Microcrack monitoring and fracture evolution of polyolefin and steel fibre concrete beams using integrated acoustic emission and digital image correlation techniques
PublikacjaThe use of polymer and steel fibres in plain concrete appears to be an excellent solution for limiting crack propagation and improving the post-ductility performance of concrete structures. Based on this premise, this study investigated the fracture evolution of polyolefin fibre-reinforced concrete (PFRC) and steel fibre-reinforced concrete (SFRC) specimens through the integrated application of two diagnostic techniques, acoustic...
-
The experimental and numerical investigation of fracture behaviour in PMMA notched specimens under biaxial loading conditions – Tension with torsion
PublikacjaThis paper presents the results of experimental fracture test of flat PMMA specimens under biaxial loading condition tension with torsion (proportional). The specimens were made in two thicknesses: 5 and 15 mm and were weakened with V-type edge notches with different root radii: 0.5; 2 and 10 mm. Thanks to the ARAMIS 3D 4 M non-contact vision system, measurement of the elongation and twist angle were recorded. During experimental...
-
Effect of adhesive compliance in the assessment of soft adhesives with the wedge test
PublikacjaWedge tests are usually analysed assuming that the free, unbonded members may be treated as encastré cantilever beams. However, if the adhesive layer is sufficiently flexible (e.g., due to low elastic modulus), then significant strain in the bonded region may occur and lead to modification of the behaviour outside this region. Using in conjunction a sensitive strain gauge method on asymmetric wedge tests and a mathematical analysis...
-
Impact damage in SiO2 nanoparticle enhanced epoxy – Carbon fibre composites
PublikacjaLow velocity impact behaviour of nano-SiO2 enhanced carbon fibre/epoxy composites for naval applications is reported. Epoxy resin matrix was enhanced by 1- 8 wt% SiO2 nanoparticles, based on industrial surface-modified nanosilica. Impact parameters: force, deformation, energy, damage size were recorded. The most pronounced effect was damage size decrease; e.g. ∼28% recorded by infrared thermography and X-ray computed radiography...
-
Monte Carlo simulations of the fracture resistance of an asphalt pavement layer
PublikacjaThe purpose of the proposed numerical model is to analyze the cracking of the wearing course in a pavement overlay, assuming a pre-existing crack that passes through the binding layer and base. The computations employed the author's simulation-based Monte Carlo material model, which describes the failure process of a Semi-Circular Bend (SCB) specimen during standard laboratory testing of asphalt concrete. A key feature of this...
-
Vibration-Based Investigation of a Historic Bell Tower to Understand the Occurrence of Damage
PublikacjaABSTRACT The paper presents a survey of the historic Arch-cathedral bell tower in Vilnius induced by the appearance of cracks in the structure after a new bell system installation. An attempt is undertaken to identify the reason for the crack occurrence and to check a possible crack influence on global structural behaviour. The research is based on dynamic measurements made in the tower during ambient vibrations and during vibrations...
-
Numerical investigations of discrete crack propagation in Montevideo splitting test using cohesive elements and real concrete micro-structure
PublikacjaThe paper is aimed at accurately predicting the discrete fracture process in concrete specimens under complex stress states in two dimensional (2D) simulations. Plain concrete specimens subjected to Montevideo splitting test (MVD) were used for consideration due to non-negligible shear stresses impact in this type of test. In order to reflect the heterogeneous nature of the concrete, the meso-structure of the samples was included...
-
Designate CTOD of Weld Metal of butt weld, No WOiO/II/108/2013
PublikacjaTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability...
-
CTOD designation for WM and HAZ in butt joint made from S460 ML steel, Expertise No. WOiO/II/82/2015
PublikacjaTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability to...
-
Designate CTOD Heat Affected Zone of butt weld, Report No: WOiO/II/76/2013
PublikacjaTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability...
-
Designate of CTOD for WM and HAZ, report no: WOiO/II/122/2014
PublikacjaTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability to...
-
Just look at to open it up: A biometric verification facility for password autofill to protect electronic documents
PublikacjaElectronic documents constitute specific units of information, and protecting them against unauthorized access is a challenging task. This is because a password protected document may be stolen from its host computer or intercepted while on transfer and exposed to unlimited offline attacks. The key issue is, therefore, making document passwords hard to crack. We propose to augment a common text password authentication interface...
-
Applying molecular dynamics simulation to take the fracture fingerprint of polycrystalline SiC nanosheets
PublikacjaGraphene-like nanosheets are the key elements of advanced materials and systems. The mechanical behavior of the structurally perfect 2D nanostructures is well documented, but that of polycrystalline ones is less understood. Herein, we applied molecular dynamics simulation (MDS) to take the fracture fingerprint of polycrystalline SiC nanosheets (PSiCNS), where monocrystalline SiC nanosheets (MSiCNS) was the reference nanosheet....
-
Assessment of unusual failure in crankshaft of heavy-duty truck engine
PublikacjaThe unusual premature failure of a heavy-duty truck engine crankshaft has been the subject of a rigorous study, and this manuscript describes it in detail. The failure was happened to begin with the growth of the crack from the surface defects, in the form of the clusters of non-metallic inclusions, in the lubrication hole zone of the first main journal, which was the stress concentration zone. A series of experiments including...
-
Size effect at aggregate level in microCT scans and DEM simulation – Splitting tensile test of concrete
PublikacjaThe paper describes an experimental and numerical study of size effect on concrete cylindrical specimens in splitting tensile test. Own experimental campaign was performed on specimens with 5 various diameters from D = 74, 105, 150, 192 and 250 mm with hardboard loading strips (distributed load according to standard methods) scaled proportionally to the specimen diameter. The crack opening-control system was applied to obtain the...
-
A coupled constitutive model for fracture in plain concrete based on continuum theory with non-local softening and eXtended Finite Element Method
PublikacjaThe paper presents a constitutive model for concrete which combines a continuous and discontinuous fracture description. In a continuum regime, two different constitutive laws were used. First, a plasticity model with a Rankine failure criterion and an associated fl ow rule was used. Second, a constitutive law based on isotropic damage mechanics was formulated. In order to capture the width of a localized zone and to obtain mesh-independent...
-
Experimental tests of reinforced concrete deep-beams
PublikacjaThe paper presents results of experimental research of the reinforced concrete deep beam with a spatial arrangement. Tested structural elements consist of the cantilever deep beam loaded on the height and transverse deep beam with hanging on it another one. The analysis includes crack morphology, effort of steel and load distribution. The article verified effectiveness of two different kind of reinforcement in both tested deep...
-
Comparative study on fracture evolution in steel fibre and bar reinforced concrete beams using acoustic emission and digital image correlation techniques
PublikacjaIn recent decades, the demand for sustainable construction practices has increased, but raw materials such as reinforcing steel remain scarce. Therefore, steel fibres have emerged as a popular and sustainable choice in the construction industry, offering a cost-effective alternative to traditional steel bar reinforcement for both flatwork and elevated structures. The purpose of this study is therefore to compare the performance...
-
Impact response of two-layered grouted aggregate fibrous concretecomposite under falling mass impact
PublikacjaTwo-layered Grouted Aggregates Fibrous Concrete Composite (TGAFCC) is a new category concrete which became popular recently and attracted the attention of researchers globally. Recent studies indicated that TGAFCC has notable improvement in mechanical properties, which has been sufficiently documented. However, the impact behaviour of TGAFCC when combined with Glass Fibre Mesh (GFM) and Textile Fibre Mesh (TFM) is still unexplored....
-
Prediction of fracture toughness in fibre-reinforced concrete, mortar, and rocks using various Machine learning techniques
PublikacjaMachine Learning (ML) method is widely used in engineering applications such as fracture mechanics. In this study, twenty different ML algorithms were employed and compared for the prediction of the fracture toughness and fracture load in modes I, II, and mixed-mode (I-II) of various materials, including fibre-reinforced concrete, cement mortar, sandstone, white travertine, marble, and granite. A set of 401 specimens of “Brazilian...
-
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
PublikacjaIn this study, different fracture surfaces caused by fatigue failure were generated from 18Ni300 steel produced by selective laser melting (SLM). Hollow round bars with a transverse hole were tested under bending-torsion to investigate the crack initiation mechanisms and fatigue life. Next, the post-failure fracture surfaces were examined by optical profilometer and scanning electron microscope. The focus is placed on the relationship...
-
4-Point beam tensile test on a soft adhesive
PublikacjaAn adhesive butt joint with a soft bondline has been studied. A series of experiments was conducted on test pieces constituted of aluminium adherends bonded with a low modulus epoxy adhesive, ScotchWeld™ 2216. The joint was subjected to four point bending, in tension/compression loading, under constant deflection rate, with the bondline being parallel to the applied load. The objective was to examine and evaluate crack nucleation...
-
Dynamic fracture of brittle shells in a space-time adaptive isogeometric phase field framework
PublikacjaPhase field models for fracture prediction gained popularity as the formulation does not require the specification of ad-hoc criteria and no discontinuities are inserted in the body. This work focuses on dynamic crack evolution of brittle shell structures considering large deformations. The energy contributions from in-plane and out-of-plane deformations are separately split into tensile and compressive components and the resulting...
-
OPTICAL STRAIN MEASUREMENT OF CONCRETE VERSUS MANUAL EXTENSOMETER MEASUREMENT BASED ON THE TEST RC DEEP BEAM IN A COMPLEX STATE OF STRESS
PublikacjaThe purpose of this study is to compare the strain measurement techniques of concrete in R-C element subjected to the monotonic load up to the failure. In the analysis manual extensometer methods of measurements and the optical system ARAMIS for non-contact three-dimensional measurements of deformation was used. The test sample was a cantilever deep beam loaded throughout the depth which was a part of the reinforced concrete deep...
-
Detection of defects in PMMA beam using shear waves - numerical simulation and experiment
PublikacjaTest doświadczalny falami sprężystymi jest częścią systemu diagnostycznego belek. Autorzy badają pole przyspieszeń wywołane przepływem fal ultradźwiękowych i jego modyfikacje wynikające z wprowadzonych uszkodzeń belki. Artykuł porównuje wyniki eksperymentalne z symulacjami numerycznymi MES. The experimental test introduced in the paper is the part of the diagnostic system utilizing the elastic waves. The authors investigate the...
-
On the use of uniaxial one-parameter damage laws for estimating fatigue life under multiaxial loading
PublikacjaThe goal of this paper is to evaluate the capabilities of different one-parameter fatigue laws to estimate crack initiation in notched components under multiaxial loading. Fatigue damage is accounted for through stress-based, strain-based, and energy-based approaches while the cyclic plasticity at the notch-controlled process zone is estimated using linear-elastic simulations. The results show that energy-based formulations established...
-
The fracture behaviour of notched PMMA specimens under simple loading conditions – Tension and torsion experimental tests
PublikacjaThis paper presents the results of experimental testing of flat PMMA specimens during uniaxial loading conditions. Two separate tests were conducted: tensile and torsion. The specimens were weakened with V-type edge notches with different root radii: 0.5; 2 and 10 mm. The specimens were made in two thickness variants: 5 and 15 mm. Monotonic tensile and torsion tests were carried out while keeping the averaged strain rate constant,...
-
Fatigue of titanium alloy Ti6Al4V with diamond structure obtained by Laser Power Bed Fusion method
PublikacjaThis paper presents the results of fatigue tests conducted on Ti6Al4V titanium alloy with diamond structure obtained by the Laser Power Bed Fusion method. Samples used in tests were printed with porosities: 81%, 73%, 50%, 34% and near-zero porosity. Samples were subjected to cyclic tests with a constant stress amplitude. The number of cycles until sample failure was registered. Obtained fatigue test results made it possible to...
-
Fatigue resistance investigation of the IC engine MB11 bearings, working under conditions of dynamic unidirectional loadings
PublikacjaThe slide bearing material MB11 fatigue resistance has been investigated with the application of SMOK - test stand in which dynamic unidirectional loadings to the test bearing is generated. Slide bearing layer consists of the bronze MB11 ( Cu Pb22 Sn 3 ) sintered to the steel shell. Each of the tested bearing has been subject to the standard 20-hour test, under conditions of the full fluid lubrication. Methodology of the experiments,...
-
Reliable method of assessing fracture properties of asymmetric bonded joints
PublikacjaTwo methods of assessing fracture properties of adhesive joints were studied. Two wedge tests: with continuous deflection and with force measurements were compared. Asymmetric geometry of the bonded joint was considered, i.e. two different plates of aluminium alloys: Al-Cu and Al-Mg, were bonded with epoxy DGEBA adhesive. The analytical model is shown to estimate the values of fracture properties: crack position and critical fracture...
-
Numerical investigations on early indicators of fracture in concrete at meso-scale.
PublikacjaFracture is a major reason of the global failure of concretes. The understanding of fracture is important to ensure the safety of structures and to optimize the material behaviour. In particular an early prediction possibility of fracture in concretes is of major importance. In this paper, concrete fracture under bending was numerically analysed using the Discrete Element Method (DEM). The real mesoscopic structure of a concrete...
-
Determination of Failure Causes of a Steam Turbine Casing
PublikacjaThe paper presents results of research and failure analysis undertaken to determine failure causes of a steam turbine casing. After 130,000 hours of service the crack in a outer shell of the turbine casing was found. The inner shell of the casing was made of cast steel grade G21CrMoV5-7, and the outer shell of grade G20CrMo4-5. Following research were performed in order to determine causes of the casing failure: chemical analysis;...
-
Experimental study of the post tensioned prestressed concrete corbels
PublikacjaThe results of experimental investigation of 6 symmetrical double prestressed corbels of variable shear span to depth ratio and variable location of prestressing bars are presented in the paper. The post ten- sioned corbels were prestressed with Macalloy 1030 bars of 25 mm in diameter. The results of the tests were compared with the cracking and load carrying capacity of corbels reinforced with passive reinforce- ment. As a result...
-
GPR simulations for diagnostics of a reinforced concrete beam
PublikacjaThe most popular technique for modelling of an electromagnetic field, the finite difference time domain (FDTD) method, has recently become a popular technique as an interpretation tool for ground penetrating radar (GPR) measurements. The aim of this study is to detect the size and the position of damage in a reinforced concrete beam using GPR maps. Numerical simulations were carried out using the finite differ-ence time domain...
-
The correlation of fractal dimension to fracture surface slope for fatigue crack initiation analysis under bending-torsion loading in high-strength steels
PublikacjaIn this study, the fractal dimension of fatigue fracture surfaces is investigated in order to find an alternative failure loading indicator. Some of many metrological factors are generalized by reducing the fracture surface structure to one factor and develop an entire fracture surface procedure by analyzing the impact of surface slope and calculation resolution. Three notched geometries are studied under cyclic bending-torsion:...
-
Ultrasound monitoring for evaluation of damage in reinforced concrete
PublikacjaThe paper deals with automated monitoring of damage evolution in concrete elements subjected to three-point bending tests. The monitoring is based on the nonlinear interactions of traveling ultrasonic waves with micro-crack zones inside the concrete specimens and surface-breaking cracks. The developed procedure assumes semi-continuous ultrasonic testing during the element full loading cycle and generation of the power spectral...
-
NONLINEAR VIBRATION ANALYSIS OF BEAM AND PLATE WITH CLOSED CRACK: A REVIEW
PublikacjaThe effect of nonlinearity is high sensitivity in damage detection, especially for closed cracks and delamination. This review illustrates the results of several researchers dealing with nonlinear effects caused by the closure of cracks in the structure, i.e., beam and plate structures. Early detection of damage is an important aspect for the structure and, therefore, continuous progress is being made in developing new and effective...
-
Instrumented End Notched Flexure - Crack propagation and process zonemonitoring. Part I: Modelling and analysis
PublikacjaAnalysis of the three-point bending, End Notched Flexure (ENF), test is presented for exploitation with a new experimental methodology using the backface strain monitoring technique. The model consists oftwo Timoshenko beams joined with a two parameter elastic foundation, to evaluate stress and strain fields in both adherends and the adhesive layer, together with the specimen compliance and energyrelease rate. This model is compared...
-
Experimental investigations of damage evolution in concrete during bending by continuous micro-CT scanning
PublikacjaThe paper describes experimental investigation results of fracture in notched concrete beams under quasi-static three-point bending. To visualize 3D fracture in concrete under bending, an extended X-ray micro-computed tomography system was used, i.e. the tomography system SkyScan 1173 was connected to the loading machine ISTRON 5569. This combined system enabled to shot images of deforming concrete beams during a continuous deformation...
-
Influence of bitumen type on cracking resistance of asphalt mixtures used in pavement overlays
PublikacjaCracking is one of the predominant distresses occurring in flexible pavements, especially in old pavements that were rehabilitated with an asphalt overlay. In such cases asphalt mixtures should be designed to ensure high resistance to reflective cracking because new asphalt layers are exposed to existing cracks of the old pavement. The nature of these cracks can be various (transverse, longitudinal as well as crazy cracking). One...
-
Performance of isotropic constitutive laws in simulating failure mechanisms in scaled RC beams
PublikacjaResults of numerical calculations of reinforced concrete (RC) beams are presented. Based on experimental results on longitudinally reinforced specimens of different sizes and shapes are investigated. Four different continuum constitutive laws with isotropic softening are used: one defined within continuum damage mechanics, an elasto-plastic with the Rankine criterion in tension and the Drucker-Prager criterion in compression, a...
-
The elasto-plastic numerical study of crack initiation in notched PMMA specimens under uniaxial loading conditions – Tension and torsion
PublikacjaThis paper presents the results of FEM numerical calculations aimed at describing the plastic strain and stress fields under critical loading conditions: tensile force or torsional moment. The calculations were carried out with reference to the results of experimental tensile and torsional tests of flat PMMA specimens weakened with V-notches of different root radii: 0.5, 2 and 10 mm. The procedure for conducting nonlinear numerical...
-
The Application of Cluster Analysis in the Assessment of the Weldability of Unalloyed Steels
PublikacjaNon-alloy steels constitute a large group of steels characterised by diversified chemical composition, structural morphology and a wide range of mechanical properties (determining weldability). The paper presents results of multidimensional analyses (based on cluster analysis) of 110 selected unalloyed steel grades. Properties adopted as diagnostic features included the chemical composition, mechanical properties (yield point)...
-
A study on microcrack monitoring in concrete: discrete element method simulations of acoustic emission for non-destructive diagnostics
PublikacjaThe research is focused on the monitoring of fracture evolution in concrete beams under three-point bending using the acoustic emission technique and the discrete element method. The main objective of the study was to numerically and experimentally investigate the mechanism behind the generation of elastic waves during acoustic emission events and their interaction with micro- and macro-cracking in concrete beams under monotonic...
-
Guided waves for monitoring of plate structures with linear cracks of variable length
PublikacjaDamage occurring at the work of plate structures may grow to a considerable size. The joint action – the detection of a defect at the earliest possible stage, the monitoring of its growth and the determination of its critical size in the context of structural reliability allows optimizing the cost of the maintenance and repair of structural elements. Thus the development of monitoring systems for permanent observation of fault...
-
Fractographic-fractal dimension correlation with crack initiation and fatigue life for notched aluminium alloys under bending load
PublikacjaIn this study, fatigue fracture surfaces of aluminium alloy 2017-T4 notched specimens were investigated under cyclic bending to find an alternative failure loading index.. The surface topographies were measured on the entire fracture area with an optical profilometer for different loading conditions. Fatigue crack initiation life Ni and total fatigue life Nf were examined using standard surface topography parameters (such as, root...
-
Two-dimensional simulations of concrete fracture at aggregate level with cohesive elements based on X-ray lCT images
PublikacjaThe paper presents results of two-dimensional meso-scale simulations of fracture in notched concrete beams subjected to three-point bending test. Concrete was assumed as a 4-phase material composed of aggregate grains placed in the cement matrix, interfacial transitional zones (ITZs) and macro-voids. The particle distribution was taken from real concrete beams on the basis of X-ray lCT images. Comprehensive numerical analyses were carried...
-
Static and dynamic concrete calculations: Breakable aggregates in DEM model
PublikacjaThe paper deals with the calculations of a 3-point bending beam under static and dynamic loads. The real microstructure was obtained from laboratory tests using micro-tomography images. The quasi-static results were compared directly with experimental data at both macro and micro levels. Subsequently, higher strain rates were applied to investigate dynamic effects. The study focused on the influence of dynamic loading on the macroscopic...
-
Analysis of an Attenuator Artifact in an Experimental Attack by Gunn–Allison–Abbott Against the Kirchhoff-Law–Johnson-Noise (KLJN) Secure Key Exchange System
PublikacjaA recent paper by Gunn–Allison–Abbott (GAA) [L. J. Gunn et al., Scientific Reports 4 (2014) 6461] argued that the Kirchhoff-law–Johnson-noise (KLJN) secure key exchange system could experience a severe information leak. Here we refute their results and demonstrate that GAA’s arguments ensue from a serious design flaw in their system. Specifically, an attenuator broke the single Kirchhoff-loop into two coupled loops, which is an...
-
Textile reinforced concrete members subjected to tension, bending, and in-plane loads: Experimental study and numerical analyses
PublikacjaTextile reinforced concrete has raised increasing research interest during the last years, mainly due to its potential to be used for freeform shell structures involving complex load situations. Yet, most experimental work has focused on test setups with primarily uniaxial loading. In the current work, such setups are complemented with a novel test setup of deep beams, including in-plane bending and shear. Further, nonlinear finite...