Katalog Danych Badawczych
-
Chemical composition of La-Sr-Ce-Ni-Ti ceramics material measured by XPS method
Dane BadawczeLa-Sr-Ce-Ni-Ti (LSCNT) based ceramics sample was manufactured by standard solid state reaction.Prepared powder was pressed into pilled and sintered in a furnace in air atmosphere for 10h. Annealing temperature was 1200 Celsius degree. To calculate chemical composition and determine valence states of the elements, X-Ray photoemission spectroscopy (XPS)...
-
Reduction of the strontium titanate doped by Ytrium ceramics observed by X-ray photoemission spectroscopy method
Dane BadawczeYtrium-doped strontium titanate (YSTF) ceramics materials were manufactured by three various methods: 1) standard solid-state reaction method from Y2O3 (Sigma Aldrich, 99,9%), TiO2 (Sigma Aldrich, 99%) and SrCO3 (Sigma Aldrich,98%), 2) Pechini method, 3) wet method.
-
Luminescence properties of TeOx gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx gels. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.88 mm measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Luminescence properties of TeOx-Tb gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Tb gel. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The sol was...
-
Luminescence properties of TeOx-Dy gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Dy gel. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions. The sol...
-
Luminescence properties of TeOx-Eu gels
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Eu gels. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The sol...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
D.C. electrical measurements of Bi2VO5.5 ceramic measured at high temperature region
Dane BadawczeD.C. electrical properties of Bi2VO5.5 ceramic was measured.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K was measured by impedance spectroscopy method.
-
XRD patterns of TeOx powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised to 75°C for the...
-
Thermal behavior of TeOx powder
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
XRD patterns of TeOx-BaO-BiO powder
Dane BadawczeThe DataSet contains the XRD patterns of the TeOx-BaO-BiO powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor), barium carbonate, and bismuth carbonate with thetraetylene glycol, water, ethanol, and acetic acid. (Samples molar concentration: 73TeO2-4BaO-3Bi2O3 and 73TeO2-3BaO-4Bi2O3)....
-
Optical properties of TeOx gels doped with a mix of rare-earth ions
Dane BadawczeThe DataSet contains the UV-Vis spectra of the TeOx gels doped with a mix of rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the different molar concentration of rare-earth ions was added, nitrates were used...
-
Optical properties TeOx gels doped with the rare-earth ions
Dane BadawczeThe DataSet contains the UV-Vis spectra of TeOx gels doped with the rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of the rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Thermal behavior of TeOx xerogel powder under different atmospheres
Dane BadawczeThe DataSet contains the results of the thermal behavior of the TeOx xerogel powder measured under different atmospheres. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution...
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
Plasmon resonance in gold-silver nanoalloys
Dane BadawczeSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Structural investigations of the Al2O3 ultra thin films
Dane BadawczeUltra-thin layers of Al2O3 were deposited by atomic layer deposition (ALD) (Beneq TFS 200 ALD system). This method provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. Samples with a thickness of 2...
-
Depth profile of the gold-silver bimetallic structures
Dane BadawczeSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
Depth profile of the chemical composition of the Au-Ag multilayers
Dane BadawczeSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched Bi2VO5.5 glass-ceramic was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched Bi2VO5.5 glass-ceramic was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 glass-ceramic measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 glass-ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
TEM imaging of Ag-Au nanoalloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of metal thin layers (Au/Ag or Ag/Au) followed by annealing under 550 Celsius degree in an argon atmosphere. The basic single layer thickness was usually ca. 3 nm. For investigations two samples wih 50% Au and 50% Ag were selected and samples 1/3 Ag - 2/3 Au and 2/3 Ag - 1/3...
-
TEM and EDX study of the Al2O3 ultra thin films
Dane BadawczeThe ultra-thin layers of Al2O3 were deposited on a silicon substrates. The method of atomic layer deposition (Beneq TFS 200 ALD system) was chosen as the proper method of dielectric layer deposition. This method provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water....
-
XPS measurements of the iron elements covered by chromium
Dane BadawczeAnticorrosive coatings are an important issue in modern materials engineering. One of the most commonly used, for that coating materials, is chrome. Three metal elements were measured, named as Turcja, WB Tech and Nomet. Names were given according to producer of elements. XPS measurements of the Cr 2p region give an ansver concering on surface chemical...
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Linear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of as-quenched 40Bi2VO5.5-60SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 593 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 593 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 30Bi2VO5.5-70SrB4O7 fully crystallized glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrcial properties of 30Bi2VO5.5-70SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
XRD patterns of V2O5 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of vanadium pentaoxide nanostructures obtained by the sol-gel with different annealing temperatures under synthetic air. The results show that crystallinity dependent on the annealing temperature.
-
XRD patterns of V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that crystallinity dependent on the annealing temperature.