Thermogravimetric analysis (TGA ) and derivative thermogravimetry (DTG) results for potassium citrate
Dane BadawczeThese data contains thermogravimetric analysis (TGA ) and derivative thermogravimetry (DTG) results for thermal decomposition of potassium citrate.
-
Raman spectra of PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures of carbonization)
Dane BadawczeThese data contain Raman spectra of PCMCA-700 (potassium citrate derived porous carbon materials obtained at 700°C ), PCMCA-800 (potassium citrate derived porous carbon materials obtained at 800°C ), PCMCA-900 (potassium citrate derived porous carbon materials obtained at 900°C ). The D peak at 1340 cm−1 and the G peak at 1592 cm−1 can be seen in all...
-
CO2 adsorption isotherms on PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures of carbonization)
Dane BadawczeThis dataset contains static CO2 adsorption isotherms on PCMCA-700 (potassium citrate derived porous carbon material obtained at 700 °C), PCMCA-800 (potassium citrate derived porous carbon material obtained at 800 °C), PCMCA -900 (potassium citrate derived porous carbon material obtained at 900 °C) adsorbents.
-
CO2 uptake capacities of PCMCA-900 (potassium citrate-derived porous carbon prepared at 900 °C) adsorbent at various temperatures
Dane BadawczeThese data contain CO2 uptake capacities of PCMCA-900 (potassium citrate-derived porous carbon prepared at 900 °C) adsorbent at various temperatures. Adsorption experiments were carried out at temperatures 0 °C, 25 °C, and 50 °C at 1 bar.
-
XPS (X-ray photoelectron spectroscopy) spectra and high-resolution spectra of C 1 s and O 1 s of the PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures)
Dane BadawczeThese data include XPS full spectra and high-resolution spectra of C 1 s and O 1 s of the (potassium citrate derivedporous carbon material obtained at 700 °C), PCMCA-800 (potassium citrate derived porous carbon material obtained at 800 °C), PCMCA (potassium citrate derived porous carbon material obtained at 900 °C). The elemental composition on the...
-
The XRD diffraction patterns of reduced LSCNT prepared using two methods and two sintering temperatures
Dane BadawczeThe dataset includes XRD diffraction patterns of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s produced using two methods, namely organic (citrate assisted) and Pechini sintered at 1000 or 1200oC under air atmosphere and reduced at 900 for 12 h in wet H2.
-
Molecular geometry of hexachlorobenzene
Dane BadawczePresented data shows molecular geometry of the ground singlet state of hexachlorobenzene and hexachlorobenzene with potassium atom in 10 angstrom distance. The geometry was obtained via MP2 and CCSD calculations using balanced polarized triple-zeta def2-TZVP basis set. Geometry is provided in the XYZ file format.
-
The SEM images of Ce0.8La0.2O2 nanocatalyst infiltrated with 10wt.% Ni prepared using soft template method
Dane BadawczeThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method and infiltrated to 10wt.% Ni in the catalyst. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate...
-
The XRD diffraction patterns of Ce0.8La0.2O2/Ni prepared using soft template method and impregnation
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s nanopowders (nanoparticles,nanocatalyst) prepared using soft template method and further impregnated with 10wt.%Ni using aqueous nitrate solution.
-
Photocatalytic degradation of acetaldehyde in high temperature reaction chamber
Dane BadawczeThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using TiO2 (titanium dioxide) as photocatalysts. It includes data on the influence of flow rate, TiO2 (titanium dioxide) filling the entire reactor, a thin layer of TiO2 (titanium dioxide) supported on KBr...
-
Powder x-ray diffraction pattern of polycrystalline Cu(IO3)2*xH2O
Dane BadawczeHydrated copper(II) iodate sample was prepared in water solution by reacting copper(II) sulfate and potassium iodate, following the method described by Peterson (J. Chem. Educ. 1957, 34, 12, 612). The sample was subsequently dried at various temperatures in order to produce an anhydrous Cu(IO3)2:
-
The XRD pattern of CeO2/10wt.%Ni with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor nitrate solution (betacyclodextrin). The dataset includes 5-90 2 theta degree measurement. Nonreduced. Sintered at 400oC for 4h.
-
Scanning Electron Microscopy images of nanocubes suspension 1 month after synthesis
Dane BadawczeThis dataset contains the SEM images of the gold nanocubes suspension in citrate buffer. The goal of the study was to evaluate the size of the synthesized nanocubes, their stability one month after the synthesis process, and to verify the optimal conditions regarding nanocubes concentration for the SEM analysis. Solutions with two different AuNC concentrations...
-
Measurements of the chemical composition of LTO:Cu powders
Dane BadawczeLithium titanate doped by copper was measured by X-ray photoemission spectroscopy (XPS). For sol-gel synthesis lithium acetate dehydrate and titanium (IV) butoxide 97% and copper (II) nitrate from Alfa Aesar were used as a reagents. Cu precursor was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate...
-
Sol-gel derived lithium titanate powders measured by XPS method
Dane BadawczeFor sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate and copper nitrate were dissolved...
-
The SEM images of Ce0.8La0.2O2 nanopowder prepared using soft template method
Dane BadawczeThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed...
-
The SEM images of CeO2 nanopowder prepared using soft template method
Dane BadawczeThe dataset includes SEM images of CeO2-s nanopowder (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate was heated up to 90oC, centrifuged and washed several...
-
Partial PLA composite surface activation by femtosecond laser ablation
Dane BadawczeThe dataset contains the studies on electrochemical activity of PLA composite (commercially available CB-PLA Protopasta), which was 3D printed in a form of 1x1cm electrodes. The electrodes were submitted to femtosecond laser ablation, etching a certain % of the electrochemically-exposed electrode size. The % value is in the name of each file. The goal...
-
Raman spectra and electrochemical data of carbon nanowall with tailored defects
Dane BadawczeThis dataset comprises of Raman spectra aquired with different excitation laser sources and the electrochemical data of defect-induced carbon nanowall electrodes (CNW).
-
XPS study of the lithium titanate doped by copper
Dane BadawczeLithium titanate doped by copper was measured by X-ray photoemission spectroscopy. For sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal...
-
Electrochemical studies of poly(lactic acid)-carbon black-nanodiamond composites
Dane BadawczeThis dataset contains electrochemical investigation on electrodes 3D printed using a new composite composed of poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The presented results contain:1. electrochemical characterisation...
-
The XRD diffraction patterns of Ce0.8La0.2O2 and CeO2 prepared using soft template method
Dane BadawczeThe dataset includes XRD patterns of Ce0.8La0.2O2-s and CeO2-s nanopowders (nanoparticles) prepared using soft template method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC, centrifuged...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 25xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using soft template precipitation method - 50xCMC
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using soft template precipitation method. CTAB was used as a micelle-based templating agent. The powders were precipitated from aqueous nitrate solution using NaOH solution and 50xCMC (critcal micelle concentration) of CTAB. Precipitates were heated up to 90oC,...
-
Temperture-programmed reduction (H2-TPR) of Ni-Mo2CTx_Mo2Ga2C and Ni-Mo2CTx_Mo3AlC2 catalysts
Dane BadawczeThe dataset includes the data for the preparation of plots illustrating the reduction peaks versus the temperature of the catalyst sample.
-
The XRD pattern of CeO2/10wt.%Cu prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Fe prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Fe. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Mn prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Mn. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Co prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Co. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Ni prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
Partial PLA composite surface activation by femtosecond laser ablation
Dane BadawczeThe dataset contains the studies on electrochemical activity of PLA composite (commercially available CB-PLA Protopasta), which was 3D printed in a form of 1x1cm electrodes. The electrodes were submitted to femtosecond laser ablation operating with different parameters. These were: gas atmosphere (He or air, data in different subfolders), the percentage...
-
The XPS spectra of Al2O3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of Al2O3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/1%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/1%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of ZrO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of ZrO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of CeO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of CeO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of SrTiO3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of SrTiO3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
SEM images of Ni-Mo2CTx/Mo2Ga2C before and after catalytic dry reforming of methane
Dane BadawczeThe dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
-
The XRD diffraction patterns of Ce0.9Gd0.1O2 prepared using modified Pechini/EDTA method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9Gd0.1O2-s nanopowder (nanoparticles) prepared using modified Pechini method consisting of CA (citric acid), PEG (propylene glycol) and EDTA. Exact amount of metal nitrates were dissolved in water followed by addition of gelling agents and heated to 100C. Obtained gel was calcined at 600C for 4h. The powder...
-
SEM images of Ni-Mo2CTx/Mo3AlC2 before and after catalytic dry reforming of methane
Dane BadawczeThe dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
-
Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses
Dane BadawczeLinear and nonlinear impedance was studied for lead-silicate glass samples doped with iron ions and alkaline oxides. The compositions of glasses were as follows: (in %mol) 50% SiO2, 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O, Li2O. All samples were prepared by the conventional melt quenching technique. The substrates were powdered...
-
The XRD diffraction patterns of annealed Ce0.9M0.1O2 powders prepared using the reverse microemulsion method
Dane BadawczeThe dataset includes XRD patterns of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared using the reverse microemulsion method. The powders were precipitated from organic-based solution of nitrates using TMAOH. The sediment was cetrifuged and rinsed with alcohol several times. Powders were dried and calcinated at 500 degrees for 2 h, followed...
-
Luminescence properties of TeOx-Dy gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Dy gel. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions. The sol...
-
Luminescence properties of TeOx-Tb gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Tb gel. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The sol was...
-
Luminescence properties of TeOx-Eu gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Eu gels. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The sol...
-
Transition dipole moment functions of the KRb molecule
Dane BadawczeElectronic transition dipole moment functions (TDMF) have been calculated for the singlet (s) and triplet (t) Sigma+ (S+), Pi (P), and Delta (D) electronic states of the KRb molecule. TDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. All results of the transition dipole moments...
-
Permanent dipole moment functions of the KRb molecule
Dane BadawczeElectronic permanent dipole moment functions (PDMF) have been calculated for the singlet (s) and triplet (t) Sigma+, Sigma-, Pi, and Delta electronic states of the KRb molecule. PDMFs are needed in understanding processes like photodissociation, photoassociation, cooling, and trapping of molecules. All results of the permanent dipole moments have been...
-
Born-Oppenheimer potential energy curves of the NaK molecule
Dane BadawczeAdiabatic potential energy curves (APEC) of the singlet (s) and triplet (t) Sigma+, Pi, and Delta electronic states have been calculated for the NaK molecule. All results of the presented molecular states have been obtained by the nonrelativistic multireference configuration interaction (MRCI) method used with pseudopotentials describing the interaction...
-
Optical properties of TeOx gels doped with a mix of rare-earth ions
Dane BadawczeThe DataSet contains the UV-Vis spectra of the TeOx gels doped with a mix of rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the different molar concentration of rare-earth ions was added, nitrates were used...
-
Optical properties TeOx gels doped with the rare-earth ions
Dane BadawczeThe DataSet contains the UV-Vis spectra of TeOx gels doped with the rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of the rare-earth ions were added, the nitrates were used as a source of rare-earth...