Ag/Pt-modified TiO2 nanoparticles for toluene photooxidation in the gas phase
PublikacjaAg/Pt-modified TiO2nanocomposites were synthesized using the sol–gel method. The effect of metal typeand amount as well as synthesis route on the photocatalytic activity in reaction of toluene removal, usedas a model volatile organic compound, was investigated. Toluene, at the concentration of about 200 ppm,was irradiated over modified TiO2using light-emitting diodes (LEDs, max= 415 nm). The results showedthat toluene could be...
-
Transparent TiO2 nanotubes supporting silver sulfide for photoelectrochemical water splitting
PublikacjaDifferences between photoelectrochemical and electrochemical activity were thoroughly investigated for the oxygen evolution reaction mediated by Ag2S deposited on two types of ordered titania substrates. Titanium dioxide nanotubes were fabricated by anodization of magnetron sputtered Ti films on ITO-coated glass substrates or directly from Ti foil. Further, Ag2S deposition on the nanotubes was carried out using successive ionic...
-
Otrzymywanie i charakterystyka TiO2 modyfikowanego nanocząstkami Au oraz Pd
PublikacjaDitlenek tytanu jest intensywnie badany od wielu lat, ze względu na jego właściwości fotokatalityczne, nietoksyczność oraz niski koszt. Ograniczeniem w zastosowaniu TiO2 jest jego niska wydajność kwantowa konwersji energii słonecznej, ze względu na szybką rekombinację nośników oraz konieczność zastosowania promieniowania UV. TiO2 absorbuje tylko 3-4% promieniowania słonecznego, ponieważ może być wzbudzony tylko promieniowaniem...
-
Effective processes of phenol degradation on Fe3O4–TiO2 nanostructured magnetic photocatalyst
Publikacja -
Activity of TiO2 Photocatalyst Modified with H2WO4 for Degradation of Organic Compounds in Water
Publikacja -
Modification of carbon-coated TiO2 by iron to increase adsorptivity and photoactivity for phenol
Publikacja -
Application of TiO2-mounted activated carbon to the removal of phenol from water
Publikacja -
Preparation of TiO2-nitrogen-doped photocatalyst active under visible light
Publikacja -
Influence of TiO2 structure on its photocatalytic activity towards acetaldehyde decomposition
Publikacja -
The role of adsorption in the photocatalytic decomposition of Orange II on carbon-modified TiO2
Publikacja -
Preparation and characterisation of visible light responsive iodine doped TiO2 electrodes
PublikacjaPraca przedstawia charakterystykę domieszkowanego jodem ditlenku tytanu (I-TiO2) otrzymanego na drodze hydrotermicznej syntezy, gdzie prekursor stanowiły komplesy tytanu (IV) z ligandami zawierającymi atom jodu. Struktura nowego materiału została opisana za pomocą technik XPS, XRD, UV-vis i FT-IR-ATR. Badania te potwierdziły, że otrzymany proszek I-TiO2 ma zmniejszoną przerwę energetyczną. Praca prezentuje również badania elektrochemiczne...
-
Gasochromic effect in nanocrystalline TiO2 thin films doped with Ta and Pd
Publikacjaw pracy zebrano wyniki badań cienkich warstw domieszkowanego tlenku tytanu. w szczególności zaprezentowano zmianę przezroczystości pod wpływem działania par alkoholu etylowego. badane warstwy zostały naniesione na szklane podłoże metodą rozpylania magnetronowego.
-
On stability of iodine doped TiO2 electrodes in pH varied aqueous electrolytes
PublikacjaW pracy przedstaiono charakterystykę elektrochemiczną warstwy domieszkowanego jodem TiO2 na podłożu platynowym. Wyniki badań prowadzone w elektrolitach o różnym pH pozowoliły na określenie właściwości na granicy faz elektroda - elektrolit. Wyznaczono zależność potencjału pasma płaskiego od pH elektrolitu, a charakter otrzymanej funkcji potwirdził stabilność proszku I-TiO2 w kontakcie s roztworem.
-
Properties of nanocrystalline TiO2:V thin films as a transparent semiconducting oxides
Publikacjaw pracy zaprezentowano wyniki badań cienkich warstw tlenku tytanu domieszkowanego wanadem. badany materiał charakteryzowano pod kątem wykorzystania, jako przezroczysty tlenek półprzewodnikowy (tos). warstwy zostały naniesione metodą rozpylania magnetronowego na szklane podłoża.
-
Influence of tb-dopant on water adsorption and wettability of TiO2 thin films
PublikacjaPraca zawiera analizę wpływu domieszki terbu w cienkiej warstwie tlenku tytanu na zwilżalność powierzchni. opisano metodę pomiaru oraz zastosowania warstw hydrofobowych. badania wykazały hydrofilowość warstw. pokazano także wpływ domieszki terbu na zwiększenie densyfikacji struktury tlenku tytanu.
-
Dihydroxyanthraquinones as stable and cost-effective TiO2 photosensitizers for environmental and biomedical applications
Publikacja -
Sulphated TiO2 Reduced by Ammonia and Hydrogen as an Excellent Photocatalyst for Bacteria Inactivation
Publikacja -
Physicochemical Characteristics of Chitosan–TiO2 Biomaterial. 1. Stability and Swelling Properties
Publikacja -
Hybrid carbon-TiO2 spheres: Investigation of structure, morphology and spectroscopic studies
Publikacja -
The Effect of Calcination Temperature on Structure and Photocatalytic Properties of WO3/TiO2 Nanocomposites
PublikacjaSeries ofWO3/TiO2 nanocompositeswere obtained by hydrothermal method followed by calcination in the temperature range from 400∘C to 900∘C. The characteristics of photocatalysts by X-ray diffractometry (XRD), scanning electron microscope (SEM), and diffuse reflectance spectroscopy (DRS) showed that increasing the calcination temperature from 400 to 900∘C resulted in change of photocatalytic activity under UV-Vis light.Moreover,...
-
Transparent thin films of Cu-TiO2 with visible light photocatalytic acitivity
PublikacjaThin films of Cu–TiO2 with a high level of transparency were prepared by a dip-coating procedure on the glass surface. CuCl2 was used as a copper precursor added during sol – gel synthesis of TiO2. The extension of optical absorption into the visible region of as-prepared thin films was indicated by UV/Vis spectroscopy. Only the anatase phase was detected by X-ray di ffraction analysis (XRD). The presence of copper in the structure...
-
Enhanced photocatalytic properties of lanthanide-TiO2 nanotubes: An experimental and theoretical study
PublikacjaA series of Er-, Yb-, Ho-, Tb-, Gd-, Pr-TiO2 nanotubes (RE-NTs) was prepared via an electrochemical method. The as-prepared photocatalysts were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV–vis absorption, scanning electron microscopy (SEM) and luminescent spectroscopy. The experiments demonstrated that toluene in the gas phase was successfully degraded under visible light (LEDs λmax = 465...
-
Preparation, characterization and photocatalytic activity of TiO2 microspheres decorated by bimetallic nanoparticles
PublikacjaComposite photocatalysts that consist of TiO2and noble metal nanostructures have been considered tobe the promising and pivotal material for accessible enhancement of the efficiency in the photocatalyticprocess carried out in the aqueous and gas phases. In this work we fabricated porous TiO2microspheresthrough a hydrothermal process followed by photochemical reduction of noble metal nanoparticles atthe TiO2surface. The morphology...
-
Resistance noise in tio2-based thin film gas sensors underultraviolet irradiation
PublikacjaBadano możliwości wykorzystania fluktuacji rezystancji w cienkich warstwach TiO2 do wykrywania gazów. Pomiary przeprowadzono, gdy próbka była oświetlona promieniowaniem ultrafioletowym o długości 370nm, w obecności gazu H2S. Stwierdzono, że fluktuacje rezystancji są indukowane promieniowaniem ultrafioletowym i pozwalają na wykrycie obecności H2S w stężeniu do 1.5 ppm.
-
PROTOTYPOWE STANOWISKO LABORATORYJNE DO OCENY WŁASNOŚCI MODYFIKOWANYCH PALIW ŻEGLUGOWYCH W ZAKRESIE ICH WPŁYWU NA WSKAŹNIKI PRACY SILNIKA
PublikacjaOd 2015 roku w Katedrze Siłowni Morskich i Lądowych Wydziału Oceanotechniki i Okrętownictwa Politechniki Gdańskiej realizowane są badania naukowe mające na celu zbudowanie specjalistycznego stanowiska laboratoryjnego, które umożliwi kompleksowe badanie silnika o zapłonie samoczynnym zasilanego różnymi rodzajami pozostałościowych paliw żeglugowym, w tym zasiarczonych i modyfikowanych. Przewiduje się, że w ramach szerokiego programu...
-
Synthesis of linear tuftsin analogues modified at the epsilon-amino group of lysine
PublikacjaZsyntetyzowano na fazie stałej nowe analogi tuftsyny i retro-tuftsyny zawierające wiązanie isopeptydowe na epsilon-aminowej grupie lizyny jako potencjalne immunostymulatory. Do syntezy wykorzystano standardową procedurę Fmoc. Po zdjęciu osłon kwasem TFA końcowe związki były oczyszczane, liofilizowane i charakteryzowane: MS, HPLC i NMR.
-
Influence of Annealing Atmospheres on Photoelectrochemical Activity of TiO2 Nanotubes Modified with AuCu Nanoparticles
PublikacjaIn this article, we studied the annealing process of AuCu layers deposited on TiO2 nanotubes (NTs) conducted in various atmospheres such as air, vacuum, argon, and hydrogen in order to obtain materials active in both visible and UV–vis ranges. The material fabrication route covers the electrochemical anodization of a Ti plate, followed by thin AuCu film magnetron sputtering and further thermal treatment. Scanning electron microscopy...
-
Highly Active TiO2 Microspheres Formation in the Presence of Ethylammonium Nitrate Ionic Liquid
PublikacjaSpherical microparticles of TiO2 were synthesized by the ionic liquid-assisted solvothermal method at different reaction times (3, 6, 12, and 24 h). The properties of the prepared photocatalysts were investigated by means of UV-VIS diffuse-reflectance spectroscopy (DRS), Brunauer–Emmett–Teller (BET) surface area measurements, scanning electron microscopy (SEM), X-ray diffraction analysis (XRD), and X-ray photoelectron spectroscopy...
-
Detoxification of parabens using UV-A enhanced by noble metals—TiO2 supported catalysts
Publikacja -
A tight-binding model of a carbon nanotube interacting with TiO2 rutile (110) surface
Publikacja -
Influence of geometry and annealing temperature in argon atmosphere of TiO2 nanotubes on their electrochemical properties
Publikacja -
Influence of Thermal Modification and Morphology of TiO2 Nanotubes on Their Electrochemical Properties for Biosensors Applications
Publikacja -
Electrochemical stability of TiO2 nanotubes deposited with silver and gold nanoparticles in aqueous environment
Publikacja -
Preparation of TiO2-based catalysts modified with thioacetamide and thiourea for visible light photocatalysis
PublikacjaZa pomocą dwóch różnych metod preparatyki przygotowano aktywne w świetle widzialnym katalizatory tytanowe modyfikowane tioacetamidem i tiomocznikiem. Aktywność fotokatalityczną otrzymanych proszków zbadano w reakcji degradacji fenolu w roztworze wodnym w obecności światła widzialnego. Zbadano wpływ ilości zastosowanej w trakcie syntezy domieszki organicznej na aktywność fotokatalityczną otrzymanych katalizatorów. Wybrane próbki...
-
The effect of nanoparticles size on photocatalytic and antimicrobial properties of Ag-Pt/TiO2 photocatalysts
PublikacjaAg-Pt-modified TiO2 nanocomposites were synthesized using the sol–gel method. Bimetallic modified TiO2 nanoparticles exhibited improved photocatalytic activity under visible-light irradiation, better than monometallic Ag/TiO2 and Pt/TiO2 nanoparticles (NPs). All modified powders showed localized surface plasmon resonance (LSPR) in visible region. The photocatalysts’ characteristics by X-ray diffractometry (XRD), scanning transmission...
-
Preparation and characterization of Pt–N/TiO2 photocatalysts and their efficiency in degradation of recalcitrant chemicals
PublikacjaSeries of Pt–N/TiO2 photocatalysts were synthesized using the sol–gel method. The photocatalysts’ characteristics by X-ray diffractometry (XRD), scanning transmission electron microscopy (STEM), diffuse reflectance spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS) showed that sample with the molar ratio Ti:N equal 1:4 and platinum nanoparticles size of about 3 nm had anatase structure, about 94 m2/g specific surface area...
-
Formation of the hollow nanopillar arrays through the laser-induced transformation of TiO2 nanotubes
PublikacjaIn the following article, we present a simple, two-step method of creating spaced, hollow nanopillars, from the titania nanotube arrays via pulsed laser-treatment. Due to the high ordering of the structure, the prepared material exhibits photonic properties, which has been shown to increase the overall photoefficiency. The optical and morphological changes in the titania nanotubes after pulsed laser-treatment with 532, 355, and...
-
TiO2 and Reducing Gas: Intricate Relationships to Direct Reduction of Iron Oxide Pellets
PublikacjaIn response to the imperative for sustainable iron production with reduced CO2 emissions, this study delves into the intricate role of TiO2 in the direct reduction of iron oxide pellets. The TiO2-dependent reducibility of iron oxide pellets utilizing H2 and CO gas across varied temperatures and gas compositions is thoroughly investigated. Our findings unveil the nuanced nature of the TiO2 effect, underscored by its concentration-dependent...
-
Preparation and Characterization of Defective TiO2. The Effect of the Reaction Environment on Titanium Vacancies Formation
PublikacjaAmong various methods of improving visible light activity of titanium(IV) oxide, the formation of defects and vacancies (both oxygen and titanium) in the crystal structure of TiO2 is an easy and relatively cheap alternative to improve the photocatalytic activity. In the presented work, visible light active defective TiO2 was obtained by the hydrothermal reaction in the presence of three different oxidizing agents: HIO3, H2O2, and...
-
Characterization of TiO2 Modified with Bimetallic Ag/Au Nanoparticles Obtained in Microemulsion System
PublikacjaFotokatalizatory TiO2 modyfikowane nanocząstkami bimetalicznymi Ag/Au przygotowano metodą mikroemulsyjną w układzie woda/surfaktant/cykloheksan. Aktywność fotokatalityczna próbek Ag/Au-TiO2 oszacowano przez wyznaczenie stopnia degradacji fenolu pod wpływem światła VIS. Fenol został użyty jako model zanieczyszczeń, ponieważ jest substancją niebezpieczną dla środowiska. Najwyższą aktywność w zakresie światła widzialnego wykazała...
-
Photosensitization of TiO2 and SnO2 by Artificial Self-Assembling Mimics of the Natural Chlorosomal Bacteriochlorophylls
PublikacjaOf all known photosynthetic organisms, the green sulfur bacteria are able to survive under the lowest illumination conditions due to highly efficient photon management and exciton transport enabled by their special organelles, the chlorosomes, which consist mainly of self-assembled bacteriochlorophyll c, d, or e molecules. A challenging task is to mimic the principle of self-assembling chromophores in artificial light-harvesting...
-
Preparation and photocatalytic activity of boron-modified TiO2 under UV and visible light
PublikacjaOtrzymano TiO2 domieszkowany borem i wyznaczono jego aktywność fotokatalityczną w zakresie światła UV i Vis. Katalizatory otrzymano metodą zol-żel lub poprzez ucieranie dwutlenku tytanu z prekursorami B. Jako źródło boru zastosowano kwas borowy lub ester trietylowy kwasu borowego. Fotoaktywność próbek badano w reakcji degradacji fenolu (Co = 0,21 mmol/dm3 ) w zakresie światła Vis lub UV. Obecność węgla i boru we wszystkich przygotowanych...
-
Photocatalytic water disinfection under the artificial solar light by fructose-modified TiO2
Publikacja -
A preliminary study on antifungal effect of TiO2-based paints in natural indoor light
Publikacja -
Modeling of TiO2-Based Electron-Selective Contacts for Crystalline Silicon Solar Cells
Publikacja -
Influence of TiO2 hydrophilicity on the photocatalytic decomposition of gaseous acetaldehyde in a circulated flow reactor
Publikacja -
Application of carbon-coated TiO2 for decomposition of methylene blue in a photocatalytic membrane reactor
Publikacja -
Gallic Acid-Functionalized, TiO2-Based Nanomaterial—Preparation, Physicochemical and Biological Properties
Publikacja -
TiO2 photoactivity in vis and UV light: The influence of calcination temperature and surface properties
PublikacjaPrzygotowano serię fotokatalizatorów w postaci tlenku tytanu (IV) kalcynowanych w różnych temperaturach od 350 do 750˚C. Charakterystyka fotokatalizatorów za pomocą metod XRD, UV-Vis/DRS, FTIR, XPS, BET oraz BJH wykazała, że próbka TiO2 aktywna w świetle widzialnym posiadała strukturę anatazu, powierzchnię właściwą ok. 200 m2/g, absorbowała światło o długości fali λ>400 nm oraz zawierała 10,1 % at. węgla (wiązanie C-C). Aktywność...
-
Silver-doped TiO2 prepared by microemulsion method: surface properties, bio- and photoactivity
PublikacjaOtrzymane fotokatalizatory typu Ag-TiO2 wykazywały wyższą aktywność w reakcjach fotodegradacji fenolu w obecności promieniowania z zakresu UV oraz światła widzialnego w porównaniu z komercyjnym katalizatorem Degussa P25 oraz czystym niedomieszkowanym TiO2, otrzymanym w mikroemulsji woda-AOT-cykloheksan. Powierzchnia właściwa (BET) otrzymanych katalizatorów wynosiła od 100 do 160 m2/g. Na podstawie analizy rentgenowskiej (XRD) stwierdzono,...