Wyszukiwarka
Filtry
wszystkich: 24397
wybranych: 614
-
Katalog
- Publikacje 7059 wyników po odfiltrowaniu
- Czasopisma 435 wyników po odfiltrowaniu
- Osoby 241 wyników po odfiltrowaniu
- Wynalazki 32 wyników po odfiltrowaniu
- Projekty 31 wyników po odfiltrowaniu
- Laboratoria 2 wyników po odfiltrowaniu
- Zespoły Badawcze 5 wyników po odfiltrowaniu
- Aparatura Badawcza 2 wyników po odfiltrowaniu
- Kursy Online 1062 wyników po odfiltrowaniu
- Wydarzenia 21 wyników po odfiltrowaniu
- Dane Badawcze 15507 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: MATERIAL GRANULOWANY
-
Probiotic properties of bacterial strains isolated form bee products.
Dane BadawczeThis folder contains information about probiotic properties of bacterial strains isolated from bee products. Additionally information about antibiotic resistance are included.
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials
Dane BadawczeThe ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
X-ray diffraction spectra of nitrogen-doped carbon in hybrid materials containing praseodymium oxide
Dane BadawczeX-ray powder diffraction patterns of samples were carried out by Philips X’Pert diffractometer, which was radiated by graphite monochromatized Cu Kα (l equal 1.540598). The operating voltage was maintained at 40 kV, the current was maintained at 30 mA and analyzed in the range from 20° to 90°. The data presented confirmed the presence of the PrBSCF...
-
Imaging of ferroelectric properties of sinter by means of Piezoresponse Force Microscopy
Dane BadawczeFerroelectricity is a property of certain materials [1], characterized by a spontaneous electrical polarization that can be reversed by applying an external electric field. Ferroelectric properties can be used to make capacitors with adjustable capacity. The permeability of ferroelectrics is not only regulated, but usually also very high, especially...
-
SEM micrographs of boron-doped nanocrystalline diamond-carbon nanospikes
Dane BadawczeThis dataset contains the Scanning Electron Microscopy (SEM) micrographs taken for rich boron-doped carbon crystalline nanospikes/nanograss structures, at different magnifications, encoded in the labels of the images. The micrographs were made using Hitachi S-3400N SEM microscope in secondary electron mode under 20 kV accelerating voltage. No additional...
-
Physicochemical studies (Raman) of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains Raman spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Scanning Electron Microscopy (SEM ) images of PC-X (porous carbon materials obtained at various temperatures)
Dane BadawczeThese data contain SEM (scanning electron microscopy) images of PC-700 (porous carbon materials obtained at 700°C), PC-800 (porous carbon materials obtained at 800°C) and PC-900 (porous carbon materials obtained at 900°C).
-
Nitrogen (N2) adsorption/desorption isotherms of PC-X (porous carbon materials obtained at various temperatures)
Dane BadawczeThese data contain nitrogen (N2) adsorption/desorption isotherms of PC-700 (porous carbon obtained at 700 °C), PC-800 (porous carbon obtained at 800°C), PC-900 (porous carbon materials obtained at 900°C). Data showed typical type-I isotherms, indicating the presence of micropores in their structures. PC-900, compared with PC-700 and PC-800, showed a...
-
X-ray Diffraction (XRD) patterns of PC-X (porous carbon materials obtained at various temperatures)
Dane BadawczeThese data contain X-ray diffraction patterns (XRD) of PC-700 (porous carbon materials obtained at 700°C), PC-800 (porous carbon materials obtained at 800°C) and PC-900 (porous carbon materials obtained at 900°C).
-
A model of stealth maritime object having some innovative solutions concerning the object form, structure and materials.
Dane BadawczeThe aim of the project is to work out a model of the stealth maritime object which will have innovative solutions concerning the object form, structure and materials. These solutions should enable a modification of combinations of the object features defining the object stealth characteristics (difficulty of the object detection in the water). It is...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials synthesized via the solid state reaction method
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
Complex modulus of Cement Bitumen Treated Material Mixture C3E4 laboratory mixed/laboratory compacted (7-365 days of curing at 20C)
Dane BadawczeDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Mixture was mixed in laboratory conditions on the basis of materials obtained from...
-
Complex modulus of Cement Bitumen Treated Material Mixture C3E4 field mixed/laboratory compacted (7-365 days of curing at 20C)
Dane BadawczeDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Mixture was mixed in the field conditions and later compacted in laboratory. Mixture...
-
Straightening of ship hull structure made of 316L stainless steel - tensile test of water cooled materia
Dane BadawczeThe AISI 316L type steel belongs to the group of chromium-nickel stainless steels. They are determined according to European standards as X2CrNiMo17-12-2 and belong to the group of austenitic stainless steels. Steels of this group are used for elements working in seawater environments, for installations in the chemical, paper, and food, industries,...
-
Broadband dielectric spectroscopy studies of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains broadband dielectric spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different...
-
Topography studies of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains topography studies with scanning electron microscope of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material...
-
Electrochemical analyses of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains cyclic voltammetry studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Thermal analyses of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains thermal analyses (TGA, DTG, DSC) studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different...
-
Rheology studies of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains MFR/MVR (melt flow rate) rheology studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The study aims to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
The scanning electron microscopy (SEM) studies of heavy boron-doped diamond oxidation under high-temperature
Dane BadawczeThe dataset contains the results of scanning electron microscopy (SEM) images of heavy boron-doped diamond (BDD) electrodes subjected to high-temperature oxidation in a furnace at 600 Celsius. The micrographs reveal the material decomposition of BDD grains due to high temperature.
-
Inventory of the existing pavement of sidewalks and roads in the Gdańsk-Oliwa district, with particular emphasis on the location of the "Polanki" market and its direct neighbourhood, stage from 2019 year.
Dane BadawczeThe document presents short description and a list of paved surfaces (sidewalks and roads) in the Gdańsk-Oliwa district, in the form of tables with a description of the street and materials used. The description consists of 21 tables: one table for each street. The description is mostly supplemented with photographic material. The area of the inventory...
-
Development of conductive porous media as packing materials for biotrickling filter – microbial fuel cell system (BTF-MFC system)
Dane BadawczeDataset presents values of electrical resistance measured for three developed conductive packimg materials for the application in a BTF-MFC system.
-
The XRD diffraction patterns of as-preapred (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co)
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co) were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
CO2 adsorption isotherms on PCMCA-X (potassium citrate derived porous carbon materials obtained at various temperatures of carbonization)
Dane BadawczeThis dataset contains static CO2 adsorption isotherms on PCMCA-700 (potassium citrate derived porous carbon material obtained at 700 °C), PCMCA-800 (potassium citrate derived porous carbon material obtained at 800 °C), PCMCA -900 (potassium citrate derived porous carbon material obtained at 900 °C) adsorbents.
-
Audit of the existing surfaces /pavements of sidewalks and roads in the Gdańsk-Oliwa district, with particular emphasis on the location of the "Polanki" market and its direct neighbourhood in the contexts of pavement design of the "Polanki"market; stage from 2019 year.
Dane BadawczeThe document presents a valorization of paved surfaces (sidewalks and roads) in the Gdańsk-Oliwa district, prapared on the basis of an preliminary inventory work – 21 tables (one table for each street ) with a description of the street and materials used, mostly supplemented with photographic material. The valorization, after the initial inventory,...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Dane BadawczeThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed in order to force the exsolution process of metallic nanoparticles.
-
The scanning spreading resistance microscopy (SSRM) studies of heavy boron-doped diamond oxidation under high-temperature
Dane BadawczeThe dataset contains the results of scanning spreading resistance microscopy (SSRM) of heavy boron-doped diamond (BDD) electrodes subjected to high-temperature oxidation in a furnace at 600 Celsius. The micrographs reveal the local change of electric properties at certainly crystallographic orientations of BDD grains and at the grain boundaries due...
-
Complex modulus of Cement Bitumen Treated Material Mixture C3E4 cores obtained from the field section (28-365 days of curing at the field and later in laboratory at 20C)
Dane BadawczeDataset presents data of complex modulus determined for cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Specimen were obtained from the field at 28, 180, 270 and 365 days after compaction....
-
Deflection measurement of field section with pavement with base course made of Cement Bitumen Treated Material Mixture C3E4 (28, 180, 270, 365 days after compaction)
Dane BadawczeDataset presents data of deflections determined for pavement with base course made of cold recycled mixture – cement bitumen treated material mixture with following binding agents: 3% cement, 4% emulsion (C3E4). Mixture was designed according to Polish requirements for the base course of pavement. Mixture was mixed in stationary plant and compacted...
-
Tensile curve of E grade steel for shipbuilding
Dane BadawczeIn the shipbuilding industry, the risk of brittle fractures developing in constructions is limited by employing certified materials of specific impact strength, determined using the Charpy method (for a given design temperature) and by exercising control over the welding processes (technology qualification, supervision of production, tests of non-destructive...
-
The luminescence study of LiGa5(1−x)O8:5xCr3+ coumpounds
Dane BadawczeInfrared luminescent materials have evoked much attention from chemists and material scientists. Although substantial progress is made in materials design, the luminescent mechanism remains ambiguous in the complex structures, presenting major barriers to developing novel infrared luminescent materials. Herein, this study aims to deliberate a complete...
-
Thermal properties. DSC analysis of poly(xylitol sebacate-co-butylene sebacate) PXBS.
Dane BadawczeIn this work, a bio-based copolyester with good mechanical properties was synthesized andcharacterized in terms of structure, main properties and biodegradability Determining the chemicalstructure of such materials is important to understand their behavior and properties. Performingan extraction of insoluble cross-linked polymer using di erent solvents...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 900 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1000 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1100 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials after reduction at 900 deg.C in hydrogen
Dane BadawczeThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) powder materials synthesized via the Pechini method after reduction in hydrogen at 900C for 10h.
-
The assessment of microbiological antimicrobial properties of PE film loaded with nanozinc filler
Dane BadawczeThe dataset contains the results of a single series of determinations of the antimicrobial properties against E. coli and S. aureus of polyethylene films containing the nanozinc filler.
-
Fourier transform infrared spectroscopy (FTIR) of pre- PXBS (0 h) and PXBS during the crosslinking process (24 h–288 h)
Dane BadawczeThe goal of this research was developing biodegradable and biocompatibile xylitol-based copolymers with improved mechanical properties, and investigating the change in their thermal and chemical properties withprogress of the cross-linking process. Using a raw material of natural origin such as xylitol, a prepolymer wasobtained by esterification and...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials after reduction at 900 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Dane BadawczeThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed to force the exsolution process of bimetallic nanoparticles.
-
Morphology and conductivity investigations of nickel-molybdenium alloy by means of Scanning Spreading Resistance Microscopy
Dane BadawczeElectrolytically deposited nickel-molybdenum alloys are interesting materials because of their high corrosion resistance and low over-potential for hydrogen evolution. Despite many studies devoted to the deposition of these alloys, the mechanism of co-deposition is not fully understood [1]. The aim of the research was to preserve the electrochemically...
-
Imaging of morphological and physicochemical changes occuring in the structure of austenitic steel due to the thermal sensitization
Dane BadawczeIn polycrystalline materials, grain boundaries are always where phenomena such as surface diffusion, sedimentation and corrosion occur. They have a significant impact on the macroscopic properties of the construction material [1]. In addition to inhomogeneities such as manganese sulphide inclusions formed during the metallurgical process, interfacial...
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_v_2
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_v_3
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_h_3
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 019_v_5
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_h_5
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.
-
3D printed ABS thermoplastic vs. steel. Dry sliding wear test in constant load & velocity ring on flat configuration. Test parameters: print layer thickness and orientation. Test symbol: 009_h_4
Dane BadawczeData gathered in sliding ring-on-block (flat contact) tribological experiment. Materials: alloy steel (heat treated) vs. ABS plastic.