XRD patterns of the V2O5 nanorods after thermal treatment under reducing atmosphere
Open Research DataThe DataSet contains the XRD patterns of V2O5 nanorods after thermal treatment under a reducing atmosphere. Samples were annealed at 450C for 2, 20, and 40h under a reducing atmosphere (94% Ar, 6% H2).
-
XRD patterns of ammonium vanadate nanocrystals
Open Research DataThe DataSet contains the XRD patterns of ammonium vanadate nanobelts obtained by the hydrothermal method with different conditions. The results show that the structure and phase compositions of samples dependent on reaction conditions.
-
XRD patterns of VO2 and V6O13 nanostructures
Open Research DataThe DataSet contains the XRD patterns of VO2 and V6O13 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under a reducing atmosphere (94% Ar, 6% H2) at 500, 600 and 700C for 10h.
-
XRD patterns of V2O5 thin film morphology dependent on substrate types
Open Research DataThe DataSet contains the XRD patterns of the V2O5 thin film structure dependent on substrate types. The as-prepared thin films were deposited on alumina, zirconium, zirconium oxide and metallic vanadium substrate, then was annealing under an oxidizing atmosphere at 600C for 10h.
-
XRD patterns of V2O5 nanostructures
Open Research DataThe DataSet contains the XRD patterns of vanadium pentaoxide nanostructures obtained by the sol-gel with different annealing temperatures under synthetic air. The results show that crystallinity dependent on the annealing temperature.
-
XRD patterns of VO2 and V2O3 nanostructures
Open Research DataThe DataSet contains the XRD patterns of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
XRD patterns of vanadium oxide nanostructures on silicon substrate obtained by V2O5 recrystallization
Open Research DataThe DataSet contains the XRD patterns of vanadium oxide nanostructures on silicon substrates obtained by recrystallization of V2O5 thin films between 800-1200°C under synthetic air. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials.
-
XRD patterns of VO2 and V2O3 thin films obtained at 500°C
Open Research DataThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon atmosphere.
-
XRD patterns of vanadium oxide nanostructures on quartz glass substrate obtained by V2O5 recrystallization
Open Research DataThe DataSet contains the XRD patterns of vanadium oxide nanostructures on quartz glass substrates obtained by recrystallization of V2O5 thin films between 800-1200°C under synthetic air. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials.
-
Chemical composition of V2O5 nanorods
Open Research DataThe DataSet contains the chemical compositions of the V2O5 nanorods on a silicon substrate. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The As-prepared thin films were annealed at 600C under a synthetic air atmosphere.
-
XRD patterns of VO2 and V2O3 thin films obtained at 700°C
Open Research DataThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (5-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon atmosphere.
-
The structure of lead-borate glasses containing nanocrystallites of iron oxides
Open Research DataThe structure of iron-doped glasses and glass-ceramics were studied. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and...
-
The luminescence study of Sr2TiO4:Sm3+ coumpounds.
Open Research DataA luminescent material based on the strontium orthotitanate (Sr2TiO4) matrix doped with 1% of a mole of samarium was obtained using the typical solid-state synthesis method under a neutral atmosphere of nitrogen. The sample was investigated using powder X-ray diffraction (XRD) and several luminescence techniques to study the phase composition, luminescence...
-
The XRD diffraction patterns of Ce(Pr,Sm)O2-s samples
Open Research DataThe dataset includes XRD diffraction patterns of Ce(Pr,Sm)O2-s samples of various stoichiometries of Pr and Sm dopants. Samples were produced using aqueous soft chemistry methods (microemulsion method).
-
XRD patterns of V2O5 thin films deposited on silicon substrate
Open Research DataThe DataSet contains the XRD patterns of V2O5 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range of 300-600C. The results show that the structure of the films dependent on the annealing temperature.
-
XRD patterns of V2O3 nanostructures
Open Research DataThe DataSet contains the XRD patterns of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that crystallinity dependent on the annealing temperature.
-
The structure of lead-silicate glasses containing nanocrystallites of iron oxides
Open Research DataThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
XRD patterns of V2O5 thin films deposited on quartz glass
Open Research DataThe DataSet contains the XRD patterns of V2O5 thin films deposited on a quartz glass substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range 200-600C. The results show that the structure of the films dependent on the annealing temperature.
-
The topography of Bi2VO5.5 ceramic measured with SEM and confocal microscope
Open Research DataThe topography of Bi2VO5.5 ceramics was measured by SEM and confocal microscope.
-
Broadband dielectric spectroscopy studies of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains broadband dielectric spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different...
-
Elemental composition of deposited sediments - Warszawska/Havla tram-route junction (2024 May)
Open Research DataThis data set contains the elemental composition results of deposited sediments collected at the tram-route junction in Gdańsk. Samples collected after fifteen months of operation of tram line.
-
The effect of cobalt addition on the corrosion behavior of near equiatomic NiTi shape memory alloy in normal saline solution, impedance and microscopic studies
Open Research DataThe electrochemical and corrosion (uniform and localized) behavior of a binary Ni52Ti48 shape memory alloy (SMA) and two ternary Ni52Ti48-xCox (x = 1.5 and 4.0 wt.%) SMAs were studied. Measurements were conducted in 0.9% NaCl solution at 37 oC. This dataset contains the results of electrochemical impedance spectroscopy (EIS) studies done on daily basis...
-
XRD patterns of MXenes catalysts
Open Research DataData contain results from XRD measurements of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios....
-
XRD patterns of TeOx powder
Open Research DataThe DataSet contains the XRD patterns of the TeOx powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised to 75°C for the...
-
XRD patterns of V2O5 thin films deposited on isotropic etching silicon substrates (111)
Open Research DataThe DataSet contains the XRD patterns of V2O5 thin films deposited on isotropic etching silicon substrates (111). The silicon wafers were etched in a mixture of nitric acid, hydrofluoric acid, and acetic acid in the ratio of 40:1:15. The soaking time for the substrates was from 30 to 90 seconds. The thin films were obtained by the sol-gel method. ...
-
Morphology and structure of V2O5 nanorods deposited on the silicon substrate after reduction
Open Research DataThe DataSet contains the XRD patterns and SEM micrographs of V2O5 nanorods on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 500C for 40 under a reducing atmosphere (94% Ar, 6% H2).
-
Microstructure of barium-vanadate glasses
Open Research DataThe structure of barium-vanadate glasses was measured by SEM and XRD techniques. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar....
-
The topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with SEM method
Open Research DataThe topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by SEM.
-
The luminescence study of (C10H16N)2MnBr4 Organic–Inorganic Hybrid
Open Research DataOrganic–inorganic hybrid metal halides have recently attracted attention in the global research field for their bright light emission, tunable photoluminescence wavelength, and convenient synthesis method. This study reports the detailed properties of (C10H16N)2MnBr4, which emits bright green light with a high photoluminescence quantum yield. Results...
-
Structure of ammonium vanadate synthesis by LPE-IonEx method
Open Research DataThe DataSet contains the XRD patterns, FTIR spectra of NH4VO3 crystals with different morphology obtained by the LPE-IonEx method.
-
The luminescence study of Bi-doped Cs2AgInCl6 double perovskite.
Open Research DataHere, we report a halide precursor acid precipitation method to synthesize Cs2AgIn1−xBixCl6 (x = 0, 0.02, 0.04, 0.08, 0.16, 0.32, 0.64, and 1) microcrystals. Cs2AgInCl6 and Bi derivative double perovskites show broadband white light emission via self-trapped excitons (STEs) and have achieved the highest internal quantum efficiency of up to 52.4% at...
-
Elemental composition of deposited sediments at the tram-route junction
Open Research DataThis data set contains the elemental composition results of deposited sediments collected at the tram-route junction in Gdańsk. Sample collection began in July 2022, when the tram lines were completed and before the rails were scrubbed (27/07/2022). The second sample round was carried out following rail scrubbing in October 2022 (7/10/2022). Since February...
-
XRD patterns of TeOx-BaO-BiO powder
Open Research DataThe DataSet contains the XRD patterns of the TeOx-BaO-BiO powder. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor), barium carbonate, and bismuth carbonate with thetraetylene glycol, water, ethanol, and acetic acid. (Samples molar concentration: 73TeO2-4BaO-3Bi2O3 and 73TeO2-3BaO-4Bi2O3)....
-
The luminescence study ofNaK2Li[Li3SiO4]4:Ce coumpounds.
Open Research DataPhosphors with a rigid and symmetrical structure are urgently needed. The alkali lithosilicate family (A[Li3SiO4]) has been extensively studied with a narrow emission band due to its unique cuboid-coordinated environment and rigid structure. However, here we demonstrate for the first time Ce-doped NaK2Li[Li3SiO4]4 phosphors with a broad emission band,...
-
The luminescence study of Sc2(1–x)Ga2xO3:Cr3+/4+ coumpounds
Open Research DataThe growing interest in the use of near-infrared (NIR) radiation for spectroscopy, optical communication, and medical applications spanning both NIR-I (700–900 nm) and NIR-II (900–1700 nm) has driven the need for new NIR light sources. NIR phosphor-converted light-emitting diodes (pc-LEDs) are expected to replace traditional lamps mainly due to their...
-
Imaging and chemical investigation of silver coating
Open Research DataThe recovery of silver from materials such as plates, still used in clinical radiography [1], or scrap jewelery is still very popular. The subject of the research, part of which was microscopic imaging, was to recreate the behavior of an electrochemically deposited silver coating. The copper electrodes were covered with a layer of silver obtained from...
-
The topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with SEM method
Open Research DataThe topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by SEM.
-
Unraveling Luminescent Energy Transfer Pathways: Futuristic Approach of Miniature Shortwave Infrared Light-Emitting Diode Design
Open Research DataPhosphor-converted shortwave infrared phosphor light-emitting diodes (pc-SWIR LEDs, 900–1700 nm) are promising next-generation portable light sources for spectroscopy, security, optical communication, and medical applications. A typical design strategy involves energy transfer from Cr3+ to Ni2+, and thus, energy transfer from Cr3+–Cr3+ pairs to Ni2+...
-
Ni-based compounds in multiwalled graphitic shell for electrocatalytic oxygen evolution reactions
Open Research DataThis study investigates Ni-based compounds (Ni, NiO, Ni3C) coated with a graphitic shell as electrocatalysts for the oxygen evolution reaction (OER). Electron paramagnetic resonance (EPR) and X-ray diffraction (XRD) are employed to identify the presence and contribution of Nickel ions (Ni0, Ni2+, Ni3+) and determine the phase composition. Electrochemical...
-
Morphology and structure of ammonium vanadates synthesis by hydrothermal method
Open Research DataThe DataSet contains the XRD patterns, FTIR spectra, and scanning electron microscopy (SEM) micrographs of ammonium vanadates synthesis by hydrothermal method from different NH4VO3 precursors. The results reveal that a mixture of (NH4)V4O10xH2O and(NH4)0.76V4O10 was obtained for both precursors, however the contribution of each phase was different for...
-
The luminescence study of SrAl11.88−xGaxO19:0.12Cr3+ coumpounds.
Open Research DataPortable near-infrared (NIR) light sources are in high demand for applications in spectroscopy, night vision, bioimaging, and many others. Typical phosphor designs feature isolated Cr3+ ion centers, and it is challenging to design broadband NIR phosphors based on Cr3+–Cr3+ pairs. Here, we explore the solid-solution series SrAl11.88–xGaxO19:0.12Cr3+...
-
Thermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with DSC method
Open Research DataThermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by DSC.
-
Selection of material for infiltration of non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ
Open Research DataThe porous electrodes used for the infiltration were prepared from A-site non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ synthesized by the conventional solid state reaction method. Screen printed electrodes (0.5 cm2) on CGO-20 substrate, were fired at 800 °C for 2 hours in an air atmosphere. Infiltration of the scaffolds was performed by a water-based precursor...