Dane BadawczeThe linear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Linear and nonlinear impedance of iron containing silicate glasses
Dane BadawczeThe linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to...
-
Hydrogen evolution reaction catalyzed by Co-based metal-organic frameworks and their derivatives
PublikacjaIn this study, Co-bearing Metal-Organic Frameworks (MOFs) are grown via a facile solvothermal process on the surface of two kinds of conductive substrates – titanium dioxide nanotubes (TiO2NT) and fluorine-doped tin oxide (FTO) glass and tested as electrodes in the electrochemical hydrogen evolution reaction (HER). The materials derived from three organic linkers - terephthalic acid (Co-BDC), 2-aminoterephthalic acid (Co-BDCNH2),...
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Dane BadawczeElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Study of oxygen electrode reactions on symmetrical porous SrTi0.30Fe0.70O3-δ electrodes on Ce0.8Gd0.2O1.9 electrolyte at 800 °C–500 °C
PublikacjaIron doped strontium titanates (SrTi1-xFexO3-δ) are an interesting mixed ionic-electronic conductor model used to study basic oxygen reduction/oxidation reactions. In this work, we performed an impedance spectroscopy study on symmetrical porous SrTi0.30Fe0.70O3-δ (STF70) electrodes on a ceriabased electrolyte. The sample was measured in varying oxygen concentration: from 0.3% to 100% in 800 °C - 500 °C temperature range. Low polarisation...
-
Featuring Semitransparent p–i–n Perovskite Solar Cells for High-Efficiency Four-Terminal/Silicon Tandem Solar Cells
PublikacjaTwo issues need to be resolved when fabricating p–i–n semitransparent perovskite solar cells (ST-PVSCs) for four-terminal (4 T) perovskite/silicon tandem solar cells: 1) damage to the underlying absorber (MAPbI3), electron transporting layer ([6,6]-phenyl-C61-butyric acid methyl ester, PCBM), and work function (WF) modifier (polyethylenimine, PEI), resulting from the harsh sputtering conditions for the transparent electrodes (TEs)...
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Dane BadawczeElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
Correlations of structural, thermal and electrical properties of sodium doped complex borophosphosilicate glass
PublikacjaBorophosphosilicate glasses with varying sodium ion concentrations were investigated for their, structural, thermal, and electrical properties. All the obtained glasses were transparent except the glass with the highest sodium content, which exhibited translucency due to inhomogeneities. Increasing sodium content led to reduced boron and silicon content while maintaining a constant B/Si ratio, indicating progressive depolymerization...
-
AFM investigation of electrode fabricated by 3D printing
Dane Badawcze3D printing, also known as additive manufacturing, has enjoyed great interest in recent years due to the versatility of this method of producing various shapes and details. Due to the possibility of precise control of the shape and composition of the printed elements, the discussed technique can be widely used in electrochemistry, including electrochemical...
-
Photoelectrochemically Active N‐Adsorbing Ultrathin TiO2 Layers for Water‐Splitting Applications Prepared by Pyrolysis of Oleic Acid on Iron Oxide Nanoparticle Surfaces under Nitrogen Environment
PublikacjaHighly performing photocatalytic surfaces are nowadays highly desirable in energy fields, mainly due to their applicability as photo water‐splitting electrodes. One of the current challenges in this field is the production of highly controllable and efficient photoactive surfaces on many substrates. Atomic layer deposition has allowed the deposition of photoactive TiO2 layers over wide range of materials and surfaces. However,...
-
Tailoring Diffusional Fields in Zwitterion/Dopamine Copolymer Electropolymerized at Carbon Nanowalls for Sensitive Recognition of Neurotransmitters
PublikacjaThe importance of neurotransmitter sensing in the diagnosis and treatment of many psychological illnesses and neurodegenerative diseases is non-negotiable. For electrochemical sensors to become widespread and accurate, a long journey must be undertaken for each device, from understanding the materials at the molecular level to real applications in biological fluids. We report a modification of diamondized boron-doped carbon nanowalls...
-
Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses
Dane BadawczeLinear and nonlinear impedance was studied for lead-silicate glass samples doped with iron ions and alkaline oxides. The compositions of glasses were as follows: (in %mol) 50% SiO2, 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O, Li2O. All samples were prepared by the conventional melt quenching technique. The substrates were powdered...
-
Efficiency of pollutants removal from landfill leachates using Nb/BDD and Si/BDD anodic oxidation
PublikacjaLandfill leachates (LLs) is a complex, refectory and difficult to depurate liquid generated from sanitary landfills. It contains excessive levels of biodegradable and in particular non-biodegradable products (e.g. heavy metals, phenols, sulphide, plasticisers). LLs are among the effluents that may pose major environmental concerns, they can be a dangerous source of pollution e.g. due to infiltration into soil and underlying water....
-
Combined effect of nitrogen-doped functional groups and porosity of porous carbons on electrochemical performance of supercapacitors
PublikacjaIn this work, nitrogen-doped porous carbons obtained from chitosan, gelatine, and green algae were investigated in their role as supercapacitor electrodes. The effects of three factors on electrochemical performance have been studied— of the specific surface area, functional groups, and a porous structure. Varying nitrogen contents (from 5.46 to 10.08 wt.%) and specific surface areas (from 532 to 1095 m2g−1) were obtained by modifying...
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
An Aqueous Exfoliation of WO3 as a Route for Counterions Fabrication—Improved Photocatalytic and Capacitive Properties of Polyaniline/WO3Composite
PublikacjaIn this paper, we demonstrate a novel, electrochemical route of polyaniline/tungsten oxide (PANI)/WO3) film preparation. Polyaniline composite film was electrodeposited on the FTO (fluorine-doped tin oxide) substrate from the aqueous electrolyte that contained aniline (monomer) and exfoliated WO3 as a source of counter ions. The chemical nature of WO3 incorporated in the polyaniline matrix was investigated using X-ray photoelectron...
-
Pulsed Laser Deposition of Bismuth Vanadate Thin Films—The Effect of Oxygen Pressure on the Morphology, Composition, and Photoelectrochemical Performance
PublikacjaThin layers of bismuth vanadate were deposited using the pulsed laser deposition technique on commercially available FTO (fluorine-doped tin oxide) substrates. Films were sputtered from a sintered, monoclinic BiVO4 pellet, acting as the target, under various oxygen pressures (from 0.1 to 2 mbar), while the laser beam was perpendicular to the target surface and parallel to the FTO substrate. The oxygen pressure strongly affects...
-
SEM micrographs of 3D printed CB-PLA samples topography after microwave treatment
Dane BadawczeThis dataset contains the electrochemical studies on microwave-activated carbon-black doped polylactic acid 3D printed electrodes.
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-35Nb2O5 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH) and Nb2O5 (≥99.9%, PLUKA AG) were...
-
Hybrid electrode materials for fast performance devices
PublikacjaEnergy storage devices such as Electrochemical Double Layer Capacitors and other types of the electrochemical capacitors require chemically stable, non-soluble, electrochemically active electrode materials compatible with appropriate electrolytes. Factors which determine their applicability are derived from so called electrochemical window of electroltes, nature of charge accumulation and their kinetics. On the other hand technological...
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
Laboratorium Syntezy Innowacyjnych Materiałów i Elementów
LaboratoriaZespół specjalistycznych urządzeń pozwala dokonywać syntezy diamentu mikro- i nanokrystalicznego oraz diamentu domieszkowanego borem i azotem do zastosowań w optoelektronice oraz nanosensoryce. Domieszkowany borem nanodiament (BDD) jest obecnie najwydajniejszym materiałem półprzewodnikowym do zastosowania w wytwarzaniu biosensorów elektrochemicznych. Laboratorium może otrzymywać ciągłe cienkie polikrystaliczne, domieszkowane elektrody...