature of 440 degrees Celsius and 450 degrees Celsius. There were no significant differences in the valence of antimony and other elements.
-
Vision of the development of transformations in the district – Gdańsk-Lower City (Dolne Miasto) district case study, study proposal no 2, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Gdańsk-Lower City (Dolne Miasto) district, study proposal no 2, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located...
-
Vision of the development of transformations in the district – Gdańsk-Lower City (Dolne Miasto) district case study, study proposal no 1, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Gdańsk-Lower City (Dolne Miasto) district, study proposal no 1, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located...
-
Vision of the development of transformations in the district – Gdańsk-Lower City (Dolne Miasto) district case study, study proposal no 3, April 2021
Dane BadawczeThe data presents results of work within the studies of the vision of the district in the context of the city, Gdańsk-Lower City (Dolne Miasto) district, study proposal no 3, from April 2021. The goal of the research process was to present the future image of the neighborhood and initial ideas of the development of transformations of the area located...
-
Analysis of the properties of the YSTF ceramics materials before and after reduction
Dane BadawczeThe valence of titanium in reduced YSTF ceramics materials was investigated. Ceramics were reduced by annealing in a hydrogen atmosphere. For comparison unreduced sample was also measured. Valance state was measured by XPS method.
-
Testing of DES toxicity towards Candida subhashii
Dane BadawczeDataset presents results of testing toxicity of selected DES solutions in mineral salt medium towards Candida subhashii.
-
XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials
Dane BadawczeIn the dataset are included raw data for the preparation of XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials.
-
The results of the assessment of the degree of deacetylation, antimicrobial activity and cytotoxicity of chitosan materials
Dane BadawczeDane prezentują wyniki pomiarowe stopnia deacetylacji 5 komerycjnych chitozanów, które przetwarzane dwiema metodami oceniono pod kątem aktywności przeciwdrobnoustrojowej i cytotoksyczności względem modelowej linii fibroblastów mysich L929. Ocenie porównawczej poddano materiały chitozanowe otrzymywane klasyczną metodą rozpuszczania w roztworze...
-
Pore size distribution of PC-X (porous carbon materials obtained at various temperatures)
Dane BadawczeThese data contain pore size distribution of PC-700 (porous carbon materials obtained at 700°C), PC-800 (porous carbon materials obtained at 800°C) and PC-900 (porous carbon materials obtained at 900°C) analyzed by the nitrogen adsorption/desorption technique.
-
Determination the method of free alcohol fermented beverage production based on roasted raw materials.
Dane BadawczeData set presents the results of monosaccharides and ethyl alcohol determination in samples of fermented cereal drink with increased health value based on barley malt and roasting of rye, chicory and beetroot, and with the addition of hops. The HPLC method with RID detector was used for determinations
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials
Dane BadawczeThe ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
X-ray diffraction spectra of nitrogen-doped carbon in hybrid materials containing praseodymium oxide
Dane BadawczeX-ray powder diffraction patterns of samples were carried out by Philips X’Pert diffractometer, which was radiated by graphite monochromatized Cu Kα (l equal 1.540598). The operating voltage was maintained at 40 kV, the current was maintained at 30 mA and analyzed in the range from 20° to 90°. The data presented confirmed the presence of the PrBSCF...
-
Scanning Electron Microscopy (SEM ) images of PC-X (porous carbon materials obtained at various temperatures)
Dane BadawczeThese data contain SEM (scanning electron microscopy) images of PC-700 (porous carbon materials obtained at 700°C), PC-800 (porous carbon materials obtained at 800°C) and PC-900 (porous carbon materials obtained at 900°C).
-
Nitrogen (N2) adsorption/desorption isotherms of PC-X (porous carbon materials obtained at various temperatures)
Dane BadawczeThese data contain nitrogen (N2) adsorption/desorption isotherms of PC-700 (porous carbon obtained at 700 °C), PC-800 (porous carbon obtained at 800°C), PC-900 (porous carbon materials obtained at 900°C). Data showed typical type-I isotherms, indicating the presence of micropores in their structures. PC-900, compared with PC-700 and PC-800, showed a...
-
X-ray Diffraction (XRD) patterns of PC-X (porous carbon materials obtained at various temperatures)
Dane BadawczeThese data contain X-ray diffraction patterns (XRD) of PC-700 (porous carbon materials obtained at 700°C), PC-800 (porous carbon materials obtained at 800°C) and PC-900 (porous carbon materials obtained at 900°C).
-
A model of stealth maritime object having some innovative solutions concerning the object form, structure and materials.
Dane BadawczeThe aim of the project is to work out a model of the stealth maritime object which will have innovative solutions concerning the object form, structure and materials. These solutions should enable a modification of combinations of the object features defining the object stealth characteristics (difficulty of the object detection in the water). It is...
-
Raman spectra of PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures of carbonization)
Dane BadawczeThese data contain Raman spectra of PCMCA-700 (potassium citrate derived porous carbon materials obtained at 700°C ), PCMCA-800 (potassium citrate derived porous carbon materials obtained at 800°C ), PCMCA-900 (potassium citrate derived porous carbon materials obtained at 900°C ). The D peak at 1340 cm−1 and the G peak at 1592 cm−1 can be seen in all...
-
Development of conductive porous media as packing materials for biotrickling filter – microbial fuel cell system (BTF-MFC system)
Dane BadawczeDataset presents values of electrical resistance measured for three developed conductive packimg materials for the application in a BTF-MFC system.
-
The XRD diffraction patterns of as-preapred (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co)
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co) were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
CO2 adsorption isotherms on PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures of carbonization)
Dane BadawczeThis dataset contains static CO2 adsorption isotherms on PCMCA-700 (potassium citrate derived porous carbon material obtained at 700 °C), PCMCA-800 (potassium citrate derived porous carbon material obtained at 800 °C), PCMCA -900 (potassium citrate derived porous carbon material obtained at 900 °C) adsorbents.
-
Selection of DES for biotrickling filtration of air polluted with hexane and cyclohexane
Dane BadawczeDataset covers selected data collected during selection of deep eutectic solvent (DES) additive to mineral salt medium (MSM) as a liquid phase during biotrickling filtration of air polluted with hexane and cyclohexane.
-
XRD patterns of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Dane BadawczeThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed in order to force the exsolution process of metallic nanoparticles.
-
XRD patterns of V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that crystallinity dependent on the annealing temperature.
-
Thermal properties of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the DSC and TG curves of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere at the selected temperature: 500C, 600C, and 1000C.
-
SEM micrographs of morphology evolution of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-800C. The...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 900 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...