Filtry
wszystkich: 137
wybranych: 127
-
Katalog
Filtry wybranego katalogu
Wyniki wyszukiwania dla: LATTICE STRUCTURES
-
The homometallic warwickite V 2 OBO 3
PublikacjaThe synthesis, structure and elementary magnetic characterization of the homometallic warwickite V2OBO3 are reported. The material adopts the orthorhombic warwickite structure type at room temperature, space group Pnma (No. 62) with lattice parameters a = 9.2317(1) Å, b = 3.1172(1) Å, and c = 9.5313(1) Å. Temperature-dependent magnetic susceptibility, electrical resistivity, and specific heat measurements show anomalies near 35 K,...
-
Structure and water uptake in BaLnCo2O6−δ (Ln =La, Pr, Nd, Sm, Gd, Tb and Dy)
PublikacjaThe structure of BaLnCo2O6-δ (Ln =La, Pr, Nd, Sm, Gd, Tb and Dy) was studied by the means of synchrotron radiation powder X-ray diffraction, neutron powder diffraction and Transmission Electron Microscopy (TEM), while water uptake properties were analysed with the use of thermogravimetry (TG) and water adsorption isotherms. The structure refinement revealed that the dominant phase in all compositions was orthorhombic with an ordering...
-
Chemical Pressure Tuning Magnetism from Pyrochlore to Triangular Lattices
PublikacjaGeometrically frustrated lattices combined with magnetism usually host quantum fluctuations that suppress magnetic orders and generate highly entangled ground states. Three-dimensionally (3D) frustrated magnets generally exist in the diamond and pyrochlore lattices, while two-dimensionally (2D) frustrated geometries contain Kagomé, triangular, and honeycomb lattices. In this work, we reported using chemical pressure to tune the magnetism...
-
Improving Thermal Insulation Properties for Prefabricated Wall Components Made of Lightweight Aggregate Concrete with Open Structure
PublikacjaPorous concrete is commonly used in civil engineering due to its good thermal insulation properties in comparison with normal concrete and high compression strength in comparison with other building materials. An extremely porous concrete, called ‘lightweight aggregate concrete with open structure’ (LAC), is used in some German plants to produce prefabricated wall components. They are used mainly in hall buildings, e.g. supermarkets....
-
From flow to jamming: Lattice Gas Automaton simulations in granular materials
PublikacjaWe introduce the first extension of a Lattice Gas Automaton (LGA) model to accurately replicate observed emergent phenomena in granular materials with a special focus on previously unexplored jamming transitions by incorporating gravitational effects, energy dissipation in particle collisions, and wall friction. We successfully reproduce flow rate evolution, density wave formation, and jamming transition observed in experiments....
-
Electrical and structural properties of Nb-doped SrTiO3
PublikacjaNiobium-doped strontium titanate synthesized via conventional solid-state reaction has been studied. Influence of niobium content on the lattice parameters and electrical conductivity has been reported. Various reduction conditions have been investigated. For samples reduced in hydrogen at 1400°C, a transition from thermally activated to metallic behavior has been observed. Maximum electrical conductivity (ca. 55 Scm−1 at 650°C)...
-
Marcinkiewicz Averages of Smooth Orthogonal Projections on Sphere
PublikacjaWe construct a single smooth orthogonal projection with desired localization whose average under a group action yields the decomposition of the identity operator. For any full rank lattice \Gamma ⊂ R^d , a smooth projection is localized in a neighborhood of an arbitrary precompact fundamental domain R^d / \Gamma. We also show the existence of a highly localized smooth orthogonal projection, whose Marcinkiewicz average under the...
-
Modeling of truss with cold-formed section and positive eccentricity in the node
PublikacjaThis work is dedicated to establishing the load carrying capacity of tensed and compressed truss’ nodes made of cold-formed open cross sections. The occurrence of bending in the truss’ nodes is the result of a specific production technology for system lattice girders assumed by the designer and the producer. The aim of this research is to present the methodology of conduct for creation of computational models that best depict the...
-
Modelowanie kratownicy z kształtowników giętych na zimno z mimośrodami dodatnimi w węźle = Modelling of truss with cold-formed section and positive eccentricyty in the node.
PublikacjaThe topic of this research is establishing load-carrying capacity of compressed and tensed chords of trusses made of cold-formed open cross-sections. Occurrence of bending in the truss’ chord is the result of specific production technology assumed by the designer and producer of lattice girder’s systems. The aim of this research is to present methodology of conduct while creating numerical models that best depict the behaviour...
-
Study of the Effect of Filling Thermoplastic Medical Polyurethane with PVA, PLA or Diatomite on the Relaxation Times Distributions of 1H NMR
PublikacjaIn this work, to characterize the mobility of diferent sections of the macromole‑ cules of polyurethane (PUR), polyvinyl alcohol (PVA), and polylactic acid (PLA), as well as the density of crosslinks of the polymer chains when using fllers, we used the distributions of spin–lattice and spin–spin relaxation times for the protons. It is shown that the rigidity of the thermoplastic polymers depends on the sizes of the granules of...
-
Crystal growth and properties of a binary intermetallic ZrBi2 compound
PublikacjaSingle crystals of ZrBi2 were grown by a self-flux method. The material adopts TiAs2 structure type with lattice parameters: a = 10.233(4) Å, b = 15.581(2) Å, c = 3.994(5) Å. Crystals of ZrBi2 were studied by means of magnetic susceptiblity, specific heat and resistivity measurements. The compound reveals a metallic-like behavior (RRR = 30). The Sommerfeld coefficient equals γ = 1.59(16) mJ mol-1 K-2 and Debye temperature ΘD =...
-
The electronic characterization of the cubic Laves-phase superconductor CaRh2
PublikacjaWe present the synthesis and experimental characterization of the electronic properties of the cubic Laves phase superconductor CaRh2. Its crystal structure was confirmed by powder X-ray diffraction and its ambient temperature lattice parameter (a = 7.5326(6) Å) is in good agreement with the literature. Magnetization, resistivity and heat-capacity measurements indicate that CaRh2 is a moderate-coupling type-II superconductor (λe-p = 0.89)...
-
A Nonlinear Model of a Mesh Shell
PublikacjaFor a certain class of elastic lattice shells experiencing finite deformations, a continual model using the equations of the so-called six-parameter shell theory has been proposed. Within this model, the kinematics of the shell is described using six kinematically independent scalar degrees of freedom — the field of displacements and turns, as in the case of the Cosserat continuum, which gives reason to call the model under consideration...
-
Nonlinear strain gradient and micromorphic one-dimensional elastic continua: Comparison through strong ellipticity conditions
PublikacjaWe discuss the strong ellipticity (SE) conditions for strain gradient and micromorphic continua considering them as an enhancement of a simple nonlinearly elastic material called in the following primary material. Recently both models are widely used for description of material behavior of beam-lattice metamaterials which may possess various types of material instabilities. We analyze how a possible loss of SE results in the behavior...
-
9-(Trichloroacetylimino)acridine monohydrate
PublikacjaThe title compound, alternatively called N-acridin-9(10H)-ylidene-2,2,2-trichloroacetamide monohydrate, C15H9Cl3N2O·H2O, crystallizes in space group P21/c with Z = 4. The acridine moieties are arranged in layers, tilted at an angle of 15.20 (4)° relative to the ac plane, while adjacent molecules pack in a head-to-tail manner. Acridine and water molecules form columns along the b axis held in place by a network of hydrogen...
-
Superconductivity and ferromagnetism in Pd doped Y9Co7
PublikacjaThe ferromagnetic superconductor Y9Co7 was chemically doped to yield the solid solution Y9Co7-xPdx for 0 < x < 0.4. The lattice parameter a does not depend on x, whereas c increases with increasing Pd content up to x ¼ 0.2, the palladium solubility limit. The transition from ferromagnetism (TC ¼ 4.25 K) to superconductivity (Tsc ¼ 2.4 K) was observed only for the parent Y9Co7 compound. For the lowest tested Pd doping level (x ¼...
-
Synthesis, structure and physical properties of new intermetallic spin glass-like compounds RE2PdGe3 (RE = Tb and Dy)
PublikacjaNew intermetallic compounds Tb2Pd1.25Ge2.75 and Dy2Pd1.25Ge2.75 have been synthesized using the arc-melting method. The crystallographic structure and magnetic, electronic transport, and thermal properties are reported. The crystal structure obtained from powder x-ray diffraction analysis suggests that these compounds crystallize in the AlB2-type structure (space group P6/mmm, no. 191) with lattice parameters a = 4.228 53(5)/4.230 54...
-
Potential Skyrmion Host Fe(IO3)3: Connecting Stereoactive Lone-Pair Electron Effects to the Dzyaloshinskii-Moriya Interaction
PublikacjaMagnetic skyrmions, which are topologically distinct magnetic spin textures, are gaining increased attention for their unique physical properties and potential applications in spintronic devices. Here we present a design strategy for skyrmion host candidates based on combinations of magnetic spin, asymmetric building units having stereoactive lone-pair electrons, and polar lattice symmetry. To demonstrate the viability of the proposed...
-
Photocatalytic activity of nitrogen doped TiO2 nanotubes prepared by anodic oxidation: The effect of applied voltage, anodization time and amount of nitrogen dopant
PublikacjaNitrogen doped TiO2 nanotube arrays were prepared by anodizing Ti foils in an organic electrolyte containing specified amounts of urea as nitrogen precursor. The photocatalytic activity of the samples was evaluated by analyzing the degradation kinetics of phenol in water. The influence of tubes’ length, tubes’ surface morphology and amount of nitrogen in the TiO2 lattice on hydroxyl radical formation efficiency, photocatalytic...
-
Crystal structure and physical properties of a novel ternary compound La15MoxGe9
PublikacjaWe present the synthesis, structural characterization and physical properties measurements of a new compound, La15MoxGe9 in Mn5Si3-type derived structure with interstitial Mo. The sample was synthesized by arc-melting method. La15MoxGe9 crystallizes in non-centrosymmetric hexagonal structure P63mc (#186) with lattice parameters a = b = 15.495(5) Å and c = 6.917(2) Å. The refinement on single X-ray diffraction data show that interstitial...
-
Intermetallic disordered magnet Gd2Pt1.1Ge2.9 and its relation to other AlB2 -type compounds
PublikacjaThe intermetallic germanide Gd 2 Pt 1.1 Ge 2.9 was synthesized using an arc-melting method. The crystal structure was characterized using powder x-ray diffraction, revealing a disordered ternary AlB 2 -type structure (space group P 6 / m m m , No. 191) with lattice parameters a = 4.2092 ( 1 ) Å and c = 4.0546 ( 2 ) Å . Physical properties were investigated by magnetic susceptibility and heat capacity measurements, which...
-
CeIr3: superconductivity in a phase based on tetragonally close packed clusters
PublikacjaWe present the crystallographic analysis, superconducting and spectroscopic characterization, and theoretical modeling of CeIr3. Lattice parameters a = 5.2945(1) Å and c = 26.219(1) Å are found for the R-3m symmetry crystal structure, which are close to the literature values. CeIr3 is a moderate type-II superconductor (κ GL = 17, λ e–p = 0.65) below 2.5 K. Ce ions exhibit a strongly intermediate valence character as evidenced by...
-
Stripe order and magnetic anisotropy in the S=1 antiferromagnet BaMoP2O8
PublikacjaMagnetic behavior of yavapaiite-type BaMoP2O8 with the spatially anisotropic triangular arrangement of the S=1Mo4+ ions is explored using thermodynamic measurements, neutron diffraction, and density-functional band-structure calculations. A broad maximum in the magnetic susceptibility around 46 K is followed by the stripe antiferromagnetic order with the propagation vector k=(12,12,12) formed below TN≃21 K. This stripe phase is...
-
Study of Integer Spin S = 1 in the Polar Magnet β-Ni(IO3)2
PublikacjaPolar magnetic materials exhibiting appreciable asymmetric exchange interactions can potentially host new topological states of matter such as vortex-like spin textures; however, realizations have been mostly limited to half-integer spins due to rare numbers of integer spin systems with broken spatial inversion lattice symmetries. Here, we studied the structure and magnetic properties of the S = 1 integer spin polar magnet β-Ni(IO3)2...
-
Crystal structure and physical properties of new Ca2TGe3 (T = Pd and Pt) germanides
PublikacjaThe crystallographic, electronic transport and thermal properties of Ca2PdGe3 and Ca2PtGe3 are reported. The compounds crystalize in an ordered variant of the AlB2 crystal structure, in space group P6/mmm, with the lattice parameters a = 8.4876(4) Å/8.4503(5) Å and c = 4.1911(3) Å/4.2302(3) Å for Ca2PdGe3 and Ca2PtGe3, respectively. The resistivity data exhibit metallic behavior with residual-resistivity-ratios (RRR) of 13 for...
-
La 15 Nb x Ge 9 : a superstructure of the Mn 5 Si 3 structure type with interstitial Nb atoms
PublikacjaThe crystal structure and elementary properties of La15NbxGe9 are reported. Single-crystal X-ray diffraction,from a crystallite with only 0.12 Nb/formula unit, reveals that this compound, although transition metal deficient, crystallizes in a hexagonal “15-1-9”-like structure type, space group P63mc (no. 186) with lattice parameters a = b = 15.5017(2) Å, c = 6.9173(2) Å. The physical properties were examined by specific heat and resistivity...
-
Transparent thin films of Cu-TiO2 with visible light photocatalytic acitivity
PublikacjaThin films of Cu–TiO2 with a high level of transparency were prepared by a dip-coating procedure on the glass surface. CuCl2 was used as a copper precursor added during sol – gel synthesis of TiO2. The extension of optical absorption into the visible region of as-prepared thin films was indicated by UV/Vis spectroscopy. Only the anatase phase was detected by X-ray di ffraction analysis (XRD). The presence of copper in the structure...
-
Charge density wave and large nonsaturating magnetoresistance in YNiC2 and LuNiC2
PublikacjaWe report a study of physical properties of two quasi-low-dimensional metals YNiC2 and LuNiC2 including the investigation of transport, magnetotransport, galvanomagnetic, and specific heat properties. In YNiC2 we reveal two subsequent transitions associated with the formation of weakly coupled charge density wave at TCDW=318K and its locking in with the lattice at T1=275K. These characteristic temperatures follow the previously...
-
Effects of V2O5 Additive on Structure and Dielectric Properties of BiNbO4 Ceramics
PublikacjaGoal of the present research was to investigate the influence of V2O5 additive on the structure and dielectric properties of BiNbO4 ceramics. To fabricate BiNbO4 ceramics with V2O5 added the solid state reaction route and pressureless sintering was utilized. Thus obtained ceramics was characterized in terms of its microstructure (SEM), chemical composition (EDS), phase composition and crystalline structure (X-ray phase and structural...
-
Large Hall and Nernst responses from thermally induced spin chirality in a spin-trimer ferromagnet
PublikacjaThe long-range order of noncoplanar magnetic textures with scalar spin chirality (SSC) can couple to conduction electrons to produce an additional (termed geometrical or topological) Hall effect. One such example is the Hall effect in the skyrmion lattice state with quantized SSC. An alternative route to attain a finite SSC is via the spin canting caused by thermal fluctuations in the vicinity of the ferromagnetic ordering transition....
-
Single crystal growth and physical properties of MCo2Al9 (M= Sr, Ba)
PublikacjaSingle crystals of SrCo2Al and BaCo2Al9 were grown using a self-flux method. A LeBail analysis of the powder X-ray diffraction patterns show that both compounds crystallize in a hexagonal (P6/mmm) crystal structure with lattice parameters: a = 7.8995(1) Å, c = 3.9159(1) Å for SrCo2Al9, and a = 7.9162(2) Å, c = 3.9702(1) Å for BaCo2Al9 aluminide. The low temperature analysis of the heat capacity measurements give a Sommerfeld...
-
Crystal Growth, Structure, and Magnetism of the 2D Spin 1/2 Triangular Lattice Material Rb3Yb(PO4)2
PublikacjaThe single-crystal growth, crystal structure, heat capacity, and anisotropic magnetization characterization of Rb3Yb- (PO4)2, a Yb-based triangular lattice material, are presented. Single-crystal X-ray diffraction shows that Rb3Yb(PO4)2 exhibits [Yb(PO4)]∞ layers, with the Yb in an ordered plane of equilateral triangles. One phosphate group oxygen that is not a near neighbor of the magnetic Yb displays positional disorder. The...
-
Local material symmetry group for first- and second-order strain gradient fluids
PublikacjaUsing an unified approach based on the local material symmetry group introduced for general first- and second-order strain gradient elastic media, we analyze the constitutive equations of strain gradient fluids. For the strain gradient medium there exists a strain energy density dependent on first- and higher-order gradients of placement vector, whereas for fluids a strain energy depends on a current mass density and its gradients....
-
9-Cyano-10-methylacridinium hydrogen dinitrate
PublikacjaThe title compound, C15H11N2+·HN2O6−, crystallizes in the monoclinic space group C2/c with four molecules in the unit cell. The planar 9-cyano-10-methylacridinium cations lie on crystallographic twofold axes and are arranged in layers, almost perpendicular to the ac plane, in such a way that neighbouring molecules are positioned in a `head-to-tail' manner. These cations and the hydrogen dinitrate anions are linked through C—H⋯O...
-
The LaPdIn 4 indide and elementary properties of the LaTIn 4 ( T = Ni, Pd, Pt) materials family
PublikacjaThe indium-rich intermetallic compound LaPdIn4 is reported, prepared by arc-melting and annealing at 600 C. Single crystal X-ray diffraction found the material to be orthorhombic, space group Cmcm (No. 63), with lattice parameters a ¼ 4.5462(3) Å, b ¼ 16.9208(10) Å, and c ¼ 7.3100(5) Å. This previously unreported indide is isostructural with LaNiIn4 and LaPtIn4. It is demonstrated that all three compounds in the LaTIn4 (T ¼ Ni,...
-
Superconductivity in the intermetallic compound Zr5Al4
PublikacjaPolycrystalline Zr5Al4 was synthesized using the arc-melting method. Powder X-ray diffraction confirms the previously reported crystal structure of the Ti5Ga4-type P63/mcm with lattice parameters: a = 8.4312(6) A , and c = 5.7752(8) A . Electrical resistivity and low-temperature magnetic susceptibility measurements indicate that Zr5Al4 exhibits superconducting behavior below 2 K. The normalized heat capacity jump at Tc= 1.82 K...
-
Growth, Crystal Structure and Magnetic Characterization of Zn-Stabilized CePtIn4
PublikacjaThe growth and characterization of CePtIn4, stabilized by 10% Zn substitution for In, is reported. The new material is orthorhombic, space group Cmcm (No. 63), with lattice parameters a = 4.51751(4) Å, b = 16.7570(2) Å, and c = 7.36682(8) Å, and the refined crystal composition has 10% of Zn substituted for In, i.e., the crystals are CePt(In0.9Zn0.1)4. Crystals were grown using a self-flux method: only growths containing Zn yielded...
-
New σ-phases in the Nb–X–Ga and Nb–X–Al systems (X = Ru, Rh, Pd, Ir, Pt, and Au)
PublikacjaPreviously unreported σ-phases in the ternary niobium-based systems Nb–X–Ga for X = Ru, Rh, Pd, Ir, Pt, Au, and Nb–X–Al for X = Ir, and Pt are presented, prepared by arc-melting followed by annealing at 1000 °C for 1 week. The phases are primitive tetragonal (P42/mnm, no. 136) with lattice parameters of a = 9.8336(2)–9.9432(1) Å and c = 5.1098(1)–5.1718(1) Å. Refinements of the single crystal X-ray diffraction data for the Ru and...
-
Superconductivity in CaBi2
PublikacjaSuperconductivity is observed with critical temperature Tc = 2.0 K in self-flux-grown single crystals of CaBi2. This material adopts the ZrSi2 structure type with lattice parameters a = 4.696(1) Å, b = 17.081(2) Å and c = 4.611(1) Å. The crystals of CaBi2 were studied by means of magnetic susceptibility, specific heat and electrical resistivity measurements. The heat capacity jump at Tc is DC/gTc = 1.41, confirming bulk superconductivity;...
-
Cu-Doped Layered Double Hydroxide Constructs the Performance-Enhanced Supercapacitor Via Band Gap Reduction and Defect Triggering
PublikacjaLayered double hydroxides (LDHs) are regarded as the excellent electrode materials for supercapacitors because of their high theoretical capacitance and abundance. However, the poor conductivity and limited reaction kinetics of LDHs restrict their practical application severely. Herein, Cu is chosen from groups VIII/IB/IIB as dopants for Co-based LDH (CuCo-LDH). The designed metal–organic framework-derived hierarchical CuCo-LDH...
-
Structure and paramagnetism in weakly correlated Y8Co5
PublikacjaWe report the basic physical properties of monoclinic Y8Co5 determined by means of magnetic susceptibility, electrical resistivity, and specific heat measurements. The crystal structure of Y8Co5 is monoclinic (P21/c) with lattice parameters a = 7.0582(6) Å, b = 7.2894(6) Å, c = 24.2234(19) Å, and β = 102.112(6)° as refined by using synchrotron powder x-ray diffraction data. The compound shows temperature independent paramagnetism...
-
Structure and hyperfine interactions in Bi1−xNdxFeO3 solid solutions prepared by solid-state sintering
PublikacjaThe series of polycrystalline ceramic powders, Bi1xNdxFeO3 (x = 0.11) was successfully synthesized by mixed oxide method followed by pressureless sintering. X-ray diffraction and Mössbauer spectroscopy were used as complementary methods to study structure and hyperfine interactions of the samples. It was found that with an increase of Nd content, within the range of x = 0.20.3 a structural phase transition from rhombohedral to...
-
Effect of nitrogen doping on TiOxNy thin film formation at reactive high-power pulsed magnetron sputtering
PublikacjaThe paper is focused on a study of formation of TiOxNy thin films prepared by pulsed magnetron sputtering of metallic Ti target. Oxygen and nitrogen were delivered into the discharge in the form of reactive gases O2 and N2. The films were deposited by high-power impulse magnetron sputtering working with discharge repetition frequency f = 250 Hz at low (p = 0.75 Pa) and high (p = 10 Pa) pressure. The substrates were on floating...
-
Structural and electrical properties of Cr-doped SrTiO 3 porous materials
PublikacjaSeries of single-phase materials with assumed formula SrTi1−xCrxO3 (where x = 0, 1, 4, 6 mol.%) were obtained by sol-gel method. The structure and microstructure of materials were characterised by X-ray diffraction and scanning electron microscopy methods. Moreover, the study of electrical properties and evaluation of chemical stability in CO2/H2O atmosphere was performed by electrochemical impedance spectroscopy and thermogravimery...
-
Pressure effects on the electronic structure and superconductivity of (TaNb)0.67(HfZrTi)0.33 high entropy alloy
PublikacjaEffects of pressure on the electronic structure, electron-phonon interaction, and superconductivity of the high entropy alloy ( TaNb ) 0.67 ( HfZrTi ) 0.33 are studied in the pressure range 0–100 GPa. The electronic structure is calculated using the Korringa-Kohn-Rostoker method with the coherent potential approximation. Effects of pressure on the lattice dynamics are simulated using the Debye-Grüneisen model and the Grüneisen...
-
Stable nanoconjugates of transferrin with alloyed quaternary nanocrystals Ag–In–Zn–S as a biological entity for tumor recognition
PublikacjaOne way to limit the negative effects of anti-tumor drugs on healthy cells is targeted therapy employing functionalized drug carriers. Here we present a biocompatible and stable nanoconjugate of transferrin anchored to Ag-In-Zn-S quantum dots modified with 11-mercaptoundecanoic acid (Tf-QD) as a drug carrier versus typical anticancer drug, doxorubicin. Detailed investigations of Tf-QD nanoconjugates without and with doxorubicin...
-
Ferromagnetism in Pr-rich binary Pr7Ru3 intermetallic compound
PublikacjaWe present the synthesis and experimental characterization of the binary intermetallic compound Pr7Ru3. The polycrystalline sample was prepared by arc melting pure Pr and Ru, followed by homogenization at 500 °C and 600 °C for 48 and 89 h, respectively. Powder x-ray diffraction confirms that Pr7Ru3 crystallizes in an orthorhombic crystal structure (Pnma, space group no. 62) with the lattice parameters: a = 7.3606(7) Å, b = 23.120(1)...
-
Sano-Tachiya-Noolandi-Hong, Onsager and Braun models vs Monte Carlo simulation of charge photogeneration in organic solids
PublikacjaThe Sano-Tachiya-Noolandi-Hong (STNH), Onsager, and Braun models as well as Monte Carlo (MC) simulations of charge recombination/separation have been applied for the first time to reproduce the results of the electromodulated photoluminescence measurements in vacuum-evaporated films of fluorescent materials commonly used in optoelectronic devices. The values of the electron-hole pair final recombination speed in the monomer emitters:...
-
Pressure effects on the superconductivity of the HfPd2Al Heusler compound: Experimental and theoretical study
PublikacjaPolycrystalline HfPd2Al has been synthesized using the arc-melting method and studied under ambient-pressure conditions by x-ray diffraction from room temperature up to 450 °C. High-pressure x-ray diffraction up to 23 GPa was also performed using Diacell-type membrane diamond anvil cells. The estimated linear thermal expansion coefficient was found to be α=1.40(3)×10−5K−1, and the bulk modulus derived from the fit to the third-order...
-
Synthesis and physical properties of the 10.6 K ferromagnet NdIr3
PublikacjaThe magnetic, transport, and thermodynamic properties of NdIr3 are reported. Its PuNi3-type crystal structure (space group R−3m), with lattice parameters a= 5.3262(1)Å and c=26.2218(3)Å, was confirmed by powder x-ray diffraction. Our measurements indicate that NdIr3 exhibits a previously unreported paramagnetic to ferromagnetic phase transition below TC=10.6 K(determined by using the Arrott plot). The magnetic susceptibility obeys...