Depth XPS profile of vanadium pentoxide
Open Research DataVanadium pentoxide sample was manufactured by sol-gel method and deposited on a substrate by spin coating technique. To determine depth profile of chemical composition of thin film, etching by Argon ion gun was used. Thin film was etched three times. Chemical composition was measured by XPS method.
-
Impedance spectroscopy of the lithium titanate doped by copper thin films
Open Research DataLithium titanate doped by copper thin films were derived by sol-gel method. Prepared gel was deposited by spin-coating technique. Samples with various content of Cu were measured by impedance spectroscopy method in a wide range of temperature, from -120 up to 150 deg.
-
The Scanning Electron Microscopy images of three arthropods
Open Research DataThe dataset contains micrographs of various arthropods made with the Scanning Electron Microscopy (SEM) technique. The images were done during the laboratory with students from the Faculty of Chemistry. Among the studied species, there is a fruit fly (lat.Drosophila melanogaster), a spider (most likely Sibianor aurocinctus), and a weevil insect (Curculionoidea).
-
SEM/EDX data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Open Research DataThis Data set include SEM and EDX results of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited layers were amorphous,...
-
TEM data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Open Research DataThis Dataset include presentation of summarized TEM investigation of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited...
-
Bacteriological and physicochemical monitoring of coastal sea waters – Gulf of Gdańsk (Baltic Sea) in 2004
Open Research DataThe dataset contains the results of a bacteriological and physicochemical studies of Gdansk Bay coastal waters within the administrative boundaries of Gdańsk city in 2004. The examined material consisted of water samples collected from 15 sampling points. Number of Escherichia coli, number of intestinal enterococci, presence of Salmonella sp., pH, temperature,...
-
Bacteriological and physicochemical monitoring of coastal sea waters – Gulf of Gdańsk (Baltic Sea) in 2006
Open Research DataThe dataset contains the results of a bacteriological and physicochemical studies of Gdansk Bay coastal waters within the administrative boundaries of Gdańsk city in 2006. The examined material consisted of water samples collected from 15 sampling points. Number of Escherichia coli, number of intestinal enterococci, presence of Salmonella sp., pH, temperature,...
-
Bacteriological and physicochemical monitoring of coastal sea waters – Gulf of Gdańsk (Baltic Sea) in 2007
Open Research DataThe dataset contains the results of a bacteriological and physicochemical studies of Gdansk Bay coastal waters within the administrative boundaries of Gdańsk city in 2007. The examined material consisted of water samples collected from 15 sampling points. Number of Escherichia coli, number of intestinal enterococci, presence of Salmonella sp., pH, temperature,...
-
Mechanical lithography in a polymer substrate using AFM in contact mode
Open Research DataMechanical lithography in a polymer substrate. Contact mode. NTEGRA Prima (NT-MDT) device. NSG 01 probe.
-
Structural and luminescence properties of B2O3-Bi2O3+10AlF3 glasses doped with Eu3+/Dy3+ ions
Open Research DataThe attached data contains the results of measurements of B2O3-Bi2O3 and B2O3-Bi2O3+10AlF3 glasses doped with Eu3+ and Dy3+ ions in different molar ratios. Glasses were synthesized by the melt quenching technique. On their basis, the structural, optical, and luminescence properties of synthesized samples were characterized. The dataset includes XRD,...
-
The voltage on bus bars of the main switchboard of the car carrier electrical power system during sea trials
Open Research DataThe dataset is part of the research results on the quality of supply voltage on bus bars of the main switchboard of the ship's electrical power system in different states of ship exploitation. The attached dataset contains the measurement results conducted onboard the car carrier during sea trials.
-
The voltage on bus bars of the main switchboard of the car carrier electrical power system at sea trials during maneuvering
Open Research DataThe dataset is part of the research results on the quality of supply voltage on bus bars of the main switchboard of the ship's electrical power system in different states of ship exploitation. The attached dataset contains the measurement results conducted onboard the car carrier at sea trials during maneuvering.
-
Split-beam echosounder data from Gdansk Deep Summer 2019
Open Research DataThe acoustic data was collected in 2019, in the Gdansk Deep, in the season: Summer. Data was collected during the day and night. Three split-beam echosounders with frequencies of 38 kHz, 120 kHz and 333 kHz were used to collect the data. The data was collected while the ship was sailing. To ensure data quality, echosounders were calibrated and passive...
-
Simulation of the weight averaging of pulse frequency modulated sensor output signal
Open Research DataThe aim of the research is investigation of the efficiency of weight averaging of pulse frequency modulated signal. It was shown that from the point of view of the reduction of the sampling error the best are polynomial weighing functions, for which the maximum of this component error decreases proportionally to the appropriate power of the number of...
-
The structure of vanadate glasses containing BaTiO3.
Open Research DataThe structure of vanadate glasses doped with BaTiO3 was measured by SEM technique. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
XPS analysis of TBBO glass
Open Research DataGlasses and glass-ceramics with nominal composition 73 TeO2– 4BaO– 3Bi2O3–18SrF2-2RE2O3 (where RE = Eu, Dy) have been synthesized by conventional melt-quenching technique and subsequent heat treatment at 370 °C for 24 h in air atmosphere. Various Eu3+ to Dy3+ molar ratio have been applied to investigate luminescence properties in both glass and glass-ceramic...
-
Split-beam echosounder data from Puck Bay autumn 2018
Open Research DataThe acoustic data was collected in 2018, in the Bay of Puck, in the seasons: autumn. Data was collected during the day and night. Three split-beam echosounders with frequencies of 38 kHz, 120 kHz and 333 kHz were used to collect the data. The data was collected at a designated study area not far from the city of Hel, while the ship was sailing. To ensure...
-
Split-beam echosounder data from Puck Bay spring 2019
Open Research DataThe acoustic data was collected in 2019, in the Bay of Puck, in the season: spring. Data was collected during the day and night. Three split-beam echosounders with frequencies of 38 kHz, 120 kHz and 333 kHz were used to collect the data. The data was collected at a designated study area not far from the city of Hel, while the ship was sailing. To ensure...
-
Split-beam echosounder data from Puck Bay spring 2019 Part II
Open Research DataThe acoustic data was collected in 2019, in the Bay of Puck, in the season: spring. Data was collected during the sunrise and sunset. Three split-beam echosounders with frequencies of 38 kHz, 120 kHz and 333 kHz were used to collect the data. The data was collected at a designated study area not far from the city of Hel, while the ship was sailing....
-
X-ray diffractometry results of the SrTi0.50Fe0.50O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.50Fe0.50O3-d (STF50) powder after ball milling. The phase composition of the investigated STF50 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.35Fe0.65O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.35Fe0.65O3-d (STF35) powder after ball milling. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.30Fe0.70O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.30Fe0.70O3-d (STF70) powder after ball milling. The phase composition of the investigated STF70 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
Cyclic polarization studies of Mg corrosion in alkaline environment
Open Research DataThe dataset contains the cyclic polarization studies of Mg (99.99%) in NaOH electrolyte at different pH values: 10, 11 and 12 aiming at understanding of Mg(OH)2 passive layer formation mechanism and conditions. The electrochemical studies were carried out in a three electrode setup, with Pt mesh as the counter electrode and Ag|AgCl as the reference...
-
The voltage on bus bars of the main switchboard of the ro-ro ship electrical power system during a layover at the port
Open Research DataThe dataset is part of the research results on the quality of supply voltage on bus bars of the main switchboard of the ship's electrical power system in different states of ship exploitation. The attached dataset contains the measurement results carried out onboard a ro-ro ship during a layover at the port.
-
The voltage on bus bars of the main switchboard of the car carrier electrical power system at sea trials during a sea voyage
Open Research DataThe dataset is part of the research results on the quality of supply voltage on bus bars of the main switchboard of the ship's electrical power system in different states of ship exploitation. The attached dataset contains the measurement results conducted onboard the car carrier at sea trials. The data were recorded during a sea voyage, under normal...
-
DLC coating in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
The structure of vanadate glass-ceramics containing BaTiO3.
Open Research DataThe structure of vanadate glass-ceramics doped with BaTiO3 was measured by SEM technique. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on...
-
Ferromagnetic nanoparticles imaging by means of Magnetic Force Microscopy
Open Research DataFerromagnetic nanoparticles can be used as building blocks for advanced thin film magnets, and can also be used in data storage and biomedical technologies. Nano-crystalline ferrites with the chemical formula NixZn (1 - x) Fe2O4, where x = 0, 0.2, 0.4, 0.6, 0.8, 1.0 show anti-corrosion properties and suppress electromagnetic interference, in the case...
-
Output voltage, current and DC-link voltages under SPWM, experimental results
Open Research DataThe dataset contains the experimental results of the project: A universal algorithm of space vector pulse width modulation for three-level three and multi-phase NPC inverters with DC-link voltage balancing. The output line-to-line voltage, output current and DC-link voltages were included. The Carrier-Based Pulse-Width Modulation (CBPWM) technique was...
-
X-ray diffractometry results of the Sr1.05Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr1.05Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr0.90Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.90Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr1.00Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr1.00Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr0.95Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.95Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
The AFM micrographs of pitting corrosion evolution on high-alloy steel 1.4301
Open Research DataThe dataset contains the results of topographic imaging of high-alloy stainless steel 1.4301 on which the pitting corrosion process was induced by electrochemical methods. The study of the effects of a local attack allows for conclusions about the intensity and mechanism of this type of corrosion. The file contains atomic force microscopy (AFM) data...
-
Split-beam echosounder data from Puck Bay winter 2019
Open Research DataThe acoustic data was collected in 2019, in the Bay of Puck, in the season: winter. Data was collected during the day and night. Three split-beam echosounders with frequencies of 38 kHz, 120 kHz and 333 kHz were used to collect the data. The data was collected at a designated study area not far from the city of Hel, on the route Hel - Gdynia and on...
-
Ellipsometric monitoring during the polarization studies of Mg corrosion in alkaline environment
Open Research DataThe dataset contains the ellipsometric results from the Mg polarization studies aiming at understanding the Mg(OH)2 passive layer formation mechanism and conditions. The single-wavelength ellipsometer ELX-02C from Dr Riss GmbH was utilized, operating He-Ne laser at 632.8 nm. The polarization conditions for the experiment are depicted in the related...
-
SEM inwestigation of the silver nanostructures
Open Research DataSilver thin films with a thickness of 1nm, 3nm, 5nm, 7nm and 9nm were deposited by a table-top magnetron sputtering unit in a pure argon plasma from a high-purity silver target. Silicon wafers was used as a substrates. As-deposired films were annealed in Ar atmosphere at 550 Celsius degree for 15 minutes.As a result of annealing, Ag nanostructures formed...
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Open Research DataWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
Fuel cell noise data
Open Research DataMeasurement data of Hydrogen PEM fuel cels. The voltage fluctuations were measured over single cels of stack of 10 cels.
-
Results and models for Novel high frequency components with non-conventional shape employing smooth geometry deformation of 3D solid with FFD
Open Research DataThe project aims to investigate the possibility of developing and manufacturing novel high frequency devices having non-standard geometries, allowing for improved electromagnetic performance over what is achievable with currently available design tools. The non-conventional geometry will be obtained by employing the free-form shape deformation technique...
-
The voltage on bus bars of the main switchboard of the ferry electrical power system during a layover at the port
Open Research DataThe dataset is part of the research results on the quality of supply voltage on bus bars of the main switchboard of the ship's electrical power system in different states of ship exploitation. The attached dataset contains the measurement results carried out onboard the ferry during a layover at the port.
-
SEM images of 8YSZ sintered using flash sintering programme
Open Research DataThe dataset contains the SEM images of 8YSZ (8mol% Y2O3-ZrO2) sintered using the flash technique in the muffle furnace. The programme was as follows: 3oC/min to 1000C - 1h hold- 3oC/min 1100C - 1h hold- 3oC/min 1200C - 2h hold- 3oC/min 1400- 30 min hold- 5oC/min 1200C - 15h hold- 4oC/min RT
-
XPS investigations of tge tin/tin oxides - CNT composites
Open Research DataThe composite of tin/tin oxide nanoparticles with graphene oxide and CMC based on laser ablation technique as an electrode material for energy storage devices were manufactured. The material exhibited a three-dimensional conducting graphene oxide network decorated with tin or tin oxide nanoparticles. The presence of tin/tin oxide in composites was...
-
Low frequency nois of supecapacitor
Open Research DataDataset contains noise measurement results on prototype electrochemical double layer capacitor. The measurement procedure is described in https://dx.doi.org/10.1515/mms-2017-0059.