Oxygen partial pressure and temperature dependence of R-CPE1 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE1 frequency of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE1 frequency at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Oxygen partial pressure and temperature dependence of R-CPE2 capacity of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Dane BadawczeThis dataset contains values of equivalent circuit element R-CPE2 capacity at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
Valorization of bio-based polyols synthesized via biomass liquefaction
Dane BadawczeAs the properties of polyols have a huge impact on the properties of manufactured polyurethanes, this study aims to determine the influence of polyethylene glycols with different molecular masses on the course of the biomass liquefaction process and bio-polyol properties. The obtained polyols were characterized by rheological studies. To confirm the...
-
The 2p XPS spectra of transition metals in Ce0.9M0.1O2
Dane BadawczeThe dataset consists of 2p XPS spectra of transition metals in Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons...
-
Physicochemical studies (Raman) of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains Raman spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
SEM image and line EDS of SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C
Dane BadawczeThis dataset contains image of the SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C with line EDS analysis results. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 20 kV in a high vacuum mode. The chemical compositions of the investigated powder...
-
Luminescence of TeO2:Eu thin films
Dane BadawczeTellurium dioxide doped by europium thin films were deposited by magnetron sputtering method and simultaneously heated at 200 oC. Presence of Eu ions and their valence states was confirmed by X-ray photoemission spectroscopy measurements. The structure of the films as well as the influence of europium dopant on crystalline structure of the films was...
-
Chemical and structural studies of screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Dane BadawczeThis dataset contains chemical analyses and structural studies by XPS and Raman spectroscopy, carried out for SPCE containing boron-doped diamond BDD foils done with scanning electron microscope. Different points for XPS analysis mark different electrode spots: A) working electrode, B) reference electrode, C) counter electrode, D) pads.
-
XPS data of MXene catalyst
Dane BadawczeData contain results from XPS measurement of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using 48% HF etching agent (MXene HF). The X-ray spectroscopy (XPS) measurements were conducted using Mg Ka (hn = 1253.6 eV) radiation in a Prevac (Poland) system equipped with a Scienta SES 2002 (Sweden) electron...
-
The XAS spectra of O-K edges, Fe-L edges in pristine, La-, and Nb-doped SFM in 3 states: as-prepared, reduced and reoxidized
Dane BadawczeThis dataset contains the normalized and exported to *.txt spectra for x-ray absorption spectroscopy. The samples analyzed were strontium ferrite molybdate based, doped with lanthanum and niobium. The powders were measured in as-prepared state (denoted in filename as AP), reduced (red) and reoxidized (reox). The filenames are written accordingly: Edge_(optional:...
-
The OpenMolcas Web: A Community-Driven Approach to Advancing Computational Chemistry
Dane BadawczeThe developments of the open-source OpenMolcas chemistry software environment since spring 2020 are described, with a focus on novel functionalities accessible in the stable branch of the package or via interfaces with other packages. These developments span a wide range of topics in computational chemistry and are presented in thematic sections: electronic...
-
SEM image and EDS map of SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C
Dane BadawczeThis dataset contains image of the SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C with EDS map analysis results. This study were performed for better understanding the chemical composition of flat like structures that occurs in electrode. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope...
-
Structure and optical measurements of Eu doped tellurium oxide thin films
Dane BadawczeThin films were deposited by magnetron sputtering method and simultaneously heated at 200 oC. Presence of Eu ions and their valence states was confirmed by X-ray photoemission spectroscopy measurements. The structure of the films as well as the influence of europium dopant on crystalline structure of the films was examined by X-ray diffraction method. ...
-
The XPS spectra of Ce0.8Ni0.2O2 prepared using microemulsion method
Dane BadawczeThe dataset includes XPS spectra of Ce0.8Ni0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
The XPS spectra of Ce0.8Cu0.2O2 prepared using microemulsion method
Dane BadawczeThe dataset includes XPS spectra of Ce0.8Cu0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
Physicochemical studies (Raman, XRD) of poly(lactic acid)-carbon black-nanodiamond composites
Dane BadawczeThis dataset contains physico-chemical examination of a new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques include Raman spectroscopy and X-ray diffraction...
-
The XPS spectra of LSCNT sintered at 1200C
Dane BadawczeThe dataset includes XPS spectra of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini). The XPS spectra were collected for all species.
-
The XPS spectra of Al2O3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of Al2O3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/1%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/1%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of ZrO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of ZrO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of CeO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of CeO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of SrTiO3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of SrTiO3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
Raman spectra of MXenes catalysts
Dane BadawczeData contain results from Raman spectroscopy of the Ti3C2Tx MXenes produced via acidic etching aluminum from MAX Phase (Ti3C2-Al-Ti3C2-Al-Ti3C2) using different etching agents, HF/HCl and HF/H2SO4 with different weight ratios (1:3, 1:4, and 1:5). The samples were labeled as MXene HF/HCl X:Y and MXene HF/H2SO4 X:Y, where X:Y means the acids weight ratios. ...
-
The XPS studies revealing the surface chemistry of Cu-Sn-TiO2 nanocomposite coatings
Dane BadawczeThe dataset contains the X-Ray Photoelectron Spectroscopy (XPS) data of nanocomposite Cu-Sn-TiO2 coatings electrodeposited from oxalic acid bath containing Cu and Sn salts as well as TiO2 nanoparticles under various treatments: mechanical stirring, ultrasonic or none. The details of the electrodeposition process are presented in the descriptor file...
-
The XPS studies of the CB-PLA electrodes after different surface treatments (chemical, electrochemical, enzymatic)
Dane BadawczeThe dataset contains the Xray Photoelectron Spectroscopy results of the studies performed under different conditions of surface activation of the CB-PLA 3D printed electrodes. The activation was performed by hydrolysis in different solvents (DMF, 1M HCl, 1M NaOH), electrolysis in 1M NaOH, enzymatic treatment in polymerase or simultaneous electrolysis...
-
XPS analysis of the GO based materials
Dane BadawczeGraphene oxides samples were measured by XPS method. The X-ray photoemission spectroscopy measurements were carried out with Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The photoelectrons...
-
New 3D printable filaments with nanodiamonds, physicochemical additives characteristics and electrochemical activity
Dane BadawczeThis dataset contains the physicochemical analyses (XRD, Raman spectroscopy, BET analyses) and electrochemical analyses (CV, EIS) for a new 3D-printable composite has been developed dedicated to electroanalytical applications. Two types of diamondised nanocarbons - detonation nanodiamonds (DNDs) and boron-doped carbon nanowalls (BCNWs) - were added...
-
Optical properties of tellurium dioxide thin films
Dane BadawczeTeO2 and TeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by optical spectroscopy. Metallic Te target and Te-Eu mosaic target with diameter of 50.8 mm were sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate...
-
Chemical composition of La-Sr-Ce-Ni-Ti ceramics material measured by XPS method
Dane BadawczeLa-Sr-Ce-Ni-Ti (LSCNT) based ceramics sample was manufactured by standard solid state reaction.Prepared powder was pressed into pilled and sintered in a furnace in air atmosphere for 10h. Annealing temperature was 1200 Celsius degree. To calculate chemical composition and determine valence states of the elements, X-Ray photoemission spectroscopy (XPS)...
-
Graphene oxide thin films deposited on a PCB board - chemical analysis
Dane BadawczeGraphene oxides based films were measured by X-ray photoemission spectroscopy (XPS) method. TheXPS measurements were carried out with the Omicron NanoTechnology UHV equipment. The hemispherical spectrophotometer was equipped with a 128-channel collector. The XPS measurements were performed at room temperature at a pressure below 1.1 × 10−8 mBar. The...
-
Plasmon resonance in gold-silver nanoalloys
Dane BadawczeSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Investigation of plasmon resonance in a silver nanoparticles
Dane BadawczeSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
Study of the chemical state of Gd in a Ba-La-Gd-Co based ceramic
Dane BadawczeBarium, Lanthanum, Gadolinium and Cobaltium precursors were used for production of ceramic materials. Samples were produced by standard solid state reaction. Samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing on a Gadolinum were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology....
-
FTIR spectra and IGC chromatograms for chemically reduced graphene oxide aerogels (rGOA)
Dane BadawczeThe effect of selected synthesis parameters on reduced graphene oxide aerogels properties was investigated using Fourier-transform infrared spectroscopy and dynamic adsorption method (Inverse Gas Chromatography, IGC). Samples were synthesized by sol-gel method by reduction induced self-assembly of graphene oxide. As a reductant l-ascorbic acid was used....
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Dane BadawczeElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Influence of the annealing condictions on the chemical structure of LaBaGdCo ceramics
Dane BadawczeCeramic samples based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by solid state reaction. After sintring in a furnance, samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology. XPS analysis...
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Dane BadawczeElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
Raman data of deuterium and hydrogen grown boron-doped diamond
Dane BadawczeRaman spectra were recorded at room temperature using a micro-Raman spectrometer (Invia, Renishaw) equipped with an edge filter with different excitation wavelengths and lasers: UV λ = 325 nm (HeCd), blue λ = 488 nm (Ar+), green λ = 514 nm (Ar+), and IR λ = 785 nm (IR diode) and 50× microscope objective. To avoid sample heating, the radiation power...
-
The changes of outlet gases concentrations from SOFC with Ce(Pr,Sm)O2-s layers
Dane BadawczeThe dataset includes The changes of outlet gases concentrations from SOFC with Ce(Pr,Sm)O2-s layers. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Dane BadawczeThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
Valence state of Manganium in a MnCoO ceramics
Dane BadawczeManganium -cobalt based ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. In order to determine valence states of the Mn, X-Ray photoemission...
-
Lanthanum investigations in ceramics annealed in a dry and wet atmosphere
Dane BadawczeCeramics based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by standard solid state reaction from oxides and carbonate powders. After sintring, samples were annealed for 2 hours or 72 hours at 300 Celsius degree in a both: wet and dry atmosphere. Results of annealing on a chemical composition and valence state of lanthanum were observed...
-
XPS analysis of TBBO glass
Dane BadawczeGlasses and glass-ceramics with nominal composition 73 TeO2– 4BaO– 3Bi2O3–18SrF2-2RE2O3 (where RE = Eu, Dy) have been synthesized by conventional melt-quenching technique and subsequent heat treatment at 370 °C for 24 h in air atmosphere. Various Eu3+ to Dy3+ molar ratio have been applied to investigate luminescence properties in both glass and glass-ceramic...
-
Austenitic stainless steel sensitization
Dane BadawczeHigh-alloy steels, thanks to their composition and content of appropriate alloying additives, are characterized by increased resistance to many corrosive environments. However, this is due to the increased sensitivity of the described construction materials to specific environmental conditions during their use. An example may be the increased susceptibility...
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Dane BadawczeData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.