Wyszukiwarka
Filtry
wszystkich: 314
wybranych: 80
-
Katalog
Filtry wybranego katalogu
Wyniki wyszukiwania dla: Thin film
-
SEM micrographs of V2O5 thin films deposited on isotropic etching silicon substrates (111)
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 thin films deposited on isotropic etching silicon substrates (111). The silicon wafers were etched in a mixture of nitric acid, hydrofluoric acid, and acetic acid in the ratio of 40:1:15. The soaking time for the substrates was from 30 to 90 seconds. The thin films were...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 700°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 500°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon...
-
XPS data of as-grown BDD, as-implanted Mn-BDD, and annealed Mn-BDD thin films
Dane BadawczeXPS survey spectra and detailed spectra O1, C1s and Mn2p of as-grown BDD, as-implanted Mn-BDD, and annealed Mn-BDD thin films. X-ray photoelectron spectroscopy (XPS) studies were conducted on an Escalab 250 Xi from Thermo Fisher Scientific with an Al Kα radiation. Results were published in the paper ( https://doi.org/10.1002/adfm.202308617)
-
Scanning electron microscopy (SEM) images of boron-doped diamond thin films at poly(lactic acid)
Dane BadawczeThe dataset contains the photos obtained by scanning electron microscope(SEM), revealing the surface morphology and cross-section of boron-doped diamond electrodes on commercially available graphene-doped polylactide acid. The boron doping level expressed as the [B]/[C] ratio in the gas phase for these studies was 500 and 10,000 ppm. The top views of...
-
Structure evolution of V2O5 thin films deposited on silicon substrate - High-Temperature X-ray Diffraction
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 thin films deposited on silicon substrates (111). The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The sol was deposited on the silicon substrate. The structure was measured in-situ during heating between 50-800°C under...
-
Luminescence properties of TeOx-2%Eu1.5%Tb1.5%Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-2%Eu1.5%Tb1.5%Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Luminescence properties of TeOx-2%Eu1.5%Tb1.5%Tm thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-2%Eu1.5%Tb1.5%Tm thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Luminescence properties of TeOx-1%Eu1.5%Tb2.5%Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-1%Eu1.5%Tb2.5%Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Structure evolution of V2O5 thin films deposited on quartz glass substrate - High-Temperature X-ray Diffraction
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 thin films deposited on guartz glass. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The sol was deposited on the quartz glass substrate. The structure was measured in-situ during heating between 50-800°C under synthetic...
-
TEM data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Dane BadawczeThis Dataset include presentation of summarized TEM investigation of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited...
-
SEM/EDX data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Dane BadawczeThis Data set include SEM and EDX results of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited layers were amorphous,...
-
Total electrical conductivity data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Dane BadawczeThis dataset includes electrical conductivity measurements results measured by van der pauw technique up to 900oC.
-
XRD data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe, annealed in a range from 400 to 900oC
Dane BadawczeDataset include collected XRD data of (Cr,Fe,Mn,Co,Ni)3O4 high-entropy spinel oxide thin films deposited by spray pyrolysis technique on amorphous SiO2 substrates and annealed from 400 to 900oC. Samples were prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers...
-
Au nanostructures coated with a ultrathin film of Al2O3 - measurements and FDTD simulations
Dane BadawczeGold plasmonic platforms have been coated with an ultra-thin films of aluminium oxide. Optical measurements, showing the influence of the thickness of Al2O3 on plasmon resonance position. The observed red-shift of the resonance location with the increase of the thickness of the Al2O3 film, can be explained by the change in the dielectric function of...
-
Depth XPS profile of vanadium pentoxide
Dane BadawczeVanadium pentoxide sample was manufactured by sol-gel method and deposited on a substrate by spin coating technique. To determine depth profile of chemical composition of thin film, etching by Argon ion gun was used. Thin film was etched three times. Chemical composition was measured by XPS method.
-
Formation of gold nanostructures detected by XPS method
Dane BadawczeGold nanostructers were manufactured by thermal dewetting of thin film. Film with thickness of 2.8 nm was deposited by magnetron sputtering method. As a result of annealing at 550 deg, nanostructures appear. Bulk gold, as-deposited gold film and metallic nanostructures were measured by XPS method.
-
XRD patterns of the V2O5 coatings after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 coatings on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 500C, 600C, and 700C for 10 under a reducing atmosphere (94% Ar, 6% H2).
-
SEM micrographs of the V2O5 coatings after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 coatings on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 600C and 700C for 10 under a reducing atmosphere (94% Ar, 6% H2).
-
Morphology and structure of V2O5 nanorods deposited on the silicon substrate after reduction
Dane BadawczeThe DataSet contains the XRD patterns and SEM micrographs of V2O5 nanorods on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 500C for 40 under a reducing atmosphere (94% Ar, 6% H2).
-
Dewetting of silver films detected by XPS method
Dane BadawczeDewetting of silver thin films was detected by XPS method. Thin metallic films were deposited by magnetron sputtering method. Formation of nanostructures , as a result of thermal annealing, was confirmed by SEM microscope. For comparision three samples were measured. Bulg gold, as-deposited silver film with thickness of 3 nm and nanostructures.
-
XRD patterns of VO2 and V6O13 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V6O13 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under a reducing atmosphere (94% Ar, 6% H2) at 500, 600 and 700C for 10h.
-
SEM micrographs of VO2 and V6O13 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V6O13 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under a reducing atmosphere (94% Ar, 6% H2) at 600 and 700C for 10h.
-
X-Ray diffraction of the metallic nanostructures
Dane BadawczeMetallic nanostructures (gold and silver) were manufactured as a thermal annealing of gold or silver thin film. Gold films with thickness of 2.8 nm were deposited on a silicon substrates using a table-top dc magnetron sputtering coater (EM SCD 500, Leica), equipped with quartz microbalance for in-situ thickness measurements. Films were deposited from...
-
Investigation of the uniformity of TeO2:Eu layer
Dane BadawczeTeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by XPS method. Te-Eu mosaic target with diameter of 50.8 mm was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the deposition chamber was below 0.2 Pa and substrate was heated at 200 oC during...
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
Temperature of formation of Au nanostructures
Dane BadawczeNanostructures were obtained via annealing of thin Au films. In order to determine possible nanoislands formation mechanisms, dependence on initial film thickness was examined. For the surface morphology studies, nanograin structure and chemical composition analysis, SEM, HR TEM and EDS measurements were performed, respectively. Morphology studies shown...
-
Plasmon resonance in gold-silver nanoalloys
Dane BadawczeSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Anomalous anisotropy of deuterium-grown boron-doped diamond and the role of boron-tetramers in the Mott-Insulator transition
Dane BadawczeWe show anisotropy in the superconductivity for boron-doped diamond thin films prepared with Microwave Plasma Assisted Chemical Vapor Deposition using deuterium-rich plasma. This anomalous phase transition is linked with the emergence of boson quantum entanglement states behaving as a bosonic insulating state. Here, we show that the superconducting...
-
Ferromagnetic nanoparticles imaging by means of Magnetic Force Microscopy
Dane BadawczeFerromagnetic nanoparticles can be used as building blocks for advanced thin film magnets, and can also be used in data storage and biomedical technologies. Nano-crystalline ferrites with the chemical formula NixZn (1 - x) Fe2O4, where x = 0, 0.2, 0.4, 0.6, 0.8, 1.0 show anti-corrosion properties and suppress electromagnetic interference, in the case...