Chemical properties of bismuth telluride – carbon composites.
Open Research DataCarbon nanotubes and amorphous carbon have been introduced into bismuth telluride matrix (in 0.15 and 0.30 wt % ratio) in order to investigate influence of carbon on composite’s thermoelectric properties. Composites with well-dispersed additives have been obtained by sonication and ball-milling. Chemical composition of materials was confirmed by XPS...
-
Nonlinear impedance of as-quenched glass 40Bi2VO5.5-60SrB4O7 after full crystallization was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of as-quenched glass 40Bi2VO5.5-60SrB4O7 afetr full crystallization was measured by impedance spectroscopy method.
-
Nonlinear impedance of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 fully crystallized glass at 813 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 fully crystallized glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50Bi2VO5.5-50SrB4O7 partially crystallized glass at 613 K measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of 50Bi2VO5.5-50SrB4O7 partially crystallized glass was measured by impedance spectroscopy method.
-
Probiotic properties of bacterial strains isolated form bee products.
Open Research DataThis folder contains information about probiotic properties of bacterial strains isolated from bee products. Additionally information about antibiotic resistance are included.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 35Bi2VO5.5-65SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 40Bi2VO5.5-60SrB4O7 annealed glass at 473 K for 3 h measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of 40Bi2VO5.5-60SrB4O7 glass annealed at 473 K for 3h was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for fully crystallized 45Bi2VO5.5-55SrB4O7 glass was measured by impedance spectroscopy method.
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 3 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 10 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Thermal properties. DSC analysis of poly(xylitol sebacate-co-butylene sebacate) PXBS.
Open Research DataIn this work, a bio-based copolyester with good mechanical properties was synthesized andcharacterized in terms of structure, main properties and biodegradability Determining the chemicalstructure of such materials is important to understand their behavior and properties. Performingan extraction of insoluble cross-linked polymer using di erent solvents...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed and next fully crystallized 50Bi2VO5.5-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear impedance of glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties of glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized was measured by impedance spectroscopy method.
-
Application of optical microsphere in fiber optic sensors for measurement of electrochemical processes
Open Research Datainvestigation of the electrochemical processes using micro-sphere fiber-optic sensor with a zinc oxide (ZnO) coating applied by Atomic Layer Deposition method (ALD). The measurements were performed in 1M KNO3 during a decomposition of Bisphenol-A
-
The ab initio and experimental study of the spectroscopic and magnetic properties of Ho(III)-EDTA
Open Research DataIn this dataset, the ab initio calculations of the electronic structure and the magnetic properties are discussed in the context of the experimental data for the Ho–EDTA complex. In the calculations different models of the cluster have been applied to examine the influence of various parts of the environment of the Ho(III)-EDTA complex on its properties....
-
PA32 aluminum alloy - tensile properties
Open Research DataIn addition to steel, aluminium alloys are the main building material used in the shipbuilding industry. Due to its undoubted advantages, such as low density (nearly three times lower than in the case of steel for shipbuilding) and high corrosion resistance, it is often used for hulls of yachts and small vessels as well as superstructures. For safety...
-
Enhancing electrical properties through in-situ controlled nanocrystallization of V2O5–TeO2 glass
Open Research DataThe dataset contains raw data and projects concerning the manuscript called "Enhancing electrical properties through in-situ controlled nanocrystallization of V2O5–TeO2 glass"
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.15Sm0.05O2-s layer
Open Research DataThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.15Sm0.05O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.2O2-s layer
Open Research DataThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.2O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Sm0.2O2-s layer
Open Research DataThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Sm0.2O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.1Sm0.1O2-s layer
Open Research DataThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.1Sm0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.05Sm0.15O2-s layer
Open Research DataThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.05Sm0.15O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
AFM and SSRM investiagtion of carbon nanowalls properties
Open Research DataStructures with limited dimensionality are of great interest in modern nanotechnology. The properties of these objects are used, among others, for the construction of modern displays or as a base for quantum computers. Carbon nanowalls, which are the subject of the imaging results contained in this collection, are also considered interesting building...
-
Influence of the presence of rhamnolipids and ionic cross-linking conditions on the mechanical properties of alginate hydrogels.
Open Research DataThe dataset contains the results of determination the effect of rhamnolipids concentration, calcium chloride concentration and ionic cross-linking time on the mechanical properties of alginate hydrogels prepared by immersing the alginate mixture limited by the dialysis membrane in an appropriate cross-linking solution containing calcium ions. The mechanical...
-
Magnetic properties of of lead-silicate glasses and nanocomposites doped with iron oxide
Open Research DataMagnetic properties of iron-doped glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15 and 20 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere...
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 593 K and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 593 K and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Determination of mechanical properties of Ti13Nb13Zr cubes made with STL technology subjected to uniaxial compression
Open Research DataThe aim of the study was to determine the mechanical properties of Ti13Nb13Zr cubes made with STL technology (3D printing). The experiments were carried out on the Hung Ta universal test machine HT-2402. Cubes with the initial dimensions of 10x10x10 mm were subjected to compression by increasing force to over 80 kN. In various experiments, the angle...
-
Imaging of ferroelectric properties of sinter by means of Piezoresponse Force Microscopy
Open Research DataFerroelectricity is a property of certain materials [1], characterized by a spontaneous electrical polarization that can be reversed by applying an external electric field. Ferroelectric properties can be used to make capacitors with adjustable capacity. The permeability of ferroelectrics is not only regulated, but usually also very high, especially...
-
Electrical properties of nanostructures in lead-silicate glasses and nanocomposites doped with iron oxide
Open Research DataElectrical properties of iron oxide nanostructures observed in silicate glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15, 20 and 25 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where...
-
Evaluation of antimicrobial properties of thermomelt adhesives modified with zinc compounds
Open Research DataThe dataset contains the results of microbiological tests of thermomelt adhesives modified with zinc compounds, whose activity was assessed for their ability to reduce the number of Escherichia coli and Staphylococcus aureus strain, representing the Gram (-) and Gram (+) bacteria, respectively. The evaluation of antimicrobial properties of samples were...
-
Nonlinear impedance as a function of A.C. voltage for glass 40Bi2VO5.5-60SrB4O7 annealed at 473 K for 3h and next fully crystallized measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrcial properties as a function of A.C. voltage for annealed at 473 K for 3h and next fully crystallized 40Bi2VO5.5-60SrB4O7 glass was measured by impedance spectroscopy method.
-
Mechanical properties of concrete mixes M0-M100 concrete mixes
Open Research DataDataset of hardneded properties of concretes containing different amount of magnetite aggregate (M0-M100) mixes.Excel file consists results of:
-
Fresh properties of concrete mixes M0-M100 concrete mixes
Open Research DataDataset of fresh properties of concretes containing different amount of magnetite aggregate (M0-M100) mixes.*. ODS - open-source spreadsheet file file consists results of:
-
Spectroscopy properties of 1,8-diazafluoren-9-one (DFO) in PVA polymer for different concentrations
Open Research DataSpectroscopy properties: absorption and fluorescence spectra of 1,8-diazafluoren-9-one (DFO) in PVA film for different concentrations of dye.
-
Determination of mechanical properties of human stomach tissues subjected to uniaxial stretching
Open Research DataThe aim of the study was to determine the biomechanical properties of the walls of the human stomach. The samples were fragments of the human stomach obtained after sleeve gastrectomy. Samples cut parallel to the stomach curves and perpendicular to the stomach curves were tested in each series. All samples were subjected to uniaxial stretching. During...