Filtry
wszystkich: 3613
wybranych: 524
Wyniki wyszukiwania dla: optical fiber sensorlong-period fiber gratingsrefractive index sensingthin filmindium tin oxideelectrochemistry
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B48/#A45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A45/#B48
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
Optical properties of MnO-B2O3 based glass
Dane BadawczeMnO-B2O3 based glass with Au nanoparticles samples were annealing for a various time (in a range of 24-96 hours) at various temperatures (from 340 up to 350 deg.). Presence of silver nanoparticles was detected by UV-VIS measurements. On the basis of change optical bandgap, Ag NPs was detected.
-
Optical Parameters Stability Over Time of Porous Phantoms Mimicking Tissues
Dane BadawczeOptical phantoms are used to validate optical measurement methods. The stability of their optical parameters over time allows them to be used and stored over long-term periods while maintaining their optical parameters. The aim of the presented research was to investigate the stability of fabricated porous phantoms, which can be used as a lung phantom...
-
Optical measurements of lithium titanate sol-gel derived thin films
Dane BadawczeNanocrystalline thin films with 800 nm thickness were prepared by sol–gel method. To examine the influence of the annealing time on as-prepared films crystallization, the coatings were heated at 550 °C for 10, 20 and 80 h. On the basis of transmission characteristic optical properties were calculated. It was found that transmission through the thin...
-
Vident-synth: a synthetic intra-oral video dataset for optical flow estimation
Dane BadawczeWe introduce Vident-synth, a large dataset of synthetic dental videos with corresponding ground truth forward and backward optical flows and occlusion masks. It can be used for:
-
Optical measurements of LTO:Cu sol-gel derived thin films
Dane BadawczeLithium titanate doped by copper thin films were manufactured by chemical, sol-gel method. Flms were deposited on a Corning glass substrated by spin coater. To calculated optical band gap and other optcal parameters, UV-VIS spectroscopy measurements were performed. For measurements selected samples with various content of Cu.
-
Optical properties TeOx gels doped with the rare-earth ions
Dane BadawczeThe DataSet contains the UV-Vis spectra of TeOx gels doped with the rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of the rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Fire Weather Index data for Poland (March – September 2019) based on high-resolution Weather Research and Forecasting Model
Dane BadawczeThis dataset contains forecasted FWI indices calculated for the period: March 1 - September 30, 2019, based on the meteorological fields derived from the Weather Research and Forecasting Model (WRF) ver. 4.2.1. For each day FWI data with the forecast range equal 24 and 48 hour were stored in GeoTIFF files. In addition, soil moisture and temperature...
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Dane BadawczeData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.
-
Structure and optical measurements of Eu doped tellurium oxide thin films
Dane BadawczeThin films were deposited by magnetron sputtering method and simultaneously heated at 200 oC. Presence of Eu ions and their valence states was confirmed by X-ray photoemission spectroscopy measurements. The structure of the films as well as the influence of europium dopant on crystalline structure of the films was examined by X-ray diffraction method. ...
-
Optical properties of TeOx gels doped with a mix of rare-earth ions
Dane BadawczeThe DataSet contains the UV-Vis spectra of the TeOx gels doped with a mix of rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the different molar concentration of rare-earth ions was added, nitrates were used...
-
Gdańsk University of Technology graduates’ length of the labour inactivity period after graduation – years 2014-2018
Dane BadawczeThe dataset includes data from the survey on the Gdańsk University of Technology graduates from years 2014-2018 on length of the labour inactivity period after graduation. The survey was conducted in the period from 2016 to 2020, two years after the respondents obtained graduate status. The research sample included 9413 respondents. To summarize, the...
-
Transmission electron microscope (TEM) and optical microscope images of pristine and silica-coated bismuth oxide and gadolinium oxide particles
Dane BadawczeCollection of raw transmission electron microscope (TEM) micrographs and optical microscope images used in the associated manuscript. All data in accessible *.tif format. Zip package contains:
-
Time period when graduates of Gdańsk University of Technology start work after graduation – years 2010-2014
Dane BadawczeThe dataset includes data from the survey on the Gdańsk University of Technology graduates from years 2010-2014 on time period when they start work after graduation. The survey was conducted in the period from 2012 to 2016, two years after the respondents obtained graduate status. The research sample included 5367 respondents. To summarize, the Gdańsk...
-
Time period when graduates of Gdańsk University of Technology start work after graduation – years 2015-2018
Dane BadawczeThe dataset includes data from the survey on the Gdańsk University of Technology graduates from years 2015-2018 on time period when they start work after graduation. The survey was conducted in the period from 2017 to 2020, two years after the respondents obtained graduate status. The research sample included 7409 respondents. To summarize, the Gdańsk...
-
UAV spectrometer reflectance and leaf area index for vegetation near Gdynia, Poland
Dane BadawczeReflectance data from the UAV flights with UV-VIS spectrometer along with leaf area index measurements for vegetaion near Gdynia, Poland.
-
Comparison of Poland, Germany and the European average using the components of the summary innovation index
Dane BadawczeThe analysis presents a comparison of the innovation policies of Poland and Germany using all the indicators included in the Summary Innovation Index (SII), then the obtained results were analyzed and conclusions were formulated.The indicators are divided into three main categories, each group of indicators shows a different aspect of the innovativeness...
-
The Gini index in Poland in 2008-2017
Dane BadawczeWhen assessing the level of poverty, one should use indicators presenting indicators of social inequality in terms of income, indicators of prosperity and poverty In Poland, the situation in terms of inequality is improving, but as measured by the Gini coefficient. The coefficient, which ranges from zero to one hundred percent, the higher it is, the...
-
Hydrological indicators of water zones in inundation, historical water levels, and forcing data for the 1881-2099 period in the lower Biebrza valley
Dane BadawczeThis data set contains hydrological (1) indicators of water source extents in the Biebrza River floodplain (NE Poland) simulated using an integrated hydrological model (IHM), (2) forcing data for the IHM, and (3) water levels in the Osowiec station from the period 1881-1910.
-
The fertility rate (TFR) in Poland in the period 1955-2017
Dane BadawczeThe fertility rate has dropped 2.5 times over the last 60 years. Immediately after the baby boom in the first half of the 1980s, many generations of women born in the second half of the 1970s, an increase in the number of births from the mid-1990s, were expected as a result of entering the age of the highest fertility age in Poland. which lasted until...
-
Bibliographic data on datasets affiliated to Most Wiedzy and indexed in Data Citation Index (retrieved by Web of Science service in December 2021)
Dane BadawczeThe file contains the number of datasetes published by the reserchers affiliated to Most Wiedzy and indexed in Data Citation Index provided by Web of Science. The Search was performed using the name of institution in the 'address' filed or 'group author' filed . Data retrieved and published during the '5th Open Science Conference (1-3.12.2021).
-
Bibliographic data on datasets affiliated to Maria Curie-Skłodowska University and indexed in Data Citation Index (retrieved by Web of Science service in February2022)
Dane BadawczeThe file contains the number of datasets published by the researchers affiliated to Maria Curie-Skłodowska University and indexed in Data Citation Index provided by Web of Science. The Search was performer using the name of institution in the address field or group author field. Data retrieved and published during the 5th Open Science Conference (1-3.12.2021)
-
Bibliographic data on datasets affiliated to Gdansk University of Technology and indexed in Data Citation Index (retrieved by Web of Science service in December 21)
Dane BadawczeThe file contains the number of datasets published by the researchers affiliated to Gdansk University of Technology and indexed in Data Citation Index provided by Web of Science. The Search was performed on the 1st of December 2021 using the name of institution in the 'address' and 'group author' field. Data retrieved and published during the 5th Open...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 64 mA. Sample 91. Image period: 5 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 64 mA. Sample 91. Pictures were taken relatively fast, with period of 5 sec in order to examine the fast fluctuations of sample temperature during...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 2,7 V at 120 mA. Sample 103. Image period: 0,5 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 2,7 V and discharged to 10 mV by constant current 120 mA. Sample 103. Thermographic pictures were taken relatively fast, with period of 0,5 sec in order to examine the fast fluctuations of sample...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,4 V at 420 mA. Sample 103. Image period: 0,5 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,4 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 0,5 sec (2 Hz) in order to examine the fast fluctuations of sample temperature during charging...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,3 V at 420 mA. Sample 103. Image period: 2 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,3 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken relatively fast, with period of 2 sec in order to examine the fast fluctuations of sample temperature during...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103. Image period: 0,5 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 0,5 sec (2 Hz) in order to examine the fast fluctuations of sample temperature during charging...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,5 V at 420 mA. Sample 103. Image period: 0,5 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,5 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 0,5 sec (2 Hz) in order to examine the fast fluctuations of sample temperature during charging...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103. Image period: 1 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 1 sec (1 Hz) in order to examine the fast fluctuations of sample temperature during charging...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,4 V at 420 mA. Sample 103. Image period: 1 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,4 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 1 sec in order to examine the fast fluctuations of sample temperature during charging - discharging...
-
Gini index in selected European Union countries in 2017.
Dane BadawczeWhen assessing the level of poverty, one should use indicators presenting indicators of social inequality in terms of income, indicators of prosperity and poverty. In Poland, the situation in terms of inequality is improving, but as measured by the Gini coefficient.
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103. Image period: 0,5 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 0,5 sec (2 Hz) in order to examine the fast fluctuations of sample temperature during charging...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103. Image period: 1 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 1 sec (1 Hz) in order to examine the fast fluctuations of sample temperature during charging...
-
Bibliographic data on datasets (from 2020) affiliated to Most Wiedzy and indexed in Data Citation Index (retrieved by Web of Science service in December 2021)
Dane BadawczeThe file contains the number of datasets published by the researchers affiliated to Most Wiedzy and indexed in Data Citation Index by Web of Science. The Search was perfprmed using the name of institution in the 'assress' filed or 'group author' field. Data retrieved and published during the 5th Open Science Conference (1-3.12.2021).
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Emission spectra of UV and fluorescent lamps
Dane BadawczeData contain emision spectra of two different UV lamps: Special "TL"E 22W/10 Black light (Philips) and Semilac UV, 36 W and also Fluorescent lamp: L22W/840 Circular Cool White, Lumilux (Osram). These spectra were recorded by USB4000 Fiber Optic Spectrometer.
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #2. Image period: 1 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 1 sec (1 Hz) in order to examine the fast fluctuations of sample temperature during charging...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #3. Image period: 0,5 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 0,5 sec (2 Hz) in order to examine the fast fluctuations of sample temperature during charging...
-
Thermographic imaging of electrochemical double layer capacitors during cycling charging - discharging 0 - 3,6 V at 420 mA. Sample 103, run #2. Image period: 0,5 sec.
Dane BadawczeDataset contains thermal images of prototype electrochemical double layer capacitor taken during cyclic charging - discharging. The sample was charged to 3,6 V and discharged to 10 mV by constant current 420 mA. Sample 103. Pictures were taken with period of 0,5 sec (2 Hz) in order to examine the fast fluctuations of sample temperature during charging...