Wyszukiwarka
Filtry
wszystkich: 2775
wybranych: 397
-
Katalog
- Publikacje 2078 wyników po odfiltrowaniu
- Czasopisma 5 wyników po odfiltrowaniu
- Wydawnictwa 1 wyników po odfiltrowaniu
- Osoby 55 wyników po odfiltrowaniu
- Wynalazki 4 wyników po odfiltrowaniu
- Projekty 2 wyników po odfiltrowaniu
- Laboratoria 2 wyników po odfiltrowaniu
- Zespoły Badawcze 3 wyników po odfiltrowaniu
- Kursy Online 174 wyników po odfiltrowaniu
- Wydarzenia 13 wyników po odfiltrowaniu
- Dane Badawcze 438 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: σ-profiles
-
Sigma profiles of DES components
Dane BadawczeThe Sigma profiles for DES components created by the COSMO-RS.
-
Jumping Wave 2D Profiles
Dane BadawczeThe file contains 2D profiles obtained from a jumping wave study in front of the tool during burnishing of 1.0562 steel by the toroidal-cone tool. Burnishing speed 30.5 m/min, feed of burnishing 0.2mm/rev Force 550 and 800 N.
-
The TPR reduction profile of Ce0.9M0.1O2
Dane BadawczeThe dataset includes the TPR reduction profiles of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared by the reverse microemulsion method. After the synthesis powders were dried, then calcined at 500 degrees for 2 h. The measurements were carried out in H2/Ar mixture from 100C to 900C. Gas flow:40ml/min and temperature ramp: 10deg/min.
-
The TPR reduction profile of MCO powder
Dane BadawczeThe dataset includes the TPR reduction profiles of MnCo2O4 (MCO) commercial powder. The dataset includes a cycle of reduction under H2/Ar mixture from 100C to 900C. Gas flow:40ml/min and temperature ramp: 10deg/min. Degassed at 200C in He for 1 h.
-
Depth XPS profile of vanadium pentoxide
Dane BadawczeVanadium pentoxide sample was manufactured by sol-gel method and deposited on a substrate by spin coating technique. To determine depth profile of chemical composition of thin film, etching by Argon ion gun was used. Thin film was etched three times. Chemical composition was measured by XPS method.
-
Depth chemical profile in a CeIr3 sample
Dane BadawczeThe polycrystalline sample of CeIr3 used in the present studies was synthesized by arc-melting cerium (4N) and iridium (3N5) in an arc furnace on a water-cooled copper hearth using a tungsten electrode under a high purity argon atmosphere. A piece of zirconium was used as an oxygen getter. First, a button of Ir was prepared by arc-melting the iridium...
-
TG and DTG profiles for plastics: LDPE, HDPE, PP, PD and PET
Dane BadawczeThe dataset includes:
-
Depth profile of the gold-silver bimetallic structures
Dane BadawczeSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
The profiles and spectrum of aqua solution of tannic acid by HPLC-DAD-MS analysis.
Dane BadawczeThe profiling of tannic acid is determined by examining the content and proportion / ratio of gallotannins [Aras et al. 2016, Clifford et al. 2007, Gauri et al. 2012, Nishizawa et al. 1982]. In order to check the ion mass distribution (TIC) in an aqueous solution of commercial tannic acid, a direct sample injection (TA) was performed into the mass spectrometer....
-
Effect of Jerusalem artichoke addition on texture profile of bread
Dane BadawczeThe dataset contains the results of Jerusalem artichoke addition on the texture of wheat bread. The following bread variants were tested: control bread, bread with 15% and 30% Jerusalem artichoke addition. Measurements were made immediately after baking. On the basis of data, the following parameters were determined: hardness, elasticity, cohesion and...
-
Measurement of the tram rail profile during a year of operation
Dane BadawczeThe aim of the work was to analyze the wear of rails during operation and to analyze the supplementation of heavy metals in the soil around the tram route, originating from wearing out rails and tram wheels.The dataset contains measurements of rail head coordinates in 9 research sections made in 8 measurement series. The wear of the rails in selected...
-
Depth profile of the chemical composition of the Au-Ag multilayers
Dane BadawczeSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
The TPO oxidation profile of CeO2/10wt.%Co with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Mn with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Ni with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Cu with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Fe with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Fe. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Cu without BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Mn without BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Co without BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPO oxidation profile of CeO2/10wt.%Ni without BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
Depth XPS profile of Fe-S layers on a titanium substrate
Dane BadawczeDepth XPS profile of Fe-S layers on a titanium substrate was measured. Material was etched by Argon ion gun and measured by XPS method. For each sample, three times per 10 minutes each was sputtered.
-
Depth profile of the composition of 8 nm Al2O3 thin film
Dane Badawcze8 nm layer of aluminum oxide (Al2O3) was deposited by ALD method on a s. Atomic layer deposition provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. To investigate the profile of concenration of...
-
Measurement of the tram rail profile during a year of operation - supplementary data
Dane BadawczeThe aim of the work was to analyze the wear of rails during operation and to analyze the supplementation of heavy metals in the soil around the tram route, originating from wearing out rails and tram wheels.The dataset contains measurements of rail head coordinates in 9 research sections made in 8 measurement series. The wear of the rails in selected...
-
Microbiological analysis of sea water and bottom sediments in Kosakowo – Gdańsk profile
Dane BadawczeThis dataset contains the results of microbiological analysis of sea water and bottom sediments in Kosakowo – Gdańsk profile in 2013 - 2014 . The tested material consisted of water samples (surface water and bottom water) and bottom sediment samples. Water and sediment samples were analysed for the following: number of Enterobacteriaceae genus bacteria,...
-
The TPR reduction profile of CeO2/10wt.%Cu with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Mn with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Co with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Ni with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Fe with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Fe. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Co without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Co. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Ni without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Cu without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The TPR reduction profile of CeO2/10wt.%Mn without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Mn. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
Hydrogen bonding part sigma profile of deep eutectic solvents and pure components
Dane BadawczeThe set includes raw data of hydrogen bonding part sigma profiles of deep eutectic solvents and pure components generated by the ADF COSMO-RS software (SCM, Netherlands).
-
Nonlinear impedance of as-quenched Bi2VO5.5 glass-ceramic was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of as-quenched Bi2VO5.5 glass-ceramic was measured by impedance spectroscopy method.
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic annealed at 423 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic annealed at 423 K was measured by impedance spectroscopy method.
-
Non-linear impedance of V2O5 nanorods obtained at 923K
Dane BadawczeThe DataSet contains the non-linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of vanadate glass-ceramics containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-35Nb2O5 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH) and Nb2O5 (≥99.9%, PLUKA AG) were...
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Nonlinear high temperature impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 glass
Dane BadawczeThe nonlinear high temperature impedance of iron- phosphate glasses doped with niobium oxide was measured. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region
Dane BadawczeNonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 3 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe nonlinear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.