Wyszukiwarka
Filtry
wszystkich: 9368
wybranych: 1168
-
Katalog
- Publikacje 1378 wyników po odfiltrowaniu
- Osoby 361 wyników po odfiltrowaniu
- Wynalazki 179 wyników po odfiltrowaniu
- Projekty 541 wyników po odfiltrowaniu
- Laboratoria 16 wyników po odfiltrowaniu
- Zespoły Badawcze 82 wyników po odfiltrowaniu
- Aparatura Badawcza 40 wyników po odfiltrowaniu
- Kursy Online 5603 wyników po odfiltrowaniu
- Dane Badawcze 1168 wyników po odfiltrowaniu
Filtry wybranego katalogu
wyświetlamy 1000 najlepszych wyników Pomoc
Wyniki wyszukiwania dla: A*
-
Compression test results of fused filamend fabricated polylactyde and polylactyde with carbon fiber filler
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of cube specimens with dimensions 30 x 30 x 30 cm3. The specimens were additively manufactured with the fused filament fabrication (FFF) method. They used two different materials polylactide (PURE PLA) and polylactide with carbon fibre filler (PLA+CF). The specimens were segregated into three...
-
Tensile test results of fused filamend fabricated polylactyde and polylactyde with carbon fiber filler
Dane BadawczeThe Dataset contains the results of the mechanical behaviour of dog-bone shaped specimens. The specimens were additively manufactured with the fused filament fabrication (FFF) method. They used two different materials polylactide (PURE PLA) and polylactide with carbon fibre filler (PLA+CF). The specimens were segregated into three groups - unsterilized,...
-
Reflectance Measurements and iCone Calorimeter Burning Results of Charcoals Derived from Lake Żabińskie (North-Eastern Poland)
Dane BadawczeThe dataset presents the results of litter burning experiments using an iCone calorimeter to assess the flammability of the major tree species in the Lake Żabińskie catchment (NE Poland) and links this to the heat release during burning to understand the influence of fire and its effects on ecosystems. Samples of litter from Betula pendula, Pinus sylvestris,...
-
Measurements of ultrasonic bulk and guided wave propagation in additively manufactured cubes and plates obtained by ultrasonic pulse velocity analyzer and scanning laser vibrometry
Dane BadawczeThe DataSet contains the results of measurements of ultrasonic wave propagation in additively manufactured samples made of polylactic acid (PLA). Three types of raster angles in two consecutive layers were assumed: 0°/90° (#1), 45°/-45° (#2) and 90°/90° (#3) with respect to the x-axis. For each printing variants a cubic sample (#C1-3) with dimensions...
-
Nanoindentation tests of the hydroxyapatite composite coatings applicated on titanium alloys by the electrophoretic method
Dane BadawczeCurrently, there are no metal materials that meet all biomechanical and biochemical requirements needed for long life implantable biomaterials. The main purpose of the study was to functionalize the surface of the titanium alloys used in biomaterial implants.
-
Data gathered in the course of therapeutic sessions carried out with patients suffering from acquired brain damages
Dane BadawczeThe dataset contains signals gathered in the course of therapeutic sessions carried out with patients suffering from acquired brain damages. Participants’ actions were monitored with an eye-gaze tracking (EGT) device and with an electroencephalogram EEG monitoring headset.
-
SEM micrographs of the austenitic stainless steel corrosion in asphalt fumes
Dane BadawczeThe dataset contains the scanning electron microscopy (SEM) studies of the austenitic stainless steels: AISI 304, AISI 316, AISI 321 and duplex stainless steel AISI 2205. The samples were polished and exposed to the installation carrying asphalt fumes at elevated temperatures (approx. ~210-240 Celsius). The exposition duration was three months. Some...
-
Displacements of bones during bending test of first metatarsophalangeal joint after arthrodesis with medially or dorsally positioned locking plate and lag screw.
Dane BadawczeThe Dataset contains the values of displacements of bone control points during the bending test of first metatarsophalangeal (MTP1) joint specimens after arthrodesis.
-
Bending test results of first metatarsophalangeal joint after arthrodesis with medially or dorsally positioned locking plate and lag screw.
Dane BadawczeThe Dataset contains the results of the bending test of first metatarsophalangeal (MTP1) joint specimens after arthrodesis.
-
The influence of chitosan hydrogels on the morphology of L929 cells
Dane BadawczeRepresentative image at 20x magnification of L929 cells following 24 h of treatment with chitosan derivatives: chitosan dissolved in carbonic acid, chitosan dissolved in carbonic acid endotoxin free, chitosan dissolved in hydroacetic acid at 1:3 diluent factor. The scale bar is 100 µm; Microscope Olympus IX83, Tokyo, Japan).
-
Cytotoxicity of chitosan hydrogels aginst L929 cells
Dane BadawczeThis study presents absorbance values of formazan product (converted from MTT) which corresponds to the cytotoxicity of chitosan compounds (dissolved in carbonic acid, dissolved in carbonic acid endotoxin free, and dissolved in hydroxyacetic acid) aginst adult mouse fibroblast L929 cells. The experiments were carried out according to the ISO 10993-5:2009(E)...
-
Long-term measurements from a photovoltaic power plant and meteorological stations at the Laboratory LINTE^2 of Gdańsk University of Technology
Dane Badawcze1) The Laboratory LINTE^2 is a large research infrastructure operated by the Faculty of Electrical and Control Engineering at Gdańsk University of Technology, to be found in Gdańsk, Poland (54.3690 N, 18.6130 E). 2) The measurements have been collected from a photovoltaic power plant located on the roof of the laboratory, having total capacity...
-
Acoustic emission signals in concrete beams under 3-point bending (polyolefin and steel fibre concrete)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of concrete beams with dimensions 40 x 40 x 160 cm3 under the 3-point bending. All specimens were manufactured based on the same concrete mixture composed of cement CEM I 42.5R (380 kg/m3), water (165 kg/m3), aggregate 0/2 mm (648 kg/m3), aggregate 2/8 mm (426 kg/m3), aggregate 8/16 mm (754...
-
Acoustic emission signals in concrete beams under 3-point bending (plain concrete, steel fibre reinforced concrete, steel bar reinforced concrete)
Dane BadawczeThe DataSet contains the results of the mechanical behaviour of concrete beams with dimensions 40 x 40 x 160 cm3under the 3-point bending. Two concrete mixes, both based on the same design, were produced in the test programme. Mixture #1 was the plain concrete (PC), consisting of cement CEM I 42.5R (380 kg/m3), water (165 kg/m3), aggregate 0/2 mm (648...
-
The corrosion studies of 3,4,5-trihydroxybenzoic acid as an effective corrosion inhibitor of low alloy steel
Dane BadawczeThe dataset contains the electrochemical studies evaluating if gallic acid is a corrosion inhibitor for low alloy steel. Three measurements were carried out each case; corrosion potential (label ecorr), electrochemical impedance spectroscopy (label eis) and cyclic polarization (label cp). The measurements were carried out in sodium chloride, acidified...
-
Self-Censorship in a Workplace: The Role of Gender, Management Position, Procedural Justice and Organizational Climate
Dane BadawczeData consist of three studies. In study 1 (N = 948) we test whether women manifest more self-censorship than men and we verify whether this effect is maintained when women and men hold managerial position. Then, we analyse the effects of procedural justice (study 2, N = 98) and communal organizational climate (study 3, N = 567) on women’s and men’s...
-
The influence of chitosan hydrogel cross-linking by agarose on coating physico-chemical properties
Dane BadawczeThis dataset contains various physicochemical analyses showing the effect of different concentration of chitosan and the cross-linking agent agarose. Each sample is labeled by C and A representing chitosan and agarose concentrations, respectively, while the exact amounts are depicted in the attached table. Fourier-transform infrared (FT-IR) spectroscopy...
-
The influence of chitosan hydrogel coating on different redox probes kinetics
Dane BadawczeThis dataset contains cyclic voltammetry studies of three redox probes: 1 mM K3[Fe(CN)6], [K4Fe(CN)6], C12H14FeO2, and [Ru(NH3)6]Cl2 dissolved in 0.1 M KCl or PBS as the primary electrolyte. The studies are made for glassy carbon electrode (GC) and glassy carbon electrode covered with thin chitosan hydrogel membrane (C2A2). Cyclic voltammograms were...
-
The results of the assessment of the degree of deacetylation, antimicrobial activity and cytotoxicity of chitosan materials
Dane BadawczeDane prezentują wyniki pomiarowe stopnia deacetylacji 5 komerycjnych chitozanów, które przetwarzane dwiema metodami oceniono pod kątem aktywności przeciwdrobnoustrojowej i cytotoksyczności względem modelowej linii fibroblastów mysich L929. Ocenie porównawczej poddano materiały chitozanowe otrzymywane klasyczną metodą rozpuszczania w roztworze...
-
Absorption and fluorescence spectra of 1,8-diazafluoren-9-one (DFO) in PVA polymer for different concentrations
Dane BadawczeAbsorption and fluorescence spectra of 1,8-diazafluoren-9-one (DFO) in PVA film for different concentrations of dye.
-
Spectroscopy properties of 1,8-diazafluoren-9-one (DFO) in PVA polymer for different concentrations
Dane BadawczeSpectroscopy properties: absorption and fluorescence spectra of 1,8-diazafluoren-9-one (DFO) in PVA film for different concentrations of dye.
-
Rheology studies of multiple times processed poly(lactic acid)-carbon black composites
Dane BadawczeThis dataset contains MFR/MVR (melt flow rate) rheology studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The study aims to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials after reduction at 900 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-preapred (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials after reduction at 900 deg.C in hydrogen
Dane BadawczeThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) powder materials synthesized via the Pechini method after reduction in hydrogen at 900C for 10h.
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co)
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co) were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
Sequencing results and other data presented in article published in Applied Microbiology and Biotechnology
Dane BadawczeThis folder contains sequences of the strains SzA14, SzA16 and SzB3. Other data presented in the article published in Applied Microbiology and Biotechnology have been also included.
-
Topography of iron-phosphate glasses doped with niobium and titanium tested by confocal microscope
Dane BadawczeThe topography of phosphate-iron glasses containing niobium and titanium were investigated with the use of confocal miscroscope. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5, 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 and 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents...
-
Analysis of the Water Level Variation at the Polish Part of the Vistula Lagoon (2008-2017)
Dane BadawczeThe dataset consists of the following data:
-
Effect of process parameters on food waste conversion - dataset 1
Dane BadawczeData obtained during studies (food waste pretreatment and conversion), describing the effect of process parameters (sonocavitation) on food waste conversion.
-
The influence of microstructure on the corrosion resistance for some titanium-based alloys
Dane BadawczeThis dataset contains scanning electron microscopy (SEM) micrographs revealing the microstructure of some Ti-based alloys, namely: Ti-6Al-4V (file name: TiV), Ti-6Al-7Nb (file name: TiNb) and TC21 (file name: TiAlSnZrMoCrNbSi) alloys and their localized corrosion as a result of passive layer breakdown in a corrosive environment, ie. 0.9% NaCl solution...
-
A set of data constituting the basis for the publication entitled "Mitochondria dysfunction is one of the causes of diclofenac toxicity in the green alga Chlamydomonas reinhardtii"
Dane BadawczeNon-steroidal anti-inflammatory drugs (NSAIDs), such as diclofenac (DCF), form a significant group of environmental contaminants. When the toxic effects of DCF on plants are analyzed, authors often focus on photosynthesis, whilemitochondrial respiration is usually overlooked. Therefore, an in vivo investigation of plant mitochondria functioning under...
-
The complete list of two-dimensional number-conserving ternary cellular automata
Dane BadawczeThis dataset contains a complete list of all 1327 two-dimensional number-conserving cellular automata with the state set {0,1,2} (the so-called ternary cellular automata) based on adjacent cells only, i.e. with the von Neumann neighborhood. The detailed definitions and the method of enumerating are given in the paper:
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B48/#A45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B37/#A35
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B21/#A21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 25 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B41/#A39
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A39/#B41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A23/#B22
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 12 min. The...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A35/#B37
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B39/#A41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#A47
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 20 min. The test...